Abstract
The formation of radiation damage in Ge above room temperature is dominated by complex dynamic annealing processes, involving migration and interaction of ballistically-generated point defects. Here, we study the dynamics of radiation defects in Ge in the temperature range of 100–160 °C under pulsed beam irradiation with 500 keV Ar ions when the total ion fluence is split into a train of equal square pulses. By varying the passive portion of the beam duty cycle, we measure a characteristic time constant of dynamic annealing, which rapidly decreases from ~8 to 0.3 ms with increasing temperature. By varying the active portion of the beam duty cycle, we measure an effective diffusion length of ~38 nm at 110 °C. Results reveal a major change in the dominant dynamic annealing process at a critical transition temperature of ~130 °C. The two dominant dynamic annealing processes have an order of magnitude different activation energies of 0.13 and 1.3 eV.
Similar content being viewed by others
Introduction
For the past decade, there has been renewed interest in the use of Ge for high-speed, low-power electronics1. Ion implantation is the preferred tool for selective-area doping of semiconductor devices. However, implantation of dopants is accompanied by the formation of lattice defects that strongly and often deleteriously influence material properties. Hence, numerous recent studies have focused on ion implantation damage in Ge2,3,4,5,6,7.
It has been well established that the buildup of radiation damage in Ge, particularly above room temperature, is complicated by pronounced dynamic annealing (DA) processes2,3,4,5,6,7,8,9,10,11,12,13. These involve migration, recombination, and clustering of mobile point defects during irradiation. Such DA is commonly manifested as a dependence of stable lattice disorder on the dose rate and sample temperature (T). Despite previous efforts2,3,4,5,6,7,8,9,10,11,12,13, the current understanding of DA in Ge is very limited, and some very basic questions about defect interaction remain unanswered. For example, after the thermalization of ballistic collision cascades, how long do mobile point defects survive and how far do they diffuse while participating in DA processes? Previous estimates of the defect relaxation time constant (τ) in Ge cover an astonishingly wide range of 12 orders of magnitude (10−11–101 s)13,14. We are unaware of any previous measurements of the effective diffusion length of mobile defects (L d ) in ion-bombarded Ge.
Here, we use a recently developed pulsed ion beam method15,16,17,18,19,20,21 to study the dynamics of radiation defect interaction in Ge bombarded with 500 keV Ar ions. We measure τ values of ~10−4–10−2 s (monotonically decreasing with T) and an L d of ~38 nm at 110 °C. Furthermore, the τ(T) dependence reveals a change in the dominant DA process at ~130 °C, which is accompanied by an order of magnitude change in the activation energy of the dominant DA process.
Experimental
Czochralski grown (100) Ge single crystals doped with Ga (with a resistivity of ~0.03 Ω cm) were bombarded in the T range of 100–160 °C with 500 keV 40Ar+ ions at 7° off the [100] direction. Previous studies8,9,10,11 have found pronounced DA in this T range. To improve thermal contact, the samples were attached to a Cu sample holder with Ag paste. All irradiations were performed in a broad beam mode15. Ion beam pulsing was achieved by applying high voltage pulses to a pair of parallel plates deflecting the beam off the final beam defining aperture. The 4 MV ion accelerator (National Electrostatics Corporation, model 4UH) at Lawrence Livermore National Laboratory was used for both ion irradiation and ion beam analysis.
Similar to our previous work15,16,17,18,19, for τ measurements, the total ion fluence was split into a train of equal square pulses, each with an instantaneous dose rate (F on ) of ~1.5×1013 cm−2 s−1 and duration (t on ) of 1 ms. Adjacent pulses in such τ measurements were separated by time t off , which was varied between 0.2 and 50 ms. For L d measurements17,20,21, the total fluence was delivered as a train of pulses with duration (t on ) varying between 0.2 and 1 ms, each with an instantaneous dose rate (F on ) of ~4.3×1013 cm−2 s−1, separated by a t off of 100 ms, which, as will be shown below, is much greater than the τ values. The inset in Fig. 1(a) shows a schematic of the time dependence of the instantaneous dose rate and defines the pulsing parameters (t on , t off , and F on ). A more detailed description of the experimental arrangement can be found elsewhere15,16,17,18,19.
