Abstract
Semiconductor nanowires are promising for photovoltaic applications1,2,3,4,5,6,7,8,9,10,11, but, so far, nanowire-based solar cells have had lower efficiencies than planar cells made from the same materials6,7,8,9,10,12,13, even allowing for the generally lower light absorption of nanowires. It is not clear, therefore, if the benefits of the nanowire structure, including better charge collection and transport14 and the possibility of enhanced absorption through light trapping4,15, can outweigh the reductions in performance caused by recombination at the surface of the nanowires and at p–n junctions. Here, we fabricate core–shell nanowire solar cells with open-circuit voltage and fill factor values superior to those reported for equivalent planar cells, and an energy conversion efficiency of ∼5.4%, which is comparable to that of equivalent planar cells despite low light absorption levels16. The device is made using a low-temperature solution-based cation exchange reaction17,18,19,20,21 that creates a heteroepitaxial junction between a single-crystalline CdS core and single-crystalline Cu2S shell. We integrate multiple cells on single nanowires in both series and parallel configurations for high output voltages and currents, respectively. The ability to produce efficient nanowire-based solar cells with a solution-based process and Earth-abundant elements22,23,24 could significantly reduce fabrication costs relative to existing high-temperature bulk material approaches.
This is a preview of subscription content, access via your institution
Access options
Subscribe to this journal
Receive 12 print issues and online access
$259.00 per year
only $21.58 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
References
Huynh, W. U., Dittmer, J. J. & Alivisatos, A. P. Hybrid nanorod–polymer solar cells. Science 295, 2425–2427 (2002).
Gur, I., Fromer, N. A., Geier, M. L. & Alivisatos, A. P. Air-stable all-inorganic nanocrystal solar cells processed from solution. Science 310, 462–465 (2005).
Wu, Y. et al. Synthesis and photovoltaic application of copper(I) sulfide nanocrystals. Nano Lett. 8, 2551–2555 (2008).
Garnett, E. & Yang, P. Light trapping in silicon nanowire solar cells. Nano Lett. 10, 1082–1087 (2010).
Law, M. et al. Nanowire dye-sensitized solar cells. Nature Mater. 4, 455–459 (2005).
Tian, B. et al. Coaxial silicon nanowires as solar cells and nanoelectronic power sources. Nature 449, 885–889 (2007).
Czaban, J. A., Thompson, D. A. & LaPierre, R. R. GaAs core–shell nanowires for photovoltaic applications. Nano Lett. 9, 148–154 (2008).
Kelzenberg, M. D. et al. Photovoltaic measurements in single-nanowire silicon solar cells. Nano Lett. 8, 710–714 (2008).
Kempa, T. J. et al. Single and tandem axial p-i-n nanowire photovoltaic devices. Nano Lett. 8, 3456–3460 (2008).
Dong, Y., Tian, B., Kempa, T. J. & Lieber, C. M. Coaxial group III-nitride nanowire photovoltaics. Nano Lett. 9, 2183–2187 (2009).
Fan, Z. et al. Three-dimensional nanopillar-array photovoltaics on low-cost and flexible substrates. Nature Mater. 8, 648–653 (2009).
Goto, H. et al. Growth of core–shell InP nanowires for photovoltaic application by selective-area metal organic vapor phase epitaxy. Appl. Phys. Express 2, 035004 (2009).
Wei, W. et al. Direct heteroepitaxy of vertical InAs nanowires on Si substrates for broad band photovoltaics and photodetection. Nano Lett. 9, 2926–2934 (2009).
Kayes, B. M., Atwater, H. A. & Lewis, N. S. Comparison of the device physics principles of planar and radial p–n junction nanorod solar cells. J. Appl. Phys. 97, 114302 (2005).
Cao, L. et al. Resonant germanium nanoantenna photodetectors. Nano Lett. 10, 1229–1233 (2010).
Martinuzzi, S. Trends and problems in cadmium sulfide (CdS)/copper sulfide (CuxS) thin film solar cells: a review. Sol. Cells 5, 243–268 (1982).
Son, D. H., Hughes, S. M., Yin, Y. & Paul Alivisatos, A. Cation exchange reactions in ionic nanocrystals. Science 306, 1009–1012 (2004).
