Abstract
Nanoporous graphene and related atomically thin layered materials are promising candidates in reverse electrodialysis research owing to their remarkable ionic conductivity and high permselectivity. The synthesis of atomically thin nanoporous membranes with a narrow pore size distribution, however, remains challenging. Here, we report the fabrication of nanoporous carbon membranes via the thermal crosslinking of core–rim structured monomers, that is, polycyclic aromatic hydrocarbons. The mechanically robust, centimetre-sized membrane has a pore size of 3.6 ± 1.8 nm and a thickness of 2.0 ± 0.5 nm. When applied to reverse electrodialysis, the nanoporous carbon membrane offers a high short-circuit current with an output power density of 67 W m−2, which is about two orders of magnitude beyond that of the classic ion-exchange membranes and current prototype nanoporous membranes reported in the literature. Crosslinked and atomically thin porous polycyclic aromatic hydrocarbon membranes therefore represent new scaffolds that will revolutionize the rapidly developing fields of sustainable energy and membrane technology.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 12 print issues and online access
$259.00 per year
only $21.58 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
References
Logan, B. E. & Elimelech, M. Membrane-based processes for sustainable power generation using water. Nature 488, 313–319 (2012).
Schroeder, T. B. H. et al. An electric-eel-inspired soft power source from stacked hydrogels. Nature 552, 214–218 (2017).
Mei, Y. & Tang, C. Y. Recent developments and future perspectives of reverse electrodialysis technology: a review. Desalination 425, 156–174 (2018).
Yip, N. Y., Brogioli, D., Hamelers, H. V. M. & Nijmeijer, K. Salinity gradients for sustainable energy: primer, progress, and prospects. Environ. Sci. Technol. 50, 12072–12094 (2016).
Giorno, L, Drioli, E. & Strathmann, H. Permselectivity of ion-exchange membranes in Encyclopedia of Membranes (Springer, 2016).
Guo, X. et al. Permselectivity and conductivity of membranes based on sulfonated naphthalenic copolyimides. J. Phys. Chem. B 111, 13694–13702 (2007).
Yip, N. Y. & Elimelech, M. Comparison of energy efficiency and power density in pressure retarded osmosis and reverse electrodialysis. Environ. Sci. Technol. 48, 11002–11012 (2014).
Geise, G. M., Hickner, M. A. & Logan, B. E. Ionic resistance and permselectivity tradeoffs in anion exchange membranes. ACS Appl. Mater. Interfaces 5, 10294–10301 (2013).
Macha, M., Marion, S., Nandigana, V. V. R. & Radenovic, A. 2D materials as an emerging platform for nanopore-based power generation. Nat. Rev. Mater. 4, 588–605 (2019).
Sint, K., Wang, B. & Král, P. Selective ion passage through functionalized graphene nanopores. J. Am. Chem. Soc. 130, 16448–16449 (2008).
Siria, A. et al. Giant osmotic energy conversion measured in a single transmembrane boron nitride nanotube. Nature 494, 455–458 (2013).
Feng, J. D. et al. Single-layer MoS2 nanopores as nanopower generators. Nature 536, 197–200 (2016).
Yang, Y. et al. Large-area graphene-nanomesh/carbon-nanotube hybrid membranes for ionic and molecular nanofiltration. Science 364, 1057–1062 (2019).
Moreno, C. et al. Bottom-up synthesis of multifunctional nanoporous graphene. Science 360, 199–203 (2018).
Angelova, P. et al. A universal scheme to convert aromatic molecular monolayers into functional carbon nanomembranes. ACS Nano 7, 6489–6497 (2013).
Bauer, T. et al. Synthesis of free-standing, monolayered organometallic sheets at the air/water interface. Angew. Chem. Int. Ed. 50, 7879–7884 (2011).
Zheng, Z. et al. Synthesis of two-dimensional analogues of copolymers by site-to-site transmetalation of organometallic monolayer sheets. J. Am. Chem. Soc. 136, 6103–6110 (2014).
