Abstract
Moiré lattices formed in twisted van der Waals bilayers provide a unique, tunable platform to realize coupled electron or exciton lattices unavailable before. While twist angle between the bilayer has been shown to be a critical parameter in engineering the moiré potential and enabling novel phenomena in electronic moiré systems, a systematic experimental study as a function of twist angle is still missing. Here we show that not only are moiré excitons robust in bilayers of even large twist angles, but also properties of the moiré excitons are dependant on, and controllable by, the moiré reciprocal lattice period via twist-angle tuning. From the twist-angle dependence, we furthermore obtain the effective mass of the interlayer excitons and the electron inter-layer tunneling strength, which are difficult to measure experimentally otherwise. These findings pave the way for understanding and engineering rich moiré-lattice induced phenomena in angle-twisted semiconductor van der Waals heterostructures.
Similar content being viewed by others
Introduction
Atomically thin heterostructures created by stacking van der Waals materials mark a new frontier in condensed matter physics1,2,3. When two monolayer crystals of the same lattice symmetries overlay on each other, a moiré superlattice may form due to a small mismatch in their lattice constants or angular alignment4,5. The latter—the twist angle between the two layers—provides a powerful tuning knob of the electronic properties of the heterostructure. Seminal results have been obtained in twisted bilayer graphene, where superconducting and correlated insulating states are created by fine control of the twist angle6,7,8,9. In semiconductors, such as transition metal dichalcogenides (TMDC) heterobilayers, the moiré lattice has a period on the length scale of an exciton, thereby providing a unique opportunity to create coupled exciton lattices hitherto unavailable in any other systems. A wide variety of phenomena, tunable with the twist angle, may become possible, ranging from single quantum-dot arrays and topological bands to strongly correlated states10,11,12,13,14.
To search for the effects of moiré lattices on excitons, split-exciton states have been reported in TMDC bilayers with very small twist angles, demonstrating localization of exciton states likely in moiré supercells15,16,17,18. However, increasing the twist angle has led to the suppression of measurable features of moiré excitons. In WS2/MoSe2 heterobilayers, it was suggested that the resonant interlayer hybridization amplifies the moiré superlattice effects on the electronic structure19; yet only a single resonance was resolved as the twist angle deviates significantly from 0° or 60°18. Existence of moiré superlattice for exciton in large-twist-angle bilayers and nontrivial effects of the twist-angle on excitons remain largely unexplored in experiments.
In this work, we show moiré excitons in heterobilayer of a wide range of twist angles and demonstrate tuning of their properties by the moiré lattice or the twist angle. Utilizing the inter- and intralayer hybrid excitons in WS2/MoSe2 bilayers, we reveal the formation of moiré reciprocal lattices with Brillouin zones of different sizes at different twist angles. We furthermore show how the moiré reciprocal lattices drastically change the properties of the moiré excitons, such as their resonance energies, oscillator strengths, and inter-/intralayer mixing. The twist-angle dependence of the moiré exciton states is well-explained by an analytical theory model based on band folding in the moiré lattice, which also consistently explain the dependence on the spin–orbit splitting of the conduction band, valley selection rules, atomic stacking orders, and the lattice symmetries. Comparing the experimental results with the model, we obtain the effective mass of the interlayer excitons, the interlayer electron-tunneling strength.
Results
The devices used in this work are WS2/MoSe2 heterobilayers with different twist angles θ, capped by few-layer hexagonal boron nitride (hBN). Details of sample fabrication and calibration of θ have been described elsewhere20,21 and provided in the “Method” section. Figure 1a shows the optical microscope image of a heterobilayer, where the sharp edges of two monolayers are aligned. The twist angle is θ = 59.8° ± 0.3°, determined optically using polarization-dependent second-harmonic-generation measurements20,21 (see Supplementary Figs. 1 and 2 and Supplementary Notes 3 and 4 for details).
Identification and analysis of inter- and intralayer hybrid excitons
We first characterize exciton hybridization in closely aligned heterobilayers, with a twist angle θ ~ 0° or 60°. In such bilayers, the Brillouin zones of the two layers closely overlap in momentum space to form nearly direct bandgaps for both the inter- and intralayer transitions (top panels of Fig. 1b). At the same time, the hole band offset is large, but the conduction-band offset is small between WS2 and MoSe2 (middle panels of Fig. 1b). Therefore interlayer electron tunneling is expected between states of the same spin and valley, which leads to hybridization between the corresponding intra- and interlayer exciton transitions that share the same hole state (bottom panels of Fig. 1b).
