Abstract
N-acetyl cysteine (NAC) is an FDA-approved drug clinically applied on a broad range of pathologies. Further research has been conducted with this drug to benefit from its antimicrobial activity potential. However, NAC has a very short half-life and therefore strategies that accomplish high local concentrations would be beneficial. In this study, covalent immobilization of NAC was performed, in order to obtain long-lasting high local concentration of the drug onto a chitosan(Ch)-derived implant-related coating. For the development of NAC-functionalized Ch films, water-based carbodiimide chemistry was applied to avoid the use of toxic organic solvents. Here we report the optimization steps performed to immobilize NAC onto the surface of pre-prepared Ch coatings, to ensure full exposure of NAC. Surface characterization using ellipsometry, water contact angle measurements and X-ray photoelectron spectroscopy (XPS), demonstrated the success of NAC immobilization at 4 mg/mL. Quartz crystal microbalance with dissipation (QCM-D) demonstrated that surface immobilized NAC decreases protein adsorption to Ch coatings. Biological studies confirmed that immobilized NAC4 avoids methicillin-resistant Staphylococcus aureus adhesion to Ch coating, impairing biofilm formation, without inducing cytotoxic effects. This is particularly interesting towards further developments as a prevention coating.
Similar content being viewed by others
Introduction
N-acetylcysteine (NAC) is a known drug widely applied in a number of different clinical conditions ranging from chronic bronchitis, acetaminophen overdose treatment, chemotherapy-induced toxicity treatment, to HIV/AIDS and psychiatric disorders1. Adding to this broad activity, NAC has been reported as having an excellent safety profile2. NAC has been researched for further applications such as tissue regeneration, mostly in orthopedic and dental implants, to reduce cytotoxicity and improve osteointegration3,4,5. Interestingly, NAC has also antimicrobial properties against both Gram-positive and Gram-negative bacteria6,7,8,9,10. Although NAC antimicrobial mechanism is not fully described, it is known that the sulfhydryl moiety of NAC acts as an antioxidant, playing a role in free radical scavenging and therefore, helping the immune system in destroying intermolecular or intramolecular disulfide bonds of bacterial proteins1,11,12. Additionally, an antibiofilm activity has been reported, including reduction of bacteria adhesion, reduction of extracellular polysaccharide production and disruption of mature biofilms6,8,13. Therefore, NAC appears to be a promising preventive or even coadjuvant in the treatment of infections, which has prompted its research after being physically adsorbed onto collagen scaffolds12, and its patenting as a catheter lock solution14. Although having variable success rates, these strategies stressed the importance of a high long lasting local NAC concentration, in order to achieve better performance. Taking these findings in consideration we hypothesized the application of covalently immobilized NAC onto a polymer in order to develop an antimicrobial coating to avoid implant-related osteomyelitis infection. To that end, we chose chitosan, a natural cationic polysaccharide with recognized antimicrobial15,16,17,18 and osteoconductive properties19,20,21. Chitosan can be easily functionalized, and a number of chitosan derivatives have been studied for pharmaceutical and medical applications22,23,24,25. Particularly, thiolated chitosans have been explored for their potential as drug delivery systems, as they possess improved mucoadhesive and permeation enhancing properties25,26. Moreover, their strong cohesive properties make them highly suitable excipients for controlled drug release25,27. Recently, Fernandes et al.28 published a study where different soluble thiolated chitosans had their antimicrobial activity reported both with a bacteria membrane model and with bacteria. In all these studies chitosan functionalization was performed in solution in the presence of excess NAC25,27,28. However, as this approach does not guarantee –SH exposure to the surface and may promote unintended crosslinking24, we propose NAC-functionalization on pre-formed chitosan films to avoid bacterial adhesion, without impairing osteoblast proliferation. For that, we optimized the production of chitosan films with increasing NAC concentrations, assessed film stability and evaluated their biological impact on: (i) Methicillin-resistant Staphylococcus aureus (MRSA) adherence, proliferation and biofilm production, and (ii) Osteoblast MC3T3-E1 cell line metabolic activity and morphology.
Results
Optimization of NAC immobilization
Control film (Ch_Buffer), Ch incubated with carbodiimide reagents EDC and NHS (Ch_EDC) and Ch functionalized with NAC at concentrations ranging from 0.4 (Ch_NAC0.4) to 20 mg/mL (Ch_NAC20) were analyzed by XPS, ellipsometry, water contact angle measurements and IRRAS.
X-ray Photoelectron Spectroscopy (XPS)
XPS survey spectra demonstrated the absence of surface contaminants, since no other elements than those expected were detected (data available online in supplementary data SSD Fig. 1). The relative atomic composition of all surfaces is described at Table 1.
Ch_Buffer was in accordance with our previous reports29,30. As expected, a small excess of C1s atomic percentage in comparison to the theoretical value was observed (supplementary SSD Table 1), due to the common carbon contamination that happens when samples are not preserved in high vacuum conditions29. Consequently, the relative atomic percentage of N1s and O1s was slightly lower than expected. Moreover, the presence of S2p at very low percentage can be assigned to oxidized sulfur (~168 eV) from MES buffer.
XPS results also demonstrated that carbodiimide reaction in the absence of NAC, allowed the direct immobilization of EDC to the Ch backbone (as depicted in Fig. 1b) as previously suggested by us17.
Ch_EDC shows a clear increase of N1s and a decrease of O1s, which is congruent with expected values (supplementary Table 1). Regarding C1s, Ch_EDC has similar total carbon amounts comparing to Ch_Buffer, however high-resolution C1s spectra allowed the detection of a higher contribution in the 287.9 eV peak assigned to C=N, suggesting the EDC immobilization onto Ch_Buffer (SSD Fig. 2).
Since EDC also has nitrogen, NAC immobilization can be specifically followed by the appearance of S2p that increased with NAC concentration present at the reaction. However, the high increase of the relative Au percentage on samples prepared with NAC concentrations >= 8 mg/mL suggests the partial detachment of the chitosan films. It is well established that free thiol groups have high affinity towards gold, therefore a NAC concentration threshold above Ch_NAC8 could be responsible for chitosan replacement by direct immobilization of NAC on gold. This explanation is supported by the observation of a ~162 eV peak in samples Ch_NAC12 to Ch_NAC20, assigned to S-Au bond.
Nevertheless, the presence of S2p at 164-165 eV (-SH), the small decrease of Au and small increase of O, suggest NAC immobilization onto Ch films until 4 mg/mL although some EDC could be present in lower NAC concentrations.
Water optical contact angle (WCA) analysis
Water optical contact angles of the control and NAC-modified Ch films are presented on Fig. 2a.
Ch_EDC sample presented increased hydrophilicity, as compared to unmodified Ch, which is congruent with the EDC immobilization onto chitosan as proposed at Fig. 1b. Chitosan functionalization with growing NAC concentrations, resulted on increasing hydrophilicity, as the water contact angle decreased from 61 ± 3° to minimum of 30 ± 1° at Ch_NAC12. Beyond this NAC concentration, water contact angle increased, which agrees with the aforementioned hypothesis of NAC-induced detachment of the hydrophilic chitosan films from gold, in consequence of competing direct thiol-mediated NAC binding to the gold surface above a NAC threshold concentration.