Nishikata, Y., Konishi, T., Morikawa, A., Kakimoto, M.-a. & Imai, Y. Preparation and monolayer thickness of Langmuir–Blodgett films of polyimides having various chemical structures. Polym. J. 20, 269–272 (1988).
Silva, N. J., Machado, F. B. C., Lischka, H. & Aquino, A. J. A. π–π stacking between polyaromatic hydrocarbon sheets beyond dispersion interactions. Phys. Chem. Chem. Phys. 18, 22300–22310 (2016).
Schneider, G. F., Calado, V. E., Zandbergen, H., Vandersypen, L. M. K. & Dekker, C. Wedging transfer of nanostructures. Nano Lett. 10, 1912–1916 (2010).
Bilkan, M. T., Şahin, O. & Yurdakul, Ş. Experimental and DFT studies of solvent effects on molecular structure and physical properties of dipyridylamine pyridine based ligand. J. Mol. Struct. 1133, 580–590 (2017).
Anariba, F., Viswanathan, U., Bocian, D. F. & McCreery, R. L. Determination of the structure and orientation of organic molecules tethered to flat graphitic carbon by ATR-FT-IR and Raman spectroscopy. Anal. Chem. 78, 3104–3112 (2006).
Maghsoumi, A. et al. Edge chlorination of hexa-peri-hexabenzocoronene investigated by density functional theory and vibrational spectroscopy. Phys. Chem. Chem. Phys. 18, 11869–11878 (2016).
Beloded, A. A., Koshechko, V. G., Pokhodenko, V. D., Nemoshkalenko, V. V. & Aleshin, V. G. X-ray photoelectron spectra of radical cations of the triphenylamine series and some heterocyclic compounds. Theor. Exp. Chem. 17, 99–103 (1981).
Susi, T., Pichler, T. & Ayala, P. X-ray photoelectron spectroscopy of graphitic carbon nanomaterials doped with heteroatoms. Beilstein J. Nanotechnol. 6, 177–192 (2015).
Yuan, K. et al. 2D heterostructures derived from MoS2-templated, cobalt-containing conjugated microporous polymer sandwiches for the oxygen reduction reaction and electrochemical energy storage. ChemElectroChem 4, 709–715 (2017).
Johra, F. T., Lee, J.-W. & Jung, W.-G. Facile and safe graphene preparation on solution based platform. J. Ind. Eng. Chem. 20, 2883–2887 (2014).
Wu, Z.-S. et al. Bottom-up fabrication of sulfur-doped graphene films derived from sulfur-annulated nanographene for ultrahigh volumetric capacitance micro-supercapacitors. J. Am. Chem. Soc. 139, 4506–4512 (2017).
Ma, Z. et al. Sulfur-doped graphene derived from cycled lithium–sulfur batteries as a metal-free electrocatalyst for the oxygen reduction reaction. Angew. Chem. Int. Ed. 54, 1888–1892 (2015).
Zuo, C. & Jagodzinski, P. W. Surface-enhanced Raman scattering of pyridine using different metals: differences and explanation based on the selective formation of α-pyridyl on metal surfaces. J. Phys. Chem. B 109, 1788–1793 (2005).
Matsuoka, R. et al. Crystalline graphdiyne nanosheets produced at a gas/liquid or liquid/liquid interface. J. Am. Chem. Soc. 139, 3145–3152 (2017).
Maghsoumi, A., Brambilla, L., Castiglioni, C., Müllen, K. & Tommasini, M. Overtone and combination features of G and D peaks in resonance Raman spectroscopy of the C78H26 polycyclic aromatic hydrocarbon. J. Raman Spectrosc. 46, 757–764 (2015).
Verzhbitskiy, I. A. et al. Raman fingerprints of atomically precise graphene nanoribbons. Nano Lett. 16, 3442–3447 (2016).
Mao, J., Cao, X., Olk, D. C., Chu, W. & Schmidt-Rohr, K. Advanced solid-state NMR spectroscopy of natural organic matter. Prog. Nucl. Magn. Reson. Spectrosc. 100, 17–51 (2017).
