Abstract
Organic microlasers hold great potentials in fabricating on-chip sensors for integrated photonic circuits due to their chemical versatility and reactivity. However, chemical vapor detection is still challenging for organic microlaser sensors, as it requires not only optical gain and self-assembly capability, but also rapid response to stimuli and long-term stability under high excitation power. In this work, a new laser dye 4,7-bis(9-octyl-7-(4-(octyloxy)phenyl)-9H-carbazol-2-yl)benzo[c][1,2,5]thiadiazole (BPCBT) is designed and synthesized, which self-assembles into microwires showing strong intramolecular charge transfer (ICT) photoluminescence with >80% quantum efficiency. It enables the lasing from BPCBT microwires under a low threshold of 16 μJ·mm−2·pulse−1 with significantly improved stability over conventional organic microlasers. The stimulated emission amplifies the fluorescence change in the BPCBT microwires under chemical vapors including various acid, acetone, and ethanol vapors, indicating high sensitivity and high selectivity of organic microlaser sensors desirable for compact sensor arrays in integrated photonics.
Similar content being viewed by others
Introduction
Organic micro/nanolasers have drawn great attention because they may serve as functional units such as miniature coherent light source on integrated photonics chips1,2,3,4,5,6. Besides high optical gain coefficient, organic dye molecules take advantages of chemical versatility as well as sensitivity to external stimuli compared with their inorganic counterpart7,8,9, which extends their potential applications from microlasers to on-chip chemical sensors. The arrays of organic microlasers could be prepared by various solution-processable methods4,10,11, providing opportunities for efficient and sensitive identification of chemicals in complicated environments. In principle, the sensitivity of these microlaser sensors would be significantly enhanced compared with that of traditional fluorescent sensors according to the light amplification nature of the stimulated emission process12,13,14. However, high-intensity excitation is usually required for laser action15, and thus the stability would become an essential issue in the fabrication of chemical sensors based on organic microlasers16,17. In addition, the excited state of these chromophores should be both highly efficient in radiative decay process and highly reactive to the introduction of trace analyte18,19. Rational design on molecular structures that combines the capabilities of lasing and sensing in excited-state processes is therefore crucial for the realization of chemical vapor detection based on organic microlasers.
Intramolecular charge transfer (ICT), in which the electron transfers from the donor to the acceptor moieties in the same molecule, can prolong the photoexcitation lifetime towards the construction of various multi-functional luminescent molecules20,21. Self-assembled microstructures of ICT molecules have been demonstrated to serve as low-threshold microlasers that may switch the output wavelength upon temperature or pump energy changes22,23. It has also been proved that the ICT complex may show superior performance towards continuous-wave pumping lasers by partially overcoming the optical loss of triplet accumulation24. The building blocks of donor and acceptor provide great possibilities in involving functional groups for chemical sensing in the molecular structures while maintaining the high optical gain for laser action25,26. More interestingly, the competition between radiative and nonradiative excited-state processes in ICT molecules would lead to a leverage effect on the population distribution of photoexcitations and thus the enhancement of sensitivity via stimulated emission26. This design strategy of ICT molecules offers a promising approach to microlaser-based chemical vapor sensors, as well as other functional on-chip units using organic microlasers in chemo/bioanalytical and environmental fields27.
In this study, we have designed and synthesized a new ICT molecule 4,7-bis(9-octyl-7-(4-(octyloxy)phenyl)-9H-carbazol-2-yl)benzo[c][1,2,5]thiadiazole (BPCBT) (see Supplementary Methods, Supplementary Scheme 1, Figs. 1 and 2) with a nearly 100% photoluminescence quantum yield (PLQY). The ICT occurs from the carbazole derivative donor to the benzothiadiazole acceptor, and has been investigated by density functional theory (DFT) calculations and steady-state spectroscopic experiments. The side alkyl chains enlarge the intermolecular distance in the self-assembled microwire structures of BPCBT molecules and avoid the possible aggregation-induced quenching. The BPCBT microwires that show over 80% PLQY can work as microlasers with a low threshold 16 μJ·mm−2·pulse−1 and superior stability beyond conventional dye-doped microlasers. As the carbazole group may form nonradiative charge-transfer state with external proton donors, the single microwire is chemically sensitive to acid vapors, and the change in its lasing intensity is dramatically enhanced compared with that in spontaneous fluorescence. Moreover, the wettability of solvent vapors leads to the morphological change of BPCBT microwires as optical microcavities, which extends the species of organic vapors for these microlaser sensors to non-reactive compounds such as acetone and ethanol.