Making use of the large difference in oscillator strength between spatially direct and indirect excitons, we identify the formation of hybrid states via the reflectance contrast (RC) spectra at 4 K: \({\rm{RC}}=\frac{{{\rm{R}}}_{{\rm{sample}}}\,-\,{{\rm{R}}}_{{\rm{sub}}}}{{{\rm{R}}}_{{\rm{sub}}}}\), where Rsample and Rsub are reflection spectrum taken from sample and substrate respectively (see Supplementary Fig. 3 and Note 5). The interlayer exciton has an oscillator strength two to three orders of magnitude weaker than that of the intralayer exciton, due to separation of the electron and hole wavefunction22,23,24, so it is typically too weak to be measurable in absorption or RC spectroscopy where the noise level is typically 1% or higher (Supplementary Fig. 4 and Note 6). However, when interlayer excitons hybridize with intralayer ones via electron or hole tunneling, the hybrid states acquire an oscillator strength through the intralayer exciton component. Therefore, we can identify the hybrid excitons via their spectral weight in the absorption spectra of the heterobilayer.
As shown in Fig. 1c, the MoSe2 monolayer region of the device (as marked on Fig. 1a) shows a strong intralayer MoSe2 A exciton resonance near 1.65 eV, while the WS2 monolayer has no exciton resonances nearby. In the bilayer, stacking of the WS2 layer is expected to lead to a red shift of MoSe2 A exciton resonance18 while also introducing an interlayer exciton transition, between an electron in WS2 and a hole in MoSe2. The interlayer exciton has a negligible oscillator strength and should not be observable in RC. However, two clearly resolved resonances appear in our bilayer, both with significant spectral weight (top two spectra in Fig. 1c). The same two resonances are also measured in photoluminescence (see Supplementary Fig. 5 and Note 7). We therefore identify them as the inter- and intralayer hybrid states, the lower (LHX) and upper hybrid excitons (UHX). Both LHX and UHX inherit an oscillator strength from their intralayer component18, with the ratio fLHX/fUHX controlled by their intralayer exciton fractions, which in turn is controlled by the energy detuning δ = EIX − EX between the uncoupled interlayer (EIX) and intralayer (EX) resonances. Therefore fLHX/fUHX greater or less than one corresponds to positive or negative detuning δ. There are multiple pairs of intra- and interlayer excitons that can hybridize. We focus on the transition region of MoSe2 A exciton first and label these states as MoA excitons, of which the hole is always in the highest MoSe2 valence band. Other pairs will be analyzed later.
As clearly seen in Fig. 1c, in the R-stacking bilayers (θ = 2. 1°), fLHX/fUHX >1, suggesting the uncoupled interlayer state lies above the intralayer one, or δR > 0. In contrast, in the H-stacking bilayer (θ = 59.8°), fLHX/fUHX <1, suggesting δH < 0. These results are consistent with the spin selection rules of the excitonic transitions illustrated in Fig. 1b25. Assuming the interlayer exciton-binding energy is about the same in R- and H-stacking bilayers26, and the difference δR − δH is comparable to the spin–orbit splitting of WS2 conduction band (Fig. 1b).
To analyze the results quantitatively, we first obtain the energies, ELHX and EUHX, and oscillator strengths of the hybrid states by fitting the RC spectra using the transfer matrix method, where the hybrid excitons are modeled as Lorentz oscillators (see “Methods”, Supplementary Fig. 3 and Note 5)25,27. The fitted spectrum agrees well with the data, as shown in Fig. 1c. Describing the hybrid modes with the coupled oscillator model, we have \({E}_{{\rm{LHX}}}-{E}_{{\rm{UHX}}}=-\sqrt{4{J}^{2}+{\delta }^{2}}\), and \(\frac{{f}_{{\rm{LHX}}}}{{f}_{{\rm{UHX}}}}=\frac{\sqrt{{\delta }^{2}\,+\,4{J}^{2}}\,+\,\delta }{\sqrt{{\delta }^{2}\,+\,4{J}^{2}}\,-\,\delta }\) (see Supplementary Note 1 for details). Thereby using the fitted ELHX,UHX and fLHX,UHX, we can obtain δ and J. As summarized in Fig. 1d, we obtain J ~ 20 meV for both R- and H-stacking and δR − δH = 25.9 ± 0.5 meV, consistent with the spin–orbit splitting of WS228, confirming the hybrid states are formed by spin-conserved interlayer electron tunneling.
