Abstract
We experimentally study nanowire-shaped spin-Hall nano-oscillators based on nanometer-thick epitaxial films of Yttrium Iron Garnet grown on top of a layer of Pt. We show that, although these films are characterized by significantly larger magnetic damping in comparison with the films grown directly on Gadolinium Gallium Garnet, they allow one to achieve spin current-driven auto-oscillations at comparable current densities, which can be an indication of the better transparency of the interface to the spin current. These observations suggest a route for improvement of the flexibility of insulator-based spintronic devices and their compatibility with semiconductor technology.
Similar content being viewed by others
Introduction
Spintronic devices driven by pure spin current have recently become a subject of intense research1,2,3,4,5,6,7,8,9,10,11,12,13,14 owing to their flexible layout not restricted by the requirement of electrical current flow through the active magnetic layer. This advantage is particularly important for the possibility to implement spintronic devices based on insulating magnetic materials, such as Yttrium Iron Garnet (YIG), known for its unmatched small magnetic damping. Additionally, the utilization of magnetic insulators eliminates the shunting of the driving electric current through the active magnetic layer, which is known to be a significant shortcoming of all-metallic spin-current devices13. In spite of the significant efforts, the YIG-based spintronics showed a relatively slow progress because of the difficulties associated with the preparation of high-quality nanometer thick YIG films. Only with the recent developments in this field15,16,17,18,19,20, the insulator-based spintronic devices became feasible8,9,10,11.
The magnetic damping in YIG films is closely related to their structural properties15,16,17,18,19,20. Therefore, high-quality YIG films are usually grown on Gadolinium Gallium Garnet (GGG) substrates providing the precise lattice matching of the two materials, while utilization of other substrates results in a significant increase of the damping constant21. This requirement limits the compatibility of YIG with traditional Si-based semiconductor technology. Additionally, it significantly reduces the flexibility of spin current-driven devices utilizing materials with strong spin-orbit interaction such as Pt for generation of spin current by the spin-Hall effect (SHE)22,23. Indeed, the requirement that the YIG film has to be grown directly on the substrate forbids fabrication of devices with double-sided injection of the spin current into the magnetic film24.
Here we demonstrate experimentally that epitaxial YIG films grown on top of Pt layers can be utilized in SHE-driven spintronic devices. We show that by injecting spin currents with moderate density, one can achieve an efficient suppression or enhancement of magnetic fluctuations, complete compensation of the natural damping, and observe a transition to the magnetization auto-oscillation regime. Surprisingly, in spite of the relatively large damping in YIG grown on Pt, the density of the electrical current necessary for the auto-oscillations onset is very close to that previously reported for high-quality YIG films grown directly on GGG. This observation suggests that the transparency of the YIG/Pt interface to the spin current25 is likely improved by growing YIG on Pt.
Results
Test devices
The schematic of the experiment is shown in Fig. 1a. The studied devices are patterned in a shape of 200 nm wide and 2 μm long nanowires from an epitaxial YIG(35 nm)/Pt(5 nm) bilayer grown on top of a GGG(110) substrate. Figure 1b and c show the results of the structural characterization of YIG/Pt/GGG. The X-ray diffraction (XRD) measurements (Fig. 1b) reveal three main Bragg peaks of YIG and GGG: 220, 440, and 660, suggesting the (110) orientation of YIG and GGG. A small peak at 2θ≈40.15° (inset in Fig. 1b) can be identified as the 111 peak of the Pt layer suggesting its (111) texture. The high-resolution transmission electron microscopy (HRTEM) in real space (Fig. 1b) confirms sharp and clean Pt/YIG and GGG/Pt interfaces. The (110) atomic planes of YIG and GGG are parallel to each other and show closely matched inter-planar spacing. This indicates that the crystal orientation of YIG is locked to that of the substrate through single-crystal Pt. Since GGG possesses the same crystal symmetry and nearly the same lattice constant (mismatch ~ 0.056%) as YIG, it is natural to choose GGG as a material for substrate.
