Abstract
The Z-scan technique uses a single beam that can be used for observing the nonlinear or optical limiting properties of materials. For the first time, the Z-scan properties dependent on the polarization of 2D carbon nanomaterial suspension were experimentally investigated using optical Z-scan technology. The Z-scan curves of graphene and graphene oxide (GO) in N-methyl-2-pyrrolidinone suspensions exhibited strong polarization-dependent characteristics. In paper, a reverse saturated absorption (RSA) dip surrounded the lens focus when the horizontal polarized beam was focused in the suspension, and two saturated absorption (SA) peaks appeared adjacent to the dip. However, for the vertical polarized beam, only one RSA dip surrounded the lens focus, and the threshold was higher than the SA for a horizontally polarized beam. The transmission of RSA for the GO suspension was evidently lower than that of the graphene suspension. The polarization-dependent characteristic can be ascribed to the laser-induced alignment in case the suspension is moved in or out of the beam focal point. Furthermore, the polarization-dependent 2D carbon nanomaterial suspension can be applied in several practical purposes such as 2D material-based optical and opto-fludic devices.
Similar content being viewed by others
Introduction
The Z-scan technique is used to measure optical nonlinearities of materials, including nonlinear absorption and refraction properties1,2. Carbon nanomaterials have garnered considerable interest owing to their unique properties and fascinating structure for utilizing the nonlinear properties of carbonaceous matter at the nanoscale, using an open-aperture3,4,5,6,7 or closed-aperture Z-scan technique8,9, especially graphene and its derivatives6,10,11,12. Optical limiting is an important property of materials and can be typically obtained using the open-aperture Z-scan technique, which can control the light intensity in a predetermined and predictable manner in addition to prevent laser damage. Several researchers have studied the optical limiting phenomenon13,14,15,16. Recently, the Z-scan properties of nanomaterial suspensions have attracted scholarly interest13,14,17,18,19,20,21,22. In particular, a liquid environment can provide nanostructures with more degrees of freedom in both rotational and translational motions as well as enable us to study the collective properties of macroscopically ordered assembly of nanomaterials—a condition that remains unrealized in their solid state23,24. Moreover, 1D or 2D nanomaterials are intrinsically anisotropic in shape, electronic, and optical properties. Therefore, their liquid suspensions can exhibit isotropic or anisotropic properties macroscopically depending on the microscopic alignment of suspended nanostructures11,23,25,26,27. An important consequence of this dynamic alignment involves the modulation of the incident laser: the aligned nanostructures will increase or decrease the optical transmission depending on the laser polarization. However, the dependence of the Z-scan properties depend on polarization is still unclarified through research, because it should not matter for either saturated absorption (SA) or reverse saturated absorption (RSA), especially for graphene and graphene oxide (GO) suspensions. Graphene has been reported to exhibit polarization-dependent optical absorption in the visible spectral range28,29, ultrafast carrier dynamics30, and double-resonant Raman31,32,33. Furthermore, black phosphorus exhibits anomalous polarization dependence of Raman scattering and crystallographic orientation34.
With pioneering novelty, this study reports the influence of polarization on the Z-scan properties of a 2D carbon nanomaterial suspension under Z-scan technology. In particular, the graphene and GO in the N-methyl-2-pyrrolidinone (NMP) and deionized (DI) water suspensions displayed polarization dependence, and the Z-scan results slightly varied for the graphene and GO suspensions.
Methods
Few-layer graphene flakes with a lateral dimension of a few micrometers are synthesized via intercalation and exfoliation of natural graphite. Single-layer graphene oxide (GO) flakes with sizes in the range of 2 ~ 10 μm are prepared by a modified Hummers’ method35. As-obtained graphene and graphene flakes are dispersed in DI water or N-methyl-2-pyrrolidone (NMP) by sonication and form stable suspensions with a concentration of 0.005–0.01% in weight percentage (wt%), corresponds to 0.002–0.004% in volume fraction (vol%).
