Abstract
An ultrasensitive methanol gas sensing device based on the quasi-molecular imprinting technology (quasi-MIT) is studied in this work. We applied the sol-gel method (ALS denotes Ag-LaFeO3 prepared by the sol-gel method) and combustion synthesis (ALC denotes Ag-LaFeO3 prepared by combustion synthesis) to prepare Ag-LaFeO3 based sensors. The morphologies and structures of the Ag-LaFeO3 materials were examined via various detection techniques. The ALSM and ALCM sensor (ALSM and ALCM denotes the devices prepared by coating the ALS and ALC materials with methanol, respectively) fabricated using the sol-gel method and combustion synthesis combined with quasi-MIT exhibit good gas sensing properties to methanol, in contrast with the two devices (ALSW and ALCW denote the devices prepared for coating the ALS and ALC materials with water, respectively) without the use of quasi-MIT. The results show that quasi-MIT introduced the target gas in the fabrication process of the device, playing an important role in the design of the ultrasensitive methanol gas sensor. The sensing response and the optimum working temperature of ALSM and ALCM gas sensor are 52.29 and 155 °C and 34.89 and 155 °C, respectively, for 5 ppm methanol, and the highest response to other gases is 8. The ALSM and ALCM gas sensors reveal good selectivity and response for methanol.
Similar content being viewed by others
Introduction
Methanol is widely used in many fields such as pigments, pharmaceuticals and chemical products. However, it is toxic and causes human nerve poisoning and cardiovascular diseases1. Therefore, the preparation of a high response and high selectivity methanol gas sensor has become an urgent problem. Currently, several methods are used to for the gas sensing and detection of methanol such as chromatography2, the spectrophotometric method3, the electrochemical method4, catalytic luminescence5 and the gas sensor method6. The first four methods require expensive instruments, leading to their high cost and large required volume and making it difficult to apply them widely. Because of its high sensitivity, simple operation, low cost and small device, gas sensing is an effective method for detecting methanol gas. However, current methanol gas sensors cannot be applied in practical use due to low response and poor selectivity7,8,9.
Metal oxide semiconductors have been used in many fields such as photocatalysis10,11, solar cells12 and as gas-sensitive materials13. Among all kinds of gas-sensitive materials, p-type semiconductor LaFeO3 is a potential gas-sensitive material due to its high gas sensing properties14 and thermostability15. However, the response and selectivity of pure LaFeO3 is poor. In our previous work16, it was shown that the gas sensing properties of LaFeO3 can be improved by doping Ag, but for practical use, the response, selectivity and operating temperature need to be improved further.
Therefore, we introduce the quasi molecular imprinting technique (quasi-MIT), which introduces the target gas into the process of material synthesis or device preparation to obtain a porous structure that is for the adsorption and desorption of methanol gas17. Additionally, quasi-MIT has the same effect as MIT but is much simpler because it does not require the identification and use of the functional monomer. Hence, we designed the Ag-LaFeO3 for ultrasensitive methanol gas sensors based on the quasi-MIT. The mesoporous materials are obtained by the sol-gel method (ALS) and combustion synthesis (ALC). The sensors were fabricated respectively using mixed pure water (ALSW) as well as methanol (ALSM) with the prepared ALS powders during the sensor fabrication process. The meaning of each abbreviation of this report is shown in Table 1. Similarly, ALCW and ALCM sensors were prepared via mixed ALC respectively with the pure deionized water and methanol. The gas-sensitive characteristics and related mechanisms of methanol gas detection by the ALSW, ALSM, ALCW and ALCM were carefully investigated. It was found that ALSM and ALCM exhibited ultrahigh sensitivity.
After the pre-synthesized Ag-LaFeO3 precursor was obtained, ALS and ALC were sintered in 800 °C to 2 h in the air, with the XRD results showing the crystalline nature of the sample. All peaks are completely identical with the orthorhombic structure of LaFeO3 as shown in Fig. 1. This diffraction pattern perfectly matches the standard JCPDS card no. 37–149318. No precursor residue was detected, indicating that the samples are highly pure. The amount of Ag is so small (mol (Ag): mol (Ag-LaFeO3 precursor) = 1%) that it cannot be detected by XRD and FTIR. The lattice parameters obtained from the refinement of the PXRD data are presented in Table 2. It is noteworthy that even though the substitution of Ag does not change the orthorhombic symmetry of the material, it results in a pseudo-tetragonal unit cell with the cell parameter ‘a’ almost equal to ‘c’. It can also be seen from the data presented in Table 2 that the lattice parameters of ALS and ALC show a slight change compared to other reports in the literature19,20,21,22,23,24,25,26.