The dependence of stable lattice damage on t off and t on was studied ex-situ at room T by ion channeling. Depth profiles of lattice disorder were measured with 2 MeV 4He+ ions incident along the [100] direction and backscattered into a detector at 164° relative to the incident beam direction. Spectra were analyzed with one of the conventional algorithms22 for extracting the effective number of scattering centers (referred to below as “relative disorder”). Values of average bulk disorder (n), discussed below, were obtained by averaging depth profiles of relative disorder over 15 channels (corresponding to an ~60-nm-wide region) centered on the maximum of the bulk damage peak. Error bars of n are standard deviations. Ion fluences in τ measurements at different Ts were chosen such that, for continuous beam irradiation, n was in the range of 0.5–0.8 (with n = 1 corresponding to full amorphization). The nuclear energy loss profile was calculated with the TRIM code (version SRIM-2013.00)23 with an atomic concentration of Ge of 4.4 × 1022 atoms cm−3 and a threshold energy for atomic displacements of 15 eV.
Results and Discussion
Figure 1(a) shows representative depth profiles of relative disorder for bombardment at T = 110 °C with continuous (t off = 0 ms) and pulsed (t off = 5 and 20 ms) beams for τ measurements. Figure 1(b) shows corresponding profiles for bombardment at T = 110 °C with pulsed (t on = 0.2, 0.3, and 0.5 ms) beams for L d measurements. The depth profiles for all irradiations herein, at Ts of 100–160 °C, have qualitatively similar shapes. They exhibit a major peak in the crystal bulk centered on ~270 nm, which corresponds to the maximum of the nuclear energy loss profile for 500 keV Ar ions. These observations are consistent with previous studies of radiation damage in Ge at room T 3,6,7.
Figure 1(b) shows that n increases with increasing t on when all the other irradiation parameters are kept constant. These results are more clearly shown in Fig. 2, where n is plotted as a function of fluence per pulse (F on t on ). As discussed previously17,20,21, in such measurements of n(F on t on ) dependencies with \({t}_{off}\gg \tau \), the interaction between mobile defects generated in different pulses is suppressed, and the n(F on t on ) dependence reflects the interaction of mobile defects created in different cascades within the same pulse. Such inter-cascade defect interaction processes become pronounced when the average lateral distance between the centers of adjacent collision cascades in each pulse \(({L}_{overlap}\approx \tfrac{1}{\sqrt{{F}_{on}{t}_{on}}})\) is comparable to or smaller than the effective diffusion length of mobile defects: \({L}_{overlap}\mathop{ < }\limits_{ \tilde {}}2{L}_{d}\) (see the inset in Fig. 2)17,20,21. For relatively heavy ion bombardment such as used in the present study, the average lateral dimensions of ballistic sub-cascades, L ballistic , also shown in the inset in Fig. 2, are ~1–2 nm, which is much smaller than L d and, hence, can be omitted in these estimates17,20,21.
For broad beam bombardment with statistically uncorrelated ion trajectories of the present study, ion impacts obey Poisson statistics with a Poisson coefficient of \(4{L}_{d}^{2}{F}_{on}{t}_{on}\) 21, where \(4{L}_{d}^{2}\) is the effective area of a cascade after defect out-diffusion. For t on < τ (i.e., when defect relaxation processes during the active part of each pulse, t on , can be neglected), the average density of elementary mobile point defects within collision cascades after each pulse can be approximated by an average density of atomic displacements: \({\rho }_{displacements}=g(\tfrac{1}{4{L}_{d}^{2}}+{F}_{on}{t}_{on})\), where g is the the number of atomic displacements produced by an ion per unit of depth. If the efficiency of stable damage formation scales linearly with the density of mobile defects (which is a good approximation for low t on values), \(n\propto {\rho }_{displacements}\propto 1+4{L}_{d}^{2}{F}_{on}{t}_{on}\). This equation is used to fit the linear portion of n(t on ) at low t on values (the solid line in Fig. 2), revealing an L d of ~38 ± 6 nm. This L d is larger than the value of ~10 nm in Ar-ion-bombarded 3C-SiC reported recently21. Interestingly, an L d of ~38 nm is very similar to that found for Si under 500 keV Ar ion irradiation at room T 17.