Results and discussion
The Z-scan properties of the carbon nanostructure suspension were measured using a traditional open-aperture Z-scan system, wherein the scan laser beam (527 nm wavelength, 150 ns pulse width, 1 kHz repetition rate) was a polarized beam focused with a lens of 10 cm focal length. The Z-scan results of graphene in the NMP suspension under horizontally and vertically polarized beams are illustrated in Fig. 1.
As depicted in Fig. 1, the Z-scan properties observed under a horizontally polarized beam varied from those detected using a vertically polarized beam. In addition to RSA-like dip surrounding the lens focus when the horizontally polarized beam is focused in suspension, two SA-like peaks appeared adjacent to the dip. However, for the vertical polarized beam, only one RSA-like dip surrounded the lens focus. In contrast, two SA-like peaks were distributed on both sides of the focus (RSA dip) for the horizontally polarized beam, implying that the SA-like peaks were situated far away from the focus, and the threshold was lower than that of the RSA-like dip. Simultaneously, the lowest normalized transmission of the horizontally polarized beam (Fig. 1a) was higher than that of the vertically polarized beam (Fig. 1b), which indicated that the RSA-like dip peculiarity of the vertically polarized beam was stronger than that of the horizontally polarized beam. Regardless of the SA peak and RSA, the dip increased with the laser energy (comparing Fig. 1a,c) and decreased with the graphene concentration (comparing Fig. 1c,e).
The influence of the solvent on the polarized Z-scan properties of the graphene suspension was investigated by using DI water as the solvent to obtain a graphene–DI water suspension, whose viscosity coefficient varied from that of the NMP36,37; the results are displayed in Fig. 2. Upon using a horizontally polarized beam, the SA peaks almost disappeared for the graphene–DI water suspension (Fig. 1). However, the SA characteristics were affected by the solution because the RSA dip remained.
The Z-scan results of GO in the NMP and DI water suspensions are illustrated in Figs. 3 and 4, respectively. Regardless of GO in the NMP or DI water suspension, SA- and RSA-like curves were observed for the horizontally polarized beams, but the RSA was observed for vertical polarization at the same incident laser power (Figs. 3 and 4). Moreover, the SA transmission of the GO–NMP suspension (Fig. 3a) was evidently higher than that of the GO–DI water suspension (Fig. 4a). Subsequently, the SA peaks disappeared as the transmission of the GO–NMP suspension increased from 10 to 60% (Fig. 3c), signifying that the concentration of the GO–NMP suspension could affect the Z-scan properties under a polarized beam. In summary, the polarized properties of the scan laser and the concentration of the suspension could affect the Z-scan properties of the GO–NMP suspension, but the influence of the solvent almost disappeared.
In case a high-intensity laser was incident on the suspension, the suspended nanostructures absorbed the incident laser energy and converted it into heat. Subsequently, the heat was transferred to the surrounding liquid, creating a local temperature gradient and natural convection. As the simulation results of flow velocity distribution by computational fluid dynamics (CFD) in our paper38, there is barely any flow when intensity laser irradiate 0.4 s, but increases considerably at 4 s. In general, a flake will experience imbalanced shear forces on its head and tail ends, which produces a net torque causing rotation of the flake39. In addition, laser-induced dynamic alignment and optical anisotropy of nanomaterials further result in polarization-dependent modulation of laser transmission38. However, the degree of laser-induced alignment varied in case the suspension was moved in or out of the focal point of the beam, and it was related to the laser intensity. Moreover, low laser intensity was observed with weak laser-induced temperature gradient and subsequent fluidic flows in case the suspension was out of focus. In comparison, a much stronger flow and subsequent alignment could be observed if the focused beam was in the vicinity of the suspension, and the flakes were vertically aligned, as depicted in Fig. 5a. Therefore, an enhanced optical transmission was produced under the horizontally polarized beam in the Z-scan experiment23,24, and two SA-like peaks appeared under horizontally polarized cases, as depicted in Figs. 1, 3, and 4. However, the vertically aligned nanomaterials blocked and scattered the incident laser (vertically polarized laser), even if the 2D carbon nanomaterials were aligned, as depicted in Fig. 5a. Therefore, the SA-like peaks did not appear in the vertically polarized case. In a word, the SA-like transmission is the result of modulation of laser induced dynamic alignment and optical anisotropy of nanomaterials, which is not the third-order nonlinear. An important criterion to determine whether the observed nonlinear-like transmission induced by third-order susceptibility χ(3) is the laser pulse width, and only sub-picosecond or short than sub-picosecond with high peak intensity can meet the timescale of electronic transitions40,41,42. But for most nanosecond laser pulses, they are too low to induce a significant nonlinear optical effect despite the observation of obvious nonlinear-like Z-scan transmission. In Fig. 2, the SA peaks did not appear for the graphene in DI water suspension under a horizontally polarized beam, which reflected that graphene cannot be appropriately aligned in the DI water as compared to the NMP solution (Fig. 1). This signified that the dispersed liquid could affect the alignment of the graphene.
