Abstract
The newly discovered nickelate superconductors so far only exist in epitaxial thin films synthesized by a topotactic reaction with metal hydrides1. This method changes the nickelates from the perovskite to an infinite-layer structure by deintercalation of apical oxygens1,2,3. Such a chemical reaction may introduce hydrogen (H), influencing the physical properties of the end materials4,5,6,7,8,9. Unfortunately, H is insensitive to most characterization techniques and is difficult to detect because of its light weight. Here, in optimally Sr doped Nd0.8Sr0.2NiO2H epitaxial films, secondary-ion mass spectroscopy shows abundant H existing in the form of Nd0.8Sr0.2NiO2Hx (x ≅ 0.2–0.5). Zero resistivity is found within a very narrow H-doping window of 0.22 ≤ x ≤ 0.28, showing unequivocally the critical role of H in superconductivity. Resonant inelastic X-ray scattering demonstrates the existence of itinerant interstitial s (IIS) orbitals originating from apical oxygen deintercalation. Density functional theory calculations show that electronegative H– occupies the apical oxygen sites annihilating IIS orbitals, reducing the IIS–Ni 3d orbital hybridization. This leads the electronic structure of H-doped Nd0.8Sr0.2NiO2Hx to be more two-dimensional-like, which might be relevant for the observed superconductivity. We highlight that H is an important ingredient for superconductivity in epitaxial infinite-layer nickelates.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 51 print issues and online access
$199.00 per year
only $3.90 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
The data that support the findings of this study are available from the Figshare data repository, https://figshare.com/articles/dataset/Critical_Role_of_Hydrogen_for_Superconductivity_in_Infinite-layer_Nickelates/21591546. Source data are provided with this paper.
Code availability
The code that supports the findings of this study is available from the corresponding author upon request.
References
Li, D. et al. Superconductivity in an infinite-layer nickelate. Nature 572, 624–627 (2019).
Hepting, M. et al. Electronic structure of the parent compound of superconducting infinite-layer nickelates. Nat. Mater. 19, 381–385 (2020).
Crespin, M., Levitz, P. & Gatineau, L. Reduced forms of LaNiO3 perovskite. Part 1—evidence for new phases: La2Ni2O5 and LaNiO2. J. Chem. Soc., Faraday Trans. 2 79, 1181–1194 (1983).
Katayama, T. et al. Epitaxial growth and electronic structure of oxyhydride SrVO2H thin films. J. Appl. Phys. 120, 085305 (2016).
Tassel, C. et al. Direct synthesis of chromium perovskite oxyhydride with a high magnetic-transition temperature. Angew. Chem. Int. Ed. 53, 10377–10380 (2014).
Yajima, T. et al. A labile hydride strategy for the synthesis of heavily nitridized BaTiO3. Nat. Chem. 7, 1017–1023 (2015).
Yajima, T. et al. Epitaxial thin films of ATiO3–xHx (A = Ba, Sr, Ca) with metallic conductivity. J. Am. Chem. Soc. 134, 8782–8785 (2012).
Poeppelmeier, K. A mixed oxide-hydride perovskite. Science 295, 1849–1849 (2002).
Matsumoto, J. et al. Superconductivity at 48 K of heavily hydrogen-doped SmFeAsO epitaxial films grown by topotactic chemical reaction using CaH2. Phys. Rev. Mater. 3, 103401 (2019).
Zeng, S. et al. Phase diagram and superconducting dome of infinite-layer Nd1−xSrxNiO2 thin films. Phys. Rev. Lett. 125, 147003 (2020).
Li, D. et al. Superconducting dome in Nd1−xSrxNiO2 infinite layer films. Phys. Rev. Lett. 125, 027001 (2020).
Lu, H. et al. Magnetic excitations in infinite-layer nickelates. Science 373, 213–216 (2021).
Zhao, D. et al. Intrinsic spin susceptibility and pseudogaplike behavior in infinite-layer LaNiO2. Phys. Rev. Lett. 126, 197001 (2021).
Cui, Y. et al. NMR evidence of antiferromagnetic spin fluctuations in Nd0.85Sr0.15NiO2. Chin. Phys. Lett. 38, 067401 (2021).
Fowlie, J. et al. Intrinsic magnetism in superconducting infinite-layer nickelates. Nat. Phys. 18, 1043–1047 (2022).
Pan, G. A. et al. Superconductivity in a quintuple-layer square-planar nickelate. Nat. Mater. 21, 160–164 (2022).
Krieger, G. et al. Charge and spin order dichotomy in NdNiO2 driven by the capping layer. Phys. Rev. Lett. 129, 027002 (2022).
Tam, C. C. et al. Charge density waves in infinite-layer NdNiO2 nickelates. Nat. Mater. 21, 1116–1120 (2022).