Figure 1(a) also shows that n decreases with increasing t off . Such an experimental n(t off ) dependence is used to evaluate τ. This is better illustrated in Fig. 3, which summarizes n(t off ) dependencies for all the Ts studied, at total fluences shown in the inset. It is seen from Fig. 3 that, for all the cases, n monotonically decreases with increasing t off . Solid lines in Fig. 3 are fits of n(t off ) dependencies via the Marquardt-Levenberg algorithm24 with a second order decay equation \((n({t}_{off})={n}_{\infty }+\tfrac{n\mathrm{(0)}-{n}_{\infty }}{1+\tfrac{{t}_{off}}{{\tau }_{2}}})\). Here, τ 2 is the characteristic decay time constant measured by fitting to the second order decay equation, and n ∞ is relative disorder for \({t}_{off}\gg {\tau }_{2}\).
We find that, across the T range studied, the best fits to n(t off ) dependencies of Fig. 3 alternate between the two simplest decay process equations: the first order (n(t off ) = n ∞ + (n(0) − n ∞) exp (−t off /τ 1)) and second order decay equations. This finding is in contrast to results of our recent pulsed beam study19 of Si that has revealed a clear switch from the second to the first order decay at a certain T. However, both first and second order fits for Ge shown in Fig. 3 have R-squared values of >0.9 (i.e., coefficients of determination, which are commonly used as a measure of the goodness of fit)25. An example of the first order decay process is the trapping of interstitials or vacancies at sinks, while vacancy–interstitial annihilation and the formation of di-vacancies are examples of the second order kinetic processes. Although it is tempting to associate the best fitting decay curves with some specific defect interaction processes, such assertions will require future modeling work as, for example, in a recent study of ion-bombarded Si19.
The τ 2(T) dependence is plotted in Fig. 4 (left axis), revealing a monotonic decrease with increasing T. Figure 4 (right axis) shows the T dependence of the DA efficiency (ξ), which we define as follows15,17: ξ = (n(0) − n ∞)/n(0). For our choice of the pulsing parameters, ξ is the magnitude of the dose rate effect, reflecting the fraction of mobile defects that participate in DA processes during continuous beam irradiation with a dose rate of F on 17. Fig. 4 shows a monotonically increasing ξ(T) dependence up to ~130 °C and saturation at ξ ≈ 100% for higher Ts. This indicates a very strong dose rate effect at \(T\mathop{ > }\limits_{ \tilde {}}130\,^\circ {\rm{C}}\), when stable lattice damage forms predominantly in inter-cascade DA processes. In this irradiation regime, the control of the beam shape and both instantaneous and average dose rates becomes critically important since relatively small changes in the dose rate can dramatically affect the level of stable damage, from barely detectable by ion channeling to full lattice amorphization.
As discussed in detail in ref.17, in measurements of τ based on n(t off ) dependencies [Figs 1(a) and 3], the fluence per pulse (F on t on ) can be chosen in order to minimize intra-pulse defect interaction, while maximizing the inter-pulse interaction. This occurs when, on average, only one ion impacts onto L d -defined areas during each pulse. This condition is satisfied when \({t}_{on}={t}_{on}^{{L}_{d}}=\tfrac{1}{4{L}_{d}^{2}{F}_{on}}\) 17. For F on = 1.5 × 1013 cm−2 s−1 and L d = 38 nm, \({t}_{on}^{{L}_{d}}\approx 1.2\,{\rm{ms}}\). Hence, we have selected t on = 1 ms for all the τ measurements of this study.
As also discussed in detail in ref.17, for \({t}_{on} < {t}_{on}^{{L}_{d}}\), the effective time between ion impacts onto L d -defined areas is not the passive part of the beam duty cycle (t off ) but \({t}_{off}^{effective}=({t}_{on}+{t}_{off})\,\tfrac{{t}_{on}^{{L}_{d}}}{{t}_{on}}\). So, the defect relaxation time constant τ can be more accurately evaluated by the analysis of \(n({t}_{off}^{effective})\) dependencies. However, the analysis of data from Fig. 3 as \(n({t}_{off}^{effective})\) gives τ values that differ only by ~10% from the τ values obtained by the analysis of n(t off ) dependencies and shown in Fig. 4. We have also found that τ is independent of the choice of t on (varied between 0.2 and 2.0 ms) when F on t on is kept constant (Fig. 5). All these observations are consistent with a recent detailed discussion of the choice of pulsing parameters17.