Twist-angle dependence of moiré-lattice-induced hybrid excitons
To study tuning of the hybrid excitons by the moiré lattice, we perform the same measurements and analysis as discussed above on 30 samples with different twist angles, and obtain how the exciton energies, oscillator strengths and interlayer tunneling vary with the changing moiré lattice. We define θ0 < 30° as the angular deviation from aligned bilayers of R- or H-stacking. θ0 = ∣θ∣ for R stacking and θ0 = ∣60° − θ∣ for H-stacking.
As shown in Fig. 2a, the MoA hybrid exciton doublets are clearly resolved for θ0 up to 6°, which would correspond to a tuning of the moiré lattice constant by nearly threefold29. The spectral weights of the doublets evolve continuously with the twist angle, reflecting the continuous increase of fLHX/fUHX and δ with θ0 (middle panel of Fig. 2c). At the same time, the interlayer coupling J decreases continuously (bottom panel of Fig. 2c). These observations show clearly moiré lattice induce hybridization and tuning of intralayer and interlayer excitons, as we explain below.
We illustrate in Fig. 2b the MoA exciton bands at different twist angles, corresponding to the six samples shown in Fig. 2a. The intralayer MoSe2A exciton transition (red band) remains direct, with the band minimum at zero center-of-mass momentum qX ~ 0, irrespective of the twist angle. It is close in energy with the interlayer exciton formed by a hole from the same MoSe2 valence band but an electron from a WS2 conduction band. This interlayer exciton band has the band minimum also at zero center-of-mass momentum: qIX ~ 0, when θ ~ 0° (θ1 in Fig. 2a, b) or 60° (θ6 in Fig. 2a, b), neglecting the small lattice constant mismatch.
As the two lattices rotate relative to each other by θ (θ2 to θ5 in Fig. 2a, b), the Brillouin zones of MoSe2 and WS2 also rotate by θ. The interlayer exciton band minimum shifts away from the intralayer exciton band minimum by momentum KW − KM for R stacking, where KM and KW are, respectively, the Brillouin zone corners for MoSe2 and WS2 layers. Due to this momentum mismatch, hybridization between intralayer MoSe2A excitons and the interlayer state at the band minimum is not allowed.
However, interlayer electron tunneling in the moiré lattice can lead to the formation of new moiré miniband states to hybridize with the optically bright intralayer excitons. As illustrated in Figs. 2b and 3c, three interlayer excitons \({\left|{{\boldsymbol{q}}}_{i}\right\rangle }_{\text{IX}}\) overlap with the optically bright intralayer exciton, where the center-of- mass momentum qi, measured relative to the band minimum of interlayer exciton, correspond to q1 = KM − KW for R stacking, with q2,3 connected to q1 by 2π/3 and 4π/3 rotations, respectively, via moiré reciprocal lattice vectors. These three interlayer states are offset from their band minimum by the kinetic energy \({\hslash }^{2}{q}_{i}^{2}/(2{M}_{\text{IX}})\), for i = 1, 2, 3, and MIX the total mass of interlayer exciton. These three states can couple due to the moiré lattice and therefore, superpose to form moiré miniband states, of which one interlayer exciton state shares the same angular momentum as the intralayer MoSe2A exciton at qX ~ 0, giving rise to the hybrid doublet we observe in angularly misaligned bilayers (see Supplementary Note 2).
When θ deviates more from 0° or 60°, the interlayer exciton formed in the moiré lattice continuously blueshifts because of the increasing kinetic energy, which explains the measured continuous blueshift of the LHX and UHX resonances, and the continuous increase of the spectral weight of LHX compared to UHX.
Theoretical analysis of moiré-lattice-induced hybrid excitons
To analyze our results more quantitatively, we develop an analytical microscopic theory based on the above understanding (see Supplementary Note 2 for details). Comparing it with the measured twist-angle dependence of the hybrid states, we obtain the key band parameters of the bilayer, including the interlayer exciton effective mass and interlayer coupling strength.