Results and discussion
Preparation of BPCBT microwires
In the BPCBT molecule, the benzothiadiazole unit is sandwiched between two carbazole groups resulting in a symmetrical D-A-D structure (Fig. 1a). The rigid carbazole group is used for stable UV light absorber that has been used in blue light-emitting diodes28, as well as in active moiety to iodide and explosive detection29,30. While the benzothiadiazole serves as a high-efficient fluorescent core with electron-withdrawing capacity that has applications in bioimaging and electroluminescence systems31,32. Thereby, the charge transfer between carbazole donor and benzothiadiazole acceptor allows for the formation of highly emissive excited states with remarkable photostability. In addition, the long alkyl groups improve the solubility of BPCBT molecules as well as protect the delocalized charge-transfer states from being quenched by strong electronic coupling with enhancing intermolecular distance33,34.
DFT calculations were performed to study the geometric and electronic structures of BPCBT molecule. Frontier orbital analyses (Fig. 1b) show that the highest occupied molecular orbital (HOMO) is mainly located on molecular skeleton, while the lowest unoccupied molecular orbital (LUMO) is located on electron-withdrawing benzothiadiazole unit. The charge-transfer feature of BPCBT molecule reduces the energy gap to ~2.70 eV compared with those of benzothiadiazole (~4.24 eV) and carbazole (~4.79 eV) molecules (Supplementary Fig. 3). As the solvent effects and the intermolecular interactions are not involved in the calculation35, these LUMO and HOMO energies obtained are not the same as the experimental values obtained from cyclic voltametric measurement (Supplementary Fig. 4). The time-dependent DFT calculation shows that the transition dipole moment (TDM) is almost parallel to the long axis of BPCBT molecule (Supplementary Fig. 5), and the benzothiadiazole and carbazole units present a distorted conformation with a dihedral angle of ~33° while the dihedral angle of carbazole and benzene rings is ~37° (Supplementary Fig. 6). As a result, the overlapping of intermolecular π-conjugated electrons is obviously reduced, and the dipole–dipole interaction between neighboring BPCBT molecules becomes dominated and facilitates the molecular packing in a preferential direction36.
The BPCBT microwires were prepared by an anti-solvent vapor diffusion method (see details in the “Methods” section)37. As shown in Fig. 1c, transmission electron microscopy (TEM) image indicates that these self-assembled microwires are highly crystalline and the corresponding selected area electron diffraction (SAED, Fig. 1d) pattern proves face-to-face distance is 4.2 Å with small angle along the direction of microwire. This agrees with the signal that appears at ~22.1° in the X-ray diffraction (XRD) measurements (Supplementary Fig. 7), which is attributed to the preferential molecular packing based on dipole–dipole interaction. The other two structural parameters (17.3 Å, 39.1 Å) are different from the size of BPCBT molecule (14.9 Å, 51.4 Å), indicating that the molecules incline in the microwire with the side chains standing on the substrate. Figure 1e presents the fluorescence microscopy image of self-assembled microwires showing bright yellow emission. A representative single microwire exhibits optical waveguiding property as the ends are much brighter than the body of microwire38.
Photoluminescence and lasing properties
The packing style of BPCBT molecules in the microwire is illustrated in Fig. 2a, in which the molecular backbones are aligned in parallel and the angle with respect to the long axis of microwire is ~20°. This unidirectional molecular alignment was demonstrated by the birefringence analysis of microwires under polarized optical microscope (POM), as shown in Fig. 2b. The two crossed microwires turn bright and dark alternately upon the rotation of polarizers39, and the high contrast shows that the defect density in these single-crystalline microwires is extremely low. Note that the maximum intensity in the polarized photoluminescence profile appeared at a cross angle of ~20° (Supplementary Fig. 8), which agrees with the direction of TDM in the microwire. The above features are beneficial to the properties of high-efficiency photoluminescence and optical waveguiding with a relatively low propagation loss (Supplementary Fig. 9) in BPCBT microwires. Besides, the light signal from a single BPCBT microwire could be efficiently coupled into neighboring wires (Supplementary Fig. 10).
