Abstract
Hydrogels are being extensively used for three-dimensional immobilization and culture of cells in fundamental biological studies, biochemical processes and clinical treatments. However, it is still a challenge to support viability and regulate phenotypic activities of cells in a structurally stable gel, because the gel becomes less permeable with increasing rigidity. To resolve this challenge, this study demonstrates a unique method to enhance the permeability of a cell-laden hydrogel while avoiding a significant change in rigidity of the gel. Inspired by the grooved skin textures of marine organisms, a hydrogel is assembled to present computationally optimized micro-sized grooves on the surface. Separately, a gel is engineered to preset aligned microchannels similar to a plant's vascular bundles through a uniaxial freeze-drying process. The resulting gel displays significantly increased water diffusivity with reduced changes of gel stiffness, exclusively when the microgrooves and microchannels are aligned together. No significant enhancement of rehydration is achieved when the microgrooves and microchannels are not aligned. Such material design greatly enhances viability and neural differentiation of stem cells and 3D neural network formation within the gel.
Similar content being viewed by others
Introduction
Design of hydrogels used for 3D cell immobilization and culture has focused mainly on tailoring permeability, which significantly affects molecular transport and subsequent viability and phenotypic activities of cells1,2,3,4. It is common to modulate the gel permeability by controlling the number of cross-links and/or introducing micropores5,6,7. For example, a hydrogel formulated to have a smaller number of cross-linking junctions presents larger pores, and, subsequently, an increased molecular diffusivity in the matrix. Separately, micropores introduced into a hydrogel contribute to increasing permeability of the gel; however, uncontrollable numbers of non-passing and isolated pores limit the range of control over permeability6. More importantly, these traditional approaches dramatically decrease rigidity and negatively influence the structural integrity of a hydrogel, specifically in a condition subject to external mechanical forces8.
Interestingly, several marine organisms present unique microstructure to facilitate molecular transports through their elastic tissue. For instance, the skin of blue whales and brain corals exhibit grooved textures so that the skin can uptake a larger mass of molecules including water when compared to flat-surfaced skin9. Separately, most plants present anisotropically aligned vascular bundles throughout their stems, so water and nutrients taken up by the root are supplied to all parts of the plant body10. Inspired by these natural systems, we hypothesized that a hydrogel engineered to present microgrooves on its surface would significantly elevate gel permeability without appreciably changing the mechanical properties of the gel (Figure 1).
Additionally, incorporation of microchannels into the microgrooved gel would further improve mass transports through the gel, specifically when microchannels are aligned with microgrooves on the surface. We examined this hypothesis by introducing microgrooves on an alginate gel surface using a microstamping technique. A diffusion-based computational simulation was used to guide the geometry of microgrooves. The microgrooved hydrogel was also uniaxially frozen and lyophilized in order to create microchannels. Microgrooves and microchannels were aligned in parallel with or orthogonal to the microgrooves to systematically evaluate effects of alignments11. Permeability of a resulting hydrogel was evaluated by measuring water diffusivity in the gel using magnetic resonance imaging (MRI) system. Multipotent, bone marrow-derived stem cells (BMSCs) were cultured in these hydrogels to evaluate the effect of gel permeability on viability and neural differentiation of stem cells. Taken together, the results of this study will greatly serve to improve controllability of transport and mechanical properties of a wide array of materials used for cell-based bioscience and bioengineering studies.
Results and Discussion
Simulation-guided Assembly of microgrooved hydrogels
First, a 2D finite element method-based computational simulation was conducted to understand and optimize the geometry of microgrooves that can significantly enhance molecular diffusion into a gel (Figure 2A). Assuming that molecular transport into a gel was solely controlled by diffusion, oxygen concentration was determined by simulating both the oxygen diffusion rate into a gel and the oxygen consumption rate12,13,14 by cells loaded in a hydrogel using Eq. (1).
where CL is the concentration of oxygen dissolved in the media, t is time, DL is the diffusivity of oxygen in a media, is the oxygen consumption rate per cell and Xv is the cell density. The grooves with a depth of 500 μm were simulated while varying the spacing of grooves from 250 to 500 and 1,000 μm. The simulation exhibited that oxygen concentration is dependent on the spacing between microgrooves on the gel surface. Specifically, oxygen concentration in the gel with grooves smaller than 500 μm-spacing would be almost 2.5-fold higher than the gel with flat surface (Figure 2A & 2B). However, decreasing spacing from 500 to 250 μm would make minimal change of oxygen concentration. In addition, a hydrogel with grooves of 1,000 μm-spacing would display a local, limited increase of oxygen concentration around edges of microgrooves. Such simple but important role of surface topology on molecular transports into a gel matrix was not proposed in the past.
To validate the computational simulation, a hydrogel was prepared through a cross-linking reaction of alginate solution under a PDMS stamp with controlled micro-patterns (Figure 3A). The cross-linking reaction between carboxylate groups of alginate and adipic acid dihyrazide (AAD) under the PDMS stamp created hydrogels with pre-defined multiple, microgrooves (Figure 3B). Hydrogels with grooves of spacing at 1,000 and 500 μm were separately prepared, since further reduction of spacing between grooves from 500 to 250 μm would not make any increase of oxygen concentration in the gel. As expected, this topological control of the gel surface minimally changed the bulk elastic modulus of the gel (Figure S1).
Effects of microgroove spacing on water transport into the hydrogel were examined by monitoring time-based diffusion of water originally placed on the gel surface using the MRI (Figure 3C and S2). Similar to the computational simulation of oxygen transport, microgrooved hydrogels displayed faster increases of water bound to a gel matrix than a hydrogel with flat surface as displayed with a more rapid increase of red color level (Figure 3C). Note that mass of water molecules bound to a gel matrix is proportional to the intensity of red color. More interestingly, decreasing the spacing between grooves from 1,000 to 500 μm led to a saturation of the gel with red-colorated bound water within 10 minutes. The gel with grooves of 1,000 μm-spacing displayed localized increase of bound water around microgrooves, similar to computational simulation of oxygen diffusion.
The diffusivity of water into hydrogels (Dwater) was quantified by fitting the time-dependent increase of the number of pixels positively colorated at an intensity level higher than 50 to a first-order kinetics, as described by Eq. (2).
where At is the area of high water concentration at time t, Dwater is the diffusivity of water, N(t) is the number of positively colorated pixel and t is the time. According to Eq. (2), decreasing spacing of grooves to 500 μm led to a 1.6-fold increase of Dwater attained with the flat hydrogel (Figure S3 and 3D). This dependency of Dwater on the microgroove spacing was attributed to an increase in the surface area-to-volume ratio of the gel (Figure 3D). Total surface area of the hydrogel with grooves of 500 μm-spacing was 1.5 times higher than that of the flat gel.
Tailoring the hydrogel permeability by aligning microchannels
Next, microgrooved hydrogels were modified to present microchannels similar to the microvascular bundle of a plant. In this process, a hydrogel was placed on a copper substrate cooled to sub-zero temperature. Then, multiple ice crystals grew along the direction perpendicular to the copper substrate (Figure 4A). This uniaxial freezing process induced the anisotropic ice crystal growth, while excluding cross-linked polymer chains from the ice crystals. The following lyophilization removed ice crystals, thus resulting in a cryogel with anisotropically aligned microchannels without isolated pores. Depending on the orientation between the gel and the copper substrate, microchannels were aligned either in parallel with microgrooves or perpendicular to the microgroove direction (Figure 4A). The diameter of individual microchannels was 100 ± 15 μm, as confirmed by imaging the fractured surface of the gel with a scanning electron microscope (Figure 4B-1). In contrast, lyophilization of hydrogels frozen in a freezing container that presented sub-zero temperature on all sides produced a cryogel that had randomly oriented micropores with poor opening and interconnectivity, termed as a microporous gel (Figure 4B-2).
In addition, we examined whether the alignment of microchannels with microgrooves of a hydrogel would affect the diffusivity of water. When microgrooved cryogels were re-hydrated by placing water on their surfaces, the cryogel with microchannels displayed a substantial increase in the fraction of bound water (i.e., red colorated area) compared with the microporous gel, as visualized with MR images (Figure 4C and S4). Note that MR images were developed from relaxation rates of water molecules in a gel matrix. The bound water is characterized by lower water relaxation rate than free water, due to a higher binding affinity of water molecules to a gel. Interestingly, the degree of increase in the fraction of bound water was more significant with the gel in which the microchannels were aligned parallel with microgrooves, termed the (//) microchanneled gel. In contrast, the gel in which the microchannels were aligned perpendicular to microgrooves, termed the (⊥) microchanneled gel, displayed a smaller increase of the fraction of bound water than the microporous gel. The role of microchannels in enhancing water transport during rehydration became insignificant with the cryogel without microgrooves.