We first compare the measured detuning δ with θ0 and the interlayer exciton kinetic energy. As discussed above, δ is given by:
where δ0 is the detuning at θ = 0° or 60° for bilayers close to R- and H-stacking, respectively. q1 is equal to 4π/(3aM), and aM is the moiré period approximated by \({a}_{0}/\sqrt{{\theta }_{0}^{2}+{\epsilon }^{2}}\), for a0 the monolayer lattice constant and ϵ the lattice constant mismatch \(| {a}_{0}-{a}_{0}^{\prime}| /{a}_{0}\) between the two layers. Equation (1) shows that δ increases quadratically with θ0. As θ0 increases from 0° to 6°, aM changes by nearly threefold, and δ − δ0 changes by sevenfold29. Fitting the measured δ vs. θ0 with Eq. (1), we find the interlayer exciton total mass MIX to be (6.9 ± 3.2)m0 and (1.41 ± 0.28)m0 for R- and H-stacking heterobilayers, respectively, for m0 the electron free mass. These values are greater than the sum of the monolayer electron and hole effective masses. One possible reason is that the electron and hole effective masses in the bilayer may have been modified due to effects such as lattice relaxation30.
We note that strain may lead to deviation in the twist angle and detuning. To minimize the effect of strain, we use devices of high structural integrity as verified by imaging and SHG (see Supplementary Note 4 and Supplementary Fig. 2 for details). The clear trends in the twist-angle dependence shown in Fig. 2 suggest that the effect of strain is relatively small and mainly leads to additional fluctuations in the measurement results above the measurement uncertainties (indicated by the error bars).
From our microscopic theory, we can also estimate the conduction-band interlayer tunneling parameter w from the coupling strength J through the relation
where ϕk and ψk are, respectively, the relative-motion wavefunction for interlayer and intralayer excitons with the normalization \((1/{\mathcal{A}}){\sum }_{{\boldsymbol{k}}}| {\psi }_{{\boldsymbol{k}}}{| }^{2}=1\) and \((1/{\mathcal{A}}){\sum }_{{\boldsymbol{k}}}| {\phi }_{{\boldsymbol{k}}}{| }^{2}=1\). Here, \({\mathcal{A}}\) is the system area, and mh,IX is the hole mass for the interlayer exciton. Because of the momentum shift (mh,IX/MIX)q1 in the integral of Eq. (2), J decreases with increasing θ0, which agrees with the experimentally observed angle dependence of J (Fig. 3c). At small θ0, J can be approximated by \(\sqrt{3}w\). Using our experimentally measured value of J at θ0 ~ 0, we estimate the interlayer tunneling w to be 11.5–14.0 meV for both R- and H-stacking bilayers.
When the twist angle θ0 is greater than 6°, the hybrid exciton doublets become hard to be resolved, likely because there is a large blue detuning and the UHX has a vanishing oscillator strength (see Supplementary Fig. 6 and Note 8).
Moiré excitons in commensurate moiré lattices at twist angles near 21.8° and 38.2°
Remarkably, pronounced and well-resolved doublets reappear in heterobilayers with θ = 20.1° ± 0.3 and 40.3° ± 0.3, as shown in Fig. 3. In the bilayer with 20.1° twist angle, the LHX has a smaller spectral weight than UHX has, corresponding to a negative detuning (δ = − 5.6 meV), which is similar to H-stacking bilayers formed at θ ~ 60°. In contrast, in the bilayer with 40.3° twist angle, the LHX has a larger spectral weight than UHX has, corresponding to a positive detuning (δ = 11.8 meV), which is similar to R-stacking bilayers formed at θ ~0°. In both devices, the coupling strength J ~8 meV is weaker than but of the same order of magnitude as aligned bilayers with θ close to 0° or 60°.
The revival of hybrid excitons in these two bilayers can be understood as a direct result of interlayer tunneling induced by a moiré lattice that is nearly commensurate with the monolayer lattices. The two twist angles are close to the two special commensurate angles 21.8° and 38.2°, respectively22, where the corresponding periodic moiré reciprocal lattices have the largest reciprocal lattice constant, \(1/\sqrt{7}\) of the monolayer reciprocal lattice constant. Corners of the Brillouin zones of the two monolayers become connected by primitive moiré reciprocal lattice vectors, as illustrated in Fig. 3d and e. The MoSe2and WS2band minima overlap again in the moiré reciprocal lattice, allowing strong nearly resonant tunneling between the intra- and interlayer states. Specifically, when θ ≈ 21.8°, K-valley of MoSe2 and \({{\rm{K}}}^{\prime}\)-valley of WS2 are connected by moiré reciprocal lattice vectors and are folded into equivalent momentum in the moiré Brillouin zone (Fig. 3d). The corresponding hybridized excitons have the same valley configuration as those in bilayers with θ ~ 60°, which is consistent with the observed negative detuning. When θ ≈ 38.2°, K-valley of MoSe2 and K-valley of WS2 are folded into equivalent momentum in the moiré Brillouin zone (Fig. 3e), and the corresponding hybridized excitons have the same valley configuration as those in bilayers with θ ~ 0°, consistent with the observed positive detuning. Moreover, since interlayer tunneling only needs one Umklapp scattering by a moiré reciprocal lattice vector, the tunneling strength remains of the same order of magnitude as in angularly aligned bilayers. Therefore, the strong revival of the hybrid excitons and their similarities with the angularly aligned bilayers show again the critical role of moiré lattice in interlayer tunneling.