The operation of the test device is based on the SHE, which converts the electrical current I flowing in the plane of the Pt layer into the out-of-plane spin current IS. The spin current is injected into the YIG layer through the YIG/Pt interface. It exerts a spin-transfer torque (STT)26,27 onto the magnetization in YIG resulting, depending on the direction of I, in an increase or decrease of the effective magnetic damping28 and in a variation of the intensity of magnetic fluctuations29. The device is magnetized by the in-plane static magnetic field H applied perpendicular to the axis of the nanowire providing the maximum efficiency of the SHE-induced STT.
Magnetooptical measurements
We study the effects of the spin current on the dynamic magnetization in YIG by using micro-focus Brillouin light scattering (BLS) spectroscopy30. We focus the probing laser light with the wavelength of 473 nm into a diffraction-limited spot on the surface of the nanowire (Fig. 1a) and analyze the light inelastically scattered from magnetic excitations. The resulting signal – the BLS intensity – is proportional to the intensity of magnetic oscillations at the given frequency.
Due to the high sensitivity of the technique, one can detect magnetic oscillations existing in YIG due to the thermal fluctuations at I = 0, which enables easy characterization of the initial state of the system before the injection of the spin current. Figure 2a shows the BLS spectrum of magnetic oscillations in the YIG nanowire recorded for I = 0 and H = 0.5 kOe, together with the spectrum of magnetic modes obtained for the experimental nanowire geometry from the micromagnetic simulations (shadowed) using the MUMAX3 software31. The latter was calculated using the independently measured saturation magnetization of YIG 4πM0 = 1.6 kG. The Gilbert damping constant was chosen to be artificially small (α = 5×10−4) to enable clear identification of the spectral peaks corresponding to different modes. The obtained spectrum shows two intense peaks marked in Fig. 2a by the vertical arrows. These peaks correspond to the two fundamental dynamic modes of the system – the edge mode (EM) and the bulk mode (BM) – characterized by different distributions of the dynamic magnetization in the direction perpendicular to the axis of the nanowire, as shown in the insets in Fig. 2a. Additional small-amplitude peaks correspond to the higher-order edge and bulk modes quantized in the direction along the nanowire5. Comparison of the simulated spectrum with that obtained by BLS shows a perfect agreement in the frequency of BM, while the experimentally obtained frequency of EM 2.5 GHz is higher than that observed in simulations. We emphasize that this result is in a good agreement with previous studies10,32. In particular, in ref.32, it was shown that, in magnetic nanowires, the experimentally observed frequencies of the edge modes are always higher than those obtained from micromagnetic simulations. This frequency mismatch was attributed to an extrinsic pinning of the magnetization at the edges of the nanowire due to the joint action of the edge roughness, edge dilution effects, the non-zero surface anisotropy, etc. Recently similar behaviors have also been reported for YIG nanowires with dimensions close to those used in this work10. We emphasize that, in spite of the observed mismatch, based on the results of micromagnetic simulations, one can clearly identify the experimental peak at 2.5 GHz as the EM peak.
Figure 2b and c illustrate modifications of the BLS spectra under the influence of the spin current. With the increase of I > 0, the intensities of both spectral peaks increase reflecting the current-induced enhancement of magnetic fluctuations29. The increase of the amplitudes of fluctuations with current results in the reduction of the effective static magnetization leading to the nonlinear redshift33,34 of the frequencies of the modes. Additional contribution to the frequency shift comes from the reduction of the effective static magnetization due to the Joule heating of the YIG film by the current flowing in the Pt layer. In particular, it results in a reduction of the frequencies of the modes at I < 0, where the long-wavelength magnetic fluctuations are suppressed by the spin current (see spectrum for I = −0.4 mA in Fig. 2b).