Ellipsometry
The spin coating process resulted in uniformly distributed Ch with 14 ± 0.6 nm thickness, which remained stable even after the reaction protocols used, as there were no thickness changes between freshly made films and buffer-incubated films (see supplementary data SSD Fig. 3). Figure 2b presents thickness of Ch before and after surface modification with NAC concentrations, ranging from 0.4 to 20 mg/mL.
The Ch_Buffer thickness was augmented after EDC reaction to 17 ± 0.9 nm, as formerly proposed by the chemical pathway presented in Fig. 1b. NAC functionalization with increasing NAC concentrations resulted on sequential thickness reduction, which may be explained by EDC replacement for NAC. Notwithstanding, thickness decrease reaches a threshold at Ch_NAC4, as beyond this concentration films are thinner than control Ch_Buffer. These results are in accordance with the increase of Au relative percentage (Table 1), reinforcing the suggestion that direct immobilization of NAC onto gold occurs with partial detachment of Ch films.
Infrared reflection absorption spectroscopy (IRRAS)
IRRAS analyses of chitosan thin films, before and after immersion on buffer solution, showed that the films remained stable even after chemical procedures undertaken (data not shown). IRRAS spectra of control and NAC-modified chitosan up to 8 mg/mL can be found online in supplementary data SSD Fig. 4.
Ch_Buffer spectrum allowed the identification of characteristic absorption bands of chitosan, in agreement with previous literature29,30,31,32,33.
Both NAC-modified chitosan and EDC-modified chitosan spectra show an increase of the amide I absorption band (1654 cm−1), which can be assigned to the amide bond established between free amine groups of Ch and carboxylic groups of NAC, and to an imine intermediate (C=N stretching typically ranges from 1690 to 1630 cm−1), respectively34. No difference was observed among spectra of Ch modified with different NAC concentrations.
Functionalization stability
To determine whether NAC covalently bound to Ch (concentrations below 8 mg/mL), remained stable over time, a soak test was performed in PBS for 14 days at room temperature. Results are depicted on Fig. 3.
As depicted in Fig. 3 samples presented a tendency to higher hydrophilicity over time, which is not statistically significant. If film degradation had occurred, part of the gold substrate should be exposed resulting on a higher water contact angle. None of the samples had water contact angle augmentation (with the exception of Ch_NAC8 at day 14), the opposite occurred.
Further stability assessment was performed by a second soak test in PBS but incubation was performed at 37 °C for 7 days. Surfaces were then analyzed by XPS and their XPS relative atomic composition, at day 0 and day 7, are presented in Table 2. Moreover, XPS spectra surveys can be found in supplementary data SSD Fig. 5 and S2p high-resolution spectra in SSD Fig. 6.
As described above (Table 1), a small oxidized S2p from MES buffer was observed on Ch_Buffer (day 0) that disappeared after 7 days in PBS at 37 °C. The decrease of C1s and increase of N1s on Ch_Buffer sample after 7 days can be explained by the release of carbon contamination, which is always observed on chitosan that is not maintained in vacuum conditions, since values are closer to the expected (theoretical values SSD_Table 1). This fact can also explain the increase of N1s and the decrease of C1s in both Ch_NAC4 and Ch_NAC8. Although a small decrease in the relative % of S2p was observed on survey measurements of NAC surfaces, their absolute amount was not so different when the S2p XPS high resolution spectrum was analyzed (SSD_Fig. 6), particularly for Ch_NAC4. Moreover, no oxidation of S2p was detected (SSD_Fig. 6). These results demonstrate the presence of the coating at the end of the 7 days period (PBS and 37 °C).
The evidences gathered throughout different surface characterization techniques suggested that 4 mg/mL is enough to reach a stable chitosan film containing NAC covalently immobilized. Therefore, in order to evaluate the effect of covalent immobilization on the antimicrobial properties of NAC, all biological assays were performed using this NAC concentration (Ch_NAC4).
Antimicrobial Activity
The antimicrobial properties of NAC-functionalized Ch were evaluated by the assessment of their capacity to avoid S. aureus adhesion, proliferation and biofilm formation, as this is the most prevalent species in osteomyelitis35,36.
Adhesion assays
The effect of developed thin films on methicillin-resistant S. aureus adhesion is demonstrated on Fig. 4a.
As seen on Fig. 4a, after the 2 h incubation period (white bars), bacteria adhered preferably to the Au substrates used as control. Ch film coating promoted a ~76% decrease in bacterial adhesion compared to Au, as previously described by us17. Covalent immobilization of NAC clearly decreased bacterial adhesion by ~95% regarding Ch films, demonstrating the anti-adhesive capacity of Ch_NAC4 films. This anti-adhesive behavior of Ch_NAC4 is not compromised in the presence of human plasma proteins as depicted on Fig. 5.
Figure 4b represents bacterial behavior at the supernatants, which shows that bulk phase bacteria were able to duplicate in number during the 2 h incubation period in MHB (white bars), as compared to the initial inoculum (grey bar). No significant difference was found between the amount of bacteria in different samples. This can be explained by the high initial inoculum that was free to proliferate on this bulk phase.
Proliferation assays
To assess the degree of proliferation of surface adherent bacteria in the 2 h incubation assay (white bars on Fig. 4a), surfaces were re-incubated in fresh MHB medium for 4 h. Results obtained are depicted by the black bars on Fig. 4a and b.
Adherent bacteria on Au and Ch_Buffer surfaces were able to proliferate, since the number of surface adherent bacteria duplicated regarding the respective values obtained on the previous 2 h adherence assay (white bars). Also, at supernatants level (black bars on Fig. 4b), high colony-forming units (CFUs) were found, suggesting that bacteria were further able to detach and proliferate in bulk phase.
In contrast, surfaces with covalently immobilized NAC maintained the low amount of adherent bacteria throughout the extended 4 h incubation period, demonstrating that adherent bacteria could not proliferate on the surface (black bars on Fig. 4a). In addition, although some adherent bacteria could be detached from the surface and proliferate in solution (black bars on Fig. 4b), they were not able to adhere on NAC-surfaces since, as described above, the number of adherent bacteria did not increase on these surfaces. Such anti-adhesive effect is further reinforced by visualization of adherent bacteria on the different surfaces by SEM, as depicted on Fig. 4C. SEM images correlate with findings made on the adhesion assays (Fig. 4a).
Bacterial Viability in adhesion assay
Viability of bacteria adhered to the surfaces was assessed using LIVE/DEAD® Bacterial Viability Kit (BaclightTM). The kit contains two fluorescent dyes: Syto9, which stains all bacteria in green; and propidium iodide (PI) that can only crossover damaged bacteria membranes and gives red stained bacteria. As PI quenches the fluorescent emission of Syto9, it is assumed that green cells are alive whereas red cells are dead. Figure 6 depicts representative images of Au, Ch_Buffer and Ch_NAC4 after a 2 h incubation adhesion assay.
Ch_Buffer presented 23% of dead bacteria adhered to the surface. This result was expected, since we previously demonstrated the antimicrobial properties of chitosan ultrathin films37. Nevertheless, the low number of adherent bacteria found on Ch_NAC4 corresponds to living bacteria, demonstrating that this surface is exerting anti-adhesive properties rather than bactericidal properties.