Moiré excitons formed with different intralayer excitons
In the above discussion, we have focused on hybrid states formed with the MoSe2A excitons, which feature large spectral weight, relatively narrow linewidths, and well-resolved doublets at small detunings. Hybrid states can also form with higher-energy bands, including the A excitons of WS2 (WA), and B excitons of WS2 and MoSe2. The B excitons have broader linewidths than the A excitons; as a result, the doublets are not well resolved. The A excitons of WS2 have a broader linewidth than A excitons of MoSe2 and generally a larger detuning. We observe well-resolved WA doublets only in bilayers with θ ~ 0°, corresponding to hybrid excitons formed by a hole in the WS2 valence band and an electron tunneling between the MoSe2 and WS2 conduction bands (Fig. 4).
It is interesting to compare the detuning for MoA and WA states for θ ~ 0°, which we label as δMoA and δWA, respectively. As shown in the schematic electronic band diagram in Fig. 4a, neglecting exciton-binding energies, the detuning of the interlayer transition from the intralayer one is the same magnitude but opposite signs between the MoA and WA states. The sum of the two detuning should be zero. However, this is different from our observation that both the LHX states have larger spectral weight for both MoA and WA states. This can be understood as due to the weaker binding energy of interlayer excitons compared to intralayer ones, resulting from electron–hole separation. The difference in intra- and interlayer exciton-binding energies, \(\Delta {E}_{{\rm{B}}}^{{\rm{R}}}={E}_{{\rm{BX}}}-{E}_{{\rm{BIX}}}\), adds to both δMoA and δWA. Assuming \(\Delta {E}_{{\rm{B}}}^{{\rm{R}}}\) is approximately the same for the MoA and WA state, the sum of δMoA and δWA becomes twice of ΔEB, or, \(\Delta {E}_{{\rm{B}}}^{{\rm{R}}}=1/2({\delta }_{{\rm{MoA}}}+{\delta }_{{\rm{WA}}})\). From our measurements of MoA and WA states in bilayers with θ < 1°, we estimate \(\Delta {E}_{{\rm{B}}}^{{\rm{R}}}\) of 10–16 meV (Fig. 4b). In comparison, values between 17 meV and 100 meV have been reported based on first principle calculations31,32,33,34 or measurements on homo-bilayers35,36,37. The relatively small values of 10–16 meV we measured may possibly be due to difference in the materials or a smaller interlayer exciton Bohr radius as a result of strong interlayer tunneling.
Discussion
In summary, we demonstrate hybrid states formed between momentum-direct, moiré-induced interlayer, and intralayer excitons in twisted WS2/MoSe2 bilayers, opening the door to studies of excitonic phenomena in twist bilayers.
Deviation of the twist angle from 0° or 60° not only does not suppress moiré excitons but provides a sensitive tuning knob of the moiré excitons’ properties. Persistence of the moiré excitons, or, the moiré lattice, is clearly manifested in the interlayer tunneling strength, which remains within the same order of magnitude over the measured range of twist angles. It is possible because momentum conservation between the twisted layers is restored by the moiré lattice, or Umklapp scattering by the moiré reciprocal lattice vector. Remarkably, while large detuning between the interlayer and intralayer states suppressed hybridization over a range of angles, pronounced hybrid moiré excitons due to strong interlayer tunneling reappears near twist angles of 21.8° and 38.2°. At these angles, moiré-lattices are formed commensurate with the monolayer lattices, bringing angularly shifted valleys of the two monolayers into equivalent momentum in the same moiré Brillouin zone, thereby enabling strong interlayer tunneling. The resulting hybrid exciton states resemble the features in heterobilayers with θ = 60° and 0°, respectively. These results are direct manifestations of the discrete translational symmetry of the underlying moiré superlattice, which enables transitions that otherwise would not conserve momentum.