However, when the focused beam was transmitted through the suspension, the highest laser intensity, highest laser-induced temperature gradient, and fastest fluidic flow caused by convection were observed at this spot. Thus, the alignment was strongly disturbed and misaligned, as depicted in Fig. 5b. In case the alignment was disintegrated, the 2D carbon nanomaterials blocked and scattered the incident laser. Simultaneously, as mentioned in our previous work43, the carbon nanomaterials absorbed the energy of the incident laser and transferred to surrounding liquid, the Raman experiment result showed that the temperature rise is only 180 °C, which is just slightly higher than the boiling temperature of water, resulting in vapor and microbuubles generation. At the same time, the CCD and ultrasound results further verified the existence of photothermal bubbles near the focus. Moreover, the photothermal microbubble strongly scattered the incident laser, which induced a normalized transmission turn-down after exhibiting the SA-like peak. The focused beam exhibited a small beam radius with an increasing number of photothermal microbubbles in the vicinity of the focus, and the scatter intensified when the focused laser passed through the suspension. Therefore, the scattering induced by the photothermal microbubbles were independent of the polarization, and both the horizontally and vertically polarized cases displayed an RSA-like dip, as depicted in Figs. 1, 2, 3 and 4.
To further verify the polarization-dependent transmission induced by the laser-induced alignment of nanomaterials in suspension, the carbon particle suspension was selected to derive various results. Consequently, the isotropic particles and Z-scan properties of the carbon particles suspended in DI water are represented in Fig. 6. The obtained results varied from those obtained for graphene and GO suspensions; the SA peak disappeared for the horizontally polarized beam, and only the RSA dip and RSA-like curve remained for the vertically polarized beam. Overall, the Z-scan curve for the horizontally polarized beam was almost identical to that of the vertical polarized beam, which implied that the Z-scan properties of the carbon particle–DI water suspension were independent of the polarized properties of the scan beam. As the carbon particles were isotropic, its isotropic properties allowed a uniform transmission of the light in all directions, even if the carbon particles were aligned by the incident laser. Therefore, the SA-like peaks were not observed for the carbon particles in DI water suspension under a horizontally polarized beam, as depicted in Fig. 6a.
Conclusion
In summary, open-aperture Z-scan results revealed that graphene and GO flakes exhibited SA- and RSA-like curves under horizontally polarized beams, whereas only the RSA-like curves were observed for vertical polarization under the same conditions. Moreover, the RSA-like dip of the GO suspension was narrower than that of the graphene suspension. In particular, the RSA thresholds of the graphene and GO suspensions were lower for the horizontal beam than those for the vertical beam. These results signified that the Z-scan characteristics of graphene and GO suspensions depend on the polarization of the incident laser, and the suspension particles were anisotropic, which could be ascribed to the laser-induced dynamic alignment of graphene or GO flakes. However, the Z-scan properties of the isotropic materials such as carbon particles are independent of the polarization of the incident laser. Simultaneously, the solvent of the graphene suspension and concentration of the GO suspension influenced the SA-like peaks under polarized laser. Furthermore, the SA-like peaks disappeared in both the graphene–DI water suspension and the high-concentration GO suspension, and only the RSA-like dip remained. Thus, the anisotropic optical responses of the liquid suspensions provided innovative routes for studying the fundamental light–matter interaction and the Z-scan curve principle, which is essential for novel 2D material-based optical and optofluidic devices.
