Abstract
We investigate using scanning tunneling microscopy and spectroscopy electronic aspects of Moiré superstructures in nanoscale Pb quantum films grown on IrTe2, which is a unique layered material with charge-order transitions into stripe phases. Pb ultrathin films exhibit a Moiré superstructure due to the lattice mismatch of Pb and IrTe2, which produces strong lateral electronic modulation of hexagonal symmetry and discreet subbands. Moreover, strongly anisotropic or 1D electronic states are formed in Pb films as modulated by the stripe charge order. Present results indicate the controllability of lateral electronic structures of various ultrathin films by extra interfacial potentials due not only to Moiré superstructures but also to novel electronic orderings of substrates.
Similar content being viewed by others
Introduction
Graphene and other two dimensional (2D) atomic layers have been one of the most intensively investigated topics in materials physics and engineering for a decade1,2,3. Beyond exploiting properties of single isolated atomic layers, assembling different atomic layers through the van der Waals interaction is expected to reveal new electronic properties and functionality4. Indeed, van der Waals interfaces of graphene with h-BN and graphene itself produced interesting electronic states such as cloned mini Dirac bands5,6,7,8 and Hofstadter states9,10. The key underlying physics is within extra 2D periodic potentials provided by highly ordered Moiré superstructures due to interfacial lattice mismatches11. However, so far the successful demonstration of 2D electronic modulations by Moiré superstructures has been limited to graphene cases and a very recent one for a semiconducting single-layer transition metal dichalchogenide heterostructure12, leaving a great room of development given the huge variety of 2D materials.
In this work, we demonstrate the modulation of 2D electronic structures of ultrathin (a few atomic layers) metal Pb films by the Moiré superstructure of a van der Waals heterointerface with a layered transition metal dichalcogenide, IrTe2. 2D quantum well states (QWS’s) of Pb films are found to be modulated laterally by the Moiré superstructure at the interface. Furthermore, the substrate features a transition into charge-ordered ground states13,14,15,16,17,18,19,20,21,22,23,24 with emergent superconductivity25,26,27,28. The stripe charge ordering and the lattice distortion accompanied provide an extra tunability into the 2D electronic states, that is, the 2D-1D dimensional crossover of electronic states. This work thus extends the scope of van der Waals electronic engineering in both materials and concept.
Figure 1A shows the Te layer exposed after cleaving a IrTe2 crystal. Below the transition temperature of 260~280 K coexist the stripe phases (S) of three degenerate orientations and a distinct hexagonal phase (H) [Fig. S1a]. Their origins are commonly the charge ordering of Ir 5d 3+ and 5d 4+, which accompanies substantial lattice distortions through the Ir dimerization. The dominant phase is the stripe phase of a 5a0 period, which is mixed with other stripes of a 3a0 or 8a0 period as reported previously13,14,15,16,17,18,19,20,21,22,23,24. On the other hand, the minor phase of a hexagonal pattern has a period of about 7.4a0 and falls into a superconducting state below 3.1 K29.
When Pb atoms are deposited on to IrTe2, well ordered flat 2D islands of Pb(111) are formed, which are very similar to the growth on other substrates30,31. For low temperature growth, flat Pb(111) islands with different thickness are formed together, where electronic states of various films are accessible simultaneously and conveniently. The growth mode depends drastically on different charge orders of the substrate. While flat islands of different heights are formed with a size of a few tens of nanometers on wide stripe domains, larger connected islands of two or three monolayer (ML) thickness preferentially grow on hexagonal domains (see Fig. 1B,C and Fig. S1 in Supporting information).
