Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

  • Article
  • Published:

Imaging of nitrogen fixation at lithium solid electrolyte interphases via cryo-electron microscopy

Nature Energy volume 8, pages 138–148 (2023)Cite this article

Subjects

Abstract

Ammonia is an important industrial chemical and is also being discussed as a potential energy carrier. Electrifying ammonia synthesis could help to decarbonize the chemical industry, as the Haber–Bosch process contributes markedly to global carbon emissions. A lithium-mediated pathway is among the most promising ambient-condition electrochemical ammonia synthesis methods. However, the role of metallic lithium and its passivation layer, the solid electrolyte interphase (SEI), remains unresolved. Here we use cryogenic transmission electron microscopy as part of a multiscale approach to explore lithium reactivity and the SEI, discovering that the proton donor (for example, ethanol) governs lithium reactivity towards nitrogen fixation. Without ethanol, the SEI passivates lithium metal, rendering it inactive for nitrogen reduction. Ethanol disrupts this passivation layer, enabling continuous reactivity at the lithium surface. As a result, metallic lithium is consumed via reactions with nitrogen, proton donor and other electrolyte components. This reactivity across the SEI is vital to device-level performance of lithium-mediated ammonia synthesis.

This is a preview of subscription content, access via your institution

Access options

Buy this article

  • Purchase on Springer Link
  • Instant access to full article PDF
Buy now

Prices may be subject to local taxes which are calculated during checkout

Fig. 1: Previously proposed reaction mechanisms of lithium-mediated ammonia synthesis.
Fig. 2: Quantification of key products.
Fig. 3: Imaging results from the ‘no HA, N2’ and ‘EtOH, N2’ model systems.
Fig. 4: XPS results from the four model systems.
Fig. 5: SEI materials and their role in LiMEAS.

Similar content being viewed by others

Data availability

The data collected and analysed for this work are included in the paper and its Supplementary Information. Source data are provided with this paper.

References

  1. MacFarlane, D. R. et al. A roadmap to the ammonia economy. Joule 4, 1186–1205 (2020).

    Article  Google Scholar 

  2. Erisman, J. W., Sutton, M. A., Galloway, J., Klimont, Z. & Winiwarter, W. How a century of ammonia synthesis changed the world. Nat. Geosci. 1, 636–639 (2008).

    Article  Google Scholar 

  3. World Fertilizer Trends and Outlook to 2022 (FAO, 2019).

  4. Maxwell, G. R. Synthetic Nitrogen Products (Kluwer Academic Publishers, 2004).

  5. Smith, C., Hill, A. K. & Torrente-Murciano, L. Current and future role of Haber–Bosch ammonia in a carbon-free energy landscape. Energy Environ. Sci. 13, 331–344 (2020).

    Article  Google Scholar 

  6. Appl, M. in Ullmann’s Encyclopedia of Industrial Chemistry 139–225 (2011).

  7. Chen, J. G. et al. Beyond fossil fuel-driven nitrogen transformations. Science 360, eaar6611 (2018).

    Article  Google Scholar 

  8. Soloveichik, G. Electrochemical synthesis of ammonia as a potential alternative to the Haber–Bosch process. Nat. Catal. 2, 377–380 (2019).

    Article  Google Scholar 

  9. Comer, B. M. et al. Prospects and challenges for solar fertilizers. Joule 3, 1578–1605 (2019).

    Article  Google Scholar 

  10. Schiffer, Z. J. & Manthiram, K. Electrification and decarbonization of the chemical industry. Joule 1, 10–14 (2017).

    Article  Google Scholar 

  11. Ludwig, T., Singh, A. R. & Nørskov, J. K. Subsurface nitrogen dissociation kinetics in lithium metal from metadynamics. J. Phys. Chem. C. 124, 26368–26378 (2020).

    Article  Google Scholar 

  12. Tsuneto, A., Kudo, A. & Sakata, T. Efficient electrochemical reduction of N2 to NH3 catalyzed by lithium. Chem. Lett. 22, 851–854 (1993).