Robinson, R. D. et al. Spontaneous superlattice formation in nanorods through partial cation exchange. Science 317, 355–358 (2007).
Luther, J. M., Zheng, H., Sadtler, B. & Alivisatos, A. P. Synthesis of PbS nanorods and other ionic nanocrystals of complex morphology by sequential cation exchange reactions. J. Am. Chem. Soc. 131, 16851–16857 (2009).
Sadtler, B. et al. Selective facet reactivity during cation exchange in cadmium sulfide nanorods. J. Am. Chem. Soc. 131, 5285–5293 (2009).
Jain, P. K., Amirav, L., Aloni, S. & Alivisatos, A. P. Nanoheterostructure cation exchange: anionic framework conservation. J. Am. Chem. Soc. 132, 9997–9999 (2010).
Trentler, T. J. et al. Solution–liquid–solid growth of crystalline III–V semiconductors: an analogy to vapor–liquid–solid growth. Science 270, 1791–1794 (1995).
Ouyang, L. et al. Catalyst-assisted solution–liquid–solid synthesis of CdS/CdSe nanorod heterostructures. J. Am. Chem. Soc. 129, 133–138 (2006).
Dong, A., Wang, F., Daulton, T. L. & Buhro, W. E. Solution–liquid–solid (SLS) growth of ZnSe–ZnTe quantum wires having axial heterojunctions. Nano Lett. 7, 1308–1313 (2007).
Lauhon, L. J., Gudiksen, M. S., Wang, D. & Lieber, C. M. Epitaxial core–shell and core–multishell nanowire heterostructures. Nature 420, 57–61 (2002).
Duan, X. F. & Lieber, C. M. General synthesis of compound semiconductor nanowires. Adv. Mater. 12, 298–302 (2000).
Li, Y. D. et al. Nonaqueous synthesis of CdS nanorod semiconductor. Chem. Mater. 10, 2301–2303 (1998).
Bragagnolo, J. A. et al. The design and fabrication of thin-film cadmium sulfide/copper(I) sulfide cells of 9.15% conversion efficiency. IEEE Trans. Electron. Dev. ED-27, 645–651 (1980).
Rothwarf, A. & Barnett, A. M. Design analysis of thin-film CdS–Cu2S solar-cell. IEEE Trans. Electron. Dev. 24, 381–387 (1977).
Bryant, F. J. & Glew, R. W. Analysis of the current–voltage characteristics of cadmium sulphide solar cells under varying light intensities. Ener. Convers. 14, 129–133 (1975).
MATLAB version R2008b (MathWorks Inc., 2008).
Barrett, S. D. Image SXM http://www.ImageSXM.org.uk (2008).
Acknowledgements
This work was supported by the Director, Office of Science, Office of Basic Energy Sciences, Materials Sciences and Engineering Division, of the US Department of Energy (contract no. DE-AC02-05CH11231). The work on devices integrated in parallel and in series was supported by the National Science Foundation (NSF, contract no. 0832819). The authors thank the National Center for Electron Microscopy for use of their facilities.
Author information
Authors and Affiliations
Contributions
J.T., Z.H. and P.Y. conceived and designed the experiments. J.T. fabricated the devices and performed the measurements. Z.H. collected and analysed the TEM images. S.B. was responsible for the scanning photocurrent mapping. H.G. provided the simulation results. J.T., Z.H. and P.Y. co-wrote the paper. All authors discussed the results and revised the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary information
Supplementary information (PDF 644 kb)
Rights and permissions
About this article
Cite this article
Tang, J., Huo, Z., Brittman, S. et al. Solution-processed core–shell nanowires for efficient photovoltaic cells. Nature Nanotech 6, 568–572 (2011). https://doi.org/10.1038/nnano.2011.139
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/nnano.2011.139
This article is cited by
-
Ultra-thin broadband solar absorber based on stadium-shaped silicon nanowire arrays
Frontiers of Optoelectronics (2022)
-
Organic white-light sources: multiscale construction of organic luminescent materials from molecular to macroscopic level
Science China Chemistry (2022)
-
Size and shape effects on effective mass, electronic and optical properties of V-shaped quantum dot: influence of an off-center donor atom, hydrostatic pressure and temperature
Journal of Computational Electronics (2022)
-
Organic superstructure microwires with hierarchical spatial organisation
Nature Communications (2021)