References
Hu, Y. et al. Anisotropic two-photon absorbers measured by the Z-scan technique and its application in laser beam shaping. JOSA B. 37, 756–761 (2020).
Sheik-Bahae, M. et al. Sensitive measurement of optical nonlinearities using a single beam. IEEE J. Quant. Electron. 26, 760–769 (1990).
Zhang, H. et al. Z-scan measurement of the nonlinear refractive index of graphene. Opt. Lett. 37, 1856–1858 (2012).
Gan, Y. et al. Enhanced optical limiting effects of graphene materials in polyimide. Appl. Phys. Lett. 104, 171105 (2014).
Li, P. et al. Enhanced optical limiting properties of graphene oxide-ZnS nanoparticles composites. Carbon 159, 1–8 (2020).
Liaros, N. et al. Nonlinear optical properties and broadband optical power limiting action of graphene oxide colloids. J. Phys. Chem. C 117, 6842–6850 (2013).
Wu, L. et al. Enhanced nonlinear optical behavior of graphene–CuO nanocomposites investigated by Z-scan technique. J. Alloys Compd. 777, 759–766 (2019).
Muruganandi, G. et al. Effect of reducing agents in tuning the third-order optical nonlinearity and optical limiting behavior of reduced graphene oxide. Chem. Phys. 488, 55–61 (2017).
Ganeev, R. et al. Nonlinear optical absorption and refraction in Ru, Pd, and Au nanoparticle suspensions. Appl. Phys. B 100, 571–576 (2010).
Li, W. et al. Ultrafast all-optical graphene modulator. Nano Lett. 14, 955–959 (2014).
Zhang, X. L. et al. Transient thermal effect, nonlinear refraction and nonlinear absorption properties of graphene oxide sheets in dispersion. Opt. Express 21, 7511–7520 (2013).
Arandian, A. et al. The effect of laser wavelength and concentration on thermal nonlinear refractive index of graphene suspensions. World Sci. Res. 10, 1550053 (2015).
Yan, L. et al. Optical limiting properties and mechanisms of single-layer graphene dispersions in heavy-atom solvents. Opt. Express. 22, 31836–31841 (2014).
Liu, Z. et al. Nonlinear optical properties of graphene oxide in nanosecond and picosecond regimes. Appl. Phys. Lett. 94, 021902 (2009).
Liaros, N. et al. Optical limiting action of few layered graphene oxide dispersed in different solvents. Opt. Mater. 36, 112–117 (2014).
Tutt, L. W. et al. A review of optical limiting mechanisms and devices using organics, fullerenes, semiconductors and other materials. Prog. Quantum. Electron. 17, 299–338 (1993).
Lim, G. K. et al. Giant broadband nonlinear optical absorption response in dispersed graphene single sheets. Nat. Photonics. 5, 554–560 (2011).
Cheng, X. et al. Controllable broadband nonlinear optical response of graphene dispersions by tuning vacuum pressure. Opt. Express. 21, 16486–16493 (2013).
Prizia, R. et al. Soret reverse saturable absorption of graphene oxide and its application in random lasers. JOSA B. 36, 19–25 (2019).
Ghasemi, F. et al. Single-step laser-assisted graphene oxide reduction and nonlinear optical properties exploration via CW laser excitation. J. Electron. Mater. 47, 2871–2879 (2018).
Kislyakov, I. M. et al. Nonlinear scattering studies of carbon black suspensions using photoacoustic Z-scan technique. Appl. Phys. Lett. 103, 151104 (2013).
Nashold, K. M. et al. Investigation of optical limiting mechanisms in carbon particle suspensions and fullerene solutions. J. Opt. Soc. Am. B. 12, 1228–1237 (1995).
Lin, F. et al. Orientation control of graphene flakes by magnetic field: Broad device applications of macroscopically aligned graphene. Adv. Mater. 29, 1604453 (2017).