    Article  Google Scholar 

  13. Tsuneto, A., Kudo, A. & Sakata, T. Lithium-mediated electrochemical reduction of high pressure N2 to NH3. J. Electroanal. Chem. 367, 183–188 (1994).

    Article  Google Scholar 

  14. Lazouski, N., Schiffer, Z. J., Williams, K. & Manthiram, K. Understanding continuous lithium-mediated electrochemical nitrogen reduction. Joule 3, 1127–1139 (2019).

    Article  Google Scholar 

  15. Andersen, S. Z. et al. A rigorous electrochemical ammonia synthesis protocol with quantitative isotope measurements. Nature 570, 504–508 (2019).

    Article  Google Scholar 

  16. Greenlee, L. F., Renner, J. N. & Foster, S. L. The use of controls for consistent and accurate measurements of electrocatalytic ammonia synthesis from dinitrogen. ACS Catal. 8, 7820–7827 (2018).

    Article  Google Scholar 

  17. Lazouski, N., Chung, M., Williams, K., Gala, M. L. & Manthiram, K. Non-aqueous gas diffusion electrodes for rapid ammonia synthesis from nitrogen and water-splitting-derived hydrogen. Nat. Catal. 3, 463–469 (2020).

    Article  Google Scholar 

  18. Suryanto, B. H. R. et al. Nitrogen reduction to ammonia at high efficiency and rates based on a phosphonium proton shuttle. Science 372, 1187–1191 (2021).

    Article  Google Scholar 

  19. Li, K. et al. Enhancement of lithium-mediated ammonia synthesis by addition of oxygen. Science 374, 1593–1597 (2021).

    Article  Google Scholar 

  20. Fichter, F., Girard, P. & Erlenmeyer, H. Elektrolytische bindung von komprimiertem stickstoff bei gewöhnlicher temperatur. Helv. Chim. Acta 13, 1228–1236 (1930).

    Article  Google Scholar 

  21. Andersen, S. Z. et al. Increasing stability, efficiency, and fundamental understanding of lithium-mediated electrochemical nitrogen reduction. Energy Environ. Sci. 13, 4291–4300 (2020).

    Article  Google Scholar 

  22. Cai, X. et al. Lithium-mediated electrochemical nitrogen reduction: mechanistic insights to enhance performance. iScience 24, 1–17 (2021).

    Article  MathSciNet  Google Scholar 

  23. Schwalbe, J. A. et al. A combined theory–experiment analysis of the surface species in lithium-mediated NH3 electrosynthesis. ChemElectroChem 7, 1542–1549 (2020).

    Article  Google Scholar 

  24. Peled, E. The electrochemical behavior of alkali and alkaline earth metals in nonaqueous battery systems—the solid electrolyte interphase model. J. Electrochem. Soc. 126, 2047–2051 (1979).

    Article  Google Scholar 

  25. Peled, E. & Menkin, S. Review—SEI: past, present and future. J. Electrochem. Soc. 164, A1703–A1719 (2017).

    Article  Google Scholar 

  26. Cheng, X. B. et al. A review of solid electrolyte interphases on lithium metal anode. Adv. Sci. 3, 1500213 (2016).

    Article  Google Scholar 

  27. Zachman, M. J., Tu, Z., Choudhury, S., Archer, L. A. & Kourkoutis, L. F. Cryo-STEM mapping of solid–liquid interfaces and dendrites in lithium-metal batteries. Nature 560, 345–349 (2018).

    Article  Google Scholar 

  28. Li, Y. et al. Correlating structure and function of battery interphases at atomic resolution using cryoelectron microscopy. Joule 2, 2167–2177 (2018).

    Article  Google Scholar 

  29. Lazouski, N. et al. Proton donors induce a differential transport effect for selectivity toward ammonia in lithium-mediated nitrogen reduction. ACS Catal. 12, 5197–5208 (2022).

