Abstract
Core–shell nanocatalysts have demonstrated potential as highly active low-Pt fuel cell cathodes for the oxygen reduction reaction (ORR); however, challenges remain in optimizing their surface and interfacial structures, which often exhibit undesirable structural degradation and poor durability. Here, we construct an unsupported nanoporous catalyst with a Pt–Pd shell of sub-nanometre thickness on Au, which demonstrates an initial ORR activity of 1.140 A mgPt−1 at 0.9 V. The activity increases to 1.471 A mgPt−1 after 30,000 potential cycles and is stable over a further 70,000 cycles. Using aberration-corrected scanning transmission electron microscopy and atomically resolved elemental mapping, the origin of the activity change is revealed to be an atomic-scale evolution of the shell from an initial Pt–Pd alloy into a bilayer structure with a Pt-rich trimetallic surface, and finally into a uniform and stable Pt–Pd–Au alloy. This Pt–Pd–Au alloy possesses a suitable configuration for ORR, giving a relatively low free energy change for the final water formation from adsorbed OH intermediate during the reaction.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 12 digital issues and online access to articles
$119.00 per year
only $9.92 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
References
Vielstich, W., Lamm, A. & Gasteiger, H. A. Handbook of Fuel Cells, Fundamentals Technology and Applications (Wiley, 2003).
Lim, B. et al. Pd-Pt bimetallic nanodendrites with high activity for oxygen reduction. Science 324, 1302–1305 (2009).
Tian, N., Zhou, Z. Y., Sun, S. G., Ding, Y. & Wang, Z. L. Synthesis of tetrahexahedral platinum nanocrystals with high-index facets and high electro-oxidation activity. Science 316, 732–735 (2007).
Wu, J. B. et al. Truncated octahedral Pt3Ni oxygen reduction reaction electrocatalysts. J. Am. Chem. Soc. 132, 4984–4985 (2010).
Stamenkovic, V. R., Mun, B. S., Mayrhofer, K. J. J., Ross, P. N. & Markovic, N. M. Effect of surface composition on electronic structure, stability, and electrocatalytic properties of Pt-transition metal alloys: Pt-skin versus Pt-skeleton surfaces. J. Am. Chem. Soc. 128, 8813–8819 (2006).
Stamenkovic, V. R. et al. Trends in electrocatalysis on extended and nanoscale Pt-bimetallic alloy surfaces. Nat. Mater. 6, 241–247 (2007).
Stamenkovic, V. R. et al. Improved oxygen reduction activity on Pt3Ni(111) via increased surface site availability. Science 315, 493–497 (2007).
Strasser, P. et al. Lattice-strain control of the activity in dealloyed core-shell fuel cell catalysts. Nat. Chem. 2, 454–460 (2010).
Cui, C. H., Gan, L., Heggen, M., Rudi, S. & Strasser, P. Compositional segregation in shaped Pt alloy nanoparticles and their structural behaviour during electrocatalysis. Nat. Mater. 12, 765–771 (2013).
Huang, X. Q. et al. High-performance transition metal-doped Pt3Ni octahedra for oxygen reduction reaction. Science 348, 1230–1234 (2015).
Chen, Z. W., Waje, M., Li, W. Z. & Yan, Y. S. Supportless Pt and Pt–Pd nanotubes as electrocatalysts for oxygen-reduction reactions. Angew. Chem. Int. Ed. 46, 4060–4063 (2007).
Zhang, L. et al. Platinum-based nanocages with subnanometer-thick walls and well-defined, controllable facets. Science 349, 412–416 (2015).
Wang, X. et al. Palladium–platinum core-shell icosahedra with substantially enhanced activity and durability towards oxygen reduction. Nat. Commun. 6, 7594 (2015).
Wang, X. et al. Pd@Pt core–shell concave decahedra: a class of catalysts for the oxygen reduction reaction with enhanced activity and durability. J. Am. Chem. Soc. 137, 15036–15042 (2015).
Gong, K. P., Su, D. & Adzic, R. R. Platinum-monolayer shell on AuNi0.5Fe nanoparticle core electrocatalyst with high activity and stability for the oxygen reduction reaction. J. Am. Chem. Soc. 132, 14364–14366 (2010).
Wang, C. et al. Multimetallic Au/FePt3 nanoparticles as highly durable electrocatalyst. Nano Lett. 11, 919–926 (2011).
