Abstract
Titanium alloys are extensively applied in biomedical industries due to their excellent material properties. However, they are recognized as difficult to cut materials due to their low thermal conductivity, which induces a complexity to their deformation mechanisms and restricts precise productions. This paper presents a new observation about the removal regime of titanium alloys. The experimental results, including the chip formation, thrust force signal and surface profile, showed that there was a critical cutting distance to achieve better surface integrity of machined surface. The machined areas with better surface roughness were located before the clear transition point, defining as the ductile to brittle transition. The machined area at the brittle region displayed the fracture deformation which showed cracks on the surface edge. The relationship between depth of cut and the ductile to brittle transaction behavior of titanium alloys in ultra-precision machining(UPM) was also revealed in this study, it showed that the ductile to brittle transaction behavior of titanium alloys occurred mainly at relatively small depth of cut. The study firstly defines the ductile to brittle transition behavior of titanium alloys in UPM, contributing the information of ductile machining as an optimal machining condition for precise productions of titanium alloys.
Similar content being viewed by others
Introduction
Titanium alloys are applied widely in aerospace and medical industries because of their superior material properties such as high strength and fracture resistance1,2,3,4. They become one of the most popular medical alloys and they are used in different complex forms such as cylinder, bar, plate, sheet and stripe5 in the real applications. They are required to machine precisely for obtaining the desired shape and an excellent surface quality in order to fulfill the medical uses. Titanium alloys hold a high yield strength and their flow stresses increase suddenly when the strain rate is over 103 s−1 in machining processes6,7, adding the challenges in the machining process. The deformation mechanism of titanium alloys in machining is extremely complicated and deviates from the other traditional alloys such as aluminum alloys and magnesium alloys8.
The low thermal conductivity of titanium alloy leads to an ineffective heat transference from the cutting zone to the surrounding9,10,11,12, causing an ineffective dissipation of cutting heat from the tool/workpiece interface. On the other hand, the ability of sustaining strength at elevated temperature of titanium alloys, the resulting working hardening on the machined surface is serious8 which further induces the high cutting force and the intensive cutting force variation3. High cutting temperature in machining processes is another problematic issue and places negative influences on machining performances13,14. Also, the phase change caused by the high cutting heat in machining leads the alternation of the deformation regime in machining processes, adding the difficulty on machining of titanium alloys especially in ultra-precision machining (UPM). In general, the machining mechanism of a material in a cutting process is mainly evaluated by the machining indicators of chip formation and tool wear15,16,17. Because of the low thermal conductivity and the extremely high strain rate induced in the machining processes of titanium alloys, the chip formation happens rapidly in the material removal process18. On the other hand, the high material shearing stress and plastic deformation with extremely high cutting temperature affect the chip formation18. Consequently, the chip formation in machining of titanium alloys is influenced by many machining factors and therefore it is difficult to conduct an analysis of cutting mechanism of titanium alloys. On the other hand, tool wear in machining of titanium alloys is serious and tool life is reported to be short19,20. The tool damage leads to the dramatic change in experimental conditions and the interrupt cutting motion in the cutting processes. Because of the frequent tool damage, the machining mechanism of titanium alloys is difficult to observe as the change in the tool condition causes the alteration of cutting mechanism. Moreover, the machined materials around the tool/workpiece interface are suffered from physical and metallurgical changes because of high cutting temperature18. In response to the above uncertainty in observing the machining indicators in machining of titanium alloys, the cutting mechanism of titanium alloys is always difficult to determine.
Cutting a groove with tilted angle was a common methodology for determining the deformation regime of brittle materials in previous literature21,22,23,24, however, it is not feasible for the case of identifying the deformation characteristic of titanium alloys which are hard and exhibit low thermal conductivity. For the low thermal conductivity materials, the thermal gradient and thermal softening effects at the tool/workpiece interface in machining processes are always dominant and accumulative; when titanium alloys are cut with an increasing depth of cut, the dynamic increase of depth of cut provides the extra fresh materials and surface areas in the machined surface, they develop an averaging effect on the cutting zone as the fresh surfaces serve as new cooling media. In this study, we cut an individual groove with different depth of cut instead of an increasing depth of cut at a single groove. In response to the material property of low thermal conductivity of titanium alloys, a sharp transition point is expected to appear on the machined surface under cutting at the same level of depth of cut.