Quartz Crystal Microbalance with Dissipation (QCM-D)
In order to clarify if the Ch_NAC4 anti-adhesive performance could be related with non-fouling properties and since the presence of proteins did not affect bacterial adhesion (Fig. 5), a QCM-D assay was used to evaluate human blood plasma proteins adsorption on the surfaces. Results are presented in Fig. 7.
QCM-D is able to detect mass increase (Δm) and structural changes such as swelling, due to the simultaneous recording of frequency (Δf) and dissipation (ΔD). Figure 7 shows the total amount of human blood plasma proteins adsorbed on different surfaces calculated using the Voigt model after 2 h of incubation followed by 2 h of rinsing with PBS. Voigt viscoelastic modeling was used to perform the QCM-D data fitting, since this model takes in account the energy losses in the system (i.e dissipation), correcting the deviation introduced by this factor. Protein adsorption was observed in all surfaces, although the mass of adsorbed proteins was lower on Ch_NAC4 (≈180 ng/cm2) than on other surfaces (Ch_Buffer ≈ 400 ng/cm2 and Au ≈ 1000 ng/cm2).
Biofilm assay
In order to evaluate surface activity during long-term bacteria interaction, biofilm assays were performed. Crystal violet (CV) staining was used as an indicator of total biofilm biomass. Results, presented in Fig. 8, clearly demonstrate that covalent immobilization of NAC provides anti-biofilm properties to the chitosan thin film. Ch_NAC4 presented the lowest value of biofilm biomass that was ~3-fold lower than that of control Ch_Buffer. No difference was observed between the controls Au and Ch_Buffer.
Influence of NAC-modified surfaces on osteoblastic cells
In order to evaluate possible cytotoxic effects of the modified surfaces on cell interaction/adhesion, osteoblastic MC3T3-E1 cells (a pre-osteoblast cell line) were cultured on top of Ch and Ch_NAC4 surfaces for 14 days under osteogenic conditions. Cell metabolic activity, cell adhesion, integrity and morphology were assessed at days 3, 7 and 14 of culture.
Regarding MC3T3-E1 proliferation, cells became confluent on Au control sample at day 3 and continued to proliferate on the followings days, covering the whole surface at day 14 of culture. On Ch_Buffer, MC3T3-E1 cells tended to agglomerate and grow forming big clusters spread throughout the Ch film surface, as previously described for other osteoblast-like cells38. On the Ch_NAC4 sample, a low number of adhered cells were observed at the initial time point (day 3), and cells were dispersed but elongated. As time progressed, cells were able to proliferate to cover most of the sample surface at day 14, as shown in Fig. 9b. In all cases, cells were well spread with a typical osteoblast-like morphology.
Therefore, as depicted in Fig. 9a, Ch film was responsible for a reduced MC3T3-E1 metabolic activity regarding Au control surface at early time point (Day 3), which was overcome on latter time points (Day 14), where metabolic activity is similar to Au control. Importantly, the metabolic activity differential between Ch_NAC4 and Ch_Buffer control was never superior to 30%, demonstrating that NAC-modified surfaces have no cytotoxic potential, according to ISO 10993-5:2009(E). These data suggest that MC3T3-E1 cells plated on top of NAC surfaces were viable and able to proliferate along the time of culture.
Discussion
NAC is an FDA-approved drug clinically applied on a broad range of pathologies1. Moreover, NAC has been reported to have antimicrobial activity against a variety of microorganisms, including the clinically relevant MRSA6,13,39,40. However, since NAC serum levels obtained with intravenous infusions (about 0.035 mg/mL)41 are much lower than the antimicrobial concentration reported in most studies (between 4 and 80 mg/mL)13,40,42,43, strategies that accomplish high local concentrations would be beneficial10,14.
In this study, covalent immobilization of NAC was performed, in order to obtain long-lasting high local concentration of the drug onto a chitosan-derived implant-related coating. For the production of NAC-functionalized chitosan films, water-based carbodiimide chemistry was applied to avoid the use of toxic organic solvents. In this frequently used chemistry, carbodiimide (EDC) reacts with the carboxylic acid from NAC to produce the O-acylisourea intermediate with an activated leaving group that can be stabilized upon reaction with NHS, producing a yet reactive intermediate. This intermediate will further react with primary amines from Ch to form amide bonds24,28. Differently from the literature, our strategy was to immobilize NAC onto the surface of previously prepared Ch films, to ensure full exposure of NAC. However, applying the aforementioned immobilization chemistry on a pre-formed chitosan film poses some challenges, namely a strict control of pH so that, on the one hand, the reaction is efficient and, on the other, solubilization of the chitosan film is avoided (while chitosan films solubilize at pH below ~6.523, literature reports suggest pH~5 as optimal for carbodiimide chemistry44). Also, a limited number of surface Ch free amines are available (Ch degree of acetylation (DA) ~15%) which might explain the NAC saturation point at 4 mg/mL. Noteworthy, a two-step immobilization procedure was tested, namely (i) NAC activation with EDC, and (ii) subsequent incubation with Ch film, but immobilization yield was not improved (data not shown).
The production of Ch-modified films was optimized and characterized by a number of different techniques (XPS, ellipsometry, water contact angle measurements, and IRRAS). Strong evidence on successful NAC covalent tethering was brought by the sum of different contributions. The success of NAC immobilization was demonstrated by XPS through observation of the S2p (~164 eV) peak assigned to free -SH group for NAC concentrations up to 8 mg/mL. However, the increased intensity of the Au4f peak (XPS) and the decreased film thickness (ellipsometry) for samples prepared with 8 mg/mL, and above, suggested a maximum NAC immobilization threshold at 4 mg/mL, corresponding to a 8.8% derivatization degree. Above this concentration threshold, some Ch detachment occurs due to the NAC’s affinity to gold, which is supported by XPS observation of the Sp2 peak at ~162 eV (Au-S).
We also demonstrated that, for low NAC concentrations, some EDC immobilization may occur, as suggested in Ch_EDC by the increase of its i) amide I absorption band (IRRAS), ii) C1s and N1s atomic percentages (XPS), iii) film thickness (ellipsometry), and iv) hydrophilicity (WCA measurements), when compared to Ch_Buffer.
Regarding stability of NAC functionalization, Ch_NAC4 was stable for 7 days in PBS at 37 °C, as the overall relative atomic composition obtained by XPS suggests Ch_NAC4 film maintenance at the end of the incubation period, with minimal NAC leaching. Also, by water contact angle measurements no significant hydrophobic increase was observed on surface wettability. These results differ from those reported by Harris et al.45, where NAC covalently immobilized onto poly(dimethyl)siloxane presented low yield and stability. This might be explained by the well-known high stability of amide bonds, as those formed between primary amines of chitosan and carboxyl groups of NAC, herein reported, in opposition to the ester bonds established between poly(dimethyl)siloxane hydroxyls and NAC carboxyl groups.