Rossi, M. et al. A broken translational symmetry state in an infinite-layer nickelate. Nat. Phys. 18, 869–873 (2022).
Gu, Q. et al. Single particle tunneling spectrum of superconducting Nd1−xSrxNiO2 thin films. Nat. Commun. 11, 6027 (2020).
Gao, Q., Zhao, Y., Zhou, X.-J. & Zhu, Z. Preparation of superconducting thin films of infinite-layer nickelate Nd0.8Sr0.2NiO2. Chin. Phys. Lett. 38, 077401 (2021).
Zhou, X. et al. Antiferromagnetism in Ni-based superconductors. Adv. Mater. 34, 2106117 (2022).
Nakamura, S., Iwasa, N., Senoh, M. & Mukai, T. Hole compensation mechanism of P-type GaN films. Jpn. J. Appl. Phys. 31, 1258–1266 (1992).
Puphal, P. et al. Investigation of hydrogen incorporations in bulk infinite-layer nickelates. Front. Phys. 10, 834682 (2022).
Malyi, O. I., Varignon, J. & Zunger, A. Bulk NdNiO2 is thermodynamically unstable with respect to decomposition while hydrogenation reduces the instability and transforms it from metal to insulator. Phys. Rev. B. 105, 014106 (2022).
Si, L. et al. Topotactic hydrogen in nickelate superconductors and akin infinite-layer oxides ABO2. Phys. Rev. Lett. 124, 166402 (2020).
Ding, X. et al. Stability of superconducting Nd0.8Sr0.2NiO2 thin films. Sci. China-Phys. Mech. Astron. 65, 267411 (2022).
Zhou, Y. et al. Real-time mass spectrometric characterization of the solid–electrolyte interphase of a lithium-ion battery. Nat. Nanotechnol. 15, 224–230 (2020).
Bang, J., Matsuishi, S. & Hosono, H. Hydrogen anion and subgap states in amorphous In–Ga–Zn–O thin films for TFT applications. Appl. Phys. Lett. 110, 232105 (2017).
Chen, Z. et al. Electronic structure of superconducting nickelates probed by resonant photoemission spectroscopy. Matter 5, 1806–1815 (2022).
Rossi, M. et al. Orbital and spin character of doped carriers in infinite-layer nickelates. Phys. Rev. B. 104, L220505 (2021).
Higashi, K., Winder, M., Kuneš, J. & Hariki, A. Core-level X-ray spectroscopy of infinite-layer nickelate: LDA + DMFT study. Phys. Rev. X. 11, 041009 (2021).
Khazaei, M. et al. Nearly free electron states in MXenes. Phys. Rev. B. 93, 205125 (2016).
Lee, K., Kim, S. W., Toda, Y., Matsuishi, S. & Hosono, H. Dicalcium nitride as a two-dimensional electride with an anionic electron layer. Nature 494, 336–340 (2013).
Matsushita, Y.-i, Furuya, S. & Oshiyama, A. Floating electron states in covalent semiconductors. Phys. Rev. Lett. 108, 246404 (2012).
Wang, J. et al. Anomalous Dirac plasmons in 1D topological electrides. Phys. Rev. Lett. 123, 206402 (2019).
Nomura, Y. et al. Formation of a two-dimensional single-component correlated electron system and band engineering in the nickelate superconductor NdNiO2. Phys. Rev. B 100, 205138 (2019).
Gu, Y., Zhu, S., Wang, X., Hu, J. & Chen, H. A substantial hybridization between correlated Ni-d orbital and itinerant electrons in infinite-layer nickelates. Commun. Phys. 3, 84 (2020).
Shen, Y. et al. Role of oxygen states in the low valence nickelate La4Ni3O8. Phys. Rev. X. 12, 011055 (2022).
Sakakibara, H., Usui, H., Kuroki, K., Arita, R. & Aoki, H. Two-orbital model explains the higher transition temperature of the single-layer Hg-cuprate superconductor compared to that of the La-cuprate superconductor. Phys. Rev. Lett. 105, 057003 (2010).
Lu, N. et al. Electric-field control of tri-state phase transformation with a selective dual-ion switch. Nature 546, 124–128 (2017).
Radoslovich, E. The structure of muscovite, KAl2(Si3Al)O10(OH)2. Acta Crystallogr. 13, 919–932 (1960).
Zhou, K.-J. et al. I21: an advanced high-resolution resonant inelastic X-ray scattering beamline at Diamond Light Source. J. Synchrotron Rad. 29, 563–580 (2022).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B. 54, 11169–11186 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B. 50, 17953–17979 (1994).
Bellaiche, L. & Vanderbilt, D. Virtual crystal approximation revisited: application to dielectric and piezoelectric properties of perovskites. Phys. Rev. B. 61, 7877–7882 (2000).
Pizzi, G. et al. Wannier90 as a community code: new features and applications. J. Phys. Condens. Matter 32, 165902 (2020).