    Article  Google Scholar 

  30. Cherepanov, P. V., Krebsz, M., Hodgetts, R. Y., Simonov, A. N. & MacFarlane, D. R. Understanding the factors determining the Faradaic efficiency and rate of the lithium redox-mediated N2 reduction to ammonia. J. Phys. Chem. C. 125, 11402–11410 (2021).

    Article  Google Scholar 

  31. Li, Y. et al. Atomic structure of sensitive battery materials and interfaces revealed by cryo-electron microscopy. Science 358, 506–510 (2017).

    Article  Google Scholar 

  32. Zhang, Z. et al. Capturing the swelling of solid-electrolyte interphase in lithium metal batteries. Science 375, 66–70 (2022).

    Article  Google Scholar 

  33. Verdouw, H., Van Echteld, J. A. & Dekkers, E. M. L. Ammonia determination based on indophenol formation with sodium salicylate. Water Res. 12, 399–402 (1977).

    Article  Google Scholar 

  34. Adams, B. D. et al. Accurate determination of coulombic efficiency for lithium metal anodes and lithium metal batteries. Adv. Energy Mater. 8, 1702097 (2018).

    Article  Google Scholar 

  35. Xiao, J. et al. Understanding and applying Coulombic efficiency in lithium metal batteries. Nat. Energy 5, 561–568 (2020).

    Article  Google Scholar 

  36. Mehta, R. in Scanning Electron Microscopy (ed. Kazmiruk, V.) 17–30 (InTech, 2012).

  37. Wang, F. et al. Chemical distribution and bonding of lithium in intercalated graphite: identification with optimized electron energy loss spectroscopy. ACS Nano 5, 1190–1197 (2011).

    Article  Google Scholar 

  38. Aurbach, D., Daroux, M. L., Faguy, P. W. & Yeager, E. Identification of surface films formed on lithium in dimethoxyethane and tetrahydrofuran solutions. J. Electrochem. Soc. 135, 1863–1871 (1988).

    Article  Google Scholar 

  39. Kanamura, K., Tamura, H., Shiraishi, S. & Takehara, Z. XPS analysis of lithium surfaces following immersion in various solvents containing LiBF4. J. Electrochem. Soc. 142, 340–347 (1995).

    Article  Google Scholar 

  40. Zhuang, G. R., Wang, K., Chen, Y. & Ross, P. N. Study of the reactions of Li with tetrahydrofuran and propylene carbonate by photoemission spectroscopy. J. Vac. Sci. Technol. A 16, 3041–3045 (1998).

    Article  Google Scholar 

  41. Andersson, E. K. W. et al. Early-stage decomposition of solid polymer electrolytes in Li-metal batteries. J. Mater. Chem. A 9, 22462–22471 (2021).

    Article  Google Scholar 

  42. Parimalam, B. S. & Lucht, B. L. Reduction reactions of electrolyte salts for lithium ion batteries: LiPF6, LiBF4, LiDFOB, LiBOB, and LiTFSI. J. Electrochem. Soc. 165, A251–A255 (2018).

    Article  Google Scholar 

  43. Wood, K. N. & Teeter, G. XPS on Li-battery-related compounds: analysis of inorganic SEI phases and a methodology for charge correction. ACS Appl. Energy Mater. 1, 4493–4504 (2018).

    Article  Google Scholar 

  44. Li, Y. et al. Revealing nanoscale passivation and corrosion mechanisms of reactive battery materials in gas environments. Nano Lett. 17, 5171–5178 (2017).

    Article  Google Scholar 

  45. Han, B. et al. Poor stability of Li2CO3 in the solid electrolyte interphase of a lithium-metal anode revealed by cryo-electron microscopy. Adv. Mater. 33, 2100404 (2021).

    Article  Google Scholar 

  46. Smith, R. L. & Miser, J. W. Compilation of the Properties of Lithium Hydride (NASA, 1963).

  47. Aurbach, D. & Weissman, I. On the possibility of LiH formation on Li surfaces in wet electrolyte solutions. Electrochem. Commun. 1, 324–331 (1999).

    Article  Google Scholar 

  48. Boyle, D. T. et al. Corrosion of lithium metal anodes during calendar ageing and its microscopic origins. Nat. Energy 6, 487–494 (2021).