Note that, at I > 0, the intensity of the EM peak, which is initially smaller than that of the BM peak (Fig. 2a), grows noticeably faster. The intensities of the peaks become approximately equal at I = 0.5 mA and the EM peak starts to strongly dominate the BM peak at larger currents. These behaviors are in agreement with the concept of the influence of the spin current on the chemical potential of magnons35, which generally predicts stronger influence of the spin current on the magnetic modes with lower frequencies.
Figure 3a shows the current dependence of the BLS intensity integrated over the spectrum, which reflects the total energy stored in magnetic modes accessible by BLS, and of its inverse value. As seen from these data, the enhancement of magnetic fluctuations is only observed for positive I, which is in agreement with the symmetry of SHE. The integral intensity grows slowly at I < 0.4 mA and then shows an abrupt increase at I≈0.5 mA followed by a saturation at I > 0.7 mA. These behaviors suggest that, at I ≈ 0.5 mA, the spin current completely compensates the intrinsic magnetic damping in YIG resulting in the onset of magnetization auto-oscillations. In agreement with the general theory of devices driven by STT36, the inverse of the integral intensity shows a linear dependence at I < 0.5 mA typical for the effect of STT on magnetic fluctuations. We emphasize that, at I < 0, the integral intensity decreases with respect to that at I = 0 by about a factor of three. This corresponds to the current-induced reduction of the thermal magnetic noise – a phenomenon, which has been previously observed for SHE systems based on metallic magnetic films29. We also note that the precisely linear current dependence of the inverse integral intensity clearly shows that the observed behaviors are solely caused by SHE, while the spin Seebeck effect37 important in Pt/YIG/GGG devices10,11 plays a negligible role in the YIG/Pt/GGG devices studied here. The YIG and Pt layer sequence matters because the Pt/YIG/GGG configuration maximizes current-induced temperature gradient across the YIG film by sandwiching it between the Pt ohmic heat source and the GGG substrate heat sink10.
The linear current dependence of the inverse integral intensity (Fig. 3a) allows the precise determination of the auto-oscillation onset current. According to the theory36, this dependence crosses zero at the current, corresponding to the complete compensation of the natural magnetic damping in YIG by the current-induced STT. By fitting the experimental data for the inverse integral intensity by a linear function and finding its zero intercept, we determine the auto-oscillation onset current IC = 0.51 mA. At this current, both the edge and the bulk mode switch to the auto-oscillation regime resulting in multi-mode auto-oscillations, similarly to all-metallic nanowire SHE oscillators5. The additional separate analysis of the current-dependent intensities of the edge and the bulk mode shows that IC is approximately the same for both modes.
Figure 3b shows the current dependences of the frequencies of the spectral peaks corresponding to the bulk and the edge mode. At |I| < IC, the frequencies of both modes reduce only slightly. The frequency shift is approximately the same for positive and negative currents indicating that the Joule heating of the YIG layer by the current plays the dominant role at small I. As the current approaches IC, the frequencies of both modes start to decrease quickly. This decrease is well correlated with the abrupt increase of the BLS intensity (Fig. 3a) confirming the dominating contribution to the frequency shift of the large intensity of magnetic oscillations excited by the spin current.
Behaviors similar to those described above were observed in a broad range of the static magnetic field H = 0.3–1.0 kOe. We show in Fig. 4a the obtained field dependencies of the density of the auto-oscillation onset current JC (squares) and of the frequencies of EM and BM at the onset of auto-oscillations (triangles). As seen from these data, within the studied range of H, the frequencies of the modes vary by more than a factor of two, while JC ≈ 5×1011 A/m2 remains nearly constant.