Regarding bacterial adhesion assays, surfaces were challenged with a very high initial inoculum over 2 h, to assess the Ch_NAC response to harsh conditions. As already reported in some studies, chitosan films were able to reduce bacterial adhesion of about 76%, as compared to naked Au surfaces17,37. This anti-adhesive property was dramatically increased for Ch_NAC4, by 95% and ~98% as compared to Ch and Au surfaces, respectively, and was not abolished in the presence of plasma proteins. The observed anti-adhesive properties of Ch_NAC4 may result from the superficial interactions between bacterial cell surface and the immobilized NAC coating. Such anti-adhesive properties might be simply ascribed to physical-chemical interactions, namely Ch_NAC4 low water contact angle, as less hydrophobic surfaces have been correlated with lower protein adsorption and bacterial adhesion46. Indeed, QCM-D assay revealed that protein adsorption was lower on Ch_NAC4 than on Ch_Buffer and Au. However, some protein adsorption was observed on Ch_NAC4 and thus, the lower bacterial adhesion may be related not only with the amount but also with the type/conformation of the adsorbed proteins47. It is well known that non-adhesive proteins such as albumin avoid bacterial adhesion, namely S. aureus 48. Moreover, Linnes et al.47 also demonstrated that fibronectin coatings were able to decrease S. epidermidis adhesion to biomaterials.
On proliferation assay, the capacity of surface adherent bacteria (from the 2 h adhesion assay) to proliferate/detach from the surface was evaluated. Results demonstrated that NAC-functionalized samples had no increased number of adhered bacteria after incubation in a fresh medium. However, some bacteria were found in the supernatants demonstrated that a minimum number of adherent bacteria were able to detach from the surface and proliferate in solution (Fig. 4a and b). Importantly, the anti-adhesive effect of the NAC-functionalized surface clearly avoids adhesion of planktonic bacteria to the surface, since the number of attached bacteria did not increase on this surface.
Bacterial viability assay clearly demonstrated that NAC effect is not bactericidal but anti-adhesive. Therefore, the antimicrobial properties attributed to soluble NAC, such as NAC-mediated destruction of disulfide bonds in proteins11, production impairment of extracellular polymeric substances (EPS) which are precursors of biofilm matrix6,42,49, may not be the explanation for immobilized NAC (Ch_NAC4).
The anti-adhesive effect observed in Ch_NAC4 may be explained by a combination of factors, namely i) the reduction of free available amine groups of Ch, which are related with the adherent dead bacteria observed on Ch_Buffer; ii) the increase of surface hydrophilicity, which can decrease bacterial adhesion directly or indirectly through the decrease of protein adsorption or the control on the type and conformation of adsorbed proteins. Therefore, it seems that the high local concentration of immobilized NAC is attributing surface characteristics that although interesting from a bacterial adhesion prevention point of view, is not congruent with the literature proposed mechanism of action. Nevertheless, it remains to be clarified if the exposed thiol group is having any direct contribution in preventing specific adhesion (e.g. degrading relevant disulfide bridges of bacterial adhesins), or if the overall mechanism is purely non-specific anti-adhesive.
Ch_NAC4 anti-adherence properties were further highlighted through the biofilm total biomass quantification, as this modified surface efficiently reduced the amount of biofilm. In contrast, the Ch_Buffer surface had its antimicrobial activity overwhelmed by the extended incubation period, meaning that the initial bactericidal effect of the surface was not sufficient to withstand the higher bacterial adhesion allowed by this surface. As this surface does not prevent protein adsorption, bacteria (both dead and alive) accumulate over time, ending up by presenting a biofilm total biomass similar to the one found for the control Au sample. The Ch_NAC4 anti-biofilm activity can be correlated with its anti-adhesion properties.
Effects of soluble NAC on eukaryotic cells have been previously addressed, with NAC being described as non-cytotoxic and even cell stimulating drug3,5,50,51. Since our most promising antimicrobial surface, Ch_NAC4, is hydrophilic and hinders bacteria adhesion, it would have been reasonable to assume that it might lead to poor cell adhesion and proliferation45. However, as NAC was immobilized on chitosan known for its osteogenic properties19,20,21,52, we expected Ch_NAC4 to present suitable cell adhesion and proliferation properties. Our results showed that the metabolic activity of cells adhered to NAC-modified samples was similar to those of controls (Au and Ch_Buffer), exhibiting a normal osteoblastic morphology. As such, Ch_NAC4 surfaces did not induced cytotoxic effects.
Conclusion
A bacterial anti-adhesive coating was developed by functionalizing a pre-formed chitosan film with NAC. This was achieved by employing a water-based carbodiimide chemistry (free of toxic organic solvents), and careful tuning of NAC concentration. Surface characterization using several techniques demonstrated the success of NAC immobilization at 4 mg/mL. Biological studies confirmed Ch_NAC4 to be a promising material, as it avoids bacterial adhesion, and impairs biofilm formation, without inducing cytotoxic effects. This is particularly interesting towards further developments as a prevention coating.
Materials and Methods
Preparation of Chitosan Ultrathin Films
A re-precipitation method31 was used to purify commercial squid pen chitosan (France Chitine), resulting on a molecular weight of 283–472 kDa with a degree of acetylation (DA) of ~15%. Chitosan ultrathin films (Ch) were prepared as previously described by us17,30 by spincoating (9000 rpm, 1 min) chitosan solution (0.4% in acetic acid w/v) onto gold substrates (Au) (1 × 1 cm2). Ch was neutralized (0.1 M NaOH), rinsed with type I water and dried with a gentle stream of argon. Au, produced as previously described by us53, was chosen due to its higher suitability for some of the surface characterization techniques used.
Functionalization with NAC
Functionalization of Ch with NAC was optimized using different NAC concentrations, namely 0.4, 2, 4, 8, 12, 16 and 20 mg/mL. Ch films were treated with a solution of 0.2 M 1-Ethyl-3-[3-dimethylaminopropyl] carbodiimide hydrochloride) (EDC; Sigma-Aldrich), 0.05 M N-hydroxysulfosuccimide (NHS; Sigma-Aldrich) and different NAC concentrations (Merck), in 0.1 M (N-morpholino)ethanesulfonic acid (MES; Sigma-Aldrich) buffer at pH 6.5, for 1 h, at 37 °C and 100 rpm. The modified films were rinsed (type I water) in an ultrasound bath (1 min; Bandelin Sonorex Digitec Bath 35 kHz) and then rinsed twice (type I water).
Surface Characterization
Firstly, samples were dried on a Vacuum Oven (Raypa, EV 50) for 1 h at 40 °C.
X-ray Photoelectron Spectroscopy (XPS)
XPS measurements were performed using a Kratos Axis Ultra HSA (UK) with PISCES software for data acquisition and analysis (from CEMUP – Centro de Materiais da Universidade do Porto). The analysis was carried out with a monochromatic Al Kα X-ray source (1486.7 eV), operating at 15 kV (90 W), in FAT mode (Fixed Analyser Transmission). Survey spectra over a range of 0–1150 eV were collected with analyzer pass energy of 80 eV. High resolution C1s, O1s, N1s, S2p and Au4f spectra were collected with analyzer pass energy of 40 eV. The photoelectrons were analyzed at a take-off angle of 70°. The binding energy (BE) scales were referenced by setting the C1s BE to 285.0 eV. Data acquisition was performed with a pressure lower than 1 × 10−6 Pa, and it was used a charge neutralization system. All spectra were fitted using XPS peak fitting software (XPSPEAK Version 4.1). All carbon spectra were fitted using asymmetrical 70% Gaussian/30% Lorentzian profiles.