Wang, S., Tang, Y., Schobert, H. H., Guo, Yn & Su, Y. FTIR and 13C NMR investigation of coal component of Late Permian coals from Southern China. Energy Fuels 25, 5672–5677 (2011).
Rollings, R. C., Kuan, A. T. & Golovchenko, J. A. Ion selectivity of graphene nanopores. Nat. Commun. 7, 11408 (2016).
Wang, L. et al. Fundamental transport mechanisms, fabrication and potential applications of nanoporous atomically thin membranes. Nat. Nanotechnol. 12, 509–522 (2017).
Jain, T. et al. Heterogeneous sub-continuum ionic transport in statistically isolated graphene nanopores. Nat. Nanotechnol. 10, 1053–1057 (2015).
Feng, J. D. et al. Observation of ionic Coulomb blockade in nanopores. Nat. Mater. 15, 850–855 (2016).
Esfandiar, A. et al. Size effect in ion transport through angstrom-scale slits. Science 358, 511–513 (2017).
Gao, J. et al. High-performance ionic diode membrane for salinity gradient power generation. J. Am. Chem. Soc. 136, 12265–12272 (2014).
Plett, T. S. et al. Solid-state ionic diodes demonstrated in conical nanopores. J. Phys. Chem. C 121, 6170–6176 (2017).
Siwy, Z. S. & Howorka, S. Engineered voltage-responsive nanopores. Chem. Soc. Rev. 39, 1115–1132 (2010).
Karnik, R., Duan, C. H., Castelino, K., Daiguji, H. & Majumdar, A. Rectification of ionic current in a nanofluidic diode. Nano Lett. 7, 547–551 (2007).
Ouyang, W., Wang, W., Zhang, H. X., Wu, W. G. & Li, Z. H. Nanofluidic crystal: a facile, high-efficiency and high-power-density scaling up scheme for energy harvesting based on nanofluidic reverse electrodialysis. Nanotechnology 24, 345401 (2013).
Weinstein, J. N. & Leitz, F. B. Electric power from differences in salinity: the dialytic battery. Science 191, 557–559 (1976).
Cao, L. et al. On the origin of ion selectivity in ultrathin nanopores: insights for membrane-scale osmotic energy conversion. Adv. Funct. Mater. 28, 1804189 (2018).
Jia, W. L. et al. 7-azaindolyl- and 2,2′-dipyridylamino-functionalized molecular stars with sixfold symmetry: self-assembly, luminescence, and coordination compounds. Chem. Eur. J. 11, 832–842 (2005).
Thompson, C. M. et al. Substituent effects on the gas sorption and selectivity properties of hexaphenylbenzene and hexabenzocoronene based porous polymers. Macromolecules 47, 8645–8652 (2014).
Pantelic, R. S. et al. Graphene: substrate preparation and introduction. J. Struct. Biol. 174, 234–238 (2011).
Hartmann, S. R. & Hahn, E. L. Nuclear double resonance in the rotating frame. Phys. Rev. 128, 2042–2053 (1962).
Metz, G., Wu, X. L. & Smith, S. O. Ramped-amplitude cross polarization in magic-angle-spinning NMR. J. Magn. Reson. Ser. A 110, 219–227 (1994).
Fung, B. M., Khitrin, A. K. & Ermolaev, K. An improved broadband decoupling sequence for liquid crystals and solids. J. Magn. Reson. 142, 97–101 (2000).
Martín-Yerga, D., Rama, E. C. & Costa-García, A. Electrochemical study and applications of selective electrodeposition of silver on quantum dots. Anal. Chem. 88, 3739–3746 (2016).
Barlag, R. et al. A student-made silver–silver chloride reference electrode for the general chemistry laboratory: ∼10 min preparation. J. Chem. Educ. 91, 766–768 (2014).
Baerends, E. J. et al. ADF2017, SCM, Theoretical Chemistry https://www.scm.com (Vrije Universiteit, Amsterdam, The Netherlands).
Berendsen, H. J. C., van der Spoel, D. & van Drunen, R. GROMACS: a message-passing parallel molecular dynamics implementation. Comput. Phys. Commun. 91, 43–56 (1995).