Discussion
The observed independence of JC from the static magnetic field is surprising, since the density of the onset current is known to be proportional to the relaxation rate Γ of the dynamic modes36,38, which generally increases with the increase of the mode frequency. In the approximation of an extended magnetic film36, the relaxation rate \(\Gamma =\alpha \gamma (H+2{\pi }{M}_{0})\) is expected to increase by about 50% as the static field varies from 0.3 to 1.0 kOe, which disagrees with the experimental data for JC (Fig. 4a). As was shown in ref.8, for YIG films with typically small Gilbert damping constant α, the additional contribution to the magnetic relaxation due to the inhomogeneous broadening effects can be significant. Taking into account that this contribution is independent of the static field (frequency), one can suggest that it fully dominates the total relaxation rate in the studied structures resulting in a field-independent onset current.
To prove this assumption we perform high-resolution ferromagnetic-resonance (FMR)-BLS measurements of the spectral linewidth of the observed magnetic modes. We excite the magnetic dynamics in the YIG nanowire by the microwave-frequency magnetic field produced by an ac current in the Pt layer and detect the magnetization response by BLS with H rotated by 5° from the direction perpendicular to the nanowire axis (see ref.39 for details). The obtained results (Fig. 4b) show that, within the measurement accuracy, the linewidths of the EM and BM are approximately equal and remain constant over the range H = 0.3–1.0 kOe. Since the linewidth directly characterizes the damping rate of the dynamic magnetization, we conclude that, in the YIG films grown on Pt, the field-dependent Gilbert-like contribution to the damping is much smaller compared to the field-independent contribution associated with the inhomogeneous broadening effects.
Finally, we quantitatively compare the characteristics of our devices with those obtained for devices based on YIG grown on GGG. The minimum onset current density 4×1011 A/m2 observed in the latter case8 is smaller by only 20% than that in our devices based on YIG grown on Pt. However, the typical linewidth in the frequency range of 2–4 GHz reported in ref.8 is by about a factor of two smaller than that in our devices. This suggests, that the significantly larger damping in YIG grown on Pt is compensated by the higher efficiency of SHE, which can be associated with the better transparency of the YIG/Pt interface to the spin current.
In conclusion, we have demonstrated that efficient spin current-driven devices can be made from YIG films grown on Pt, where the auto-oscillation characteristics are not adversely affected by the unavoidably increased magnetic damping. Our observations suggest a route for implementation of highly flexible insulator-based spintronic devices, where both interfaces of the magnetic-insulator film are available for spin-current injection. Our results should stimulate further development of spintronic devices based on magnetic insulators.
Methods
Sample fabrication
The details of the growth of the YIG/Pt bilayer as well as its structural and static magnetic characterization can be found in ref.20. The patterning of the bilayer is performed by defining a negative resist etching mask in the shape of a nanowire with two contact pads via a single e-beam lithography step. The mask pattern is then transferred to the film via ion mill etching, and the remaining resist is removed by oxygen plasma cleaning.
Magneto-optical measurements
Micro-focus BLS measurements were performed by focusing light produced by a continuous-wave single-frequency laser operating at the wavelength of 473 nm into a diffraction-limited spot. The light scattered from magnetic oscillations was analyzed by a six-pass Fabry-Perot interferometer TFP-1 (JRS Scientific Instruments, Switzerland) to obtain information about the BLS intensity proportional to the square of the amplitude of the dynamic magnetization at the location of the probing spot. All measurements were performed at room temperature.
Simulations
The micromagnetic simulations were performed by using the software package MuMax3 (ref.31). The computational domain with dimensions of 2×0.2×0.035 µm³ was discretized into 20×4×35 nm³ cells. The FMR mode was excited by a 15 ps wide sinc pulse of the out-of-plane magnetic field. The spatial map of the dynamic magnetization was reconstructed based on the Fourier analysis of the dynamic response of the magnetization. The standard value for the exchange stiffness of 3.66×10−12 J/m was used, while the value of the saturation magnetization 4πM0 = 1.6 kG was determined from the BLS spectra of thermally excited magnons at I = 0 mA. The Gilbert damping constant of 5×10−4 was chosen artificially low to allow for a low pulse width and therefore enable a high resolution of the excited modes.