Since the hybrid excitons are formed in moiré reciprocal lattices, their properties dependent sensitively on the moiré period, or the twist angle. Utilizing the twist angle degree of freedom, we demonstrate tuning of the moiré exciton properties and furthermore obtain fundamental parameters of the bilayer system that are difficult to measure otherwise, including conduction-band splitting of WS2 induced by spin–orbital coupling, the effective mass of the interlayer excitons in R- and H-stacking bilayers, interlayer electron-tunneling strength, and the difference of binding energies between intra- and interlayer excitons at the presence of interlayer tunneling.
These hybrid excitons inherit large oscillator strengths from the intralayer component that may allow strong exciton–photon coupling while, at the same time, inherit static dipole moment from the spatially indirect interlayer component that leads to long-range interactions. In a moiré lattice, both the oscillator strength and dipole interactions depend sensitively on, and can be tuned by the twist angle. The twisted WS2/MoSe2 bilayers may provide tunable, nonlinear, exciton and polariton lattice systems for exotic states of matter, such as topological excitons and exciton crystals, with novel applications in nanophotonics and quantum information science10,11,12,13,38,39,40,41,42,43,44,45,46,47,48,49,50,51,52,53.
Methods
Sample fabrication
Monolayer MoSe2, WS2, and few-layer hBN flakes are obtained by mechanical exfoliation from bulk crystals. A polyethylene terephthalate (PET) stamp was used to pick up the top hBN, WS2 monolayer, MoSe2 monolayer, and the bottom hBN under a microscope. After picking up all the layers, PET stamp was then stamped onto the sapphire substrate, and the PET was dissolved in dichloromethane for six hours at room temperature.
Optical measurements
For low-temperature measurements, the sample is kept in a 4 K cryostat (Montana Instrument). The excitation and collection are carried out with a home-built confocal microscope with an objective lens with a numerical aperture (NA) of 0.42. For reflection contrast measurement, white light from a tungsten halogen lamp is focused on the sample with a beam size of 10 μm in diameter. The spatial resolution is improved to be 2 μm by using pinhole combined with confocal lenses. The signal is detected using a Princeton Instruments spectrometer with a cooled charge-coupled camera.
Data availability
Data are available from the authors upon reasonable request.
Code availability
Code is available from the authors upon reasonable request.
References
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Novoselov, K. S., Mishchenko, A., Carvalho, A. & Castro Neto, A. H. 2D materials and van der Waals heterostructures. Science 353, aac9439–aac9439 (2016).
Rivera, P. et al. Valley-polarized exciton dynamics in a 2D semiconductor heterostructure. Science 351, 688–691 (2016).
Kuwabara, M., Clarke, D. R. & Smith, D. A. Anomalous superperiodicity in scanning tunneling microscope images of graphite. Appl. Phys. Lett. 56, 2396–2398 (1990).
Zhang, C. et al. Interlayer couplings, Moiré patterns, and 2D electronic superlattices in MoS2/WSe2 hetero-bilayers. Sci. Adv. 3, e1601459 (2017).
Cao, Y. et al. Unconventional superconductivity in magic-angle graphene superlattices. Nature 556, 43–50 (2018).
Cao, Y. et al. Correlated insulator behaviour at half-filling in magic-angle graphene superlattices. Nature 556, 80–84 (2018).
Chen, G. et al. Signatures of tunable superconductivity in a trilayer graphene moiré superlattice. Nature 572, 215–219 (2019).
Chen, G. et al. Evidence of a gate-tunable Mott insulator in a trilayer graphene moiré superlattice. Nat. Phy. 15, 237–241 (2019).
Wu, F., Lovorn, T. & MacDonald, A. H. Topological exciton bands in moiré heterojunctions. Phys. Rev. Lett. 118, 147401 (2017).
Yu, H., Liu, G.-B., Tang, J., Xu, X. & Yao, W. Moiré excitons: from programmable quantum emitter arrays to spin-orbit-coupled artificial lattices. Sci. Adv. 3, e1701696 (2017).
Wu, F., Lovorn, T. & MacDonald, A. H. Theory of optical absorption by interlayer excitons in transition metal dichalcogenide heterobilayers. Phys. Rev. B 97, 035306 (2018).
Wu, F., Lovorn, T., Tutuc, E. & MacDonald, A. H. Hubbard model physics in transition metal dichalcogenide Moiré bands. Phys. Rev. Lett. 121, 026402 (2018).