Additionally, water diffusion into the hydrogel was evaluated by measuring mass of the hydrogel over time while incubating the gel in aqueous media for 2 hrs. Agreed with MR images, the (//) microchanneled gel displayed the most rapid increase of the gel mass (Figure 4D). The diffusivity of water (Dwater) was calculated by fitting the increase of gel mass over time to Eq. (3)
where Wt and W∞ are the mass of a hydrogel at time t and at equilibrium swelling, respectively and L is the initial gel thickness. Very interestingly, Dwater of the (//) microchanneled gel was 1.8-fold higher than the microporous gel (Figure 4E). In contrast, there was minimal difference of Dwater between the microporous gel and the (⊥) microchanneled gel. Such enhanced water transport within the (//) microchanneled hydrogel is due to the larger number density of interconnected microchannels than the (⊥) microchanneled hydrogel, because of anisotropic growth of ice crystals in parallel with pre-defined microgrooves. The uniaxial freezing process to prepare the (⊥) microchanneled hydrogel likely encountered the discontinued ice crystal growth in the microgrooved area of the gel, because of blocked heat transfer in the microgrooves. Additionally, it is likely that water entry into the (⊥) microchanneled gel is highly limited at the intersection of microgrooves and microchannels.
Whereas the incorporation of microchannels into the hydrogel made a higher increase in the gel permeability than the microporous gel, it made much a smaller decrease of the elastic modulus of the matrix (Figure 4F). Note that the elastic modulus of the (⊥) microchanneled gel was only 1.4-fold smaller than that of the original hydrogel before freeze-drying. This smaller decrease in gel stiffness is likely due to the anisotropically extruded orientation of polymers during uniaxial freezing15,16, thus compensating effects of microchannels on decreasing stiffness of the gel. In contrast, the elastic modulus of the microporous gel was 14-fold lower than the original gel.
Analysis of the gel capability to improve metabolic activity and neural differentiation
Finally, the microgrooved gels assembled above were modified with cell adhesion oligopeptides17 to test whether the controlled hydrogel permeability improves metabolic activity and neural differentiation of bone marrow-derived stem cells (BMSCs) cultured in the gel (Figure 5A). BMSCs were loaded into the hydrogel by rehydrating the freeze-dried cryogel with cell suspension. The elastic modulus of the microchanneled hydrogel used in this cell culture study was 49 ± 4.3 kPa, while that of the microporous gel was 8 ± 1.7 kPa.
According to a MTT assay used to identify positively colored metabolically active cells, BMSCs cultured in the microchanneled hydrogel remained more metabolically active when grooves with 500 μm-spacing were present on the surface (Figure 5B). In addition, the (//) microchanneled hydrogel was more advantageous to increasing the number of metabolically active BMSCs than the (⊥) microchanneled gel. In contrast, the microgrooves on the microporous gel surface did not make a significant contribution to elevating metabolic activity of cells. The MTT absorbance (at 570 nm) of cells cultured on a 2D glass substrate was 0.286 (±0.06), which is almost same as the microporous gel with microgrooves.
Additionally, microgrooves and microchannels introduced into the gel orchestrated to elevate the neural differentiation level of BMSCs evaluated with density of neurons, a ratio of neuron to glial cells and calcium transport of differentiated cells. Incubation of the BMSC-laden hydrogel in the neural differentiation media activated differentiation of BMSCs to neuronal cells that express microtubule-associated protein (MAP2). BMSCs can also differentiate to glial cells that express glial fibrillary acidic protein (GFAP)18,19,20,21. Interestingly, cells cultured in the microporous hydrogel with an elastic modulus of 10 kPa formed a cluster independent of microgrooves on the gel surface, while those cultured in the microchanneled hydrogel with an elastic modulus of 50 kPa were fully stretched (Figure 5C). The cellular clusters formed in the soft microporous hydrogel were morphologically similar to cells loaded into a microchanneled hydrogel with an elastic modulus of 7 kPa (results not shown). It is also noteworthy that number of cells in the gel was larger with presence of microgrooves for both microporous and microchanneled hydrogels.
More interestingly, compared with cells cultured in the microporous gel (see second row in Figure 5C-1), BMSCs differentiated within the (//) microchanneled hydrogel formed a larger density of neurons and a smaller number of glial cells (see second row in Figure 5C-2 & 5D). Interestingly, differentiated neuronal cells aligned to each other in the (//) microchanneled gel, while differentiated ones in the microporous gel were aggregated. More interestingly, the glial to neuron ratio with the (//) microchanneled gel was 4-fold smaller than the microporous gel (Figure 5E).
The microgrooves of the gel played an important role on the neural differentiation level and the glial-to-neuron ratio, termed G/N ratio. For this analysis, the microchanneled hydrogel free of microgrooves was used as a control. According to the water diffusion analysis presented in Figure 4E, diffusivity of water in the control gel was two-fold smaller than the (//) microchanneled gel. Interestingly, neural density in the control gel system was almost two-fold lower than that attained with the (//) microchanneled gel. Conversely, the G/N ratio was two-fold higher with the control gel, which implicates that the (//) microchanneled gel with a higher permeability greatly supported differentiation of BMSCs to neuron-like cells.