References
Demidov, V. E. et al. Magnetic nano-oscillator driven by pure spin current. Nature Mater. 11, 1028–1031 (2012).
Liu, L., Pai, C.-F., Ralph, D. C. & Buhrman, R. A. Magnetic oscillations driven by the spin Hall effect in 3-terminal magnetic tunnel junction devices. Phys. Rev. Lett. 109, 186602 (2012).
Liu, R. H., Lim, W. L. & Urazhdin, S. Spectral characteristics of the microwave emission by the spin Hall nano-oscillator. Phys. Rev. Lett. 110, 147601 (2013).
Demidov, V. E., Urazhdin, S., Zholud, A., Sadovnikov, A. V. & Demokritov, S. O. Nanoconstriction-based spin-Hall nano-oscillator. Appl. Phys. Lett. 105, 172410 (2014).
Duan, Z. et al. Nanowire spin torque oscillator driven by spin orbit torques. Nature Commun. 5, 5616 (2014).
Demidov, V. E. et al. Spin-current nano-oscillator based on nonlocal spin injection. Sci. Rep. 5, 8578 (2015).
Demidov, V. E. et al. Excitation of coherent propagating spin waves by pure spin currents. Nature Commun. 7, 10446 (2016).
Collet, M. et al. Generation of coherent spin-wave modes in yttrium iron garnet microdiscs by spin–orbit torque. Nature Commun. 7, 10377 (2016).
Demidov, V. E. et al. Direct observation of dynamic modes excited in a magnetic insulator by pure spin current. Sci. Rep. 6, 32781 (2016).
Safranski, C. et al. Spin caloritronic nano-oscillator. Nature Commun. 8, 117 (2017).
Lauer, V. et al. Auto-oscillations in YIG/Pt microstructures driven by the spin Seebeck effect, arXiv:1612.07305 (2016).
Chen, T. et al. Spin-torque and spin-Hall nano-oscillators. Proc. IEEE 104, 1919–1945 (2016).
Demidov, V. E. et al. Magnetization oscillations and waves driven by pure spin currents. Phys. Rep. 673, 1–31 (2017).
Awad, A. A. et al. Long-range mutual synchronization of spin Hall nano-oscillators. Nature Physics 13, 292–299 (2017).
Sun, Y. et al. Growth and ferromagnetic resonance properties of nanometer-thick yttrium iron garnet films. Appl. Phys. Lett. 101, 152405 (2012).
Hahn, C. et al. Comparative measurements of inverse spin Hall effects and magnetoresistance in YIG/Pt and YIG/Ta. Phys. Rev. B 87, 174417 (2013).
d’Allivy Kelly, O. et al. Inverse spin Hall effect in nanometer-thick YIG/Pt system. Appl. Phys. Lett. 103, 082408 (2013).
Tang, C. et al. Exquisite growth control and magnetic properties of yttrium iron garnet thin films. Appl. Phys. Lett. 108, 102403 (2016).
Hauser, C. et al. Yttrium iron garnet thin films with very low damping obtained by recrystallization of amorphous material. Sci. Rep. 6, 20827 (2016).
Aldosary, M. et al. Platinum/yttrium iron garnet inverted structures for spin current transport. Appl. Phys. Lett. 108, 242401 (2016).
Che, P. et al. Short-wavelength spin waves in yttrium iron garnet micro-channels on silicon. IEEE Magn. Lett. 7, 3508404 (2016).
Dyakonov, M. I. & Perel, V. I. Possibility of orienting electron spins with current. Sov. Phys. JETP Lett. 13, 467–469 (1971).
Hirsch, J. E. Spin Hall effect. Phys. Rev. Lett. 83, 1834–1837 (1999).
Li, J. et al. Observation of magnon-mediated current drag in Pt/yttrium iron garnet/Pt(Ta) trilayers. Nature Commun. 7, 10858 (2016).