Tong, Q. et al. Topological mosaics in moiré superlattices of van der Waals heterobilayers. Nat. Phys. 13, 356–362 (2017).
Jin, C. et al. Observation of moiré excitons in WSe2/WS2 heterostructure superlattices. Nature 567, 76–80 (2019).
Tran, K. et al. Evidence for moiré excitons in van der Waals heterostructures. Nature 567, 71–75 (2019).
Seyler, K. L. et al. Signatures of moiré-trapped valley excitons in MoSe2/WSe2 heterobilayers. Nature 567, 66–70 (2019).
Alexeev, E. M. et al. Resonantly hybridized excitons in moiré superlattices in van der Waals heterostructures. Nature 567, 81–86 (2019).
Ruiz-Tijerina, D. A. & Fal’ko, V. I. Interlayer hybridization and moiré superlattice minibands for electrons and excitons in heterobilayers of transition-metal dichalcogenides. Phys. Rev. B 99, 125424 (2019).
Zhang, L. et al. Highly valley-polarized singlet and triplet interlayer excitons in van der Waals heterostructure. Phys. Rev. B 100, 041402 (2019).
Paik, E. Y. et al. Interlayer exciton laser of extended spatial coherence in atomically thin heterostructures. Nature 576, 80–84 (2019).
Yu, H., Wang, Y., Tong, Q., Xu, X. & Yao, W. Anomalous light cones and valley optical selection rules of interlayer excitons in twisted heterobilayers. Phys. Rev. Lett. 115, 187002 (2015).
Ross, J. S. et al. Interlayer exciton optoelectronics in a 2D heterostructure p-n junction. Nano Lett. 17, 638–643 (2017).
Van der Donck, M. & Peeters, F. M. Interlayer excitons in transition metal dichalcogenide heterostructures. Phys. Rev. B 98, 115104 (2018).
Hsu, W.-T. et al. Tailoring excitonic states of van der Waals bilayers through stacking configuration, band alignment, and valley spin. Sci. Adv. 5, 12 (2019).
Lu, N. et al. Twisted MX2/MoS2 heterobilayers: effect of van der Waals interaction on the electronic structure. Nanoscale 9, 19131–19138 (2017).
Li, Y. et al. Measurement of the optical dielectric function of monolayer transition-metal dichalcogenides: MoS2, MoSe2, WS2, and WSe2. Phys. Rev. B 90, 205422 (2014).
Liu, G.-B., Xiao, D., Yao, Y., Xu, X. & Yao, W. Electronic structures and theoretical modelling of two-dimensional group-VIB transition metal dichalcogenides. Chem. Soc. Rev. 44, 2643–2663 (2015).
Rasmussen, F. A. & Thygesen, K. S. Computational 2D materials database: electronic structure of transition-metal dichalcogenides and oxides. J. Phys. Chem. C 119, 13169–13183 (2015).
Nam, N. N. T. & Koshino, M. Lattice relaxation and energy band modulation in twisted bilayer graphene. Phys. Rev. B 96, 075311 (2017).
Latini, S., Winther, K. T., Olsen, T. & Thygesen, K. S. Interlayer excitons and band alignment in MoS2/hBN/WSe2 van der Waals heterostructures. Nano Lett. 17, 938–945 (2017).
Chaves, A., Azadani, J. G., Özçelik, V. O., Grassi, R. & Low, T. Electrical control of excitons in van der Waals heterostructures with type-II band alignment. Phys. Rev. B 98, 121302 (2018).
Gillen, R. & Maultzsch, J. Interlayer excitons in MoSe2/WSe2 heterostructures from first principles. Phys. Rev. B 97, 165306 (2018).
Ovesen, S. et al. Interlayer exciton dynamics in van der Waals heterostructures. Commun. Phys. 2, 23 (2019).
Horng, J. et al. Observation of interlayer excitons in MoSe2 single crystals. Physical Review B 97, 241404 (2018).
Gerber, I. C. et al. Interlayer excitons in bilayer MoS2 with strong oscillator strength up to room temperature. Phys. Rev. B 99, 035443 (2019).
Sung, J. et al. Broken mirror symmetry in excitonic response of reconstructed domains in twisted MoSe2/MoSe2 bilayers. Nat. Nanotechnol. 15, 750–754 (2020).
Xu, W. et al. Correlated fluorescence blinking in two-dimensional semiconductor heterostructures. Nature 541, 62–67 (2017).