Water Contact Angle (WCA)
Contact angle measuring system from Data Physics, model OCA 15, equipped with a video CCD-camera and SCA 20 software was used with sessile drop method, as described at53. Drops of type I water (4 µL) were deposited onto the samples surfaces and images were taken every 2 s over 300 s. Droplet profiles were fitted using Young-Laplace formula, and the WCA of each sample was calculated by extrapolating the time dependent curve to zero. Results are the average of two measurements on three independent samples.
Ellipsometry
Film thickness was measured with an imaging ellipsometer, model EP3, from Nanofilm Surface Analysis, in a polarizer-compensator-sample-analyzer (PCSA) mode (null ellipsometry). The light source was a solid-state laser (532 nm). The Au refractive index (n) and extinction coefficient (k) were determined by using a delta and psi spectrum with a variation of angle between 65° and 71° [(n) of 0.6477 (k) of 2.6007 was obtained for Au]. Four regions-of-interest were used to correct for any instrument misalignment. The thickness of modified Ch was determined considering n = 1.54 and k = 0, for the Ch54. Results presented are the average of three measurements on each of three samples.
Infrared reflection absorption spectroscopy (IRRAS)
IRRAS spectra were obtained on a Perkin Elmer FTIR spectrophotometer, model 2000, coupled with a VeeMax II Accessory (PIKE) and a liquid-nitrogen-cooled MTC detector. Instrument purge with dry nitrogen (for 5 min before and during each sample analysis) was performed to avoid water vapor adsorption. Similar Au was used as a background. Incident light was p-polarised and spectra were collected using the 80° grazing angle reflection mode. For each sample, 100 scans were performed with 4 cm−1 resolution.
Functionalization stability
Stability of immobilized NAC assay was performed by soaking NAC-modified films in PBS for 7 and/or 14 days at 37 °C and room temperature, respectively. Samples representative of Day 0 (controls) were immersed in PBS for 1 h and then rinsed and dried under a gentle stream of argon. Surfaces from the 7 days soaking period at 37 °C were analyzed by XPS as explained in section 5.3.1. Surfaces from the 14 days soaking period at room temperature had their WCA measured before (Day 0) and after 7 and 14 days soaking. Samples were rinsed as explained at 2.2. Results are the average of two measurements on three independent replicates.
Bacterial assays
Bacterial Strains, Media and Growth Conditions
Methicillin-resistant Staphylococcus aureus strain (MRSA) was bought from the American Type Culture Collection (ATCC 33591), and streaked onto Tryptic Soy Agar (TSA; Merck). Bacterial suspension was obtained from overnight culture in Tryptic Soy Broth (TSB; Merck) at 37 °C, 150 rpm, and concentration was adjusted by Optical Density (600 nm) (confirmed by retrospective viable count).
Surfaces disinfection
Test surfaces were incubated successively in 70% ethanol and sterile water, and then dried in sterile environment. These samples were then placed on 24-well flat bottom cellular suspension plates (Sarstedt, Ldt, Newton, USA).
Adherence assay
Firstly, samples were stabilized in Mueller-Hinton Broth (MHB) for 30 min. Adjusted bacterial suspension was then added to the wells (107 CFU/mL), and incubated at 37 °C for 2 h. Afterwards, samples were rinsed with sterile phosphate-buffered saline (PBS) solution and fixed with 4% (w/v) paraformaldehyde (PFA; Sigma–Aldrich) for 20 min. After rinsing with sterile PBS, samples were stained with VECTASHIELD® Mounting Medium with 40,6-diamidino-2-phenylindole (DAPI; Vector). Images were obtained with an inverted fluorescence microscope (Axiovert 200 M, Zeiss, Germany) (eight fields on each of triplicate replicates were obtained with a 1000x magnification, a net area ~0.1181 mm2/sample). ImageJ software manual counting mode was used to obtain bacterial counts. Also, supernatants were diluted, plated in triplicate on TSA and incubated at 37 °C for 18 h for colony forming units (CFU) counting. Results presented are representative of one of the three independent experiments with 3 replicates each performed.
Adherence assay in the presence of plasma proteins
Firstly, samples were stabilized in PBS or PBS with 1%(v/v) human plasma (provided by Centro Hospitalar de S. João, Porto) for 30 min. Adjusted bacterial suspension was then added to the wells (107 CFU/mL), and incubated at 37 °C for 2 h. Afterwards, samples were rinsed with PBS solution and fixed with 4% (w/v) paraformaldehyde (PFA; Sigma–Aldrich) for 20 min. After rinsing with sterile PBS and samples were stained with VECTASHIELD® Mounting Medium with DAPI (Vector). Images were acquired as explained above. ImageJ software manual counting mode was used to obtain bacterial counts. Three replicates were used for each sample.
Proliferation assay
For proliferation assays, samples that were incubated during 2 h with bacterial suspension (as described in 5.4.3.) were rinsed with sterile PBS, and immersed in fresh MHB in a new 24-well plate for 4 h at 37 °C and 100 rpm. At the end of this period, surfaces were rinsed with sterile PBS, fixed and visualized as described above (5.4.3). Supernatants were also plated for CFU counting. Results presented are representative of one of the three independent experiments with 3 replicates each performed.
Bacterial Viability of adhered bacteria
To assess the viability of adherent bacteria in the different surfaces, a bacteria adherence assay was performed as described in section 5.4.3. After the 2 h incubation period samples were rinsed in NaCl 0.9% and stained with a combination dye of the LIVE/DEAD® Bacterial Viability Kit (BaclightTM) for 15 min in the dark. Briefly, the kit contains two fluorescent dyes, Syto9 which stains all bacteria in green, and propidium iodide (PI) which can only crossover damaged cells membranes and gives red stained cells. As PI quenches the fluorescent emission of Syto9, it is assumed that green cells are alive whereas red cells are dead. Images were obtained as previously explained in section 5.4.3. Five replicates of each sample were analyzed by acquiring six fields of each replicate with a 630x magnification.
QCM-D Testing: Adsorption of proteins from human plasma
Gold-coated QCM-D sensors (fundamental frequency of 5 MHz) were purchased from Biolin Scientific. The sensors cleaning procedure consisted in a 10 min oxidation in a ultraviolet (UV) oven, followed by immersion in a “piranha” solution (3 parts hydrogen peroxide (H2O2) solution (Merck, 30% vol.) to 7 parts of Sulfuric acid (H2SO4) (Merck)). Afterwards, sensors were rinsed and sonicated for 3 min in type 2 water and dried with a gentle argon stream. After cleaning, the sensors were spincoated as previously explained in section 5.1.