To check the purity of the samples and the interaction between the functional groups, we analyzed the Ag-LaFeO3 cross-linker, ALS and methacrylic acid (MAA) by FT-IR spectroscopy in the 500–4000 cm−1 range as shown in Fig. 2. The FT-IR spectrum of the synthesized Ag-LaFeO3 cross-linker (curve (a)) exhibits a peak at ~3442 cm−1 corresponding to the stretching vibration of -OH of H2O27. The strong peaks at ~565 cm−1 and ~1632 cm−1 are the flexural vibration of Fe-O and La-O. Curve (c) shows the curve of MAA, and the peak around ~1210 cm−1 and the peak at ~1709 cm−1 are the vibration of C-O and carbonyl in carboxylic acid, respectively. Curve (b) shows the curve of ALS, where the disappearance of the peaks at ~1210 cm−1 and ~1709 cm−1 compared to the MAA curve suggested an interaction between Ag-LaFeO3 and MAA. The mutual effect is attributed to the coordination between the groups in MAA and lanthanum in the Ag-LaFeO3 cross-linker, and it is proven that the metal carbonyl complex is formed28.
The pattern and microspore structure of the ALC and ALS were detected via SEM and are shown in Fig. 3. Fig. 3(a,b) shows the appearance of the ALC as a tile, and Fig. 3(f,g) (at low magnification) exhibits stone-like morphologies of the ALS. Fig. 3(c,h) shows featured outer-sides of the ALC and ALS. The ALC shows bulk with porous features composed of many interconnected smaller sized particles, and the thickness of this sample is 0.8 μm. The outside of ALS is solid with the thicknesses of 2.1 μm. The enlarged image of the selected areas of the ALC and ALS samples (Fig. 3(d,i)) shows a porous structure with a micron-scale size. The number of the pores on the surface of ALS is greater than that on the ALC surface. High-powered SEM images in Fig. 3(e,j) are also clearly displayed. Porous morphologies of the samples would make the target gases diffuse in or escape from the inner parts of the sensing films faster than for their solid counterparts and consequently will improve the responses to the target gases.
TEM provides insight into the morphology of the ALC and ALS as shown in Fig. 4. The images clearly show that the ALS (Fig. 4(a)) exhibit irregular bulk shape, which is consistent with the results of SEM. As shown in the image, the ALS consisted of many particles with the diameters as high as tens of nanometers. Fig. 4(d) shows the bulk structural characteristics of the ALC. Based on the image shown in Fig. 4(e), ALC is found to be comprised of a large number of interstitial Ag-LaFeO3 particles. There are many pores on the surface of the bulk with the pore size of approximately 50 nm, which is in accordance with the results observed in the high-magnification SEM image (Fig. 3(j), 400000x). High-magnification TEM images of the ALC and ALS are shown in Fig. 4(b,f) and the clearly observed the lattice stripes indicate good crystallinity. To obtain a clearer image of the lattice fringes, Fig. 4(c,g) shows a more distinct image of the selected areas. The fringe spacing of ALS and ALC are 0.35 nm and 0.32 nm, respectively.
The specific surface areas of the ALC and ALS mesoporous materials are determined by the N2 adsorption desorption isotherm curve and the distribution curves of the pore size are shown in Fig. 5. According to the International Union of Pure and Applied Chemistry, the H3 hysteresis loop indicates the pores are slit-like and formed by particle aggregation29. The ALS and ALC show obvious hysteresis loops at the P/P0 ranges of 0.6–1. Thus, the existence of pores is proven.