Zhang, J., Sasaki, K., Sutter, E. & Adzic, R. R. Stabilization of platinum oxygen-reduction electrocatalysts using gold clusters. Science 315, 220–222 (2007).
Sasaki, K. et al. Highly stable Pt monolayer on PdAu nanoparticle electrocatalysts for the oxygen reduction reaction. Nat. Commun. 3, 1115 (2012).
Chen, A. C. & Holt-Hindle, P. Platinum-based nanostructured materials: synthesis, properties, and applications. Chem. Rev. 110, 3767–3804 (2010).
Yu, T., Kim, D. Y., Zhang, H. & Xia, Y. N. Platinum concave nanocubes with high-index facets and their enhanced activity for oxygen reduction reaction. Angew. Chem. Int. Ed. 50, 2773–2777 (2011).
Chen, C. et al. Highly crystalline multimetallic nanoframes with three-dimensional electrocatalytic surfaces. Science 343, 1339–1343 (2014).
Koenigsmann, C. et al. Enhanced electrocatalytic performance of processed, ultrathin, supported Pd-Pt core-shell nanowire catalysts for the oxygen reduction reaction. J. Am. Chem. Soc. 133, 9783–9795 (2011).
Wang, J. X. et al. Oxygen reduction on well-defined core-shell nanocatalysts: particle size, facet, and Pt shell thickness effects. J. Am. Chem. Soc. 131, 17298–17302 (2009).
Adzic, R. R. Platinum monolayer electrocatalysts: tunable activity, stability, and self-healing properties. Electrocatalysis 3, 163–169 (2012).
Zhao, X. et al. Octahedral Pd@Pt1.8Ni core-shell nanocrystals with ultrathin PtNi alloy shells as active catalysts for oxygen reduction reaction. J. Am. Chem. Soc. 137, 2804–2807 (2015).
Weissmüller, J. et al. Charge-induced reversible strain in a metal. Science 300, 312–315 (2003).
Snyder, J., Fujita, T., Chen, M. W. & Erlebacher, J. Oxygen reduction in nanoporous metal-ionic liquid composite electrocatalysts. Nat. Mater. 9, 904–907 (2010).
Xing, Y. C. et al. Enhancing oxygen reduction reaction activity via Pd-Au alloy sublayer mediation of Pt monolayer electrocatalysts. J. Phys. Chem. Lett. 1, 3238–3242 (2010).
Liu, P. P., Ge, X. B., Wang, R. Y., Ma, H. Y. & Ding, Y. Facile fabrication of ultrathin Pt overlayers onto nanoporous metal membranes via repeated Cu UPD and in situ redox replacement reaction. Langmuir 25, 561–567 (2009).
Bliznakov, S. T., Vukmirovic, M. B., Yang, L., Sutter, E. A. & Adzic, R. R. Pt monolayer on electrodeposited Pd nanostructures: advanced cathode catalysts for PEM fuel cells. J. Electrochem. Soc. 159, F501–F506 (2012).
Kuttiyiel, K. A. et al. Pt monolayer on Au-stabilized PdNi core-shell nanoparticles for oxygen reduction reaction. Electrochim. Acta 110, 267–272 (2013).
Chen, G. X. et al. Interfacial effects in iron-nickel hydroxide–platinum nanoparticles enhance catalytic oxidation. Science 344, 495–499 (2014).
Najmaei, S. et al. Vapour phase growth and grain boundary structure of molybdenum disulphide atomic layers. Nat. Mater. 12, 754–759 (2013).
Sun, Y. et al. Direct atomic-scale confirmation of three-phase storage mechanism in Li4Ti5O12 anodes for room-temperature sodium-ion batteries. Nat. Commun. 4, 1870 (2013).
Chen, C. C. et al. Three-dimensional imaging of dislocations in a nanoparticle at atomic resolution. Nature 496, 74–77 (2013).
Xu, R. et al. Three-dimensional coordinates of individual atoms in materials revealed by electron tomography. Nat. Mater. 14, 1099–1103 (2015).
Jiang, Y. et al. Direct atom-by-atom chemical identification of nanostructures and defects of topological insulators. Nano Lett. 13, 2851–2856 (2013).
Kothleitner, G. et al. Quantitative elemental mapping at atomic resolution using X-ray spectroscopy. Phys. Rev. Lett. 112, 085501 (2014).
Gan, L. et al. Element-specific anisotropic growth of shaped platinum alloy nanocrystals. Science 346, 1502–1506 (2014).