Figure 4 shows that the τ values are in the range of ~10−4–10−2 s. These are much larger than defect relaxation time scales previously studied by molecular dynamics simulations14, which are appropriate for evaluating defect dynamics on time scales \(\mathop{ < }\limits_{ \tilde {}}{10}^{-9}\,{\rm{s}}\). The only experimental estimate of τ for Ge that we are aware of is by Posselt et al.13 for focused ion beam (channeled 30 keV Ga) irradiation. They13 estimated a lower limit of 10 s at 20 °C and an upper limit of 10 ms at 250 °C. Extrapolating our measurements, we find τ values of ~0.5 μs and 40 ms at 250 and 20 °C, respectively. This is consistent with the upper limit (τ < 10 ms) but is well below the lower limit (τ > 10 s) given by Posselt et al.13. This apparent inconsistency could be related to a more complex τ(T) dependence at lower Ts, different irradiation conditions, or limitations of estimating τ based on the dose rate effect17.
Comparing DA in Ge to that in other semiconductors, we note that our τ values of ~0.3–8 ms in Ge (at 100–160 °C) are similar to those for Si (~0.2–14 ms in a wider T range from −20 to 140 °C), 3C-SiC (τ = 3 ms at 100 °C), and 4H-SiC (τ of ~1–5 ms at 25–250 °C) recently measured with the pulsed ion beam technique15,16,17,18,19. Despite such similarity of the range of the τ values measured, the details of defect interaction dynamics are strongly material dependent. First, we note that these previous pulsed-beam studies of different materials16,18,19 were performed at different Ts. Only at 100 °C, do data sets for these four materials overlap, yielding τ 1 values of 8.9 ± 1.5, 0.98 ± 0.07, 4.6 ± 0.8, and 6.9 ± 1.2 ms for Ge, Si, 3C-SiC, and 4H-SiC, respectively, irradiated with 500 keV Ar ions16,18,19. Hence, among these four materials, Ge exhibits the slowest defect interaction dynamics at 100 °C (an order of magnitude slower than for Si). The ratio of τ for different materials, however, strongly depends on T since different materials have uniquely different τ(T) dependencies, and more work is currently needed to understand any possible correlation between basic materials properties and τ values.
The τ parameter describes the dynamic interaction of mobile point defects produced in different pulses and, hence, in different collision cascades. In other words, τ is a parameter of inter-cascade (rather than intra-cascade) defect interaction. To gain insight into such inter-cascade defect dynamics, we replot the τ 2(T) dependence in Arrhenius coordinates as shown in the inset of Fig. 4. The second order DA rate is defined as \(\tfrac{1}{{\tau }_{2}(n\mathrm{(0)}-{n}_{\infty })}\), and kT has the usual meaning. Two well defined Arrhenius regions, above and below 130 °C, are clearly revealed in the inset of Fig. 4. Linear fitting of the data gives activation energies of 1.28 ± 0.07 eV and 0.13 ± 0.03 eV, above and below 130 °C, respectively. When the n(t off ) dependencies from Fig. 3 are fitted with the first order decay equation (and the DA rate defined as \(\tfrac{1}{{\tau }_{1}}\)), we find activation energies of 1.1 and 0.2 eV, above and below 130 °C, respectively. Hence, the choice of any particular form of the decay equation to fit experimental n(t off ) dependencies in order to quantify the DA rate is not a critical factor in measurements of activation energies.
How are these activation energies related to energy barriers of basic defect migration and interaction processes? It is tempting to associate the activation energies measured here with migration energies of interstitials and vacancies. This is, however, not straightforward. Indeed, previous estimates of point defect migration energies in Ge are limited and, more importantly, vary widely. All the previous experimental estimates of vacancy and interstitial migration energies in Ge have been indirect, with values ranging from 0.2 to 1.3 eV for vacancies26,27,28 and 0.16 eV for interstitials27. Similarly, theoretical studies predict migration energies of 0.1–0.7 eV for vacancies29 and 0.3–1.4 eV for interstitials29,30. Hence, the identification of the energetic barriers of different defect migration or interaction processes will need to await further studies that could enable future modeling of DA in pulsed-ion-irradiated Ge, similar to what was recently reported for Si19, for which elementary defect migration processes are much better understood than for Ge.
Finally, we discuss a transition temperature (T c ) of ~130 °C, which is consistent with Ts previously reported (~114–155 °C)8,9,10 above which damage buildup depends strongly on T and the dose rate. It also agrees with the T of a post-irradiation defect annealing stage (rather than DA)31,32,33,34. This T c is much larger than the Ts at which primary defects in Ge become mobile, which appears to occur below ~200 K31,34,35,36. Our results clearly show that a T c of 130 °C corresponds to a change in the dominant DA mechanism. What are these two dominant mechanisms? The fact that ξ reaches a saturation of ~100% above T c could suggest that the defect clusters produced during cascade thermalization and intra-cascade DA are no longer stable, and DA becomes dominated by inter-cascade processes. However, comprehensive theoretical studies, benchmarked against our experimental data, are required to better understand the atomistics of DA in Ge.