Figure 1D,E shows 2 ML Pb islands on a part of the surface with stripe and hexagonal domains coexisting. Moiré patterns are observed in Pb layers on top of both domains. Pb islands on the hexagonal domain (hereafter H-Pb islands) exhibit a regular and isotropic Moiré structure [Fig. 1D and center of the Fig. S1a] but a less regular pattern of a marginally different periodicity and orientation is observed on the stripe domain (hereafter S-Pb islands) [Fig. 1E]. The fast Fourier transformation of the STM images in Fig. 1F,G indicate that the Moiré superstructure on H-Pb (S-Pb) islands has a periodicity of 2.61 nm (2.73 nm), which corresponds to a Moiré angle of 19 ± 2 (23 ± 2) degree due basically to a 11% lattice mismatch between Pb(111) and IrTe2 (see Fig. S2 in Supporting information). The small difference between H-Pb and S-Pb islands is due to the extra strain in the hexagonal phase29. On S-Pb islands, the Moiré structure is mixed with an additional stripe modulation of the same periodicity and orientation with the underlying stripe order (Fig. S1e in Supporting information). On the other hand, the hexagonal charge order pattern overlaps very closely with the Moiré superstructure leaving no noticeable footprint of its own on Pb islands.
Electronic states within well ordered Pb films are quantized vertically to form 1D QWS’s, which are well defined 2D electronic states laterally30,31,32,33. These QWS’s are well resolved in STS (tunneling dI/dV) spectra for empty states as shown in Fig. 2A. In filled state, QWS’s are observed only at very low energies near the Fermi energy30,31,32,33. The QWS energies agree well with our own density functional theory (DFT) calculations for floating films [Fig. 2B] and the previous works30,31,32,33. We map local density of states (LDOS) of each QWS laterally to reveal the effect of Moiré superstructures. The QWS LDOS exhibits strong lateral modulations as shown in Fig. 2C,D, whose periodicity follows exactly that of the Moiré superstructure. Very intriguingly, the LDOS of the first QWS above Fermi level for the S-Pb films shows a linear pattern indicating 1D electronic states laterally, which will be discussed later. All LDOS modulations are due to the small energy splitting or shift of electronic states between dark and bright LDOS regions, which varies between 10 and 300 meV with a tendency to increase for a thinner film and for a QWS closer to the Fermi energy (see Fig. 3 and Fig. S3 in Supporting information). As shown by lower energy spectral features without energy shifts in Fig. 3A, the QWS energy change cannot be explained by any overall energy shift such as the local work function change.
The QWS energy splitting is thus most clearly seen for the thinnest film, 2 ML, especially on H-Pb films where the hexagonal Moiré superstructure is better ordered (see Fig. S4 in Supporting information). As shown in Fig. 3, the QWS’s are split into three subbands with distinct LDOS lateral patterns and the energy splitting amounts to 120 meV. The split states have distinct LDOS patterns, which are located on the high symmetry sites A (Fig. 3E) and B (Fig. 3C) or split around A/B (Fig. 3D). The LDOS patterns of the states on A and B sites are essentially the same as those of the Moiré superstructure of graphene with Dirac subbands8. While less resolved, consistent energy splittings can also be found on Pb films on stripe domains. We argue that the periodic lateral potential provided by the Moiré superstructure is strong enough to split each QWS into subbands and this effect gets stronger for thinner films and closer to Fermi level.
This conclusion is corroborated by DFT calculations. Figure 4A is an atomic structure of a unitcell of the 2 ML Pb film on top of a single layer IrTe2. In this model, the supercell size is 2.74 nm and the Moiré angle is 22.9 degree, which are quite well matched with the experiment. The van der Waals contribution is calculated to be about 65% of the whole interfacial energy gain. One can see that the film is corrugated, that is, strained, due to the Moiré potential and A, B and C sites have distinct stacking registries with the substrate [Fig. 4B]. The vertical corrugation with B sites protruded is consistent with the STM topography (Fig. 3A) where those sites are brighter. The calculated DOS indicates the complex energy splitting of the QWS which mainly comes from the P z orbital of Pb (see Fig. S5 in Supporting information). We compared the fully relaxed structure shown in Fig. 4A and also the Pb film of the same strained structure but the IrTe2 layer detached. The size of energy splittings and the LDOS patterns of the split QWS are better reproduced in the latter structure. The calculated LDOS patterns are shown in Fig. 4. This suggests that the QWS splitting in the present case is more closely related to the periodic structural distortion of the film than the direct electronic coupling with the substrate. The effect of the lateral strain on a QWS has been well known in compound semiconductor multilayer structures34,35. Note that the present structure model for the IrTe2 layer is so simple that the charge ordering and its complex electronic structure are not included at all. This limitation makes it difficult to account for the electronic coupling effect accurately. Nevertheless, it is clear that the Moiré superstructure, the periodically corrugated film structure, induces strong electronic modulation on the Pb film.