As shown in Fig. 2c, the dichloromethane solution of BPCBT (10−5 M) presented two absorption bands located at ~340 and ~430 nm, corresponding to the 1Lb ← 1A transition of carbazole group40 and the ICT transition of BPCBT, respectively. In comparison, the PL spectrum shows only the feature of ICT transition which is centered at ~585 nm with a large Stokes shift41,42. The absorption of BPCBT misscrowires is similar to that of its dilute solution expect for a tail toward longer wavelength due to light scattering43. The photoluminescence band of microwires becomes narrower compared with that of BPCBT solution, because the confinement of geometric configurations reduces the degree of freedom of molecular vibrations44. No intermolecular transition is observed and the ICT transition is still predominated in microwires, and the PLQY of BPCBT microwires is over 80% (Supplementary Fig. 11) which is close to the near-unity PLQY of monomers. It attributes to steric hindrance effects enlarging intermolecular distances, keeping intrinsic monomer emission. As a result, the photoluminescence lifetime (Fig. 2d) of BPCBT microwires (~6.3 ns) is also close to that of solution (~5.2 ns), as the π-electron coupling between neighboring molecules is quite weak in the microwire.
The high PLQY and relatively long excited-state lifetime of BPCBT microwires are important to achieve laser action at low threshold, and the lasing characterization of single microwires was performed on a home-built optical microscope system equipped with a pulsed laser source (Supplementary Fig. 12). As shown in Fig. 3a, a broad spontaneous emission band was observed from the wire tip at a low pump fluence (~13 μJ·mm−2·pulse−1). A series of sharp peaks emerged on top of the broad band when the excitation energy was increased to ~19 μJ·mm−2·pulse−1. Diffraction pattern appeared around the wire tip under a high pump fluence (~24 μJ·mm−2·pulse−1) which indicates a typical Fabry-Pérot (FP) type resonance along the microwire45. The microwire laser shows a threshold at ~16 μJ·mm−2·pulse−1 in the excitation power dependence profile, accompanied with a sharp decrease from 75 to 1 nm in the full width at half maximum (FWHM) of emission band (Fig. 3b). The performance of microlasers based on BPCBT microwires is highly comparable to previously reported laser dyes of carbozole derivatives (Supplementary Table 1). The electric-field distributions of FP-type microcavities (Fig. 3c) indicate that the resonant modes can be described as Δλ = λ2/2nL, where Δλ, λ, n, and L are mode spacing, wavelength, refractive index, and length of microwire, respectively46. Accordingly, the mode spacing Δλ decreases with the increase in the length of microwire L (Supplementary Fig. 13), and the refractive index calculated from the theoretical fitting with FP-type optical resonance is ~2.72 (Fig. 3d), which is higher than that of normal organic crystals due to the close molecular packing along the microwire axis47.
The ultralow threshold is essential for the improved operation stability of BPCBT microlasers. As shown in Fig. 3e, the lasing spectra decreased by ~20% after the first 100 k pulses but remained almost unchanged during the excitation of 100 to 200 k pulses, which indicates that the microwire laser can keep stable multi-mode lasing output during the operation. Figure 3f shows the time-dependent output intensities from BPCBT microlasers, in which the operations at room temperature (RT) and 60 °C would not cause severe degradation of BPCBT chromophores in the microwires. A polymeric microlaser, [4-(dicyanomethylene)-2-methyl-6-(4-dimethylaminostyryl)-4H-pyran] (DCM) doped polystyrene microsphere, was prepared as a control sample to demonstrate the superior stability of BPCBT microlasers. The rigid moiety and nonplanar structure of BPCBT molecule facilitate its thermal and photochemical stability which is essential to the reliable sensing of chemical vapors.
Chemical vapor detection
The carbazole group is known to be sensitive to protonic acids via the protonation interaction48. This allows for the detection of acid vapor by monitoring the change in emission intensity from BPCBT microwires. By adding several drops of HCl into BPCBT solution, an immediate decrease in fluorescence intensity was detected as nonradiative decay was introduced by the interaction between BPCBT and HCl (Supplementary Fig. 14). However, the response of single BPCBT microwire when being exposed to saturated HCl vapor becomes quite limited (<10%), as shown in Fig. 4a. This is probably because the HCl cannot penetrate into the body and only can be adsorbed to the surface which would not be able to completely quench the photoluminescence of microwire (Supplementary Fig. 15). Interestingly, the lasing emission from BPCBT microwire excited above threshold totally disappeared upon the exposure to HCl vapor (Fig. 4b), which demonstrates the enhancement of sensitivity due to the amplification through stimulated emission process. The limiting concentration of HCl to completely quench lasing is as low as ~100 ppm (Fig. 4c). In addition, the lasing can recover in a short time and remains sensitive to HCl vapor repeatedly (Fig. 4d).