    Article  Google Scholar 

  49. Stevie, F. A., Garcia, R., Shallenberger, J., Newman, J. G. & Donley, C. L. Sample handling, preparation and mounting for XPS and other surface analytical techniques. J. Vac. Sci. Technol. A 38, 063202 (2020).

    Article  Google Scholar 

Download references

Acknowledgements

K.M., K.S. N.L., and C.K.K. gratefully acknowledge support by the National Science Foundation under grant number 2204756. K.S. and N.L. acknowledge support from the National Science Foundation Graduate Research Fellowship under grant number 1745302. Cryo-EM data were acquired at the Electron Imaging Center for Nanomachines (EICN) at the University of California, Los Angeles’s California NanoSystems Institute (CNSI). Y.L. and X.Y. were supported in part by the National Science Foundation under grant number CBET-2143677. This work also made use of the MRSEC Shared Experimental Facilities at Massachusetts Institute of Technology (MIT), supported by the National Science Foundation under award number DMR-1419807. We thank the staff scientists at both UCLA EICN and MIT MRSEC for their training and expertise. We also thank M. Wolski of Daramic for providing us with polyporous separator samples, F. Frankel for feedback on figure design and K. Williams, N. Corbin, H. J. Song, G. Junor, G. Hobold and all the members of the Li and Manthiram research groups for productive and helpful discussions.

Author information

Author notes

  1. These authors contributed equally: Katherine Steinberg and Xintong Yuan.

Authors and Affiliations

  1. Department of Chemical Engineering, Massachusetts Institute of Technology, Cambridge, MA, USA

    Katherine Steinberg & Nikifar Lazouski

  2. Department of Chemical & Biomolecular Engineering, University of California, Los Angeles, Los Angeles, CA, USA

    Xintong Yuan & Yuzhang Li

  3. Division of Chemistry and Chemical Engineering, California Institute of Technology, Pasadena, CA, USA

    Channing K. Klein & Karthish Manthiram

  4. California NanoSystems Institute (CNSI), University of California, Los Angeles, Los Angeles, CA, USA

    Matthew Mecklenburg

Authors
  1. Katherine Steinberg
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Xintong Yuan
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Channing K. Klein
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Nikifar Lazouski
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Matthew Mecklenburg
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Karthish Manthiram
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Yuzhang Li
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

K.S., K.M. and Y.L. conceptualized the paper. K.S. developed the experimental methodology for product quantification, sample preparation for imaging and characterization and collection of XPS spectra. X.Y. and Y.L. developed the experimental methodology for SEM and cryo-EM. K.S. performed product quantification, SEM imaging and XPS experiments, and K.S. and C.K. prepared samples for cryo-EM. X.Y. carried out cryo-EM and SEM imaging. Y.L. performed EELS characterization. M.M. advised on microscopy and imaging analysis. C.K. and K.S. performed the validation. K.S. prepared the figures and wrote the original draft of the manuscript and Supplementary Information, and N.L, Y.L., K.M., C.K., X.Y. and K.S. reviewed and edited its contents. K.M. and Y.L. supervised the work.

Corresponding authors

Correspondence to Karthish Manthiram or Yuzhang Li.

Ethics declarations

Competing interests

The authors declare no competing interests.

Peer review

Peer review information

Nature Energy thanks Matteo Cargnello, Chongmin Wang and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Figs. 1–35, Notes 1–12 and Methods.

Supplementary Data 1

Source data for Supplementary Figures.

Source data

Source Data Fig. 2

Statistical source data.

Source Data Fig. 3

Statistical source data.

Source Data Fig. 4

Statistical source data.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Steinberg, K., Yuan, X., Klein, C.K. et al. Imaging of nitrogen fixation at lithium solid electrolyte interphases via cryo-electron microscopy. Nat Energy 8, 138–148 (2023). https://doi.org/10.1038/s41560-022-01177-5

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1038/s41560-022-01177-5

This article is cited by

Search

Advanced search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing