Abstract
Based on the first-principles calculations and experimental measurements, we report that the hexagonal phase of ternary transition metal pnictides TT’X (T=Zr, Hf; T’=Ru; X=P, As), which are well-known noncentrosymmetric superconductors with relatively high transition temperatures, host nontrivial bulk topology. Before the superconducting phase transition, we find that HfRuP belongs to a Weyl semimetal phase with 12 pairs of type-II Weyl points, while ZrRuAs, ZrRuP and HfRuAs belong to a topological crystalline insulating phase with trivial Fu-Kane \({{\mathbb{Z}}}_{2}\) indices but nontrivial mirror Chern numbers. High-quality single crystal samples of the noncentrosymmetric superconductors with these two different topological states have been obtained and the superconductivity is verified experimentally. The wide-range band structures of ZrRuAs have been identified by ARPES and reproduced by theoretical calculations. Combined with intrinsic superconductivity, the nontrivial topology of the normal state may generate unconventional superconductivity in both bulk and surfaces. Our findings could largely inspire the experimental searching for possible topological superconductivity in these compounds.
Similar content being viewed by others
Introduction
Topological insulators (TIs)1,2 and semimetals3,4,5,6,7 have received a tremendous amount of attention in the last decade due to the appearance of exotic properties, such as spin-momentum locked gapless surface state in TIs8,9, Fermi-arc states10,11,12 and negative magnetoresistance in Weyl semimetals (WSMs)7,13,14. These insulators can be characterized by topological invariants/indices, like Fu-Kane \({{\mathbb{Z}}}_{2}\) indices15 and mirror Chern numbers16,17 for TIs and topological crystalline insulators (TCIs), respectively. However, WSMs are topological metallic states with discrete accidental twofold degenerate points, described by the three-dimensional (3D) Weyl equation. Due to the lack of strict Lorentz invariance, the type-II Weyl points can be strongly tilted18, which have no analogy in high-energy physics. In contrast to the point-like bulk Fermi surfaces of the type-I WSMs7,19,20,21,22,23,24,25, these type-II WSMs26,27,28,29,30 have both electron pockets and hole pockets touching at the Weyl points, resulting in various novel physical properties31,32.
Topological materials that host superconductivity are ideal systems to detect topological superconductivity (TSC) and Majorana fermions33,34,35,36,37,38,39. The topological surface Dirac-cone states can be used to generate two-dimensional (2D) TSC induced by the intrinsic bulk superconductivity40,41,42,43. Very recently, the superconducting gap of the predicted topological surface Dirac-cone states in FeTe1-xSex44,45 has been detected in recent angle-resolved photoemission spectroscopy (ARPES)46 and scanning tunneling microscope experiments47. In noncentrosymmetric WSMs, 3D time-reversal symmetric TSC can arise from sign-changing superconductivity in Fermi surfaces with different Chern numbers48,49. However, to the best of our knowledge, almost all noncentrosymmetric WSMs need external pressure or doping to induce or enhance superconductivity50,51,52,53,54,55. Due to the lack of suitable candidates, 3D TSC is studied very little experimentally. Therefore, the material proposal of a WSM with high-quality single crystals and relatively higher superconducting transition temperature (\({T}_{\mathrm{C}}\)) is of great interest.
Ternary transition metal pnictides TT’X (T=Zr, Hf; T’=Ru; X=P, As) are a series of well-known superconductors56,57. As we know, there are three different types of crystal structures for these compounds57,58, i.e. the Fe\({}_{2}\)P-type hexagonal structure (h-phase), the TiNiSi-type orthorhombic structure (o-phase), and the TiFeSi-type orthorhombic structure (o\(^{\prime}\)-phase). Superconductivity is found in both h- and o-phases, and the superconducting transition temperature \({T}_{\mathrm{C}}\) is generally higher for h-phase than that for o-phase. In this work, we only focus on the h-phase of TT’X, exhibiting relatively high \({T}_{\mathrm{C}}\) (such as 12.7 K for HfRuP56, 13.3 K for ZrRuP and 12 K for ZrRuAs57). Based on the first-principles calculations, the nontrivial topological properties of these materials in the normal state (above \({T}_{\mathrm{C}}\)) are revealed. When spin-orbit coupling (SOC) is ignored, they possess two nodal rings slightly above the Fermi energy (\({E}_{\mathrm{F}}\)) in the \({k}_{z}=0\) plane, with each surrounding a K point in the hexagonal Brillouin zone (BZ). After the consideration of SOC, they enter either a WSM phase (e.g., HfRuP) with 12 pairs of type-II Weyl points (WPs) due to the lack of inversion symmetry, or a topological crystalline insulating (TCI) phase (e.g., ZrRuAs) with trivial Fu-Kane \({{\mathbb{Z}}}_{2}\) indices59 but nontrival mirror Chern numbers. The nontrivial electronic topology in these materials could intrigue tremendous experimental study of the interplay between topological electronic states and superconductivity.
Results and discussion
Crystal structure and electronic band structures
The h-phase of TT’X is of space group \(P\bar{6}2m\) (#189) with a layered structure. Each layer in the hexagonal lattice is occupied by either T and X atoms or T’ and X atoms. All atoms have positions in the layers parallel to the crystallographic ab-plane and separated by a half of the lattice constant c. The triangular clusters of three T’ atoms (T’\({}_{3}\)) are formed in the ab-plane. In the crystal structure of the TT’X shown in Fig. 1a, b, the T’\({}_{3}\) clusters and the planer structure are clearly shown. The high-symmetry k-points and surface projections are shown in Fig. 1c. The structure has two kinds of mirror symmetries, \({m}_{z}\;{\mathrm{and}}\;{m}_{x}\), which are vital to define the mirror Chern numbers as will be shown below. Meantime, we have successfully grown the single crystals of ZrRuAs and HfRuP, as shown in Fig. 1d, e, respectively. The hexagonal structure and superconductivity are confirmed by the x-ray diffraction (XRD) and resistivity measurements, respectively. More details and data (i.e., magnetic susceptibility) can be found in the Supplementary Material.
We first checked the electronic band structure without SOC. Among these compounds, we mainly investigated HfRuP and ZrRuAs for details in the following, as typical examples of the type-II WSM phase and TCI phase, respectively. More results on other compounds are presented in the Supplementary Material. From the band dispersion of HfRuP in Fig. 2a, one can notice there is a direct energy gap shadowed in light blue near \({E}_{\mathrm{F}}\), except the band crossings along both \(M-K\,{\mathrm{and}}\,K-\Gamma\) lines. These two lines are actually in the \({k}_{z}=0\) plane, where the \({m}_{z}\) symmetry is present. The \({m}_{z}\) eigenvalues of the two crossing bands are computed to be \(\pm \!1\), respectively. Thus, the two crossing points are parts of the \({m}_{z}\)-protected nodal rings, each of which surrounds a K point in the \({k}_{z}=0\) plane, as depicted in Fig. 2c. This situation is different from that in CaAgAs60, where there is only one nodal ring surrounding the \(\Gamma\) point. The two nodal rings circled around two K points are also found for all other compounds (see electronic band structures of ZrRuAs, HfRuAs and ZrRuP in Supplementary Section A). We conclude that the band inversion happens at the K point, which is supported by the theory of topological quantum chemistry61,62. By exchanging the highest valence band (\({\Gamma }_{4}\)) and the lowest conduction band (\({\Gamma }_{1}\)) at the K point (with little group \({D}_{3h}\)) only, the occupied bands become trivial, being a linear combination of elemental band representations61.
After including SOC, the band structure doesn’t change too much, but the bands do split due to the lack of inversion symmetry. To confirm the reliability of the density functional theory (DFT) band structures, we have performed ARPES measurement for ZrRuAs, shown in Fig. 2f–i. The observed spectra along H-K-H and L-M-L lines match very well with the DFT calculations (red lines in Fig. 2g, i), especially for the low-energy bands. We clearly see that the energy bands at K point are much lower than that at M point. In addition, the degeneracy of the two nodal rings is lifted by SOC. The 2D time-reversal invariant (TRI) planes (e.g., \({k}_{y}=0\,{\mathrm{and}}\,{k}_{z}=0\) etc.) become fully gapped, making the \({{\mathbb{Z}}}_{2}\) invariants well-defined. In CaAgAs, the single nodal line enclosing \(\Gamma\) point guarantees that the \({k}_{y}=0\) (or \({k}_{z}=0\)) plane is \({{\mathbb{Z}}}_{2}\) nontrivial with an infinitesimal SOC gap. But, it’s not the case with two nodal rings around two K points. The \({{\mathbb{Z}}}_{2}\) invariants for both \({k}_{y}=0\,{\mathrm{and}}\,{k}_{z}=0\) planes remain trivial in the series of these compounds. Note that the \({k}_{y}=0\) plane is gapped even without SOC, and no gapless point is found in all TRI planes. To confirm triviality of \({{\mathbb{Z}}}_{2}\) invariants, we have calculated the Wannier charge centers (WCCs) of the \({k}_{z}\)-directed (\({k}_{y}\)-directed) Wilson loops as a function of \({k}_{x}\) (called Wilson-loop bands) for the \({k}_{y}=0\) (\({k}_{z}=0\)) plane. The results of ZrRuAs are shown in Fig. 3a, b, suggesting a trivial \({{\mathbb{Z}}}_{2}\) invariant in the \({k}_{y}=0\) plane and \({k}_{z}=0\) plane. Accordingly, the Fu-Kane \({{\mathbb{Z}}}_{2}\) indices59 for the 3D bulk are computed to be (0;000) for all the compounds. The detailed calculations for the \({{\mathbb{Z}}}_{2}\) invariants in all six TRI planes (only four of them are distinct due to the symmetry) are presented in Supplementary Section B63. Furthermore, the symmetry indicators64,65,66,67 for these compounds are computed to be \({{\mathbb{Z}}}_{3m,0}=1\;{\mathrm{and}}\;{{\mathbb{Z}}}_{3m,\pi }=0\), revealing the topological nature of the SOC gap (shadowed in light blue) in Fig. 2b.
Mirror Chern numbers and WPs
Due to the presence of mirror symmetry, the mirror Chern number is well defined as long as the mirror plane is fully gapped. Because time-reversal symmetry commutes with the mirror symmetries, the Chern numbers satisfy \({C}_{i}=-{C}_{-i}\), with the subscript \(\pm i\) representing the mirror eigenvalues in the presence of SOC. With time-reversal symmetry, the mirror Chern number is defined as \({C}_{m}=({C}_{+i}-{C}_{-i})/2\). As we know, it can be further reduced to \({\chi }_{+i}-{\chi }_{-i}\) in half of the mirror plane, where \({\chi }_{+i(-i)}\) is easily obtained in the plot of Wilson-loop bands, by counting the number of the positively-sloped bands crossing a horizontal reference line (the dashed line in Fig. 3c, d) and subtracting from it the number of the negatively-sloped crossing ones in the mirror eigenvalue \(+i\,(-i)\) subspace. The results of ZrRuAs for the \({k}_{z}=0\) plane are shown in Fig. 3b. The mirror Chern number \({C}_{{m}_{z}}\) in ZrRuAs is computed to be \(-2\) for the \({k}_{z}\) = 0 plane, while it’s zero for the \({k}_{z}=\pi\) plane. That’s the case for all the compounds (see more in Supplementary Section C).
The lack of inversion symmetry allows the appearance of WPs in the systems. The nonzero mirror Chern number \({C}_{{m}_{z}}=-2\) suggests there are some strings of gauge singularities (i.e., the Dirac string) going through the \({k}_{z}=0\) plane68, which have to either terminate at WPs in the 3D BZ, or thread some other nontrivial planes. Our systematic calculations show that these compounds can be classified into two classes: (i) one has zero Chern number \({C}_{{m}_{x}}=0\) with 12 pairs of type-II WPs, termed a WSM phase; (ii) the other one has nonzero mirror Chern number \({C}_{{m}_{x}}=2\) with no WPs, termed a TCI phase. In the WCCs of HfRuP for the \({k}_{x}=0\) plane in Fig. 3c, \({C}_{{m}_{x}}\) is obtained to be 0. WPs are found in this compound, which is consistent with the topological WSM phase. However, for ZrRuAs, HfRuAs and ZrRuP, \({C}_{{m}_{x}}\) turns out to be 2, as shown in Fig. 3d and in Supplementary Section C. Accordingly, no WP is found in these three materials. The detailed calculations of mirror Chern numbers are presented in Supplementary Section C.
By checking the energy gap and the associated topological monopole charge, we find that six pairs of WPs emerge from each nodal ring. Thus, there are 12 pairs of WPs in total (as shown in the first BZ in Fig. 2c). They reside at the same energy, because they are all related by either time-reversal symmetry or the crystalline symmetry \({D}_{3h}\) (including 12 symmetry operators). The coordinate of the WP W1 enclosed by a dashed circle in Fig. 2c is [0.2761\({\bf{a}}\)*, \(-0.4654{\bf{b}}\)*, 0.02439\({\bf{c}}\)*]. From the band dispersion of the WP W1 along the \({k}_{z}\)-direction (Fig. 2d) and the P-Q direction (Fig. 2e), we conclude that it belongs to a type-II WP69, and its energy level (\({E}_{\mathrm{W}}\)) is about 28 meV above \({E}_{\mathrm{F}}\) (i.e., \({E}_{\mathrm{W}}\) − \({E}_{\mathrm{F}}=28\) meV), very close to the Fermi energy. The topological monopole charge is computed with the Wilson-loop method applied on an enclosed manifold surrounding a single WP. The monopole charge of the WP W1 is +1. The distribution of all the WPs above the \({k}_{z}=0\) plane is illustrated in Fig. 2c, with the “+(o)” symbol representing the topological monopole charge of \(+1(-1)\), while these below the \({k}_{z}=0\) plane possess the opposite monopole charge shown in Fig. 2c because of the \({m}_{z}\) symmetry.
Fermi arcs on surfaces
Surface Fermi arcs connecting the projections of two WPs with opposite chirality are expected in a WSM. For this purpose, the surface spectrum is computed based on the surface Green’s function method70 in the maximally localized Wannier function (MLWF) Hamiltonian of a half-infinite structure. First, the (001)-surface energy contour of HfRuP is obtained in Fig. 4a with \(E-{E}_{\mathrm{W}}=0\) meV. Since the two WPs with opposite chirality project onto the same point on the (001)-surface, no topological arc states are guaranteed to come out from the projections. However, we find that there are two trivial arc states (following the two dashed guiding lines) coming out of each WP projection: one is crossing the \({k}_{x}=0\) line; the other one is crossing the BZ boundary, (i.e., the \(\bar{K}-\bar{M}\) line. Second, the computed (100)-surface energy contour is presented in Fig. 4b. Since they are type-II WPs, the WPs should be located at the touching points between the electron pocket and the hole pocket. We do see that the projected points A and B are the touching points of two pockets. The constant energy contour with energy slightly below (or above) \({E}_{\mathrm{W}}\) is presented in Supplementary Section D. We find that two surface Fermi arc states (indicated by dashed lines) are connected to the projected points (i.e., A and B). For the projected point C, it’s hard to see any surface state from it, because it is not projected onto a proper surface. At last, the computed (010)-surface energy contour is obtained and shown in Fig. 4c, where the WPs with the same chirality project onto each other. As long as the projected electron/hole pockets (enclosing the projections of the WPs) are separated from each other, two topological Fermi arc states can be expected. Unfortunately, the metallic bulk states are projected into a big continuum, which makes the Fermi arc states invisible. Our ARPES experiment to search for the arc states on the (100)-surface is still in process.
Exotic TSC
With intrinsic superconductivity, topological materials are promising platforms to realize TSCs owing to the nontrivial topology of the wave function in normal states. For example, surface Dirac fermions can realize a 2D TSC even for an s-wave pairing state40,44. Also, the FS topology in the normal state directly affects the TSC. In 3D, the integer topological quantum number in a TRI superconductor is determined by the sign of the pairing order parameter and the first Chern number of the Berry phase gauge field on the FSs2. A WSM phase of a superconductor hosts the nontrivial FSs originating from WPs. Providing the two key ingredients: the nontrivial FSs and superconductivity, the WSM phase of HfRuP can be served as a good platform to realize the TRI TSC in 3D. Besides, the previous works71,72 report that the nontrivial mirror Chern number can generate multiple Majorana fermions in Cd\({}_{3}{\mathrm{As}}_{2}\) and SrRuO\({}_{4}\). These compounds in the TCI phase are very promising candidates to search for the topological crystalline superconductors too.
Discussion
Based on the DFT calculations, we find that there are two nodal rings in the band structure without SOC for the h-phase of TT’X, which is different from the situation in CaAgAs. After including SOC, they enter either a WSM phase with 12 pairs of type-II WPs, or a TCI phase with non-zero mirror Chern numbers. The single crystals for the two distinct topological phases are grown successfully. Their superconductivity and electronic band structures are verified by our resistivity, magnetic susceptibility and ARPES measurements, respectively. The series of Ru-based compounds are the desired single-crystal materials, which host both superconductivity below \({T}_{\mathrm{C}}\) and topological states above \({T}_{\mathrm{C}}\). The experimental study of the interplay between superconductivity and Weyl or nontrivial mirror Chern states would be stimulated after this work.
At the stage of finalizing the present paper, we are aware of the mention of Weyl nodes in similar materials in the ref. 73. Our result of WPs in HfRuP is consistent with it, while the result for ZrRuP is different. That is because the topology (the annihilation of Weyl points) in ZrRuP may be sensitive to the parameters of the structure.
Methods
The first-principles calculations were performed based on the DFT with the projector augmented wave (PAW) method74,75 as implemented in VASP package76,77. The generalized gradient approximation (GGA) of Perdew-Burke-Ernzerhof (PBE) type was adopted for the exchange-correlation functional78. The kinetic energy cutoff of the plane wave basis was set to 400 eV. A 10 × 10 × 16 k-point mesh for BZ sampling was adopted. The experimental lattice parameters were employed79,80. The internal atomic positions were fully relaxed until the forces on all atoms were smaller than 0.01 eV/Å (the relaxed atomic positions are shown in Supplementary Section A). The electronic structures were carried out both with and without SOC. The topological invariants and chiral charge were computed through the Wilson-loop technique. The MLWF method was used to calculate the surface states81.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Change history
19 March 2020
A Correction to this paper has been published: https://doi.org/10.1038/s41524-020-0290-0
References
Hasan, M. Z. & Kane, C. L. Colloquium: topological insulators. Rev. Mod. Phys. 82, 3045–3067 (2010).
Qi, X.-L. & Zhang, S.-C. Topological insulators and superconductors. Rev. Mod. Phys. 83, 1057–1110 (2011).
Wan, X., Turner, A. M., Vishwanath, A. & Savrasov, S. Y. Topological semimetal and Fermi-arc surface states in the electronic structure of pyrochlore iridates. Phys. Rev. B 83, 205101 (2011).
Xu, G., Weng, H., Wang, Z., Dai, X. & Fang, Z. Chern semimetal and the quantized anomalous hall effect in HgCr2Se4. Phys. Rev. Lett. 107, 186806 (2011).
Wang, Z. et al. Dirac semimetal and topological phase transitions in A3Bi (A= Na, K, Rb). Phys. Rev. B 85, 195320 (2012).
Wang, Z., Weng, H., Wu, Q., Dai, X. & Fang, Z. Three-dimensional dirac semimetal and quantum transport in Cd3As2. Phys. Rev. B 88, 125427 (2013).
Weng, H., Fang, C., Fang, Z., Bernevig, B. A. & Dai, X. Weyl semimetal phase in noncentrosymmetric transition-metal monophosphides. Phys. Rev. X 5, 011029 (2015).
Pan, Z.-H. et al. Electronic structure of the topological insulator \({{\rm{Bi}}}_{2}{{\rm{Se}}}_{3}\) using angle-resolved photoemission spectroscopy: evidence for a nearly full surface spin polarization. Phys. Rev. Lett. 106, 257004 (2011).
Zhang, H., Liu, C.-X. & Zhang, S.-C. Spin-orbital texture in topological insulators. Phys. Rev. Lett. 111, 066801 (2013).
Xu, N. et al. Observation of weyl nodes and Fermi arcs in tantalum phosphide. Nat. Commun. 7, 11006 (2016).
Xu, S.-Y. et al. Discovery of a weyl fermion semimetal and topological Fermi arcs. Science 349, 613–617 (2015).
Wang, C. et al. Observation of Fermi arc and its connection with bulk states in the candidate type-ii Weyl semimetal WTe2. Phys. Rev. B 94, 241119 (2016).
Huang, X. et al. Observation of the chiral-anomaly-induced negative magnetoresistance in 3D Weyl semimetal TaAs. Phys. Rev. X 5, 031023 (2015).
Zhang, C.-L. et al. Signatures of the Adler-Bell-Jackiw chiral anomaly in a Weyl fermion semimetal. Nat. Commun. 7, 10735 (2016).
Fu, L., Kane, C. L. & Mele, E. J. Topological insulators in three dimensions. Phys. Rev. Lett. 98, 106803 (2007).
Hsieh, T. H. et al. Topological crystalline insulators in the snte material class. Nat. Commun. 3, 982 (2012).
Nie, S., Xu, X. Y., Xu, G. & Fang, Z. Band gap anomaly and topological properties in lead chalcogenides. Chinese Phys. B 25, 037311 (2016).
Soluyanov, A. A. et al. Type-ii Weyl semimetals. Nature 527, 495 (2015).
Huang, S.-M. et al. A Weyl fermion semimetal with surface fermi arcs in the transition metal monopnictide TaAs class. Nat. Commun. 6, 7373 (2015).
Lv, B. et al. Experimental discovery of Weyl semimetal TaAs. Phys. Rev. X 5, 031013 (2015).
Lv, B. et al. Observation of Weyl nodes in TaAs. Nat. Phys. 11, 724 (2015).
Lv, B. et al. Observation of Fermi-arc spin texture in TaAs. Phys. Rev. Lett. 115, 217601 (2015).
Nie, S., Xu, G., Prinz, F. B. & Zhang, S.-c Topological semimetal in honeycomb lattice LnSi. Proc. Natl Acad. Sci. USA 114, 10596–10600 (2017).
Nie, S. et al. Magnetic semimetals and quantized anomalous Hall effect in EuB6. Preprint at https://arxiv.org/abs/1907.10051 (2019).
Wang, Z. et al. Time-reversal-breaking Weyl fermions in magnetic Heusler alloys. Phys. Rev. Lett. 117, 236401 (2016).
Deng, K. et al. Experimental observation of topological fermi arcs in type-II Weyl semimetal MoTe2. Nat. Phys. 12, 1105 (2016).
Jiang, J. et al. Signature of type-II Weyl semimetal phase in MoTe2. Nat. Commun. 8, 13973 (2017).
Tamai, A. et al. Fermi arcs and their topological character in the candidate type-II Weyl semimetal MoTe2. Phys. Rev. X 6, 031021 (2016).
Liang, A. et al. Electronic evidence for type ii Weyl semimetal state in MoTe2. Preprint at arXiv:1604.01706 (2016).
Wang, Z. et al. MoTe2: a type-II Weyl topological metal. Phys. Rev. Lett. 117, 056805 (2016).
Kumar, N. et al. Extremely high magnetoresistance and conductivity in the type-II Weyl semimetals WP2 and MoP2. Nat. Commun. 8, 1642 (2017).
Shekhar, C. et al. Extremely large magnetoresistance and ultrahigh mobility in the topological Weyl semimetal candidate NbP. Nat. Phys. 11, 645 (2015).
Yan, B., Jansen, M. & Felser, C. A large-energy-gap oxide topological insulator based on the superconductor BaBiO3. Nat. Phys. 9, 709 (2013).
Wu, X. et al. \({{\rm{CaFeAs}}}_{2}\): A staggered intercalation of quantum spin hall and high-temperature superconductivity. Phys. Rev. B 91, 081111 (2015).
Schoop, L. M. et al. Dirac metal to topological metal transition at a structural phase change in \({{\rm{Au}}}_{2}{\rm{Pb}}\) and prediction of F 2 topology for the superconductor. Phys. Rev. B 91, 214517 (2015).
Chang, T.-R. et al. Topological dirac surface states and superconducting pairing correlations in \({{\rm{PbTaSe}}}_{2}\). Phys. Rev. B 93, 245130 (2016).
Wang, Y.-Q. et al. Spontaneous formation of a superconductor-topological insulator-normal metal layered heterostructure. Adv. Mater. 28, 5013–5017 (2016).
Bian, G. et al. Prediction of nontrivial band topology and superconductivity in \({\rm{M}}{{\rm{g}}}_{2}{\rm{Pb}}\). Phys. Rev. Mater. 1, 021201 (2017).
Nie, S. et al. Topological phases in the \({{\rm{TaSe}}}_{3}\) compound. Phys. Rev. B 98, 125143 (2018).
Fu, L. & Kane, C. L. Superconducting proximity effect and majorana fermions at the surface of a topological insulator. Phys. Rev. Lett. 100, 096407 (2008).
Fu, L. & Berg, E. Odd-parity topological superconductors: theory and application to \({{\rm{Cu}}}_{x}{{\rm{Bi}}}_{2}{{\rm{Se}}}_{3}\). Phys. Rev. Lett. 105, 097001 (2010).
Alicea, J. New directions in the pursuit of majorana fermions in solid state systems. Rep. Prog. Phys. 75, 076501 (2012).
Sato, M. & Ando, Y. Topological superconductors: a review. Rep. Prog. Phys. 80, 076501 (2017).
Wang, Z. et al. Topological nature of the \({{\rm{FeSe}}}_{0.5}{{\rm{Te}}}_{0.5}\) superconductor. Phys. Rev. B 92, 115119 (2015).
Xu, G., Lian, B., Tang, P., Qi, X.-L. & Zhang, S.-C. Topological superconductivity on the surface of fe-based superconductors. Phys. Rev. Lett. 117, 047001 (2016).
Zhang, P. et al. Observation of topological superconductivity on the surface of an iron-based superconductor. Science 360, 182–186 (2018).
Wang, D. et al. Evidence for majorana bound states in an iron-based superconductor. Science 362, 333–335 (2018).
Qi, X.-L., Hughes, T. L. & Zhang, S.-C. Topological invariants for the fermi surface of a time-reversal-invariant superconductor. Phys. Rev. B 81, 134508 (2010).
Hosur, P., Dai, X., Fang, Z. & Qi, X.-L. Time-reversal-invariant topological superconductivity in doped Weyl semimetals. Phys. Rev. B 90, 045130 (2014).
Pan, X.-C. et al. Pressure-driven dome-shaped superconductivity and electronic structural evolution in tungsten ditelluride. Nat. Commun. 6, 7805 (2015).
Kang, D. et al. Superconductivity emerging from a suppressed large magnetoresistant state in tungsten ditelluride. Nat. Commun. 6, 7804 (2015).
Qi, Y. et al. Superconductivity in Weyl semimetal candidate MoTe2. Nat. Commun. 7, 11038 (2016).
Chen, F. et al. Superconductivity enhancement in the s-doped Weyl semimetal candidate MoTe2. Appl. Phys. Lett. 108, 162601 (2016).
Li, Y. et al. Concurrence of superconductivity and structure transition in Weyl semimetal tap under pressure. npj Quantum Mater. 2, 66 (2017).
Xu, Y. et al. Topological nodal lines and hybrid Weyl nodes in YCoC2. APL Mater. 7, 101109 (2019).
Barz, H., Ku, H., Meisner, G., Fisk, Z. & Matthias, B. Ternary transition metal phosphides: High-temperature superconductors. Proc. Natl Acad. Sci. USA 77, 3132–3134 (1980).
Meisner, G. & Ku, H. The superconductivity and structure of equiatomic ternary transition metal pnictides. Appl. Phys. A 31, 201–212 (1983).
Müller, R., Shelton, R., Richardson, J. & Jacobson, R. Superconductivity and crystal structure of a new class of ternary transition metal phosphides T’TP (T=Zr, Nb, Ta and T’=Ru, Rh). J. Less Common Metals 92, 177–183 (1983).
Fu, L., Kane, C. L. & Mele, E. J. Topological insulators in three dimensions. Phys. Rev. Lett. 98, 106803 (2007).
Yamakage, A., Yamakawa, Y., Tanaka, Y. & Okamoto, Y. Line-node dirac semimetal and topological insulating phase in noncentrosymmetric pnictides CaAgx (x=P, As). J. Phys. Soc. Jpn. 85, 013708 (2015).
Bradlyn, B. et al. Topological quantum chemistry. Nature 547, 298–305 (2017).
Vergniory, M. et al. A complete catalogue of high-quality topological materials. Nature 566, 480–485 (2019).
Tang, F. et al. Comprehensive search for topological materials using symmetry indicators. Nature 566, 486–489, https://doi.org/10.1038/s41586-019-0937-5 (2019).
