Abstract
Light-emitting diodes (LEDs) based on perovskite quantum dots have shown external quantum efficiencies (EQEs) of over 23% and narrowband emission, but suffer from limited operating stability1. Reduced-dimensional perovskites (RDPs) consisting of quantum wells (QWs) separated by organic intercalating cations show high exciton binding energies and have the potential to increase the stability and the photoluminescence quantum yield2,3. However, until now, RDP-based LEDs have exhibited lower EQEs and inferior colour purities4,5,6. We posit that the presence of variably confined QWs may contribute to non-radiative recombination losses and broadened emission. Here we report bright RDPs with a more monodispersed QW thickness distribution, achieved through the use of a bifunctional molecular additive that simultaneously controls the RDP polydispersity while passivating the perovskite QW surfaces. We synthesize a fluorinated triphenylphosphine oxide additive that hydrogen bonds with the organic cations, controlling their diffusion during RDP film deposition and suppressing the formation of low-thickness QWs. The phosphine oxide moiety passivates the perovskite grain boundaries via coordination bonding with unsaturated sites, which suppresses defect formation. This results in compact, smooth and uniform RDP thin films with narrowband emission and high photoluminescence quantum yield. This enables LEDs with an EQE of 25.6% with an average of 22.1 ±1.2% over 40 devices, and an operating half-life of two hours at an initial luminance of 7,200 candela per metre squared, indicating tenfold-enhanced operating stability relative to the best-known perovskite LEDs with an EQE exceeding 20%1,4,5,6.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
The data that support the findings of this study are available from the corresponding authors.
References
Kim, Y.-H. et al. Comprehensive defect suppression in perovskite nanocrystals for high-efficiency light-emitting diodes. Nat. Photon. 15, 148–155 (2021).
Hong, K., Le, Q. V., Kim, S. Y. & Jang, H. W. Low-dimensional halide perovskites: review and issues. J. Mater. Chem. C 6, 2189 (2018).
Gao, X. et al. Ruddlesden–Popper perovskites: synthesis and optical properties for optoelectronic applications. Adv. Sci. 6, 1900941 (2019).
Jiang, Y. et al. Reducing the impact of Auger recombination in quasi-2D perovskite light-emitting diodes. Nat. Commun. 12, 336 (2021).
Kong, L. et al. Smoothing the energy transfer pathway in quasi-2D perovskite films using methanesulfonate leads to highly efficient light-emitting devices. Nat. Commun. 12, 1246 (2021).
Sun, C. et al. High-performance large-area quasi-2D perovskite light-emitting diodes. Nat. Commun. 12, 2207 (2021)
Jena, A. K., Kulkarni, A. & Miyasaka, T. Halide perovskite photovoltaics: background, status, and future prospects. Chem. Rev. 119, 3036 (2019).
Xing, G. et al. Low-temperature solution-processed wavelength-tunable perovskites for lasing. Nat. Mater. 13, 476–480 (2014).
Dou, L. et al. Solution-processed hybrid perovskite photodetectors with high detectivity. Nat. Commun. 5, 5404 (2014).
Quan, L. N., Arquer, F. P. G., Sabatini, R. P. & Sargent, E. H. Perovskites for light emission. Adv. Mater. 30, 1801996 (2018).
Shen, H. et al. Visible quantum dot light-emitting diodes with simultaneous high brightness and efficiency. Nat. Photon. 13, 192–197 (2019).
Won, Y.-H. et al. Highly efficient and stable InP/ZnSe/ZnS quantum dot light-emitting diodes. Nature 575, 634–638 (2019).
Ly, K. T. et al. Near-infrared organic light-emitting diodes with very high external quantum efficiency and radiance. Nat. Photon. 11, 63–68 (2017).
Wu, T.-L. et al. Diboron compound-based organic light-emitting diodes with high efficiency and reduced efficiency roll-off. Nat. Photon. 12, 235–240 (2018).
Cho, H. et al. Overcoming the electroluminescence efficiency limitations of perovskite light-emitting diodes. Science 350, 1222 (2015).
Richter, J. M. et al. Enhancing photoluminescence yields in lead halide perovskites by photon recycling and light out-coupling. Nat. Commun. 7, 13941 (2016).
Xing, G. et al. Transcending the slow bimolecular recombination in lead-halide perovskites for electroluminescence. Nat. Commun. 8, 14558 (2017).
Miyata, A. et al. Direct measurement of the exciton binding energy and effective masses for charge carriers in organic-inorganic tri-halide perovskites. Nat. Phys. 11, 582–587 (2015).
Quintero-Bermudez, R. et al. Compositional and orientational control in metal halide perovskites of reduced dimensionality. Nat. Mater. 17, 900–907 (2018).
Ma, D. et al. Chloride insertion-immobilization enables bright, narrowband, and stable blue-emitting perovskite diodes. J. Am. Chem. Soc. 142, 5126 (2020).
deQuilettes, D. W. et al. Photoluminescence lifetimes exceeding 8 μs and quantum yields exceeding 30% in hybrid perovskite thin films by ligand passivation. ACS Energy Lett. 1, 438 (2016).
Braly, I. L. et al. Hybrid perovskite films approaching the radiative limit with over 90% photoluminescence quantum efficiency. Nat. Photon. 12, 355–361 (2018).
Lin-Vien, D., Colthup, N. B., Fateley, W. G. & Grasselli, J. G. in The Handbook of Infrared and Raman Characteristic Frequencies of Organic Molecules Ch. 16 (Academic Press, 1991).
Lin-Vien, D., Colthup, N. B., Fateley, W. G. & Grasselli, J. G. in The Handbook of Infrared and Raman Characteristic Frequencies of Organic Molecules Ch. 6 (Academic Press, 1991).
Lin-Vien, D., Colthup, N. B., Fateley, W. G. & Grasselli, J. G. in The Handbook of Infrared and Raman Characteristic Frequencies of Organic Molecules Ch. 3 (Academic Press, 1991).
Wang, H. et al. A multi-functional molecular modifier enabling efficient large-area perovskite light-emitting diodes. Joule 4, 1977 (2020).
Dong, Y., et al. Bipolar-shell resurfacing for blue LEDs based on strongly confined perovskite quantum dots. Nat. Nanotechnol. 15, 668–674 (2020).
Lin, K. et al. Perovskite light-emitting diodes with external quantum efficiency exceeding 20 per cent. Nature 562, 245–248 (2018).
Shen, Y. et al. High-efficiency perovskite light-emitting diodes with synergetic outcoupling enhancement. Adv. Mater. 31, 1901517 (2019).
Ilavsky, J. Nika: software for two-dimensional data reduction. J. Appl. Cryst. 45, 324 (2012).
Jiang, Z. GIXSGUI: a MATLAB toolbox for grazing-incidence X-ray scattering data visualization and reduction, and indexing of buried three-dimensional periodic nanostructured films. J. Appl. Cryst. 48, 917 (2015).
Kresse, G. & Furthmüller, J. Vienna Ab-Initio Simulation Package (VASP) (Vienna Univ., 2001).
Perdew, J. P.; Burke, K., Ernzerhof, M. Perdew, Burke, and Ernzerhof reply. Phys. Rev. Lett. 80, 891 (1998).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953 (1994).
Forrest, S. R., Bradley, D. D. C. & Thompson, M. E. Measuring the efficiency of organic light-emitting devices. Adv. Mater. 15, 1043 (2003).
Li, H. et al. A review of characterization of perovskite film in solar cells by spectroscopic ellipsometry. Sol. Energy 212, 48 (2020).
Jellison, G. E. Jr Data analysis for spectroscopic ellipsometry. Thin Solid Films 234, 416 (1993).
Zhao, B. et al. High-efficiency perovskite-polymer bulk heterostructure light-emitting diodes. Nat. Photon. 12, 783–789 (2018).
Meng, S.-S., Li, Y.-Q. & Tang, J.-X. Theoretical perspective to light outcoupling and management in perovskite light-emitting diodes. Org. Electron. 61, 351 (2018).
Zhu, R., Luo, Z. & Wu, S.-T. Light extraction analysis and enhancement in a quantum dot light emitting diode. Opt. Express 22, A1783 (2014).
Cho, C. et al. The role of photon recycling in perovskite light-emitting diodes. Nat. Commun. 11, 611 (2020).
Acknowledgements
This publication is based in part on work supported by the Natural Sciences and Engineering Research Council of Canada (NSERC, number 537463-18), the National Natural Science Foundation of China (numbers 51802102, 21805101, 51902110 and 61905107), the Natural Science Foundation of Fujian Province (numbers 2020J06021 and 2019J01057) and the National Key R&D Program of China (number 2019YFB1704600). We also acknowledge Huawei Canada for financial support and thank C. Zhu of the Advanced Light Source for assistance with GIWAXS measurements; G. Xing and J. Guo at University of Macau for LED light distribution measurements; C. Cui, S. Bian and J. Lu at Huaqiao University for optical constant measurements; and the National Institute of Metrology (NIM) of China for cross-checking LED measurements.