Conclusion
In summary, we have used the pulsed ion beam method to study defect interaction dynamics in Ge bombarded in the T range of 100–160 °C with 500 keV Ar ions. Results have revealed that, with increasing T, τ decreases monotonically in the range of ~0.3–8 ms. We have estimated an L d of ~38 nm. There is a major change in the dominant DA process at a critical temperature of 130 °C, which separates two defect accumulation regimes characterized by defect relaxation rates with very different activation energies of 0.13 ± 0.03 and 1.28 ± 0.07 eV. These results provide an important step toward the understanding of the mechanisms of radiation damage buildup in Ge.
References
Pillarisetty, R. Academic and industry research progress in germanium nanodevices. Nature 479, 324 (2011).
Decoster, S. et al. Transition metal impurities on the bond-centered site in germanium. Phys. Rev. Lett. 102, 065502 (2009).
Decoster, S. & Vantomme, A. Implantation-induced damage in Ge: strain and disorder profiles during defect accumulation and recovery. J. Phys. D. Appl. Phys. 42, 165404 (2009).
Koffel, S., Scheiblin, P., Claverie, A. & Benassayag, G. Amorphization kinetics of germanium during ion implantation. J. Appl. Phys. 105, 013528 (2009).
Kucheyev, S. O., Bradby, J. E., Ruffell, S., Li, C. P., Felter, T. E. & Hamza, A. V. Segregation and precipitation of Er in Ge. Appl. Phys. Lett. 90, 221901 (2007).
Impellizzeri, G., Mirabella, S. & Grimaldi, M. G. Ion implantation damage and crystalline-amorphous transition in Ge. Appl. Phys. A 103, 323 (2010).
Gomez-Selles, J. L., Claverie, A., Sklenard, B., Benistant, F. & Martin-Bragado, I. Atomistic simulation of damage accumulation and amorphization in Ge. J. Appl. Phys. 117, 055703 (2015).
Holmén, G. & Högberg, P. A study of the production and removal of radiation defects in Ge using secondary electron emission. Radiat. Eff. 12, 77 (1972).
Haynes, T. E. & Holland, O. W. Comparative study of implantation-induced damage in GaAs and Ge: Temperature and flux dependence. Appl. Phys. Lett. 59, 452 (1991).
Holland, O. W. & Haynes, T. E. Damage saturation during high-energy ion implantation of Si1 - x Ge x. Appl. Phys. Lett. 61, 3148 (1992).
Belyakov, V. S. & Titov, A. I. Stationary amorphous layer formation during 5 keV Ar+ ion bombardment of Ge. Radiat. Eff. Defects Solids 138, 231 (1996).
Birtcher, R. C. Energy-dependent amorphization of Ge by Ne, Ar or Kr ion irradiation. Philos. Mag. B 73, 677 (1996).
Posselt, M., Bischoff, L., Grambole, D. & Herrmann, F. Competition between damage buildup and dynamic annealing in ion implantation into Ge. Appl. Phys. Lett. 89, 151918 (2006).
Nordlund, K. et al. Defect production in collision cascades in elemental semiconductors and fcc metals. Phys. Rev. B 57, 7556 (1998).
Myers, M. T., Charnvanichborikarn, S., Shao, L. & Kucheyev, S. O. Pulsed ion beam measurement of defect diffusion lengths in irradiated solids. Phys. Rev. Lett. 109, 095502 (2012).
Wallace, J. B., Bayu Aji, L. B., Shao, L. & Kucheyev, S. O. Time constant of defect relaxation in ion-irradiated 3C-SiC. Appl. Phys. Lett. 106, 202102 (2015).
Wallace, J. B., Charnvanichborikarn, S., Bayu Aji, L. B., Myers, M. T., Shao, L. & Kucheyev, S. O. Radiation defect dynamics in Si at room temperature studied by pulsed ion beams. J. Appl. Phys. 118, 135709 (2015).
Bayu Aji, L. B., Wallace, J. B., Shao, L. & Kucheyev, S. O. Non-monotonic temperature dependence of radiation defect dynamics in silicon carbide. Sci. Rep. 6, 30931 (2016).