Zhang, W., Han, W., Jiang, X., Yang, S.-H. & Parkin, S. S. P. Role of transparency of platinum–ferromagnet interfaces in determining the intrinsic magnitude of the spin Hall effect. Nature Physics 11, 496–502 (2015).
Slonczewski, J. C. Current-driven excitation of magnetic multilayers. J. Magn. Magn. Mater. 159, L1–L7 (1996).
Berger, L. Emission of spin waves by a magnetic multilayer traversed by a current. Phys. Rev. B 54, 9353–9358 (1996).
Ando, K. et al. Electric manipulation of spin relaxation using the spin Hall effect. Phys. Rev. Lett. 101, 036601 (2008).
Demidov, V. E. et al. Control of magnetic fluctuations by spin current. Phys. Rev. Lett. 107, 107204 (2011).
Demidov, V. E. & Demokritov, S. O. Magnonic waveguides studied by microfocus Brillouin light scattering. IEEE Trans. Mag. 51, 0800215 (2015).
Vansteenkiste, A. et al. The design and verification of MuMax3. AIP Advances 4, 107133 (2014).
Duan, Z. et al. Spin wave eigenmodes in transversely magnetized thin film ferromagnetic wires. Phys. Rev. B 92, 104424 (2015).
Krivosik, P. & Patton, C. E. Hamiltonian formulation of nonlinear spin-wave dynamics: Theory and applications. Phys. Rev. B 82, 184428 (2010).
Dzyapko, O. et al. Magnon-magnon interactions in a room-temperature magnonic Bose-Einstein condensate. Phys. Rev. B 96, 064438 (2017).
Demidov, V. E. et al. Chemical potential of quasi-equilibrium magnon gas driven by pure spin current. Nat. Commun. 8, 1579 (2017).
Slavin, A. & Tiberkevich, V. Nonlinear auto-oscillator theory of microwave generation by spin-polarized current. IEEE Trans. Mag. 45, 1875 (2009).
Uchida, K. et al. Observation of the spin Seebeck effect. Nature 455, 778–781 (2008).
Slonczewski, J. C. Excitation of spin waves by an electric current. J. Magn. Magn. Mater. 195, L261–L268 (1999).
Demidov, V. E., Urazhdin, S., Edwards, E. R. J. & Demokritov, S. O. Wide-range control of ferromagnetic resonance by spin Hall effect. Appl. Phys. Lett. 99, 172501 (2011).
Acknowledgements
This work was primarily supported as part of the Spins and Heat in Nanoscale Electronic Systems (SHINES), an Energy Frontier Research Center funded by the U.S. Department of Energy, Office of Basic Energy Sciences (BES) under Award No. DE-SC0012670. The work of M.E. and V.E.D. was supported by the Deutsche Forschungsgemeinschaft. A.P.N., A.B.R. and S.O.D acknowledge support by the program Megagrant № 14.Z50.31.0025 of the Russian Ministry of Education and Science.
Author information
Authors and Affiliations
Contributions
M.E. and V.E.D. performed BLS measurements and data analysis. M.E. performed micromagnetic simulations. A.P.N., A.B.R., K.S. and X.L. performed data analysis. M.A.and J.S. deposited YIG\Pt bilayer films. C.S., I.B., X.L. and I.N.K. designed and made the nanowire samples. S.O.D. formulated the experimental approach and managed the project. All authors co-wrote and discussed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Evelt, M., Safranski, C., Aldosary, M. et al. Spin Hall-induced auto-oscillations in ultrathin YIG grown on Pt. Sci Rep 8, 1269 (2018). https://doi.org/10.1038/s41598-018-19606-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-19606-5
This article is cited by
-
Electrical detection of spin pumping in van der Waals ferromagnetic Cr2Ge2Te6 with low magnetic damping
Nature Communications (2023)
-
Spin–orbit torque nano-oscillator with giant magnetoresistance readout
Communications Physics (2020)
-
Spin torque nano-oscillator driven by combined spin injection from tunneling and spin Hall current
Communications Physics (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.