Lindahl, E., Hess, B. & van der Spoel, D. GROMACS 3.0: a package for molecular simulation and trajectory analysis. J. Mol. Model. 7, 306–317 (2001).
Van Der Spoel, D. et al. GROMACS: fast, flexible, and free. J. Comput. Chem. 26, 1701–1718 (2005).
Hess, B., Kutzner, C., van der Spoel, D. & Lindahl, E. GROMACS 4: algorithms for highly efficient, load-balanced, and scalable molecular simulation. J. Chem. Theory Comput. 4, 435–447 (2008).
Pronk, S. et al. GROMACS 4.5: a high-throughput and highly parallel open source molecular simulation toolkit. Bioinformatics 29, 845–854 (2013).
Abraham, M. J. et al. GROMACS: high performance molecular simulations through multi-level parallelism from laptops to supercomputers. SoftwareX 1–2, 19–25 (2015).
Páll, S., Abraham, M. J., Kutzner, C., Hess, B. & Lindahl, E. in Solving Software Challenges for Exascale (eds Markidis, S. & Laure, E.) 3–27 (Springer International Publishing, 2015).
Humphrey, W., Dalke, A. & Schulten, K. VMD: visual molecular dynamics. J. Mol. Graph. 14, 33–38 (1996).
York, D. M., Darden, T. A. & Pedersen, L. G. The effect of long‐range electrostatic interactions in simulations of macromolecular crystals: a comparison of the Ewald and truncated list methods. J. Chem. Phys. 99, 8345–8348 (1993).
Bussi, G., Donadio, D. & Parrinello, M. Canonical sampling through velocity rescaling. J. Chem. Phys. 126, 014101 (2007).
Horn, H. W. et al. Development of an improved four-site water model for biomolecular simulations: TIP4P-Ew. J. Chem. Phys. 120, 9665–9678 (2004).
Vega, C. & de Miguel, E. Surface tension of the most popular models of water by using the test-area simulation method. J. Chem. Phys. 126, 154707 (2007).
Chen, F. & Smith, P. E. Simulated surface tensions of common water models. J. Chem. Phys. 126, 221101 (2007).
Jorgensen, W. L., Maxwell, D. S. & Tirado-Rives, J. Development and testing of the OPLS all-atom force field on conformational energetics and properties of organic liquids. J. Am. Chem. Soc. 118, 11225–11236 (1996).
Kaminski, G. A., Friesner, R. A., Tirado-Rives, J. & Jorgensen, W. L. Evaluation and reparametrization of the OPLS-AA force field for proteins via comparison with accurate quantum chemical calculations on peptides. J. Phys. Chem. B 105, 6474–6487 (2001).
Martin, M. G. Comparison of the AMBER, CHARMM, COMPASS, GROMOS, OPLS, TraPPE and UFF force fields for prediction of vapor–liquid coexistence curves and liquid densities. Fluid Phase Equilib. 248, 50–55 (2006).
Martínez, J. M. & Martínez, L. Packing optimization for automated generation of complex system’s initial configurations for molecular dynamics and docking. J. Comput. Chem. 24, 819–825 (2003).
Martínez, L., Andrade, R., Birgin, E. G. & Martínez, J. M. PACKMOL: a package for building initial configurations for molecular dynamics simulations. J. Comput. Chem. 30, 2157–2164 (2009).
Roe, D. R. & Cheatham, T. E. PTRAJ and CPPTRAJ: software for processing and analysis of molecular dynamics trajectory data. J. Chem. Theory Comput. 9, 3084–3095 (2013).
Acknowledgements
This work is supported by the Netherlands Organization for Scientific Research (Vidi 723.013.007), the European Research Council (ERC) Proof of Concept NANOPORE (no. 780004). We acknowledge Nederlandse Organisatie voor Wetenschappelijk Onderzoek (NWO) Exact and Natural Sciences for the use of the supercomputer facilities at SURFsara. H.Q. and U.K. gratefully acknowledge the financial support by the German Research Foundation (DFG) and the Ministry of Science, Research and the Arts (MWK) of Baden-Wuerttemberg in the framework of the “SALVE” (Sub-Angstrom Low-Voltage Electron Microscopy) project (DFG KA 1295/21-1). S. G. Lemay is acknowledged for the general discussion about nanofluidics. W. Fu and X. Zhang are acknowledged for the discussions about ionic conductance. J. van Gerwen and C. van Helvoirt are acknowledged for the XPS measurements.