As illustrated in Fig. 5a, the absorption of incident ultraviolet photons would excite the ground state (GS) to the local excited state (LES) of carbazole groups, and consequently generate the ICT state between carbazole and benzothiadiazole in BPCBT molecules. The laser action of BPCBT microwires may take place when the population inversion condition is fulfilled. When HCl is adsorbed to the microwire, a newly formed excited state upon the charge transfer (CT) from carbazole to HCl provides an alternative nonradiative decay route to the LES of carbazole groups. In this case, the population inversion is no longer fulfilled and thus the laser action from BPCBT microwire is turned off. As shown in Fig. 5b, the quenching efficiency of lasing intensity upon HCl exposure is increased by ~10 times compared with that of photoluminescence from BPCBT microwires. The significant enhancements on sensing properties of BPCBT microwires to various acid vapors (e.g., HBr, HI, and HNO3) were also demonstrated (Supplementary Figs. 16–18). In comparison, the vapors of organic solvents (acetone and ethanol) cannot quench the photoluminescence; however, a change in lasing output was detected upon the adsorption of solvent molecules on the microwire. The lasing modes also varied after the exposure to solvents (Supplementary Fig. 19) as the FP-type optical resonator of microwires is influenced. This interpretation was further verified by the variation of lasing modes upon the temperature change (Supplementary Fig. 20). The sensitivity to acetone vapor is slightly higher than that to ethanol, because the BPCBT microwires can be dissolved by acetone but not ethanol. Note that both photoluminescence and lasing are immune to exposure in H2O vapor as the surface of BPCBT microwires is hydrophobic. Therefore, the lasing process in BPCBT microwires not only enhances the sensitivity but also improves the selectivity to chemical vapors, showing the potentials of organic microlasers in the fabrication of on-chip multi-channel sensor arrays for complex analytes49.
Conclusion
In summary, the luminescent ICT molecule named BPCBT was designed and synthesized with high optical gain, high stability, and chemical sensitivity. The self-assembled microwires of BPCBT molecules take advantages of high PLQY and large Stokes shift, and can work as organic microlasers with a low threshold of ~16 μJ·mm−2·pulse−1. The superior stability of laser action from BPCBT microwires enables the detection of various chemical vapors including various acid vapors, acetone, and ethanol with these microlasers. The enhanced sensitivity and improved selectivity of lasing sensors based on BPCBT microwires opens up a new avenue to the on-chip chemical detectors in integrated photonics applications.
Methods
Preparation of BPCBT microwires
BPCBT microwires were prepared by a one-step anti-solvent vapor diffusion method37. Typically, the BPCBT compound (1 mg) was dissolved into a mixture of dichloromethane and methanol (1:1, 50 mL), and a vial of transparent solution (2 × 10−5 M) was obtained after stirring for 15 min. Then a vial of 1 mL obtained solution was placed in a closed beaker containing ethanol (3 mL) as the anti-solvent. After 3 h the suspension of BPCBT microwires was obtained in the vial. The size of microwires increased with the increase of aging time. The suspension was drop-casted on the substrates for further characterizations. In addition, the DCM-doped polystyrene microspheres were prepared by an emulsion-solvent-evaporation method according to previous report50.
Measurements
The analysis of structure and crystallinity of BPCBT microwires was carried out on a transmission electron microscope (JEOL JEM-1011) and an X-ray diffractometer (Panalytical Empyrean) with Cu Kα radiation (λ = 1.54056 Å). The cyclic voltammetric measurement was conducted with Pt disk and Pt wire as the working and counter electrodes, Ag/AgCl electrode (sat. KCl) as the reference electrode, and n-Bu4NPF6 (0.1 M) as supporting electrolyte. The fluorescence images were taken on an inverted optical microscope (Nikon Ti-U) excited with the UV band (330–380 nm) of a mercury lamp. The polarized dark-field optical microscopy images were captured with an upright polarizing microscope (Nikon ECLIPSE Ci-POL). The absorption and photoluminescence spectra were obtained from a UV-visible-NIR spectrophotometer (Hitachi UH4150) and a fluorescence spectrophotometer (Hitachi, F-7000), respectively. The absolute quantum yields of BPCBT solution and microwires were recorded on an absolute quantum yield spectrometer (Hamamatsu C11347) equipped with an integrating sphere apparatus and a 150 W CW Xenon light source. The decay curves of photoluminescence were measured with a Quantaurus-Tau fluorescence lifetime spectrometer (Hamamatsu Photonics C11367-31). Optically pumped lasing measurements were carried out on a home-built far-field micro-PL system. For sensing of chemical vapors, the BPCBT microwires and chemical vapors were sealed in a 3D printed chamber to provide an atmosphere with constant vapor concentration. Before each sensing measurement, the air flow was injected to evacuate residual vapors in the chamber. The spectra were collected through an inverted optical microscope before/after the exposure of chemical vapors, and further analyzed to evaluate the sensing properties.
Calculations
The molecular geometry was optimized by Gaussian 0951 at B3lyp/6-31G** level in the gas phase, and the molecular orbitals were calculated using time-dependent density functional theory (TDDFT) at B3lyp/6-31G** level. A commercial finite-element-methods-based software (Comsol Multiphysics 5.0) was used for the numerical simulations. The sizes of calculation regions were 1 × 0.2 µm2 and 2 × 0.2 µm2 using a scattering boundary condition with a background refractive index of air (n = 1.0), and the refractive indexes of the wires were set to 2.72 at 606 nm.
Reporting summary
Further information on research design is available in the Nature Research Reporting Summary linked to this article.
Data availability
The main data supporting the finding of this study are available within the paper and its Supplementary Information file. Other relevant data are available from the corresponding author upon reasonable request.
Code availability
The Gaussian 09 package, Revision B.01 was employed for all the DFT calculations. The software and instructions for its use are available at https://gaussian.com/. The Comsol Multiphysics 5.0 was used for numerical simulations. The software and instructions for its use are available at https://cn.comsol.com/.
References
Zhao, J. Y. et al. Full-color laser displays based on organic printed microlaser arrays. Nat. Commun. 10, 870 (2019).
Wei, G. Q., Wang, X. D. & Liao, L. S. Recent advances in 1D organic solid-state lasers. Adv. Funct. Mater. 29, 1902981 (2019).
Zhang, Q. et al. A room temperature low-threshold ultraviolet plasmonic nanolaser. Nat. Commun. 5, 4953 (2014).
Liao, Q. et al. An organic microlaser array based on a lateral microcavity of a single J-aggregation microbelt. Angew. Chem. Int. Ed. 54, 7037–7041 (2015).
Xu, F. F. et al. Flat-panel laser displays based on liquid crystal microlaser arrays. CCS Chem. 2, 369–375 (2020).
Zhang, W., Yao, J. N. & Zhao, Y. S. Organic micro/nanoscale lasers. Acc. Chem. Res. 49, 1691–1700 (2016).
Zhang, J. J., Zou, Q. & Tian, H. Photochromic materials: more than meets the eye. Adv. Mater. 25, 378–399 (2013).
Wang, Y. et al. Equilibrium and thermodynamic studies of chromic overcrowded fluorenylidene-acridanes with modified fluorene moieties. Commun. Chem. 3, 1–10 (2020).
Yanai, N. et al. Guest-to-host transmission of structural changes for stimuli-responsive adsorption property. J. Am. Chem. Soc. 134, 4501–4504 (2012).
Wu, J. J. et al. Near-infrared organic single-crystal nanolaser arrays activated by excited-state intramolecular proton transfer. Matter 2, 1233–1243 (2020).
Feng, J. G. et al. Random organic nanolaser arrays for cryptographic primitives. Adv. Mater. 31, 1807880 (2019).
Gu, F. X. et al. Single whispering-gallery mode lasing in polymer bottle microresonators via spatial pump engineering. Light.: Sci. Appl. 6, e17061 (2017).
Ta, V. D., Chen, R. & Sun, H. D. Coupled polymer microfiber lasers for single mode operation and enhanced refractive index sensing. Adv. Optical Mater. 2, 220–225 (2014).