He, L. et al. Graphene oxide liquid crystals for reflective displays without polarizing optics. Nanoscale 7, 1616–1622 (2015).
Shen, T. Z. et al. Electro-optical switching of graphene oxide liquid crystals with an extremely large Kerr coefficient. Nat. Mater. 13, 394–399 (2014).
He, X. et al. Wafer-scale monodomain films of spontaneously aligned single-walled carbon nanotubes. Nat. Nanotechnol. 11, 633–638 (2016).
Rossi, D. et al. Orientational control of colloidal 2D-layered transition metal dichalcogenide nanodiscs via unusual electrokinetic response. ACS Nano 9, 8037–8043 (2015).
Ye, Q. et al. Polarization-dependent optical absorption of graphene under total internal reflection. Appl. Phys. Lett. 102, 021912 (2013).
Ding, L. et al. Fiber optical sensor based on polarization-dependent absorption of graphene. SPIE. 10323, 103237R (2017).
Yan, X. Q. et al. Experimental observation of polarization-dependent ultrafast carrier dynamics in multi-layer graphene. Arxiv e-Prints 1743, 1301 (2013).
Yoon, D. et al. Strong polarization dependence of double-resonant Raman intensities in graphene. Nano Lett. 8, 4270–4274 (2008).
Lee, J. U. et al. Polarization dependence of double resonant Raman scattering band in bilayer graphene. Carbon 72, 257–263 (2014).
Sasaki, K. et al. Polarition dependence of Raman spectra in strained graphene. Phys. Rev. B 82, 205407 (2010).
Kim, J. et al. Anomalous polarization dependence of Raman scattering and crystallographic orientation of black phosphorus. Nanoscale 7, 18708–18715 (2015).
Zhou, X. et al. A scalable, solution-phase processing route to graphene oxide and graphene ultralarge sheets. Chem. Comm. 46, 2611–2613 (2010).
Korson, L. et al. Viscosity of water at various temperatures. J. Phys. Chem. 73, 34–39 (1969).
Millero, F. J. Relative viscosity and apparent molal volume of N-methylpropionamide solutions at various temperatures. J. Phys. Chem. 72, 3209–3214 (1968).
Zhang, Q. et al. Laser-induced dynamic alignment and nonlinear-like optical transmission in liquid suspensions of 2D atomically thin nanomaterials. Opt. Express 29, 36389–36399 (2021).
Lin, F. et al. Graphene oxide liquid crystals: Synthesis, phase transition, rheological property, and applications in optoelectronics and display. Nanoscale Res. Lett. 10, 1–16 (2015).
Kuzyk, M. G. et al. Frequency dependence of the 438 optical Kerr effect and third-order electronic nonlinear-optical processes of organic 439 liquids. J. Opt. Soc. Am. B 6, 154–164 (1989).
Hendry, E. et al. Coherent 441 nonlinear optical response of graphene. Phys. Rev. Lett. 105, 097401 (2010).
Alfano, R. R. et al. Electronic mechanism for production of self-phase modulation. Phys. Rev. A 6, 433 (1972).
Zhang, Q. et al. Photoacoustic identification of laser-induced microbubbles as light scattering centers for optical limiting in a liquid suspension of graphene nanosheets. Nanoscale 12, 7109–7115 (2020).
Acknowledgements
Q.H.Z acknowledges support from the National Natural Science Foundation of China (No.U2004162, 61805071) and Key Scientific and Technological projects in the Henan Province of China (No. 202102310002, 212102210245, 222102240054).
Author information
Authors and Affiliations
Contributions
Q.Z. wrote the manuscript and did the experiments in the manuscript. X.W. improved this manuscript. J.H. proposed the structure of this paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, Q., Wu, X. & Han, J. The influence of laser-induced alignment on Z-scan properties of 2D carbon nanomaterials suspension dependent on polarization. Sci Rep 12, 10127 (2022). https://doi.org/10.1038/s41598-022-14577-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-022-14577-0
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.