Po, H. C., Vishwanath, A. & Watanabe, H. Complete theory of symmetry-based indicators of band topology. Nat. Commun. 8, 50 (2017).
Song, Z., Zhang, T., Fang, Z. & Fang, C. Quantitative mappings between symmetry and topology in solids. Nat. Commun. 9, 3530 (2018).
Kruthoff, J., de Boer, J., van Wezel, J., Kane, C. L. & Slager, R.-J. Topological classification of crystalline insulators through band structure combinatorics. Phys. Rev. X 7, 041069 (2017).
Zhang, T. et al. Catalogue of topological electronic materials. Nature 566, 475 (2019).
Bernevig, B. A. It’s been a Weyl coming. Nat. Phys. 11, 698 (2015).
Xu, Y., Zhang, F. & Zhang, C. Structured Weyl points in spin-orbit coupled fermionic superfluids. Phys. Rev. Lett. 115, 265304 (2015).
Sancho, M. P. L., Sancho, J. M. L., Sancho, J. M. L. & Rubio, J. Highly convergent schemes for the calculation of bulk and surface green functions. J. Phys. F: Metal Phys. 15, 851–858 (1985).
Kobayashi, S. & Sato, M. Topological superconductivity in dirac semimetals. Phys. Rev. Lett. 115, 187001 (2015).
Ueno, Y., Yamakage, A., Tanaka, Y. & Sato, M. Symmetry-protected majorana fermions in topological crystalline superconductors: theory and application to \({{\rm{Sr}}}_{2}{{\rm{RuO}}}_{4}\). Phys. Rev. Lett. 111, 087002 (2013).
Ivanov, V. & Savrasov, S. Y. Monopole mining method for high-throughput screening for Weyl semimetals. Phys. Rev. B 99, 125124 (2019).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Meisner, G. P. & Ku, H. C. The superconductivity and structure of equiatomic ternary transition metal pnictides. Appl. Phys. A 31, 201–212 (1983).
Meisner, G., Ku, H. & Barz, H. Superconducting equiatomic ternary transition metal arsenides. Mater. Res. Bull. 18, 983–991 (1983).
Marzari, N., Mostofi, A. A., Yates, J. R., Souza, I. & Vanderbilt, D. Maximally localized wannier functions: theory and applications. Rev. Mod. Phys. 84, 1419–1475 (2012).
Acknowledgements
We thank Dr. Xianxin Wu and Prof. Xi Dai for helpful discussions. This work was supported by the National Natural Science Foundation of China (11504117, 11774399, 11622435, U1832202), Beijing Natural Science Foundation (Z180008), the Ministry of Science and Technology of China (2016YFA0300600, 2016YFA0401000 and 2018YFA0305700), the Chinese Academy of Sciences (XDB28000000, XDB07000000), the Beijing Municipal Science and Technology Commission (Z181100004218001, Z171100002017018). H.W. acknowledges support from the Science Challenge Project (No. TZ2016004), the K.C. Wong Education Foundation (GJTD-2018-01). Y.S. acknowledges the National Key Research and Development Program of China (No. 2017YFA0302901). Z.W. acknowledges support from the National Thousand-Young-Talents Program and the CAS Pioneer Hundred Talents Program.
Author information
Authors and Affiliations
Contributions
Z.W. and H.W. conceived and designed the project. Y.Q., S.N. and Z.W. performed all the DFT calculations, Y.Q., S.N., C.F., Z.W., H.W. and Z.F. did the theoretical analysis. C.Y. and Y.S. contributed in sample growth. L.K., T.Q. and H.D. carried out the ARPES experiment. All authors contributed to the manuscript writing.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Qian, Y., Nie, S., Yi, C. et al. Topological electronic states in HfRuP family superconductors. npj Comput Mater 5, 121 (2019). https://doi.org/10.1038/s41524-019-0260-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41524-019-0260-6
This article is cited by
-
Superconductivity in unconventional metals
npj Computational Materials (2024)
-
Reaching the Full Potential of Machine Learning in Mitigating Environmental Impacts of Functional Materials
Reviews of Environmental Contamination and Toxicology (2022)
-
Discovery of \({\hat{\boldsymbol{C}}}_2\) rotation anomaly in topological crystalline insulator SrPb
Nature Communications (2021)