Wallace, J. B. et al. The role of Frenkel defect diffusion in dynamic annealing in ion-irradiated Si. Sci. Rep. 7, 39754 (2017).
Charnvanichborikarn, S., Myers, M. T., Shao, L. & Kucheyev, S. O. Pulsed ion beam measurement of defect diffusion lengths in irradiated solids. J. Phys. Condens. Matter 25, 162203 (2013).
Bayu Aji, L. B., Wallace, J. B., Shao, L. & Kucheyev, S. O. Effective defect diffusion lengths in Ar-ion bombarded 3C-SiC. J. Phys. D. Appl. Phys. 49, 19LT01 (2016).
Schmid, K. Some new aspects for the evaluation of disorder profiles in silicon by backscattering. Radiat. Eff. 17, 201 (1973).
Ziegler, J. F., Ziegler, M. D. & Biersack, J. P. SRIM - The stopping and range of ions in matter. Nucl. Instr. and Meth. B 268, 1818 (2010).
Levenberg, K. A Method for the Solution of Certain Problems in Least Squares. Q. Appl. Math 2, 164 (1944).
Cornell, J. A. & Berger, R. D. Factors that influence the value of the coefficient of determination in simple linear and nonlinear regression models. Phytopathology 77, 63 (1987).
Whan, R. E. Investigations of Oxygen-Defect Interactions between 25 and 700 K in Irradiated Germanium. Phys. Rev. 140, A690 (1965).
Ershov, S. N., Panteleev, V. A., Nagornkh, S. N. & Chernyakhovskii, V. V. Determination of the migration energy of vacancies and of intrinsic interstitial atoms in silicon in the temperature interval 400–600 K. Sov. Phys. Solid State 19, 11 (1977).
Hiraki, A. Experimental determination of diffusion and formation energies of thermal vacancies in germanium. J. Phys. Soc. Japan 21, 34 (1966).
Vanhellemont, J., Śpiewak, P. & Sueoka, K. On the solubility and diffusivity of the intrinsic point defects in germanium. J. Appl. Phys. 101, 036103 (2007).
Carvalho, A. et al. Self-interstitial in germanium. Phys. Rev. Lett. 99, 175502 (2007).
Mooney, P. M., Poulin, F. & Bourgoin, J. C. Annealing of electron-induced defects in n-type germanium. Phys. Rev. B 28, 3372 (1983).
Ouden, G. Den Small-Angle Scattering of X-Rays by Neutron-Irradiated Germanium. J. Appl. Phys. 39, 4509 (1968).
Elsayed, M., Arutyunov, N. Yu, Krause-Rehberg, R., Oganesyan, G. A. & Kozlovski, V. V. Formation and annealing of vacancy-P complexes in proton-irradiated germanium. Acta Mater. 100, 1 (2015).
Christian Petersen, M., Nylandsted Larsen, A. & Mesli, A. Divacancy defects in germanium studied using deep-level transient spectroscopy. Phys. Rev. B 82, 075203 (2010).
Brown, W. L. & Augustyniak, W. M. Energy, Orientation, and Temperature Dependence of Defect Formation in Electron Irradiation of nType Germanium. J. Appl. Phys. 30, 1300 (1959).
Slotte, J., Kilpeläinen, S., Tuomisto, F., Räisänen, J. & Larsen, A. N. Direct observations of the vacancy and its annealing in germanium. Phys. Rev. B 83, 235212 (2011).
Acknowledgements
This work was funded by the Nuclear Energy Enabling Technology (NEET) Program of the US DOE, Office of Nuclear Energy and performed under the auspices of the US DOE by LLNL under Contract DE-AC52-07NA27344. J.B.W. would like to acknowledge the LGSP for funding.
Author information
Authors and Affiliations
Contributions
J.B.W. performed the experiments and data analysis with assistance from L.B.B.A. and wrote the manuscript with input from S.O.K., L.B.B.A., and L.S.; S.O.K. supervised the project.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wallace, J.B., Bayu Aji, L.B., Shao, L. et al. Dynamic annealing in Ge studied by pulsed ion beams. Sci Rep 7, 13182 (2017). https://doi.org/10.1038/s41598-017-13161-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-13161-1
This article is cited by
-
Impact of pre-existing disorder on radiation defect dynamics in Si
Scientific Reports (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.