Gierschner, J., Varghese, S. & Park, S. Y. Organic single crystal lasers: a materials view. Adv. Optical Mater. 4, 348–364 (2016).
Chen, Y. et al. Tunable Raman laser in a hollow bottle-like microresonator. Opt. Express 25, 16879–16887 (2017).
Zhang, C. H. et al. Dual-color single-mode lasing in axially coupled organic nanowire resonators. Sci. Adv. 3, e1700225 (2017).
Matino, F., Persano, L., Camposeo, A. & Pisignano, D. Laser systems and networks with organic nanowires and nanofibers. Adv. Optical Mater. 7, 1900172 (2019).
You, L., Zha, D. J. & Anslyn, E. V. Recent advances in supramolecular analytical chemistry using optical sensing. Chem. Rev. 115, 7840–7892 (2015).
Jiang, X. Y. et al. Highly-sensitive optical organic vapor sensor through polymeric swelling induced variation of fluorescent intensity. Nat. Commun. 9, 3799 (2018).
Xie, Z. L. et al. Hydrogen-bonding-assisted intermolecular charge transfer: a new strategy to design single-component white-light-emitting materials. Adv. Funct. Mater. 27, 1703918 (2017).
Lu, H. G. et al. Highly efficient far red/near-infrared solid fluorophores: aggregation-induced emission, intramolecular charge transfer, twisted molecular conformation, and bioimaging applications. Angew. Chem. Int. Ed. 55, 155–159 (2016).
Dong, H. Y. et al. Broadband tunable microlasers based on controlled intramolecular charge-transfer process in organic supramolecular microcrystals. J. Am. Chem. Soc. 138, 1118–1121 (2016).
Zhang, W., Yan, Y. L., Gu, J. M., Yao, J. N. & Zhao, Y. S. Low-threshold wavelength-switchable organic nanowire lasers based on excited-state intramolecular proton transfer. Angew. Chem. Int. Ed. 54, 7125–7129 (2015).
Zhou, Z. H. et al. Experimentally observed reverse intersystem crossing-boosted lasing. Angew. Chem. Int. Ed. 59, 21677–21682 (2020).
Liu, T. H. et al. Dual-mode photonic sensor array for detecting and discriminating hydrazine and aliphatic amines. ACS Appl. Mater. Interfaces 12, 11084–11093 (2020).
Gao, Z. H. et al. Proton-controlled organic microlaser switch. ACS Nano 12, 5734–5740 (2018).
He, L., Özdemir, Ş. K., Zhu, J., Kim, W. & Yang, L. Detecting single viruses and nanoparticles using whispering gallery microlasers. Nat. Nanotechnol. 6, 428–432 (2011).
Lin, S. L. et al. Highly efficient carbazole-π-dimesitylborane bipolar fluorophores for nondoped blue organic light-emitting diodes. Adv. Mater. 20, 3947–3952 (2008).
Vetrichelvan, M., Nagarajan, R. & Valiyaveettil, S. Carbazole-containing conjugated copolymers as colorimetric/fluorimetric sensor for iodide anion. Macromolecules 39, 8303–8310 (2006).
Zhang, C. Y., Che, Y. K., Yang, X. M., Bunes, B. R. & Zang, L. Organic nanofibrils based on linear carbazole trimer for explosive sensing. Chem. Commun. 46, 5560–5562 (2010).
Neto, R. A., Carvalho, P. H. & Correa, J. R. Benzothiadiazole derivatives as fluorescence imaging probes: beyond classical scaffolds. Acc. Chem. Res. 48, 1560–1569 (2015).
Chen, L. et al. White electroluminescence from star-like single polymer systems: 2, 1, 3-benzothiadiazole derivatives dopant as orange cores and polyfluorene host as six blue arms. Adv. Mater. 23, 2986–2990 (2011).
Zhou, J. D., Zhang, W. Q., Liu, L. L., Xie, Z. Q. & Ma, Y. G. Aggregation structures of organic conjugated molecules on their optoelectronic properties. Chin. Chem. Lett. 27, 1350–1356 (2016).
Zhang, X. T., Dong, H. L. & Hu, W. P. Organic semiconductor single crystals for electronics and photonics. Adv. Mater. 30, e1801048 (2018).
Luo, H. et al. A cruciform electron donor-acceptor semiconductor with solid-state red emission: 1D/2D optical waveguides and highly sensitive/selective detection of H2S gas. Adv. Funct. Mater. 24, 4250–4258 (2014).