QCM-D system (Q-Sense E4 instrument, Biolin Scientific) was used to monitor in real time the frequency (Δf) and dissipation (ΔD) shifts on the Au, Ch_Buffer and Ch_NAC4-QCM-D sensors related to protein adsorption. Briefly, samples were pre-incubated with PBS in static conditions for 30 min to establish a baseline. Afterwards, 500 μL/sensor of a 1% (v/v) of human plasma (provided by Centro Hospitalar de S. João, Porto) in PBS was injected in the system at a constant flow rate of 0.1 μL/min. After injection, incubation proceeded in static conditions for 2 h. Rinsing was performed with PBS, at a constant flow rate of 0.1 μL/min during 2 h. The entire experiment was conducted at 37 °C.
Data were treated using the Voigt model, since it takes in account the viscoelastic contributions of the hydrated layer. Data from the 3rd to the 11th harmonics were collected and used in the analysis. The density and viscosity of the human plasma solution was established at 1.35 g/cm3 and 0.0014 kg/ms−1, respectively55,56.
Results are presented in mass per area (ng/cm2). Results are average of 3 independent assays with 2 replicates per sample.
Scanning Electron Microscopy (SEM) visualization
Adherent bacteria were fixed with a freshly prepared solution of 1.5% glutaraldehyde (Merck) in 0.14 M sodium cacodylate (Merck) buffer for 30 min at room temperature. After fixation, samples were rinsed twice with PBS. Adherent bacteria were dehydrated in a graded ethanol series (50, 60, 70, 80, 90, and 99%, for 10 min each). Finally, 0.01 mL hexamethyldisilazane (Sigma) was added to each sample and left to dry overnight. Micrographs of the adhesion and proliferation assays were taken using a high resolution Scanning Electron Microscopy with X-ray Microanalysis, JEOL JSM 6301 F/Oxford INCA Energy 350 (from CEMUP – Centro de Materiais da Universidade do Porto). Electron beam intensity of 5 kV (accelerating voltage) and magnification of 1000x were applied. To increase the surface conductivity, samples were sputtered with Au/Pd for 60 s and 15 mA current using the SPI module sputter coater equipment.
Biofilm assay
S. aureus overnight culture in TSB (100 μL) was added to 5 mL of TSB-0.25% glucose and incubated for 4 h at 37 °C, 150 rpm. Then, 100 µL of this suspension were added to each well containing test surfaces already immersed in 900 µL of TSB-0.25% glucose. After a 2 h incubation period at 37 °C, surfaces were gently rinsed three times with sterile PBS and re-incubated with 1000 µL of TSB-0.25% glucose for 24 h. Finally, surfaces were rinsed with sterile PBS and left to dry. At this point, surfaces were stained with crystal violet 1% for 5 min and then washed with type 2 water. Crystal violet was solubilized in dimethyl sulfoxide (DMSO, Merck) and absorbance was read at 570 nm. Results are the average of three independent assays on each of three independent samples.
Cellular Biocompatibility
Cell culture
MC3T3-E1 calvaria pre-osteoblast cells (purchased from the European Collection of Cell Cultures - ECACC) were cultured in complete α-modified minimal essential medium (α-MEM, Gibco) supplemented with 10% (v/v) heat-inactivated fetal bovine serum (FBS; Gibco) and 1% (v/v) Penicillin/Streptomycin (P/S; Gibco). The cells were maintained at 37 °C in humidified atmosphere of 5% CO2, and media were refreshed every 2 to 3 days. At pre-confluence, MC3T3-E1 cells were harvested using trypsin solution (0.25% w/v trypsin, 0.1% w/v glucose and 0.05% w/v ethyldiaminetetracetic acid in PBS) and were plated on top of chitosan and chitosan-modified films (n = 5) at a density of 2.0 × 104 cells, under osteogenic conditions (complete α-MEM supplemented with 50 µg/ml ascorbic acid and 10 mM β-glycerophosphate). Multiwells culture plates were previously coated with polyhydroxyethylmethacrylate (pHEMA) at a final density of 0.8 mg/cm2 to avoid adhesion of the cells to the bottom and walls of the well. Tissue culture coverslips were used as positive controls. All experiments were performed using cells until passage 13.
Cytotoxicity assays
Cell metabolic activity and morphology were evaluated at 3, 7 and 14 days of culture. Cell metabolic activity was analysed by the Resazurin assay. Briefly, cells were incubated with 10% (v/v) Resazurin solution (0.1 mg/mL; Sigma–Aldrich) for 4 h at 37 °C. After incubation, three 150 μL/well samples were transferred to a 96-well black plate and fluorescence was measured (530 nm Ex/590 nm Em) in a microplate reader (BioTek Synergy Mx, Molecular Devices). Cell morphology was assessed by staining the filamentous actin cytoskeleton of the cells, through immunocytochemistry. For that, medium was removed from the wells, and cells were washed twice with PBS at room temperature (RT) and fixed in 4% (w/v) PFA (Sigma–Aldrich) for 10 min. Cells were then washed with PBS and permeabilized for 5 min with ice-cold 0.1% (v/v) Triton X-100 in PBS. After one PBS rinse, samples were incubated with 1% (w/v) bovine serum albumin (BSA) (Gibco, Alfagene) for 30 min at 37 °C. Afterwards, samples were incubated with Alexa Fluor® 594 phalloidin antibody (1:100; Molecular Probes, Invitrogen) in PBS for 20 min in the dark at RT. Samples were washed twice with PBS to remove unbound antibody, and mounted with VECTASHIELD® with DAPI. Samples were protected from light and kept at −20 °C until further analysis by inverted fluorescence microscopy (Zeiss AxioVision Microscope).
Statistical analysis
For statistical analysis, one-way analyses of variance followed by Tukey’s post hoc testing were used. The non-parametric Kruskal–Wallis test was applied when Gaussian distribution was not confirmed. Analyses were performed using the GraphPad Prism program. Data are expressed as the mean ± standard deviation (SD), and p values of <0.05 were considered significant. Data available on request from the authors.
References
Samuni, Y., Goldstein, S., Dean, O. M. & Berk, M. The chemistry and biological activities of N-acetylcysteine. Biochim. Biophys. Acta 1830, 4117–4129, https://doi.org/10.1016/j.bbagen.2013.04.016 (2013).
Kao, L. W. et al. What is the rate of adverse events after oral N-acetylcysteine administered by the intravenous route to patients with suspected acetaminophen poisoning? Ann. Emerg. Med. 42, 741–750, https://doi.org/10.1016/S0196064403005080 (2003).
Tsukimura, N. et al. N-acetyl cysteine (NAC)-mediated detoxification and functionalization of poly(methyl methacrylate) bone cement. Biomaterials 30, 3378–3389, https://doi.org/10.1016/j.biomaterials.2009.02.043 (2009).
Minamikawa, H. et al. Amino acid derivative-mediated detoxification and functionalization of dual cure dental restorative material for dental pulp cell mineralization. Biomaterials 31, 7213–7225, https://doi.org/10.1016/j.biomaterials.2010.06.018 (2010).
Lee, Y. H. et al. Bone regeneration around N-acetyl cysteine-loaded nanotube titanium dental implant in rat mandible. Biomaterials 34, 10199–10208, https://doi.org/10.1016/j.biomaterials.2013.08.080 (2013).
Olofsson, A. C., Hermansson, M. & Elwing, H. N-acetyl-L-cysteine affects growth, extracellular polysaccharide production, and bacterial biofilm formation on solid surfaces. Appl. Environ. Microbiol. 69, 4814–4822 (2003).
Marchese, A. et al. Effect of fosfomycin alone and in combination with N-acetylcysteine on E. coli biofilms. Int. J. Antimicrob. Agents 22(Suppl 2), 95–100 (2003).
Perez-Giraldo, C. et al. Influence of N-acetylcysteine on the formation of biofilm by Staphylococcus epidermidis. J. Antimicrob. Chemother. 39, 643–646 (1997).
del Prado, G. et al. Biofilm formation by Streptococcus pneumoniae strains and effects of human serum albumin, ibuprofen, N-acetyl-l-cysteine, amoxicillin, erythromycin, and levofloxacin. Diagn. Microbiol. Infect. Dis. 67, 311–318, https://doi.org/10.1016/j.diagmicrobio.2010.03.016 (2010).
Zhao, T. & Liu, Y. N-acetylcysteine inhibit biofilms produced by Pseudomonas aeruginosa. BMC Microbiol. 10, 140, https://doi.org/10.1186/1471-2180-10-140 (2010).
Sevier, C. S. & Kaiser, C. A. Formation and transfer of disulphide bonds in living cells. Nat Rev Mol Cell Biol 3, 836–847, https://doi.org/10.1038/nrm954 (2002).
Yamada, M., Ishihara, K., Ogawa, T. & Sakurai, K. The inhibition of infection by wound pathogens on scaffold in tissue-forming process using N-acetyl cysteine. Biomaterials 32, 8474–8485, https://doi.org/10.1016/j.biomaterials.2011.07.074 (2011).
Oosterhof, J. J. et al. The influence of antimicrobial peptides and mucolytics on the integrity of biofilms consisting of bacteria and yeasts as affecting voice prosthetic air flow resistances. Biofouling 19, 347–353, https://doi.org/10.1080/08927010310001612054 (2003).
Aslam, S. et al. N-acetylcysteine lock solution prevents catheter-associated bacteremia in rabbits. Int. J. Artif. Organs 35, 893–897, https://doi.org/10.5301/ijao.5000139 (2012).
Kong, M., Chen, X. G., Xing, K. & Park, H. J. Antimicrobial properties of chitosan and mode of action: a state of the art review. Int. J. Food Microbiol. 144, 51–63, https://doi.org/10.1016/j.ijfoodmicro.2010.09.012 (2010).
Carlson, R. P., Taffs, R., Davison, W. M. & Stewart, P. S. Anti-biofilm properties of chitosan-coated surfaces. J. Biomater. Sci. Polym. Ed 19, 1035–1046, https://doi.org/10.1163/156856208784909372 (2008).
Costa, F., Maia, S., Gomes, J., Gomes, P. & Martins, M. C. Characterization of hLF1-11 immobilization onto chitosan ultrathin films, and its effects on antimicrobial activity. Acta Biomate.r 10, 3513–3521, https://doi.org/10.1016/j.actbio.2014.02.028 (2014).
Hu, X. et al. An in vitro assessment of titanium functionalized with polysaccharides conjugated with vascular endothelial growth factor for enhanced osseointegration and inhibition of bacterial adhesion. Biomaterials 31, 8854–8863, https://doi.org/10.1016/j.biomaterials.2010.08.006 (2010).
Moutzouri, A. G. & Athanassiou, G. M. Attachment, spreading, and adhesion strength of human bone marrow cells on chitosan. Ann. Biomed. Eng. 39, 730–741, https://doi.org/10.1007/s10439-010-0188-y (2011).
Kawai, T. et al. Biological fixation of fibrous materials to bone using chitin/chitosan as a bone formation accelerator. J. Biomed. Mater. Res. B Appl Biomater 88, 264–270, https://doi.org/10.1002/jbm.b.31177 (2009).
Bumgardner, J. D. et al. The integration of chitosan-coated titanium in bone: an in vivo study in rabbits. Implant Dent. 16, 66–79, https://doi.org/10.1097/ID.0b013e3180312011 (2007).
Enescu, D. & Olteanu, C. E. Functionalized chitosan and its use in pharmaceutical, biomedical, and biotechnological research. Chem. Eng. Commun. 195, 1269–1291, https://doi.org/10.1080/00986440801958808 (2008).
Dash, M., Chiellini, F., Ottenbrite, R. M. & Chiellini, E. Chitosan-A versatile semi-synthetic polymer in biomedical applications. Prog. Polym. Sci. 36, 981–1014, https://doi.org/10.1016/J.Progpolymsci.2011.02.001 (2011).
Miles, K. B., Ball, R. L. & Matthew, H. W. Chitosan films with improved tensile strength and toughness from N-acetyl-cysteine mediated disulfide bonds. Carbohydr. Polym. 139, 1–9, https://doi.org/10.1016/j.carbpol.2015.11.052 (2016).
Liu, D. et al. Potential advantages of a novel chitosan-N-acetylcysteine surface modified nanostructured lipid carrier on the performance of ophthalmic delivery of curcumin. Sci. Rep. 6, 28796, https://doi.org/10.1038/srep28796 (2016).
Bernkop-Schnurch, A., Hornof, M. & Guggi, D. Thiolated chitosans. Eur. J. Pharm. Biopharm. 57, 9–17 (2004).
Wang, X. et al. Chitosan-NAC nanoparticles as a vehicle for nasal absorption enhancement of insulin. J. Biomed. Mater. Res. B Appl. Biomater. 88, 150–161, https://doi.org/10.1002/jbm.b.31161 (2009).
Fernandes, M. M., Francesko, A., Torrent-Burgues, J. & Tzanov, T. Effect of thiol-functionalisation on chitosan antibacterial activity: Interaction with a bacterial membrane model. React. Funct. Polym. 73, 1384–1390, https://doi.org/10.1016/J.Reactfunctpolym.2013.01.004 (2013).
Amaral, I. F., Granja, P. L. & Barbosa, M. A. Chemical modification of chitosan by phosphorylation: an XPS, FT-IR and SEM study. J. Biomater. Sci. -Polym. Ed. 16, 1575–1593, https://doi.org/10.1163/156856205774576736 (2005).
Nogueira, F., Goncalves, I. C. & Martins, M. C. Effect of gastric environment on Helicobacter pylori adhesion to a mucoadhesive polymer. Acta Biomater. 9, 5208–5215, https://doi.org/10.1016/j.actbio.2012.09.011 (2013).
Oliveira, J. R., Martins, M. C. L., Mafra, L. & Comes, P. Synthesis of an O-alkynyl-chitosan and its chemoselective conjugation with a PEG-like amino-azide through click chemistry. Carbohydr. Polym. 87, 240–249, https://doi.org/10.1016/j.carbpol.2011.07.043 (2012).
Osman, Z. & Arof, A. K. FTIR studies of chitosan acetate based polymer electrolytes. Electrochim. Acta 48, 993–999, https://doi.org/10.1016/S0013-4686(02)00812-5 (2003).
Lawrie, G. et al. Interactions between alginate and chitosan biopolymers characterized using FTIR and XPS. Biomacromol. 8, 2533–2541, https://doi.org/10.1021/Bm070014y (2007).