Author information
Authors and Affiliations
Contributions
E.H.S. and Z.W. supervised the project. D.M. and E.H.S. conceived the idea, designed the experiments and wrote the manuscript. D.M. and Y.K. synthesized and purified TFPPO. D.M. and K.L. prepared the RDP thin films, performed XPS and PL characterization, and fabricated LEDs. D.M., Y.D. and Y.L. performed TA measurements. H.C. performed DFT calculations. A.H.P. and A.J. performed GIWAXS measurements. D.W. performed optical modelling. Y.-K.W. performed XRD and AFM measurements. K.L. and B.C. performed SEM and TEM measurements. D.M., K.L., F.Y., Z.-H.L. and Z.W. performed LED measurements. P.L. performed ultraviolet photoelectron spectroscopy measurements. J.Z.F. performed FTIR measurements. Y.K. analysed the NMR data. All authors discussed the results and commented on the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature thanks Tae-Woo Lee, Henry Snaith and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
Extended Data Fig. 1 Characteristics of control, TPPO-treated and TFPPO-treated RDPs.
a–c, GIWAXS profiles. d–f, Excitation power-dependent PLQY of control, TPPO-treated and TFPPO-treated RDPs with and without PMMA additives. g, Time-resolved PL decay curves. h, Photostability under continuous excitation using a laser diode (365 nm, about 180 mW cm-2) in a nitrogen-filled glovebox. The half-lives are 6 nm, 13 nm and 65 min, respectively. i, XRD profiles. The crystallite sizes calculated using the Scherrer equation are 11.4 nm, 7.5 nm and 6.5 nm, respectively.
Extended Data Fig. 2 Optical characteristics of TPP-treated and TFPP-treated RDPs.
a, TA spectra at a delay time ranging from 0 ps to 50 ps. b, TA spectra at delay times of 1 ps, 2 ps, 5 ps, 10 ps and 50 ps. c, PL spectra. The inset shows the chemical structure of TPP and TFPP, respectively.
Extended Data Fig. 3 Film morphology.
Top-view SEM and AFM images of control, TPPO-treated and TFPPO-treated RDP thin films with and without PMMA additives.
Extended Data Fig. 4 Density functional theory simulations.
a, TFPPO binding with the unsaturated lead dangling bonds at the perovskite edge through P=O:Pb and forming hydrogen bonds with the ammonium tails of the PEA organic cations (N-H…F) shows a binding energy of 1.88 eV. b, TFPPO with only P=O:Pb (no N-H…F) shows a binding energy of 1.23 eV.
Extended Data Fig. 5 Ultraviolet photoelectron spectroscopy characteristics.
a, Second electron cut-off. b, Valence band spectra of control, TPPO-treated and TFPPO-treated RDPs (from left to right).
Extended Data Fig. 6 Supplementary LED characteristics.
a, Luminance versus current density curves; b, EL spectra of LEDs based on control, TPPO-treated and TFPPO-treated RDPs. c, Box plot of 40 devices based on TFPPO-treated RDPs (made across four batches). d, e, Angle-dependent EL intensity and spectra of LEDs based on TFPPO-treated RDPs. f, EQE versus current density curves of commercial OLEDs measured in our lab at Huaqiao University (HQU) and at the National Institute of Metrology (NIM) of China.
Extended Data Fig. 7 Optical modelling.
a, TEM image of LEDs based on TFPPO-treated RDPs, top-view SEM and AFM images of the PEDOT:PSS:PFI layer on ITO substrates. b, Refractive indices of the HTL, RDP and ETL layers for numerical simulations. c, Power dissipation channels for planar LEDs (left), outcoupling efficiency of planar LEDs as a functional of ERCL (middle) and power dissipation channels for LEDs with a randomly-nanostructured interface between HTL and RDPs (right).
Rights and permissions
About this article
Cite this article
Ma, D., Lin, K., Dong, Y. et al. Distribution control enables efficient reduced-dimensional perovskite LEDs. Nature 599, 594–598 (2021). https://doi.org/10.1038/s41586-021-03997-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41586-021-03997-z
This article is cited by
-
Valley-centre tandem perovskite light-emitting diodes
Nature Nanotechnology (2024)
-
Spin coating epitaxial heterodimensional tin perovskites for light-emitting diodes
Nature Nanotechnology (2024)
-
Vapour-deposited perovskite light-emitting diodes
Nature Reviews Materials (2024)
-
Phase dimensions resolving of efficient and stable perovskite light-emitting diodes at high brightness
Nature Photonics (2024)
-
Phase distribution management in quasi-2D perovskite films toward highly efficient amplified spontaneous emission pumped by nanosecond pulsed laser
Science China Materials (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.