Fuel Cell Technologies Office Multi-Year Research, Development, and Demonstration Plan Section 3.4 (Office of Energy Efficiency and Renewable Energy, 2016).
Wanjala, B. N. et al. Nanoscale alloying, phase-segregation, and core-shell Evolution of gold-platinum nanoparticles and their electrocatalytic effect on oxygen reduction reaction. Chem. Mater. 22, 4282–4294 (2010).
Koenigsmann, C., Sutter, E., Chiesa, T. A., Adzic, R. R. & Wong, S. S. Highly enhanced electrocatalytic oxygen reduction performance observed in bimetallic palladium-based nanowires prepared under ambient, surfactantless conditions. Nano Lett. 12, 2013–2020 (2012).
Wang, G. W. et al. Pt skin on AuCu intermetallic substrate: a strategy to maximize Pt utilization for fuel cells. J. Am. Chem. Soc. 136, 9643–9649 (2014).
Bian, T. et al. Epitaxial growth of twinned Au-Pt core-shell star-shaped decahedra as highly durable electrocatalysts. Nano Lett. 15, 7808–7815 (2015).
Shen, L. L., Zhang, G. R., Miao, S., Liu, J. Y. & Xu, B. Q. Core-shell nanostructured Au@NimPt2 electrocatalysts with enhanced activity and durability for oxygen reduction reaction. ACS Catal. 6, 1680–1690 (2016).
Jewell, S. & Kimball, S. M. Mineral Commodity Summaries 2016 (US Geological Survey and US Department of the Interior, 2016).
Massalski, T. B. in Binary Alloy Phase Diagrams Second Edition Plus Updates (eds Okamoto, H., Subramanian, P. R. & Kacprzak, L. ) 8033 (ASM International, 1996).
Alonso, C. et al. The evaluation of surface diffusion coefficients of gold and platinum atoms at electrochemical interfaces from combined STM-SEM imaging and electrochemical techniques. J. Electrochem. Soc. 137, 2161–2166 (1990).
Nørskov, J. K. et al. Origin of the overpotential for oxygen reduction at a fuel-cell cathode. J. Phys. Chem. B 108, 17886–17892 (2004).
Keith, J. A. & Jacob, T. Theoretical studies of potential-dependent and competing mechanisms of the electrocatalytic oxygen reduction reaction on Pt(111). Angew. Chem. Int. Ed. 49, 9521–9525 (2010).
Serrano, J., Rubio, A., Hernández, E., Muñoz, A. & Mujica, A. Theoretical study of the relative stability of structural phases in group-III nitrides at high pressures. Phys. Rev. B 62, 16612–16623 (2000).
Knudsen, J. et al. A Cu/Pt near-surface alloy for water-gas shift catalysis. J. Am. Chem. Soc. 129, 6485–6490 (2007).
Andersson, K. J., Calle-Vallejo, F., Rossmeisl, J. & Chorkendorff, I. Adsorption-driven surface segregation of the less reactive alloy component. J. Am. Chem. Soc. 131, 2404–2407 (2009).
Attard, G. A. & Brew, A. Cyclic voltammetry and oxygen reduction activity of the Pt{110}-(1 × 1) surface. J. Electroanal. Chem. 747, 123–129 (2015).
Stephens, I. E. L., Bondarenko, A. S., Grønbjerg, U., Rossmeisl, J. & Chorkendorff, I. Understanding the electrocatalysis of oxygen reduction on platinum and its alloys. Energy Environ. Sci. 5, 6744–6762 (2012).
Calle-Vallejo, F. et al. Finding optimal surface sites on heterogeneous catalysts by counting nearest neighbors. Science 350, 185–189 (2015).
Greeley, J. et al. Alloys of platinum and early transition metals as oxygen reduction electrocatalysts. Nat. Chem. 1, 552–556 (2009).
Yan, X. J. et al. Atomic layer-by-layer construction of Pd on nanoporous gold via underpotential deposition and displacement reaction. RSC Adv. 5, 19409–19417 (2015).
Egerton, R. F. Electron Energy-Loss Spectroscopy in the Electron Microscope 3rd edn (Springer, 2011).
Li, C. et al. Dynamic observation of oxygen vacancies in hafnia layer by in situ transmission electron microscopy. Nano Res. 8, 3571–3579 (2015).