Author information
Authors and Affiliations
Contributions
G.F.S. supervised the project. X.L. performed the monomer synthesis and characterization. X.L. and M.H. performed the membrane synthesis, characterization and ionic conductance measurements. H.Q. and U.K. conducted HRTEM and HAADF-STEM measurements. D.C., G.J.A.S. and F.B. performed the MD simulations. K.B.S.S.G., D.C., G.J.A.S., F.B. and H.d.G. performed the solid-state NMR studies. All authors contributed to discussions. X.L. wrote the manuscript with help from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Nanotechnology thanks Yongsheng Chen and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data
Extended Data Fig. 1 MD simulations analysis of HPAHBC molecules on water surface.
a–c, Schematic visualization of starting conformations for the HPAHBC molecules at the beginning of the MD simulation, vertical (a), stacked (b), planar (c); carbon atoms are shown in grey and nitrogen atoms in blue balls (hydrogens are omitted). d, Illustration of the tilt angle Φ (red arc) between the plane of the HBC ring defined by three specific carbon atom on the edge (yellow balls) and the x–y plane; carbon atoms in grey, nitrogen atoms in blue (hydrogens are omitted). The cpptraj module of AmberTools are used for the calculation of the HBC plane. e, Distribution of tilt angle (Φ) per each molecule from MD simulations with the increasing amount of HPAHBC molecules, from 1 to 6, and different starting point conformation, vertical (red), stacked (blue), planar (green). With the red circle at 90° and the concentric blue-green circle at 0°, we underline the starting point for the tilt angle at the beginning of the pre-equilibration simulations, for vertical and stacked-planar conformation, respectively. f, Distribution of number of hydrogen bonds (H-bonds) per HPAHBC molecule from MD simulations with increasing amount of the HPAHBC molecules, from 1 to 6, and different starting point conformation, vertical (red), stacked (blue), planar (green). Gromacs Tool (gmx hbond) is used for the calculation of the number of hydrogen bonds determined based on cutoffs for the angle Hydrogen–OH–N 125º and the distance OH–N 3.5 Å. OH is regarded as the donor, N as the acceptor. The distribution curves were obtained via Gaussian broadening with default standard deviation.
Extended Data Fig. 2 Solid-state NMR spectra of HPAHBC powder annealed at different temperatures.
As the temperature increases from 400 degrees to 550 degrees, the peaks marked with blue dots gradually vanish, which is attributed to decomposition of the dipyridylamino rim.
Supplementary information
Supplementary Information
Supplementary Figs. 1–26, Tables 1–5 and refs. 1–13.
Source data
Source Data Fig. 1
Numerical data.
Source Data Fig. 2
Numerical data.
Source Data Fig. 3
Numerical data.
Source Data Fig. 4
Numerical data.
Source Data Extended Data Fig. 1
Numerical data.
Rights and permissions
About this article
Cite this article
Liu, X., He, M., Calvani, D. et al. Power generation by reverse electrodialysis in a single-layer nanoporous membrane made from core–rim polycyclic aromatic hydrocarbons. Nat. Nanotechnol. 15, 307–312 (2020). https://doi.org/10.1038/s41565-020-0641-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41565-020-0641-5
This article is cited by
-
Vertical iontronic energy storage based on osmotic effects and electrode redox reactions
Nature Energy (2024)
-
Bioinspired light-driven chloride pump with helical porphyrin channels
Nature Communications (2024)
-
Photoelectric responsive ionic channel for sustainable energy harvesting
Nature Communications (2023)
-
Hierarchically engineered nanochannel systems with pore-in/on-pore structures
NPG Asia Materials (2023)
-
Two-dimensional capillaries assembled by van der Waals heterostructures
Nano Research (2023)