The BJH method (Fig. 5(a,b), inset) shows that ALS and ALC have porous structures. The size of the hole ranges from 2 nm to 90 nm, and the main peak is positioned at 45–47 nm. The SBET values of the ALS and ALC were 5.66 m2 g−1 and 4.72 m2 g−1, respectively. The BET analysis indicated that ALS has a larger surface area, which means that ALS can provide sufficient surface for the gas reaction.
The factors important for the gas-sensing mechanism include the surface control procedure, particle size, surface condition and adsorption and desorption of oxygen30. The characteristics of the gas sensor are affected by the surface states of the ALS and ALC. The XPS spectra of ALC and ALS were obtained in order to analyze the valence states of each element. Fig. 6(a,e) shows the XPS results for the ALS and ALC, with the standard peak of C1s at 284.8 eV. The spectra confirm the presence of Ag (3d, 4p), La (3d, 4p, 4d), Fe (2p), and O (1 s), indicating the high purity of the product. The XPS La 3d and Fe 2p energy levels display that the lanthanum ions and iron ions exist in the +3 state31. For the La 3d core level peaks (Fig. 6(b,f)), two peaks of lanthanum are seen from the peak; one is 3d5/2 of La3+ at 833.6 eV, and the other one is 3d3/2 of La3+ ions at 850.5 eV, which is due to the spin-orbit splitting of lanthanum oxide. Fig. 6(c,g) shows the XPS patterns of Fe 2p in ALS and ALC, and the two peaks of Fe 2p3/2 and Fe 2p1/2 were surveyed at 709.7 and 723.6 eV, respectively, which is due to the Fe3+ in the oxides32. The O 1 s XPS patterns (Fig. 6(d,h)) are wide as well as asymmetrical. At least two O chemical states are observed; one is OL at 528.2 eV, and the other one is OH at 530.5 eV, where OL is attributed to lattice oxygen, and OH is ascribed to the chemically adsorbed O− or OH−. Therefore, the O 1 s XPS patterns fit two chemical conditions by Gauss’ rule33. The 528.2 eV peak of the OL XPS spectrum is ascribed to the role of La-O and Fe-O of LaFeO3. The 530.5 eV peak of the OH XPS is attributed to the OH− resulting mainly from the chemically adsorbed water; this is due to lanthanum oxide, which can easily absorb moisture in the air. This metal-support interaction is a major element in the analysis of the mechanism of gas sensor. Figure 7(a,b) shows the XPS full spectra of Ag-LaFeO3 and LaFeO3, respectively. It can be seen from Fig. 7(c,d) that after the introduction of Ag, the binding energy corresponding to Fe and La shifted to a small direction. This shows that the doping of Ag is successful, but the amount of doping is too small to be detected. Therefore, the high magnification of Ag 3d is not available.
In order to evaluate the response of the gas sensor to methanol, the response of the prepared materials to 5 ppm methanol was detected at the operating temperatures in the 5–250 °C range. The gas response value reaches the maximum at the operating temperatures of 155 °C, 175 °C, 155 °C and 155 °C for ALSW, ALSM, ALCW and ALCM, respectively; as the operating temperature increases, the response decreases, as shown in Fig. 7(a–d). Therefore, 175 °C, 155 °C, 155 °C and 155 °C were used as the best operational temperatures of the ALSW, ALSM, ALCW and ALCM sensors, respectively.
Then, the response and selectivity of the four sensors were analyzed based on the data in Fig. 8. The responses of ALSM (52.29, Fig. 8(a)) and ALCM (34.89, Fig. 8(d)) are obviously superior to those of ALSW (23.6, Fig. 8(b)) and ALCW (23.2, Fig. 8(c)) for 5 ppm methanol at the best working temperature, compared to the reported values, and a good response is observed, as shown in Table 3 34,35,36,37,38,39,40,41. All four sensors exhibit good selectivity to methanol. ALSM exhibits the best gas sensing properties among all devices (Fig. 8(e)) because the methanol molecules were introduced into the process of equipment preparation, which result in more methanol gas scattered on the surface of ALSM when ALSM was alternately placed in methanol gas and air. This will improve the gas response to methanol.
Fig. 9 shows the relationships between the response and methanol concentration for the ALSM, ALSW, ALCW and ALCM in the methanol concentration range from 1 to 5.5 ppm. It can be seen in Fig. 9(a1–d1) that the responses increased linearly with the methanol concentration increasing from 1 to 5.5 ppm. The sensors can be used for real-time detection of methanol at the optimal working temperature. It can be found in Fig. 9(a2–d2) that the response of the sensor device exhibits a step-like distribution under different methanol concentrations. The response value dramatically increased with the increase in the methanol concentration. Furthermore, the response and recovery time are 32 s and 37 s, 34 s and 36 s, 37 s and 49 s, 36 s and 42 s.
For sensors based on metal oxides, several factors affect the gas sensing properties, such as surface area, porous structure and particle size. This further influences the spread and adsorption of the gases42. Methanol can interact with Ag-LaFeO3 in the preparation of the materials, which will further optimize the structure of ALSM. The structure of the materials was further optimized by introducing methanol into the device fabrication. This mechanism of the sensors ALSM and ALCM is defined as the excimer imprinting technique. Then, the mechanism of MIT was analyzed in detail43,44,45. ALSM and ALCM show better responses than ALSW and ALCW. This means that the preparation method of the device plays an important role in improving the response of the gas sensor. The gas sensing properties of the device are improved by the large surface area and multiple recognition sites of the gas sensing material46,47.
The working principle of the sensor is based on the change of the conductivity caused by the reaction between the gas molecule and the surface of the material. The porous structure of the material promotes the reaction of the gas and further improves the gas sensing property of the material. During the test process, the sensor was exposed to air at first, and oxygen adsorbed on the surface of LaFeO3 combined with the free electrons trapped on the LaFeO3 surface to form O2−, O−, O2− and other oxygen ions48. The reactions are as follows:
This process will form a thin space charge layer, and relatively low barriers are formed to lower the resistance49. When the material is in the presence of methanol (CH3OH), the reducing gases react with the adsorbed oxygen forming CO2 and H2O and releasing the electrons50. The space charge layer on the SLFO surface becomes thick, and the sensor resistance increases (Fig. 10). The reaction process is as follows:
In summary, in this work, we applied quasi-MIT to design a methanol gas sensor. The experimental result indicates that the response and operating temperature of ALSM, ALSW, ALCW and ALCM are 52.29 and 155 °C, 23.60 and 175 °C, 23.20 and 155 °C, and 34.89 and 155 °C, respectively. The response and recovery time respectively are 32 s and 37 s, 34 s and 36 s, 37 s and 49 s, 36 s and 42 s. The maximum response to the other test gases is 8. The ALSM and ALCM sensors exhibit the most excellent responses. The design of a high-sensitivity methanol gas sensor based on quasi-MIT mechanism is reasonable. Furthermore, the pore number and specific surface area of ALSM are larger than those of ALCM, which accelerates the target gases to diffuse in or escape from the inner regions; therefore, ALSM displays a better gas response than ALCM. Our method is proven to be innovative for the design of a high-sensitivity methanol gas sensing device. This work provides important guidance for the design of high-response gas sensors.
Methods
Preparation of ALS
The chemical reagents used in the experiment were analytical reagents that were used without further treatment. The solvent is highly pure water (18 MΩ cm at 25 °C). In the prototype process, citric acid, lanthanum nitrate, iron nitrate, silver nitrate, PEG and deionized water were mixed under stirring at 90 °C for 10 hours as solution A. Then, solution A was placed in the microwave synthesizing device (CEM) for 4 hours at 75 °C. Methanol mixed with MAA was treated for 30 min by magnetic stirring and was let to stand to form solution B. Then, azobisisobutyronitrile (AIBN) was mixed with methanol, solution B and solution A. The final solution was treated by magnetic stirring at 50 °C for 12 h with a water bath and was then dried. Finally, the white powder of ALS was obtained after annealing at 800 °C for 2 h in an oven.
Preparation of ALC
The ALC powder was synthesized via the combustion synthesis; here, citric acid, lanthanum nitrate, iron nitrate, silver nitrate, PEG and deionized water were mixed under stirring at 90 °C for 10 hours as solution D. The final mixture was treated for 30 min by magnetic stirring, and the prepared samples were oven-dried at 85 °C. The xerogel was heated at 300 °C for 30 min, and then sintering at 800 °C was carried out to obtain ALC.
Device fabrication
The mesoporous material was fabricated via the sol-gel method (ALS) as well as combustion synthesis (ALC). The as-synthesized samples (ALS, ALC) were mixed with deionized water (ALSW and ALCW) and methanol (ALSM and ALCM) and ground to a mushy solution. For the detailed description of the fabrication method of the sensors, see ref.51.
Characterization
X-ray diffraction (XRD) spectra were obtained using a Japan AXS D/MAX-3BX advanced device handled at 25 mA and 35 kV with Cu Kα scattered at 1.5406 Å wavelengths. The detailed morphology features and crystallization conditions of the material were surveyed via field emission scanning electron microscopy (FESEM, S-3400N) as well as transmission electron microscopy (JEM-2100, Hitachi, Japan). The functional group was identified by Fourier transform infrared spectroscopy (FT-IR, FTS-40). The BET surface area (SBET) of the material was measured using a Quadrasorb-evo instrument.
References
Patel, N. G., Patel, P. D. & Vaishnav, V. S. Indium tin oxide (ITO) thin film gas sensor for detection of methanol at room temperature. Sens. Actuators, B 96, 180–189 (2003).
Hu, H. C. & Chai, X. S. Determination of methanol in pulp washing filtrates by desiccated full evaporation headspace gas chromatography. J. Chromatogr. A 1222, 1–4 (2012).
Wrobel, K. D., Rodríguez, M. & Aguilar, F. J. A. Determination of methanol ino, o-dimethyldithiophosphoric acid (DMDTPA) of technical grade by UV/vis spectrophotometry and by HPLC. Talanta. 66, 125–129 (2005).
Lin, J. W. & Shaw, S. Y. The potential of CO2 laser photoacoustic spectrometry for detection of methanol in alcoholic beverage. Sens. Actuators, B 94, 535–544 (2009).
Fernandes, H. L. et al. Simultaneous determination of methanol and ethanol in gasoline using NIR spectroscopy: effect of gasoline composition. Talanta. 75, 804–810 (2008).
Nogami, M., Maeda, T. & Uma, T. A methanol gas sensor based on inorganic glass thin films. Sens. Actuators, B 137, 603–607 (2009).
Li, C. C. et al. Enhanced gas sensing properties of ZnO/SnO2 hierarchical architectures by glucose-induced attachment. CrystEngComm 13, 1557–1563 (2011).
Dai, M. J. et al. Hierarchical assembly of α-Fe2O3 nanorods on multiwall carbon nanotubes as a high performance sensing material for gas sensors. ACS Appl. Mater. Interfaces. 9, 8919–8928 (2017).
Jaisutti, R. et al. Ultrasensitive room temperature operable gas sensors using p-type Na: ZnO nano-flowers for diabetes detection. ACS Appl. Mater. Interfaces. 9, 8796–8804 (2017).
Ahmed, J. & Mao, Y. B. Synthesis, characterization and electro-catalytic properties of delafossite CuGaO2. J. Solid. State. Chem. 242, 77–85 (2016).
AlShehri, S. M. et al. Synthesis, characterization, and enhanced photocatalytic properties of NiWO4 nanobricks. New J. Chem. 41, 8178–8186 (2017).
Ahmed, J. et al. Scalable synthesis of delafossite CuAlO2 nanoparticles for p-type dye-sensitized solar cells applications. J. Alloy. Compd 591, 275–279 (2014).
Steffes, H. et al. Fabrication parameters and NO2 sensitivity of reactively RF-sputtered In2O3 thin films. Sens. Actuators, B 68, 249–253 (2000).
Chen, J. et al. α-Fe2O3 Nanotubes in gas sensor and lithium-ion battery applications. Adv. Mater. 17, 582–586 (2005).
Zhu, Q. et al. A new and high response gas sensor for methanol using molecularly imprinted technique. Sens. Actuators, B 207, 398–403 (2015).
Zhang, Y. et al. A highly sensitive and selective formaldehyde gas sensor using a molecular imprinting technique based on Ag-LaFeO3. J. Mater. Chem. C 2, 10067–10072 (2014).
S. Palimar, S. et al. Investigation of Ca substitution on the gas sensing potential of LaFeO3 nanoparticles towards low concentration SO2 gas. Dalton Trans. 45, 13547–13555 (2016).
Aleksandar, N. et al. Heterogeneous photo-fenton degradation of organics using highly efficient Cu-doped LaFeO3 under visible light. J. Ind. Eng. Chem. 61, 53–64 (2018).
Mitra, A. et al. Improved magneto-electric properties of LaFeO3 in La0.8Gd0.2Fe0.97Nb0.03O3. Ceram. Int. 44, 4442–4449 (2018).
Manzoor, S. & Husain, S. Influence of Zn doping on structural, optical and dielectric properties of LaFeO3. Mater. Res. Express 5, 055009 (2018).
Mahapatra, A. S. et al. Modulation of magnetic and dielectric property of LaFeO3 by simultaneous doping with Ca2+ and Co2+-ions. J. Alloy. Compd. 743, 274–282 (2018).
Schön, A. et al. Non stoichiometric La1−yFeO3 perovskite-based catalysts as alternative to commercial three-way-catalysts? – Impact of Cu and Rh doping. Appl. Catal. B-Environ 223, 167–176 (2018).
Salah, L. M. et al. Structural, magnetic, and electrical properties of Gd-substituted LaFeO3 prepared by co-precipitation method. J. Aust. Ceram. Soc. 54, 357–368 (2018).
She, S. et al. Systematic study of oxygen evolution activity and stability on La1−xSrxFeO3−δ perovskite electro catalysts in alkaline media. ACS Appl. Mater. Interfaces 10, 11715–11721 (2018).
Tan, W. H. et al. Design of SnO2-based highly sensitive ethanol gas sensor based on quasi molecular-cluster imprinting mechanism. Sens. Actuators, B 212, 47–54 (2015).
Song, P. et al. Synthesis and gas sensing properties of biomorphic LaFeO3 hollow fibers templated from cotton. Sens. Actuators, B 147, 248–254 (2010).
Daniela, O. R., Nicolas, B. D. & Marcos, F. A. Spectroscopic studies of lanthanide complexes of varying nuclearity based on a compartmentalised ligand. Dalton. t. 44, 17175–17188 (2015).
Pablos, J. L. et al. Selective detection and discrimination of nitro explosive vapors using an array of three luminescent sensory solid organic and hybrid polymer membranes. Sens. Actuators, B 212, 18–27 (2015).
Lin, X. et al. Using but anal fermentation waste water for biobutanol production after removal of inhibitory compounds by micro/mesoporous hyper-cross-linked polymeric adsorbent. Acs. Sustain. Chem. Eng. 3, 702–709 (2015).
Korotcenkov, G. et al. The role of doping effect on the response of SnO2-based thin film gas sensors: analysis based on the results obtained for Co-doped SnO2 films deposited by spray pyrolysis. Sens. Actuators, B 182, 112–124 (2013).
Zhang, R. et al. Effect of hard-template residues of the nanocasted mesoporous LaFeO3 with extremely high surface areas on catalytic behaviors for methyl chloride oxidation. J. Mater. Chem. A 2, 17329–17340 (2014).
Rida, K. et al. Effect of strontium and cerium doping on the structural characteristics and catalytic activity for C3H6 combustion of perovskite LaCrO3 prepared by sol-gel. Appl. Catal. B. Environ. 84, 457–467 (2008).
Masys, Š. et al. Electronic structure of LaNiO3−x thin films studied by x-ray photoelectron spectroscopy and density functional theory. Phys. Rev. b. 82, 3603–3612 (2010).
Deng, S. J. et al. A highly sensitive VOC gas sensor using p-type mesoporous Co3O4 nanosheets prepared by a facile chemical coprecipitation method. Sens. Actuators, B 233, 615–623 (2016).
Li, Y. X. et al. A high performance methanol gas sensor based on palladium -platinum-In2O3 composited nano-crystalline SnO2. Sens. Actuators, B 237, 133–141 (2016).
Wei, N. et al. Hierarchical assembly of In2O3 nanoparticles on ZnO hollow nanotubes using carbon fibers as templates: Enhanced photocatalytic and gas sensing properties. J. Colloid. Interf. Sci. 498, 263–270 (2017).
Lu, Y. et al. Hierarchical heterostructure of porous NiO nanosheets on flower like ZnO assembled by hexagonal nanorods for high-performance gas sensor. Ceram. Int. 43, 7508–7515 (2017).
Zhang, S. et al. In2O3 nanosheets array directly grown on Al2O3 ceramic tube and their gas sensing performance. Ceram. Int. 43, 7942–7947 (2017).
Zolghadr, S., Khojier, K. & Kimiagar, S. Study of sensitivity and selectivity of α-Fe2O3 thin films for different toxic gases and alcohols. Mater. Sci. Semicon. Proc. 54, 6–13 (2016).
Liu, L. P. et al. Room temperature impedance spectroscopy-based sensing of formaldehyde with porous TiO2 under UV illumination. Sens. Actuators, B 185, 1–9 (2013).
Zhu, L. H. et al. Gas sensors based on metal sulfide Zn1−xCdxS nanowires with excellent performance. ACS Appl. Mater. Interfaces. 7, 20793–20800 (2015).
Wagner, T. et al. Mesoporous materials as gas sensors. Chem. Soc. Rev. 42, 4036–4053 (2013).
Li, D. et al. Molecular imprinting sensor based on quantum weak measurement. Biosens. Bioelectron. 94, 328–334 (2017).
Lakshmi, D. et al. Electrochemical sensor for catechol and dopamine based on a catalytic molecularly imprinted polymer conducting polymer hybrid recognition element. Anal. Chem. 81, 3576–3584 (2009).
Panasyuk, T. L., Mirsky, V. M. & Wolfbeis, O. S. Electropolymerized molecularly imprinted polymers as receptor layers in capacitive chemical sensors. Anal. Chem. 71, 4609–4613 (1999).
Hyodo, T. et al. Gas sensing properties of ordered mesoporous SnO2 and effects of coating thereof. Sens. Actuators, B 93, 590–600 (2003).
Waitz, T. et al. Ordered mesoporous In2O3: synthesis by structure replication and application as a methane gas sensor. Adv. Funct. Mater. 19, 653–661 (2009).
Chen, H. et al. One-pot synthesis and improved sensing properties of hierarchical flowerlike SnO2 assembled from sheet and ultra-thin rod subunits. Sens. Actuators, B 194, 447–453 (2014).
Benali, A. et al. Structural, electrical and ethanol sensing properties of double-doping LaFeO3 perovskite oxides. Ceram. Int. 40, 14367–14373 (2014).
Liang, Y. Q. et al. Design of a highly sensitive ethanol sensor using a nano-coaxial p-Co3O4/n-TiO2 hetero junction synthesized at low temperature. Nanoscale 5, 10916–10926 (2013).
Zhang, Y. M. et al. Ag-LaFeO3 fibers, spheres, and cages for ultrasensitive detection of formaldehyde at low operating temperatures. Phys. Chem. Chem. Phys. 19, 6973–6980 (2017).
Acknowledgements
This work was supported by National Natural Science Foundation of China (No. 51562038 and 51402257).
Author information
Authors and Affiliations
Contributions
Q. Rong contributed to the preparation of the manuscript and Fig. 1–9. Q.J. Liu, Y.M. Zhang and Q. Rong initiated the research and planned and coordinated all of the experimental work. Q.J. Liu, J. Zhang and Z.Q. Zhu were involved in all discussions regarding the interpretation of the data. J.C. Hu and K.J. Li were involved in the preparation of ALSM and ALSW. H.P. Wang and M.P. Chen were involved in the preparation of ALCW, ALCM and the fabrication of the sensor. Q. Rong and T.P. Lv performed the measurements and analyzed the sensing properties. J. Zhang and Z.Q. Zhu characterized the materials.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Rong, Q., Zhang, Y., Hu, J. et al. Design of ultrasensitive Ag-LaFeO3 methanol gas sensor based on quasi molecular imprinting technology. Sci Rep 8, 14220 (2018). https://doi.org/10.1038/s41598-018-32113-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-32113-x
Keywords
This article is cited by
-
CuO/ZnO Heterojunction Nanograins: Methanol Vapour Detection
Journal of Electronic Materials (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.