Galindo, P. L. et al. The Peak Pairs algorithm for strain mapping from HRTEM images. Ultramicroscopy 107, 1186–1193 (2007).
Sales, D. L. et al. Critical strain region evaluation of self-assembled semiconductor quantum dots. Nanotechnology 18, 475503 (2007).
Goedecker, S., Teter, M. & Hutter, J. Separable dual-space Gaussian pseudopotentials. Phys. Rev. B 54, 1703–1710 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Tripković, V., Skúlason, E., Siahrostami, S., Nørskov, J. K. & Rossmeisl, J. The oxygen reduction reaction mechanism on Pt(111) from density functional theory calculations. Electrochim. Acta 55, 7975–7981 (2010).
Lide, D. R. CRC Handbook of Chemistry and Physics (CRC Press, 2003).
Li, Y. F., Liu, Z. P., Liu, L. L. & Gao, W. G. Mechanism and activity of photocatalytic oxygen evolution on titania anatase in aqueous surroundings. J. Am. Chem. Soc. 132, 13008–13015 (2010).
Bajdich, M., García-Mota, M., Vojvodic, A., Nørskov, J. K. & Bell, A. T. Theoretical investigation of the activity of cobalt oxides for the electrochemical oxidation of water. J. Am. Chem. Soc. 135, 13521–13530 (2013).
Acknowledgements
We thank JEOL Ltd. and FEI Ltd. for their generous supports to the STEM and EDS analyses. This work was financially supported by the National 973 Program Project of China (2012CB932800), the National Natural Science Foundation of China (51572016, 51671145 and U1530401), the National Program for Thousand Young Talents of China, the Tianjin Municipal Education Commission, the Tianjin Municipal Science and Technology Commission, and the Fundamental Research Funds of Tianjin University of Technology. Y.D. also acknowledges the Fundamental Research Funds of Shandong University for sponsoring this research. J.Luo acknowledges useful discussions with X. Ke. L.-M.L. gratefully acknowledges the computational support from the Beijing Computational Science Research Center (CSRC) and Guangdong Supercomputer.
Author information
Authors and Affiliations
Contributions
Y.D., J.Luo and L.-M.L. co-supervised the whole work. Y.D. conceived and designed the electrocatalysts and the electrochemical experiments. J.Li and W.-X.W. performed the sample preparation and the electrochemical experiments. X.-B.L. performed the first-principles calculations, to which Z.-K.T. contributed. L.-M.L. conducted and analysed the calculations. J.Luo proposed the STEM and elemental mapping experiments and performed the analysis and evaluation thereof, to which C.L., Y.G., L.G. and S.M. contributed. E.O. and E.Y. operated the aberration-corrected JEOL and FEI STEM instruments, respectively. Y.D., H.-M.Y. and J.Li analysed the results of the electrochemical experiments, and Y.-L.S. and J.H. contributed to the discussion thereof. J.Li, H.-M.Y., Y.D., J.Luo and L.-M.L. prepared the figures and co-wrote the manuscript. All authors discussed the results, drew conclusions and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Methods, Supplementary Tables 1–3, Supplementary Figures 1–17. (PDF 11139 kb)
Supplementary Data 1
POSCAR file containing information on the supercell and atomic positions for the DFT calculations with Pt. (XLS 67 kb)
Rights and permissions
About this article
Cite this article
Li, J., Yin, HM., Li, XB. et al. Surface evolution of a Pt–Pd–Au electrocatalyst for stable oxygen reduction. Nat Energy 2, 17111 (2017). https://doi.org/10.1038/nenergy.2017.111
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/nenergy.2017.111
This article is cited by
-
Identifying the distinct roles of dual dopants in stabilizing the platinum-nickel nanowire catalyst for durable fuel cell
Nature Communications (2024)
-
Emerging strategies and developments in oxygen reduction reaction using high-performance platinum-based electrocatalysts
Nano Research (2024)
-
Overcoming the Electrode Challenges of High-Temperature Proton Exchange Membrane Fuel Cells
Electrochemical Energy Reviews (2023)
-
Atomic scale visualizations of low-angle grain boundary mediated plasticity by coupled dislocation climb and glide in nanoporous gold
Nano Research (2023)
-
PtCu subnanoclusters epitaxial on octahedral PtCu/Pt skin matrix as ultrahigh stable cathode electrocatalysts for room-temperature hydrogen fuel cells
Nano Research (2023)