Socrates, G. Infrared and Raman characteristic group frequencies: tables and charts. 3rd edition edn, (John Wiley & Sons Ltd, 2001).
Faber, C. et al. Comparable efficacies of the antimicrobial peptide human lactoferrin 1–11 and gentamicin in a chronic methicillin-resistant Staphylococcus aureus osteomyelitis model. Antimicrob. Agents Chemother. 49, 2438–2444, https://doi.org/10.1128/AAC.49.6.2438-2444.2005 (2005).
Toms, A. D., Davidson, D., Masri, B. A. & Duncan, C. P. The management of peri-prosthetic infection in total joint arthroplasty. J. Bone Joint Surg. Br. 88, 149–155, https://doi.org/10.1302/0301-620X.88B2.17058 (2006).
Costa, F. M., Maia, S. R., Gomes, P. A. & Martins, M. C. Dhvar5 antimicrobial peptide (AMP) chemoselective covalent immobilization results on higher antiadherence effect than simple physical adsorption. Biomaterials 52, 531–538, https://doi.org/10.1016/j.biomaterials.2015.02.049 (2015).
Chua, P. H., Neoh, K. G., Kang, E. T. & Wang, W. Surface functionalization of titanium with hyaluronic acid/chitosan polyelectrolyte multilayers and RGD for promoting osteoblast functions and inhibiting bacterial adhesion. Biomaterials 29, 1412–1421, https://doi.org/10.1016/j.biomaterials.2007.12.019 (2008).
El-Feky, M. A. et al. Effect of ciprofloxacin and N-acetylcysteine on bacterial adherence and biofilm formation on ureteral stent surfaces. Pol. J. Microbiol. 58, 261–267 (2009).
Aslam, S. & Darouiche, R. O. Role of antibiofilm-antimicrobial agents in controlling device-related infections. Int. J. Artif. Organs 34, 752–758, https://doi.org/10.5301/ijao.5000024 (2011).
Prescott, L. F., Donovan, J. W., Jarvie, D. R. & Proudfoot, A. T. The disposition and kinetics of intravenous N-acetylcysteine in patients with paracetamol overdosage. Eur. J. Clin. Pharmacol. 37, 501–506 (1989).
Drago, L., De Vecchi, E., Mattina, R. & Romano, C. L. Activity of N-acetyl-L-cysteine against biofilm of Staphylococcus aureus and Pseudomonas aeruginosa on orthopedic prosthetic materials. Int. J. Artif. Organs 36, 39–46, https://doi.org/10.5301/ijao.5000135 (2013).
Leite, B. et al. Combined effect of linezolid and N-acetylcysteine against Staphylococcus epidermidis biofilms. Enferm. Infecc. Microbiol. Clin. 31, 655–659, https://doi.org/10.1016/j.eimc.2012.11.011 (2013).
Hermanson, G. T. Bioconjugate techniques (1996).
Harris, C. A. et al. Reduction of protein adsorption and macrophage and astrocyte adhesion on ventricular catheters by polyethylene glycol and N-acetyl-L-cysteine. J. Biomed. Mater. Res. A 98, 425–433, https://doi.org/10.1002/jbm.a.33130 (2011).
Cunliffe, D., Smart, C. A., Alexander, C. & Vulfson, E. N. Bacterial adhesion at synthetic surfaces. Appl. Environ. Microbiol. 65, 4995–5002 (1999).
Linnes, J. C., Mikhova, K. & Bryers, J. D. Adhesion of Staphylococcus epidermidis to biomaterials is inhibited by fibronectin and albumin. J. Biomed. Mater. Res. A 100, 1990–1997, https://doi.org/10.1002/jbm.a.34036 (2012).
Felgueiras, H. P. et al. Octadecyl Chains Immobilized onto Hyaluronic Acid Coatings by Thiol-ene “Click Chemistry” Increase the Surface Antimicrobial Properties and Prevent Platelet Adhesion and Activation to Polyurethane. ACS Appl. Mater. Interfaces 9, 7979–7989, https://doi.org/10.1021/acsami.6b16415 (2017).
Quah, S. Y., Wu, S., Lui, J. N., Sum, C. P. & Tan, K. S. N-acetylcysteine inhibits growth and eradicates biofilm of Enterococcus faecalis. J. Endod. 38, 81–85, https://doi.org/10.1016/j.joen.2011.10.004 (2012).
Ueno, T., Yamada, M., Igarashi, Y. & Ogawa, T. N-acetyl cysteine protects osteoblastic function from oxidative stress. J. Biomed. Mater. Res. A 99, 523–531, https://doi.org/10.1002/jbm.a.33211 (2011).
Yamada, M. et al. N-acetyl cysteine alleviates cytotoxicity of bone substitute. J. Dent. Res. 89, 411–416, https://doi.org/10.1177/0022034510363243 (2010).
Lieder, R. et al. In vitro bioactivity of different degree of deacetylation chitosan, a potential coating material for titanium implants. J. Biomed. Mater. Res. A 100, 3392–3399, https://doi.org/10.1002/jbm.a.34283 (2012).
Martins, M. C., Ratner, B. D. & Barbosa, M. A. Protein adsorption on mixtures of hydroxyl- and methyl-terminated alkanethiols self-assembled monolayers. J. Biomed. Mater. Res. A 67, 158–171, https://doi.org/10.1002/jbm.a.10096 (2003).
Lundin, M., Macakova, L., Dedinaite, A. & Claesson, P. Interactions between chitosan and SDS at a low-charged silica substrate compared to interactions in the bulk-the effect of ionic strength. Langmuir 24, 3814–3827, https://doi.org/10.1021/la702653m (2008).
Fischer, H., Polikarpov, I. & Craievich, A. F. Average protein density is a molecular-weight-dependent function. Protein Sci. 13, 2825–2828, https://doi.org/10.1110/ps.04688204 (2004).
Chick, H. & Lubrzynska, E. The Viscosity of Some Protein Solutions. Biochem. J. 8, 59–69 (1914).
Acknowledgements
This work was financed by FEDER funds through COMPETE 2020 (POCI), Portugal 2020 and FCT/MCTES through POCI-01-0145-FEDER-007274; NORTE-01-0145-FEDER-000012; Norte-01-0145-FEDER-000024 and FCT grants UID/Multi/04378/2013.
Author information
Authors and Affiliations
Contributions
F.C. contributed on the conception of experiments, performed the experiments and wrote the paper. D.M.S. and M.L. conceived and designed cell culture experiments, and assisted its assessment. P.P. performed the Q.C.M.-D. experiments, and assisted its assessment. P.G. assisted on the surface chemical characterization assessment. M.C.L.M. conceived and designed experiments. All authors reviewed and agreed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Costa, F., Sousa, D.M., Parreira, P. et al. N-acetylcysteine-functionalized coating avoids bacterial adhesion and biofilm formation. Sci Rep 7, 17374 (2017). https://doi.org/10.1038/s41598-017-17310-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-17310-4
This article is cited by
-
Repositioning of a mucolytic drug to a selective antibacterial against Vibrio cholerae
Journal of Microbiology (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.