Unuchek, D. et al. Room-temperature electrical control of exciton flux in a van der Waals heterostructure. Nature 560, 340–344 (2018).
Wang, G. et al. Colloquium: excitons in atomically thin transition metal dichalcogenides. Rev. Mod. Phys. 90, 021001 (2018).
Tang, Y. et al. Simulation of Hubbard model physics in WSe2/WS2 moiré superlattices. Nature 579, 353–358 (2020).
Regan, E. C. et al. Mott and generalized Wigner crystal states in WSe2/WS2 moiré superlattices. Nature 579, 359–363 (2020).
Shimazaki, Y. et al. Strongly correlated electrons and hybrid excitons in a moiré heterostructure. Nature 580, 472–477 (2020).
Merkl, P. et al. Ultrafast transition between exciton phases in van der Waals heterostructures. Nat. Mater. 18, 691–696 (2019).
Wang, Z. et al. Evidence of high-temperature exciton condensation in two-dimensional atomic double layers. Nature 574, 76–80 (2019).
Zhang, X.-X. et al. Gate-tunable spin waves in antiferromagnetic atomic bilayers. Nat. Mater. 19, 838–842 (2020).
Karni, O. et al. Infrared interlayer exciton emission in MoS2/WSe2 heterostructures. Phys. Rev. Lett. 123, 247402 (2019).
Scuri, G. et al. Electrically tunable valley dynamics in twisted WSe2/WSe2 bilayers. Phys. Rev. Lett. 124, 217403 (2020).
Tang, Y. et al. Spatially mixed moiré excitons in two-dimensional van der Waals superlattices. Preprint at https://arxiv.org/abs/2002.10067 (2020).
Bai, Y. et al. Excitons in strain-induced one-dimensional moiré potentials at transition metal dichalcogenide heterojunctions. Nat. Mater. 19, 1068–1073 (2020).
Jauregui, L. A. et al. Electrical control of interlayer exciton dynamics in atomically thin heterostructures. Science 366, 870–875 (2019).
Huang, Z. et al. Robust room temperature valley Hall effect of interlayer excitons. Nano Lett. 20, 1345–1351 (2020).
Zhou, Y. et al. Controlling excitons in an atomically thin membrane with a mirror. Phys. Rev. Lett. 124, 027401 (2020).
Acknowledgements
L.Z., R.G., S.H, S.F., and H.D. acknowledge support by the Army Research Office under Award W911NF-17-1-0312. H.D. also acknowledges support by the National Science Foundation under Award DMR-1838412 and by the Air Force Office of Scientific Research under Award FA2386-18-1-4086. S.F. also acknowledges support by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under Award Number DE-SC0017971. F.W. acknowledges support by Laboratory for Physical Sciences. K.W. and T.T. acknowledge support from the Elemental Strategy Initiative conducted by the MEXT, Japan, Grant Number JPMXP0112101001, JSPS KAKENHI Grant Number JP20H00354 and the CREST (JPMJCR15F3), JST.
Author information
Authors and Affiliations
Contributions
H.D. and L.Z. conceived the experiment. L.Z. and Z.Z. fabricated the device and performed the measurements. F.W. performed the modeling and calculations. L.Z. and H.D. performed data analysis. R.G. performed tunneling estimation. D.W., S.H., K.K., and T.G. assisted the fabrication. K.W. and T.T grew hBN single crystals. H.D. and S.F. supervised the projects. L.Z., F.W., and H.D. wrote the paper with inputs from other authors. All authors discussed the results, data analysis, and wrote the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, L., Zhang, Z., Wu, F. et al. Twist-angle dependence of moiré excitons in WS2/MoSe2 heterobilayers. Nat Commun 11, 5888 (2020). https://doi.org/10.1038/s41467-020-19466-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-19466-6
This article is cited by
-
Tuning commensurability in twisted van der Waals bilayers
Nature (2024)
-
Excitonic devices based on two-dimensional transition metal dichalcogenides van der Waals heterostructures
Frontiers of Chemical Science and Engineering (2024)
-
Twistronics and moiré excitonic physics in van der Waals heterostructures
Frontiers of Physics (2024)
-
Distinct moiré textures of in-plane electric polarizations for distinguishing moiré origins in homobilayers
Science China Physics, Mechanics & Astronomy (2023)
-
Interlayer exciton dynamics of transition metal dichalcogenide heterostructures under electric fields
Nano Research (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.