While QWS’s and the Moiré superstructure Pb films have been extensively investigated11,30,31,32,33,36, only few works reported the lateral LDOS modulation of QWS following the Moiré superstructure31. These modulations were observed in the intensity31 and energy36 of a QWS peak, which were qualitatively attributed to the lateral variation of the electron screening or the interfacial phase shift31, respectively36, without any theoretical analysis. The electron screening to reduce the QWS intensity is not related to the energy splitting observed here. Moreover, the gradual lateral variation of the interfacial phase shift is not compatible with the energy splitting of a QWS (Fig. S4 Supporting information). Note also that the interfacial phase shift is an oversimplified model, which assumes the film structure and band structure undistorted in contrast to the present experimental and calculated results.
The present case is one of very few demonstrations of the Moiré modulation of 2D electronic states beyond the single layer graphene cases5,6,7,8,9,10 and can be applied to various ultrathin films of metal, semiconductors, and insulators since these films would have QWS 2D bands when sufficiently thin. To the best of our knowledge, the only other case is a very recent one for a semiconducting single-layer transition metal dichalchogenide heterostructure12. The observed electronic modulation therein is remarkably similar to the present result. This work didn’t try to model the whole Moiré supercell as performed here but instead used simpler epitaxial structures with different interlayer registries, mimicking A, B, and C sites, separately. Therefore, while the strain of the film cannot easily be addressed, the electronic interlayer coupling was discussed in detail. We, thus, believe that this and the present results are complimentary to grasp the whole mechanism of the Moiré modulation of 2D electronic states, indicating both the importance of the interlayer stacking registry and the strain of the film.
On the other hand, the STM topography shows not only the Moiré superstructure but also an extra modulation due to a stripe charge order pattern for S-Pb films [Figs 1 and 2]. When the QWS energy becomes closer to the Fermi energy than 1.6 eV, the hexagonal (honeycomb) LDOS pattern evolves gradually into 1D stripe patterns (see also Fig. S2). The stripe LDOS pattern is related to the QWS energy splitting of about 60–140 meV (see Fig. S3 in Supporting information). This indicates the presence of a stripe potential at the interface, which competes with the hexagonal Moiré potential becomes dominating at a low energy. The 1D or uniaxial interfacial potential can be provided by the stripe charge order of the substrate which induces a substantial uniaxial lattice corrugation (about 10% vertically) and a strong charge modulation on the surface Te layer23. The formation of a 1D Moiré superstructure and 1D electronic states under uniaxial strain in a van der Waals interfaces was theoretically suggested very recently37. Probing further the 1D nature of the uniaxially strained QWS would be very interesting but out of the scope of the present work. The present result suggests that an emergent electronic superstructure of the substrate can offer an extra knob into the 2D electronic engineering at van der Waals heterointerfaces beyond the lattice mismatch. The proximity coupling of exotic electronic states of the substrate with those of the overlayer film may be expected at such a ‘complex’ heterointerface.
Methods
Sample preparation
Single crystals of IrTe2 were grown by Te flux using pre-sintered IrTe2 polycrystals as reported previously19. Samples are cleaved in a vacuum better than 5 × 10−10 torr at room temperature or 86 K, lower than the transition temperature. Pb is grown at 86 K or room temperature. In the case of low temperature deposition, we perform an annealing to room temperature for 12–16 Hour.
STM measurement
All the STM measurements were obtained with a commercial ultrahigh vacuum cryogenic STM (Specs, Germany) in the constant-current mode with PtIr tips at 4.3 K. The differential conductance, dI/dV, was measured using the lock-in detection with a modulation of 1.17 kHz.
DFT calculations
Density functional theory calculations were performed using the Vienna Ab initio Simulation Package38. The projector augmented-wave potentials39 with the Perdew, Burke, and Ernzerhof exchange-correlation energy40 and the DFT-D3(BJ) method41,42 were used to simulate the system. A lattice constant of the supercell is 27.375 Å and a vacuum region is almost 10 Å. (\(\sqrt{63}\times \sqrt{63}\)) Pb (111) bilayers are on the (7 × 7) 1T-IrTe2 monolayer with a twisted angle 2.7 degree. The atoms of the slab system were fully relaxed except lower telluriums fixed to represent the bulk property of the 1T-IrTe2 substrate. The plane wave cut-off energy was set to 210.86 eV and the Monkhorst-Pack k-point mesh was 3 × 3 × 1.
References
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).
Castro Neto, A. H. et al. The electronic properties of graphene. Rev. Mod. Phys. 81, 109 (2009).
Geim, A. K. Graphene: Status and prospects. Science 324, 1530–1534 (2009).
Geim, A. K. & Grigorieva, I. V. van der Waals heterostructures. Nature 499, 415 (2013).
Gomes, K., Mar, W., Ko, W., Guinea, F. & Manoharan, H. Designer Dirac fermions and topological phases in molecular graphene. Nature 483, 306 (2012).
Yankowitz, M. et al. Emergence of superlattice Dirac points in graphene on hexagonal boron nitride. Nat. Phys. 8, 382 (2012).
Wijk, M., Schuring, A., Katsnelson, M. & Fasolino, A. Moiré patterns as a probe of interplanar interactions for graphene on h-BN. Phys. Rev. Lett. 113, 135504 (2014).
Ponomarenko, L. et al. Cloning of Dirac fermions in graphene superlattices. Nature 497, 594 (2013).
Yu, G. et al. Hierarchy of Hofstadter states and replica quantum Hall ferromagnetism in graphene superlattices. Nat. Phys. 10, 525 (2014).
Dean, C. R. et al. Hofstadter’s butterfly and the fractal quantum Hall effect in moiré superlattices. Nature 497, 598 (2013).
Hupalo, M. et al. Interface relaxation and electronic corrugation in the Pb/Si(111)–Pb–α −√3×√3. Phys. Rev. B 71, 193408 (2005).
Zhang, C. et al. Interlayer couplings, Moire patterns, and 2D electronic superlattices in MoS2/WSe2 hetero-bilayers. Sci. Adv. 3, e1601459 (2017).
Ko, K.-T. et al. Charge-ordering cascade with spin–orbit Mott dimer states in metallic iridium ditelluride. Nat. Commun. 6, 7342 (2015).
Hsu, P.-J. et al. Hysteretic melting transition of a soliton lattice in a commensurate charge modulation. Phys. Rev. Lett. 111, 266401 (2013).
Machida, T. et al. Visualizing the effect of structural supermodulation on electronic structure of IrTe2 by scanning tunneling spectroscopy. Phys. Rev. B 88, 245125 (2013).
Kim, H. S. et al. Structural versus electronic distortions in IrTe2 with broken symmetry. Phys. Rev. B 90, 201103 (2014).
Qing Li et al. Bond competitions and phase evolution of the IrTe2 surface. Nat. Commun. 5, 5358 (2014).
Eom, M. J. et al. Dimerization-induced Fermi-surface reconstruction in IrTe2. Phys. Rev. Lett. 113, 266406 (2014).
Yang, J. J. et al. Charge-orbital density wave and superconductivity in the strong spin-orbit coupled IrTe2:Pd. Phys. Rev. Lett. 108, 116402 (2012).
Pascut, G. L. et al. Dimerization-induced cross-layer quasi-two-dimensionality in metallic IrTe2. Phys. Rev. Lett. 112, 086402 (2014).
Cao, H. et al. Origin of the phase transition in IrTe2: Structural modulation and local bonding instability. Phys. Rev. B 88, 115122 (2013).