Li, Y. J., Liu, T. F., Liu, H. B., Tian, M. Z. & Li, Y. L. Self-assembly of intramolecular charge-transfer compounds into functional molecular systems. Acc. Chem. Res. 47, 1186–1198 (2014).
Zang, L., Che, Y. & Moore, J. S. One-dimensional self-assembly of planar π-conjugated molecules: adaptable building blocks for organic nanodevices. Acc. Chem. Res. 41, 1596–1608 (2008).
Wang, X. X. et al. High-quality in-plane aligned CsPbX3 perovskite nanowire lasers with composition-dependent strong exciton-photon coupling. ACS Nano 12, 6170–6178 (2018).
Kim, Y. S. et al. Highly sensitive phototransistor with crystalline microribbons from new π-extended pyrene derivative via solution-phase self-assembly. Chem. Commun. 47, 8907–8909 (2011).
Tsai, M. H. et al. Highly efficient organic blue electrophosphorescent devices based on 3, 6-bis(triphenylsilyl)carbazole as the host material. Adv. Mater. 18, 1216–1220 (2006).
Peng, X. J. et al. Heptamethine cyanine dyes with a large stokes shift and strong fluorescence: a paradigm for excited-state intramolecular charge transfer. J. Am. Chem. Soc. 127, 4170–4171 (2005).
Qin, W. et al. Facile synthesis of efficient luminogens with AIE features for three-photon fluorescence imaging of the brain through the intact skull. Adv. Mater. 32, 2000364 (2020).
Wang, S. T. et al. Benzo[1,2-b:4,5-b’]dithiophene-based cruciforms: syntheses, crystal structures, and charge transport properties. ACS Appl. Mater. Interfaces 5, 663–671 (2013).
Bloess, A. et al. Microscopic structure in a Shpol’skii system: a single-molecule study of dibenzanthanthrene in n-tetradecane. J. Phys. Chem. A 105, 3016–3021 (2001).
O’Carroll, D., Lieberwirth, I. & Redmond, G. Microcavity effects and optically pumped lasing in single conjugated polymer nanowires. Nat. Nanotechnol. 2, 180–184 (2007).
Wang, S. et al. Solution-phase synthesis of cesium lead halide perovskite microrods for high-quality microlasers and photodetectors. Adv. Optical Mater. 5, 1700023 (2017).
Liu, D. et al. Organic laser molecule with high mobility, high photoluminescence quantum yield, and deep-blue lasing characteristics. J. Am. Chem. Soc. 142, 6332–6339 (2020).
Pfister, G. & Williams, D. J. Mechanism of fluorescence quenching by acids in N-isopropyl carbazole. J. Chem. Phys. 59, 2683–2689 (1973).
Jiang, X. F., Zou, C. L., Wang, L., Gong, Q. & Xiao, Y. F. Whispering-gallery microcavities with unidirectional laser emission. Laser Photonics Rev. 10, 40–61 (2015).
Venkatakrishnarao, D. & Chandrasekar, R. Engineering the self-assembly of DCM dyes into whispering-gallery-mode μ-hemispheres and Fabry-pèrot-type μ-rods for visible-NIR (600–875 nm) range optical microcavities. Adv. Optical Mater. 4, 112–119 (2016).
Frisch, M. J. et al. Gaussian 09, Revision B.01 (Gaussian, Inc., 2013).
Acknowledgements
This work was supported financially by the Ministry of Science and Technology of China (Grant No. 2018YFA0704802) and the National Natural Science Foundation of China (Grant Nos. 21925604, 21873105).
Author information
Authors and Affiliations
Contributions
C.Z. and Y.K.C. conceived the idea and supervised the project. X.W. performed molecule synthesis. Z.M.C. performed the crystal preparation and optical measurements. C.H.D contributed to the theoretical calculations. Z.M.C., C.H.D., C.Z., and Y.K.C. analyzed the data. Z.M.C., C.Z., and Y.K.C. wrote the manuscript. All authors reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Communications Chemistry thanks the anonymous reviewers for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Chen, Z., Dai, C., Xiong, W. et al. Stable organic self-assembled microwire lasers for chemical vapor sensing. Commun Chem 4, 97 (2021). https://doi.org/10.1038/s42004-021-00534-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s42004-021-00534-x
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.