The ductile to brittle behavior of brittle materials has been extensively investigated previously25,26, and the ductile machining strategy is widely adopted to improve surface finishing of the brittles materials. However, up to now, limited researches have reported the machining characteristics of titanium alloys, the fracture mechanism of these alloys in the material removal process in UPM is ever fewer reported. This paper aims to reveal the ductile to brittle transition regime of titanium alloys in UPM and shows the effects of depth of cut on the critical cutting distance and the ductile to brittle transition behavior of titanium alloys. We reported that there was a ductile deformation region on the machined surface of titanium alloys which showed a lower level of elastic recovery and better surface integrity, and it was highly depended on depth of cut. The cutting area outside the ductile deformation region suffered from a higher level of material swelling and the brittle fracture deformation, resulting of poorer surface integrity and the generation of uncut materials, which was defined as a brittle deformation region. The experimental results of cutting force, cutting profile, surface roughness, chip formation and machined surface in the different areas of machined surface were investigated and they gave out the evidences of above phenomenon. The clear crack was appeared at the ductile and brittle transition point which located in between of the machined surface of lower and higher elastic recovery. The cutting distance that started to appear the brittle fracture was denoted as the critical cutting distance. The present study firstly defines the ductile to brittle deformation mechanism and the critical cutting distance of titanium alloys in UPM, providing the information of optimal machining condition in precision machining of titanium alloys.
Method
Titanium alloys Ti6Al4V (TC4) which contain 0.25% of iron, 0.2% of oxygen, 6% aluminum, 4% of beta phase stabilizer, 6% alpha phase stabilizer and remaining parts of titanium were used for the experiments. The length and diameter of titanium alloys were 40 mm and 16 mm respectively. Titanium alloys underwent straight line cuttings by the single point diamond tool. Depth of cut in the experiments was adjusted from 2 μm–7 μm with 1 μm interval value; therefore, six straight lines were cut individually on the titanium alloys’ surface with different depth of cut. Feedrate (cutting velocity) was set as 150 mm/min and unchanged throughout the experiments. The radius and height of diamond tool were 1.494 mm and 10.186 mm respectively. The chips were observed under scanning electron microscopy (SEM) machine Hitachi HT3030. The cutting force in three directions was captured by a force sensor Kistler 9256 C. Moore Nanotech 350FG (4 axis Ultra-precision machine) was used for diamond cutting. Surface roughness and the cutting profile of machined surface were measured by Wyko NT8000 Optical Profiling System, which is the optical profiler using non-contact measurement. The experimental setup is shown in Fig. 1. The fixture with the workpiece was hold on to the ultra-precision machine by the vacuum suction. The diamond tool moved in the upward direction and provided the straight line cutting on the workpiece, forming the groove on the machined surface.
Results and Discussion
Chip formation
The chip morphology and segmentation occupy the crucial roles in observing the machinability and the machining mechanism of titanium alloys. The chip formations generated at different depth of cut are shown in Fig. 2 (a–f). Cook27 explained the relationship between the chip morphology and cutting temperature in the cutting process of titanium alloys; when the thermal softening effect in the primary deformation zone was dominant over the strain hardening effect, the chip would appear as a serrated shape. According to Fig. 2(a), for the chip formation generated at depth of cut 2 μm, the length of saw tooth was the largest in comparison to that of generated at other depth of cut, this explained the thermal softening effect was stronger at relatively small depth of cut. The intensive thermal softening effect at the tool/workpiece interface further promoted the ductile deformation at the cutting zone, therefore, the length of saw-tooth decreased with depth of cut increase, and the degree of ductile deformation decreased with the cutting thickness increased.
The chip edge showed the saw-tooth shape at the cutting conditions of depth of cut 2 μm–4 μm, the saw-tooth edge gradually disappeared when depth of cut increased to 5 μm or above. Moreover, according to Fig. 2 (a–c), the void nucleation was observed near the chip edge at depth of cut 2 μm–4 μm; the void nucleation inside the chip suggests the ductile fracture in the cutting process28,29,30, which provided the evidence of the existence of ductile deformation at those depth of cut. For the chip formations generated at higher depth of cut 5 μm–7 μm as shown in Fig. 2 (d–f), the shapes of those chips were entire without any void, which implied that the brittle deformation was dominant over the whole cutting process without involving ductile mode cutting. The above experimental results explained that the cutting thickness governed the ductile and brittle deformation of UPM of titanium alloys.
On the other hand, the periodic saw-tooth was observed in the chip edge at depth of cut 2 μm–4 μm, which the length of saw-tooth in the chip edge was inhomogeneous in one single chip. The parts of chip edge displayed the longer saw-tooth while other parts displayed the shorter saw-tooth. This finding is matched with the report from Sun. S et al.31, which they observed that the periodic chip edge appeared in the cross section of chips in turning of titanium alloys. The periodic chip structures were disappeared when depth of cut increased to 5 μm–7 μm. The generations of inhomogeneous chip edge at depth of cut 2 μm–4 μm indicated that the brittle and ductile deformation occurred simultaneously at one single cut at relatively small depth of cut, similarly, the generations of homogeneous chip edge at depth of cut 5 μm–7 μm implied that the brittle deformation was the only deformation mechanism at relatively large depth of cut. The corresponding areas of brittle and ductile deformations on the chip edge are denoted as letters “B” and “D” respectively in Fig. 2 (a–f).
Cutting profile and surface quality
The cutting profiles of machined groove at depth of cut 2 μm–7 μm are shown in Fig. 3. According to Fig. 3, the cutting profiles of every individual machined groove (2 μm–7 μm) showed various depth along a constant depth of cut, which was caused by the material swelling effect. Actually, the material swelling effect commonly occurs in UPM. The materials that are melted become viscous fluid under continuous cutting and the material fluid localizes at the two sides and the bottom of the tool edge. The metal fluid solidifies and expands when temperature of the machined surface decreases32,33, as a result, the machined surface swells and apparent tool marks are left on the machined surface, introducing the deviation of actual cutting depth from the assigned one. The microscopes of three areas of each machined groove were captured, they are denoted as X, Y and Z as the figures shown. The letters of X, Y and Z with the subscript of depth of cut denoted as the machined areas with “a lower level of material swelling”, “a transition point of lower material swelling to higher material swelling” and “a higher level material swelling” respectively. The depth variation among the individual machined groove was different from that of each other, and it is highly depended on depth of cut. According to Fig. 3, for depth of cut 2 μm–4 μm, the depth of machined groove varied along the machined surface, the depth of machined groove firstly decreased and then reached to the lowest value, the depth increased again in the following cutting distance, demonstrating the different degrees of material swelling at one single cut. For the machined groove generated at depth of cut 5 μm–7 μm, the cutting profiles of them appeared distinctively, the decreasing/increasing rate of depth in the cutting profile was smaller. The above results suggested that the material swelling rate changed when depth of cut was various, and therefore, the cutting mechanism altered when depth of cut changed.
Areas X of all machined grooves displayed differently from areas Y and Z; areas X had the smoother and finer surfaces in comparison to that of the areas Y and X generated in all depth of cut, there was no tear on the surface and surface edge at areas X. For areas Y, there was a clear crack on the groove edge (shown as red circles in Fig. 3), it became the important indicator for the transition point from the lower material swelling area to the higher material swelling area and the start of ductile to brittle transition, the crack was defined as the transition point of ductile to brittle area. The machined surfaces of areas Z displayed coarseness, the left of groove edge at areas Z contained cracks (shown as blue circle in Fig. 3) and they were the footprints of uncut materials which were generated by the brittle deformation under the brittle fracture mode.
Surface roughness of areas X, Y and Z at depth of cut 2 μm–7 μm is shown in Fig. 4. The results are consistent with the cutting profiles shown in Fig. 3, because of the brittle deformation and fracture tearing of chip at areas Z, it could been seen that surface finishing obtained in areas X was superior than that of areas Z, which surface roughness of areas X was always smaller than that of areas Z. Especially for the surface generated at depth of cut 3 μm and 4 μm, the difference of surface roughness between these two areas was remarkably large, this large variation was again counted by the different deformation modes at the area X (ductile) and the area Z (brittle). For areas Y at all depth of cut, surface roughness was the highest among other areas; the underlying reason was the formation of the crack at the ductile to brittle transition point, consequently, the ragged surface caused the worst surface quality.
The cutting distance between areas X and Y is expressed as d, it explained the minimum/critical cutting distance of the brittle fracture deformation and the start of coarsened surface appearance. The graph of d versus depth of cut is shown in Fig. 5. The minimum/critical cutting distance increased with depth of cut increase.
Figure 6 shows the deep material swelling percentage of areas X and Z after the diamond cutting, which was determined by the difference between the assigned and actual cutting depth at the bottom of machined surface. Deep material swelling is caused by the expanded materials after the solidification of melted metal fluid in cutting. According to Fig. 6 the material swelling effect was serious for titanium alloys in UPM, the material swelling percentage was over at least 40% for both areas X and Z no matter the value of depth of cut, it is one of the important machining characteristics of titanium alloys, which is low elastic modulus materials.
Cutting Force analysis
Figure 7 shows the thrust force of machined groove generated at depth of cut 2 μm–7 μm. The thrust force was used to identify the level of deep material swelling at the bottom area of the machined surface9,10,11. The higher value of thrust force means the higher level of deep material swelling on the machined surface and vice via. According to Fig. 7, the thrust force was varied through a single cut, it implied that the material swelling level was varied alone one machine groove and it was consistence to the different values of cutting depth on the individual machined groove as shown in Fig. 3. The variation of thrust force decreased with depth of cut increase. The thrust forces fluctuated largely at depth of cut 2 μm–4 μm, and it became flatter and more stable at depth of cut 5 μm–7 μm. In general, the implications of thrust force patterns in Fig. 7 were matched to the cutting profiles shown in Fig. 3.
As illustrating in Fig. 7, the patterns of increasing/decreasing trend of thrust force at depth of cut 2 μm–4 μm were different from that of depth of cut 5 μm–7 μm. For the thrust forces generated at depth of cut 2 μm–4 μm, the thrust forces firstly decreased and following with an increasing trend, the sharp lowest points were observed at the transition points. On the contrary, for the thrust forces at depth of cut 5 μm–7 μm, the thrust force patterns displayed dissimilarly, they showed relatively flat comparing to that of smaller depth of cut 2 μm–4 μm, which showed a comparable lower increasing/decreasing rate, and the highest sharp transition points were demonstrated in the thrust force signals. Actually, the increase and decrease of thrust forces at constant depth of cut implied that there were two cutting mechanisms at one single cut. The demonstration of relatively flat patterns in the thrust forces at depth of cut 5 μm–7 μm explained only one cutting mechanism throughout the whole cutting processes; with the information of chip formation and cutting profile discussed above, it can be concluded that the whole cutting processes conducted at depth of cut 5 μm–7 μm are described as brittle machining without a ductile material removal process.
Conclusion
In this study, the cutting mechanism of titanium alloys in UPM was firstly revealed through experimental approaches. The experimental results displayed the existence of brittle and ductile deformation mechanism and the ductile to brittle transition behavior. The critical machining parameters for conducting ductile machining of titanium alloys are both the cutting distance and depth of cut. Ductile machining of titanium alloys in UPM occurs when the cutting distance is not over the critical cutting distance. The critical cutting distance increases with depth of cut increase. The ductile to brittle transition behavior mainly happens at smaller depth of cut (in this study, the depth of cut was 2 μm–4 μm), cutting at higher depth of cut would result of the single brittle removal mode. This study provides the important information of implementing ductile machining of titanium alloys in UPM, supporting to improve surface finishing and surface integrity of precise medical components.
Data availability statement
The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.
References
Ezugwu, E. O. & Wang, Z. M. Titanium alloys and their machinability—a review. Journal of materials processing technology. 68.3, 262–274 (1997).
Arrazola, P. J. et al. Machinability of titanium alloys (Ti6Al4V and Ti555. 3). Journal of materials processing technology. 209(5), 2223–2230 (2009).
Pramanik, A. Problems and solutions in machining of titanium alloys. The International Journal of Advanced Manufacturing Technology. 70(5-8), 919–928 (2014).
Nouari, M. & Makich, H. Experimental investigation on the effect of the material microstructure on tool wear when machining hard titanium alloys: Ti–6Al–4V and Ti-555. International Journal of Refractory Metals and Hard Materials. 41, 259–269 (2013).
Khorev, A. I. High-strength titanium alloy VT23 and its applications in advanced welded and brazed structures. Welding International. 24(4), 276–281 (2010).
Wulf, G. L. High strain rate compression of titanium and some titanium alloys. International Journal of Mechanical Sciences. 21(12), 713–718 (1979).
Follansbee, P. S. & Gray, G. T. An analysis of the low temperature, low and high strain-rate deformation of Ti− 6Al− 4V. Metallurgical and Materials Transactions A 20(5), 863–874 (1989).
Sun, F. et al. Investigation of early stage deformation mechanisms in a metastable β titanium alloy showing combined twinning-induced plasticity and transformation-induced plasticity effects. Acta Materialia. 61(17), 6406–6417 (2013).
Kong, M. C., Lee, W. B., Cheung, C. F. & To, S. A study of materials swelling and recovery in single-point diamond turning of ductile materials. Journal of materials processing technology. 180(1), 210–215 (2006).
Lee, W. B., Cheung, C. F. & To, S. Characteristics of microcutting force variation in ultraprecision diamond turning. Materials and Manufacturing Processes. 16(2), 177–193 (2001).
Cheung, C. F. & Lee, W. B. Characterisation of nanosurface generation in single-point diamond turning. International Journal of Machine Tools and Manufacture. 41(6), 851–875 (2001).
Yu, H. Y. Variation of elastic modulus during plastic deformation and its influence on springback. Materials & Design. 30(3), 846–850 (2009).
Cleveland, R. M. & Ghosh, A. K. Inelastic effects on springback in metals. International Journal of Plasticity. 18(5), 769–785 (2002).
Luo, L. & Ghosh, A. K. Elastic and inelastic recovery after plastic deformation of DQSK steel sheet. Transactions-American Society of Mechanical Engineers Journal of Engineering Materials and Technology. 125(3), 237–246 (2003).
Setti, D., Sinha, M. K., Ghosh, S. & Rao, P. V. Performance evaluation of Ti–6Al–4V grinding using chip formation and coefficient of friction under the influence of nanofluids. International Journal of Machine Tools and Manufacture 88, 237–248 (2015).
Pervaiz, S., Rashid, A., Deiab, I. & Nicolescu, M. Influence of tool materials on machinability of titanium-and nickel-based alloys: a review. Materials and Manufacturing Processes. 29(3), 219–252 (2014).
Davim, J. P. & Figueira, L. Machinability evaluation in hard turning of cold work tool steel (D2) with ceramic tools using statistical techniques. Materials & design. 28(4), 1186–1191 (2007).
Bayoumi, A. E. & Xie, J. Q. Some metallurgical aspects of chip formation in cutting Ti-6wt.% Al-4wt.% V alloy. Materials Science and Engineering: A. 190(1–2), 173–180 (1995).
Wang, Z. G., Rahman, M. & Wong, Y. S. Tool wear characteristics of binderless CBN tools used in high-speed milling of titanium alloys. Wear. 258(5), 752–758 (2005).
Komanduri, R. & Von Turkovich, B. F. New observations on the mechanism of chip formation when machining titanium alloys. Wear 69(2), 179–188 (1981).
Zhang, X., Arif, M., Liu, K., Kumar, A. S. & Rahman, M. A model to predict the critical undeformed chip thickness in vibration-assisted machining of brittle materials. International Journal of Machine Tools and Manufacture 69, 57–66 (2013).
Foy, K., Wei, Z., Matsumura, T. & Huang, Y. Effect of tilt angle on cutting regime transition in glass micromilling. International Journal of Machine Tools and Manufacture. 49(3), 315–324 (2009).
Gao, W., Hocken, R. J., Patten, J. A. & Lovingood, J. Experiments using a nano-machining instrument for nano-cutting brittle materials. CIRP Annals-Manufacturing Technology. 49(1), 439–442 (2000).
Wang, J., Fang, F. & Zhang, X. An experimental study of cutting performance on monocrystalline germanium after ion implantation. Precision Engineering. 39, 220–223 (2015).
Bifano, T. G., Dow, T. A. & Scattergood, R. O. Ductile-regime grinding: a new technology for machining brittle materials. Journal of engineering for industry. 113(2), 184–189 (1991).
Blackley, W. S. & Scattergood, R. O. Ductile-regime machining model for diamond turning of brittle materials. Precision engineering. 13(2), 95–103 (1991).
Cook, N. H. Chip formation in machining titanium. In Proceedings of the Symposium on Machine Grind. Titanium, Watertown Arsenal MA 1–7 (1953, March).
Bradley, D. & Yilong, B. Ductile fracture and ductility—with applications to metalworking. Academic, London Google Scholar (1987).
Rogers, H. C. The effect of material variables on ductility (1968).
Hua, J. & Shivpuri, R. Prediction of chip morphology and segmentation during the machining of titanium alloys. Journal of Materials Processing Technology. 150(1), 124–133 (2004).
Sun, S., Brandt, M. & Dargusch, M. S. Characteristics of cutting forces and chip formation in machining of titanium alloys. International Journal of Machine Tools and Manufacture. 49.7, 561–568 (2009).
To, S., Cheung, C. F. & Lee, W. B. Influence of material swelling on surface roughness in diamond turning of single crystals. Materials science and technology. 17(1), 102–108 (2001).
Yip, W. S. & To, S. Reduction of material swelling and recovery of titanium alloys in diamond cutting by magnetic field assistance. Journal of Alloys and Compounds. 722, 525–531 (2017).
Acknowledgements
The works described in this paper are supported by the Research Committee of The Hong Kong Polytechnic University (Project Code: RTTL) and the National Natural Science Foundation of China (51675455).
Author information
Authors and Affiliations
Contributions
W.S. Yip and S. To. conceived and conducted the experiments, analyzed the results. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yip, W.S., To, S. Ductile and brittle transition behavior of titanium alloys in ultra-precision machining. Sci Rep 8, 3934 (2018). https://doi.org/10.1038/s41598-018-22329-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-22329-2
This article is cited by
-
Precipitation effect on Surface roughness at Ti-6Al-4 V ELI alloy during Ultra-Precision Machining
International Journal on Interactive Design and Manufacturing (IJIDeM) (2023)
-
The potentiality of sinking EDM for micro-impressions on Ti-6Al-4V: keeping the geometrical errors (axial and radial) and other machining measures (tool erosion and work roughness) at minimum
Scientific Reports (2019)
-
Control of the ductile and brittle behavior of titanium alloys in diamond cutting by applying a magnetic field
Scientific Reports (2019)
-
Effect of ultrasonic vibration on ultra-precision diamond turning of Ti6Al4V
The International Journal of Advanced Manufacturing Technology (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.