Acknowledgements
L.Q. acknowledges the support by National Natural Science Foundation of China (grant nos. 12274061, 52072059 and 11774044), Science and Technology Department of Sichuan Province (grant nos. 2021JDJQ0015 and 2022ZYD0014) and Fundamental Research Funds for the Central Universities (grant no. ZYGX2020J023). X.S. and B.H. acknowledge the support from the NSFC (grant no. 12088101) and NSAF (grant no. U2230402). We thank Diamond Light Source for providing beam time under proposal ID NT30296. S.L. thanks Australian Research Council Discovery Projects (grant nos. DP220103229 and DP19013661) for the financial support. Computations were done at Tianhe-JK cluster at CSRC. TOF–SIMS was conducted in the University of New South Wales Mark Wainwright Analytical Centre.
Author information
Authors and Affiliations
Contributions
L.Q. designed the project. L.Q., K.-J.Z. and B.H. interpreted the experimental and theoretical data and supervised the project. X.D. performed thin film growth, XRD measurement, electrical properties and Hall effect characterizations. M.X. and Y.Z. helped with film growth and post-reduction. H.L. helped with electrical properties measurement. X.W. and Q.W. helped with film growth and physical property system measurements. C.C.T., J.C., M.G.-F., S.A. and K.-J.Z. performed XAS and RIXS measurements. J.Z. and S.L. performed SIMS measurements. M.W. and P.G. performed the transmission electron microscopy measurements. X.S. and B.H. performed DFT calculations. H.X. and X.Z. helped with DFT theory study. All the authors participated in data analysis and discussion. K.-J.Z., X.D., L.Q. and B.H. drafted the manuscript with input from all authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature thanks the anonymous reviewers for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Extended data figures and tables
Extended Data Fig. 1 Characterization of perovskite structure and description of topotactical reduction process.
a, b, Typical RHEED intensity oscillation and RHEED pattern along SrTiO3 [101] azimuth direction for Nd0.8Sr0.2NiO3 films. The oscillations indicate that the film grows layer by layer during the initial stage of growth. The layer-by-layer growth gradually disappeared as the film thickened. c, Typical XRD of as-grown Nd0.8Sr0.2NiO3 films. Nd0.8Sr0.2NiO3 (001) and (002) diffraction peaks are located at 23.7° and 48.3°, respectively d, Illustration of the reduction heating process. During the reduction time the sample is maintained at the temperature of 300 °C.
Extended Data Fig. 2 X-ray diffraction for all Nd0.8Sr0.2NiO2Hx films.
XRD scans of films with reduction time varied from 1 min to 420 min. The insert picture shows the corresponding c lattice parameters.
Extended Data Fig. 3 SIMS spectra of other elements in thin film and substrate.
SIMS signals of O, Ti, Ni, Sr, Nd secondary ions in the films under different H doping levels.
Extended Data Fig. 4 Crystal structure and SIMS spectrum of mica.
a, Crystal structure of mica with the formula of KAl2[AlSi3O10](OH)2. b, SIMS spectrum of H, O, Al, K, Si secondary ions in mica as a reference sample for calibration.
Extended Data Fig. 5 Zoom-in view of ρ(T) with different H concentrations.
The temperature-dependent resistivities of Nd0.8Sr0.2NiO2Hx films with x varying from 0.19 to 0.33.
Extended Data Fig. 6 Crystal structure of Nd0.8Sr0.2NiO2Hx.
a-c, Lowest energy configurations of Nd0.8Sr0.2NiO2Hx (x = 0, 0.25 and 0.5) in 2×2×2 supercell, where H forms 1D chain structure along c direction [see details in Supplementary Note 12]. The green shaded areas indicate the unit cells. These structures are used for electronic structure calculations in Fig. 4.
Extended Data Fig. 7 RIXS spectra of Nd0.8Sr0.2NiO2Hx.
Low-energy RIXS intensity maps (a-c) and the integrated quasielastic region (d–f) of three Nd0.8Sr0.2NiO2Hx samples with x = 0.19 (a, d), 0.26 (b, e) and 0.33 (c, f), respectively. No sign of CDWs is present in any probed samples.
Supplementary information
Supplementary Information
Supplementary Notes 1–18, Figs. 1–19, Tables 1 and 2 and references.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Ding, X., Tam, C.C., Sui, X. et al. Critical role of hydrogen for superconductivity in nickelates. Nature 615, 50–55 (2023). https://doi.org/10.1038/s41586-022-05657-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41586-022-05657-2
This article is cited by
-
Superexchange and charge transfer in the nickelate superconductor La3Ni2O7 under pressure
Science China Physics, Mechanics & Astronomy (2024)
-
Signatures of superconductivity near 80 K in a nickelate under high pressure
Nature (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.