Joseph, B. et al. Local structural displacements across the structural phase transition in IrTe2: Order-disorder of dimers and role of Ir-Te correlations. Phys. Rev. B 88, 224109 (2013).
Kim, K. et al. Origin of first-order-type electronic and structural transitions in IrTe2. Phys. Rev. Lett. 114, 136401 (2015).
Oh, Y. S., Yang, J. J., Horibe, Y. & Cheong, S.-W. Anionic depolymerization transition in IrTe2. Phys. Rev. Lett. 110, 127209 (2013).
Fujisawa, Y. et al. Visualizing the Pt doping effect on surface and electronic structure in Ir1−xPtxTe2 by scanning tunneling microscopy and spectroscopy. J. Phys. Soc. Jpn. 84, 043706 (2015).
Kamitani, M. et al. Superconductivity in CuxIrTe2 driven by interlayer hybridization. Phys. Rev. B 87, 180501 (2013).
Guo, J., Qi, Y. & Hosono, H. Structure and superconductivity in pyrite Ir0.95−xRhxTe2: A comparison with analogous selenides. Phys. Rev. B 87, 224504 (2013).
Yu, D. J. et al. Fully gapped s-wave-like superconducting state and electronic structure in Ir0.95Pd0.05Te2 single crystals with strong spin-orbital coupling. Phys. Rev. B 89, 100501 (2014).
Kim, H. S. et al. Nanoscale superconducting honeycomb charge order in IrTe2. Nano Lett. 16, 4260 (2016).
Hong, I.-P. et al. Decay mechanisms of excited electrons in quantum-well states of ultrathin Pb islands grown on Si(111): Scanning tunneling spectroscopy and theory. Phys. Rev. B 80, 081409 (2009).
Lu., S. M. et al. Strength modulation of quantum-well states in Pb islands with periodic distortions on Si(111). Phys. Rev. B 75, 113402 (2007).
Wei, C. M. & Chou, M. Y. Theory of quantum size effects in thin Pb(111) films. Phys. Rev. B 66, 233408 (2002).
Chiang., T.-C. Photoemission studies of quantum well states in thin films. Surf. Sci. Rep. 39, 181–235 (2000).
Xu, Z., Wassermeier, M., Li, Y. J. & Petroff, P. M. Lateral band gap modulation by buried stressor structures in compounds semiconductor quantum-well structures. Appl. Phys. Lett. 60, 586 (1992).
Shimose, Y., Kikugawa, T. & Nagai, H. Lateral modulation in strain-compensated MQW structures. https://doi.org/10.1109/ICIPRM.1995.522116 (1995).
Alfeder, I. B., Narayanamurti, V. & Chen, D. M. Imaging Subsurface Reflection Phase with Quantized Electrons. Phys. Rev. Lett. 88, 206801 (2002).
Tong, Q. et al. Topological mosaics in moiré superlattices of van der Waals heterobilayers. Nat. Phys. 13, 356 (2017).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Grimme, S., Ehrlich, S. & Goerigk, L. Effect of the damping function in dispersion corrected density functional theory. J. Comp. Chem. 32, 1456 (2011).
Acknowledgements
This work is supported by Institute for Basic Science (Grant No. IBS-R014-D1). YHC and SWC are partially supported by the Max Planck POSTECH/KOREA Research Initiative Program (Grant No. 2011–0031558) through NRF of Korea funded by MEST. We acknowledge Tae-Hwan Kim for the technical help of in STM measurements.
Author information
Authors and Affiliations
Contributions
Hyo Sung Kim carried out the STM measurements. Gyeongcheol Gye and Sung-Hoon Lee performed the DFT calculations. Lihai Wang and Sang-Wook Cheong synthesized the crystals. Hyo Sung Kim and Han Woong Yeom analyzed the data and wrote the manuscript. Han Woong Yeom designed and supervised the research.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Kim, H.S., Gye, G., Lee, SH. et al. Moiré Superstructure and Dimensional Crossover of 2D Electronic States on Nanoscale Lead Quantum Films. Sci Rep 7, 12735 (2017). https://doi.org/10.1038/s41598-017-12851-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-12851-0
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.