We further analyzed the action potential morphology of differentiated neuron-like cells by imaging calcium channels of the cell. The level of calcium signals in the differentiated neuronal cells was evaluated with fluorescence arising from Fluo-4 AM bound with calcium ions in living cells. No significant difference in the level of calcium ion was detected between undifferentiated BMSCs and differentiated neuronal cells, when they were cultured on a 2D substrate (Figure S5). The neuronal cells differentiated in the gel without microgrooves did not present a higher level of calcium ions, either (see the third row in Figure 5C, S6 and S7). In contrast, with the microgrooved gel, neuronal cells in the (//) microchanneled gel expressed a 2.5-fold higher level of anisotropically aligned calcium channels than those in the microporous gel.
According to previous studies conducted by activating neural differentiation of BMSCs on hydrogels with controlled stiffness, neural differentiation of BMSCs is enhanced on a hydrogel with similar softness of brain tissue22. In contrast, our finding that neural differentiation of BMSCs cultured in a gel is enhanced with the stiffer (//) microchanneled gel compared to the softer microporous gel implicates that transport property of a matrix is a more pre-dominant factor than mechanical property with the 3D cell culture. However, controlling stiffness of the (//) microchanneled gel may allow us to tune mechanical signals of the matrix at a given permeability and attain a synergy to further elevate neural differentiation levels of BMSCs.
By combining MR images of the rehydrated gel with cellular metabolic and phenotypic activities, the results of this study address the beneficial role of bound water on 3D cell culture and further tissue development. We suggest that water molecules bound to a gel matrix do not only facilitate molecular transports into a gel matrix but also support cellular adhesion to microchannels of a gel matrix. Conversely, free water molecules implicate insufficient rehydration of a gel matrix, which leads to limited molecular transports and cell adhesion.
In addition, it is noteworthy that the difference of cellular metabolic and phenotypic activities between the microporous and microchanneled hydrogel may be partially attributed to the difference of mechanical stiffness. Cellular clusters formed in the microporous gel were morphologically similar to those found in a microchanneled gel with similar softness. Therefore, to better address the underlying mechanism, it is necessary to systematically study balanced effects of matrix permeability and stiffness on cellular response in a 3D matrix in future studies.
Conclusion
Overall, this study successfully demonstrated that bio-inspired assembly of a hydrogel to present microchannels aligned in parallel with microgrooves of optimal spacing (i.e., 500 μm) allowed us to tune mass transports in the gel, without significantly softening the gel. The perpendicular alignment between microgrooves and microchannels or the incorporation of randomly aligned micropores into the hydrogel with microgrooves did not improve water diffusion into the 3D gel matrix. We suggest that such advanced tuning of the dependency between permeability and stiffness of the gel should be attributed to the orchestrated controls of microgrooves-induced surface area, interconnectivity of microchannels and organized densification of polymers resulting from uniaxial freezing. Therefore, we could demonstrate the improved cellular metabolic and phenotypic activities in a stiff but permeable gel system. We envision that such bio-inspired orchestration of surface topology and microchannel architecture of a gel would be highly useful to culturing a wide array of stem and progenitor cells for fundamental bioscience studies and cell therapies. It would be also advantageous to improving viability and metabolic activities of yeasts and bacterial cells used in a variety of biochemical processes23. Additionally, the material assembly principle can be readily extended to fabricating a variety of material systems used in both biological and non-biological applications.
Methods
Computational simulation
The oxygen distribution in a cell-laden gel was simulated using the Comsol Multiphysics 4.3. A 200,000 cell-laden gel disk with 1 cm-diameter and 1 mm–thickness was simulated. The spacing of groove with 500 μm-depth was varied from 200 to 500 and 1,000 μm. The initial concentration of oxygen and the oxygen consumption of each cell were approximated to be 200 μmol/L and 100 fmol/h, respectively12,13,14. The diffusion coefficient of oxygen in hydrogels was approximated to be 2 × 10−10 m2/s. All simulations were made in meters, seconds and kilograms. Each sample was simulated for a period of 5 hours.
Hydrogel assembly
Based on simulation results, alginate hydrogels with microgrooves of controlled spacing were assembled by activating cross-linking reaction between alginate and adipic acid dihydrazide on a poly(dimethoxysiloxane) (PDMS) stamp with pre-defined, positive patterns. Both unmodified alginate and alginate conjugated with oligopeptides containing Arg-Gly-Asp sequence17, termed RGD peptides, were used to prepare the gel. The microchanneled hydrogel was prepared by placing the flat or microgrooved gel on a copper plate at sub-zero temperature to induce uniaxially aligned ice crystals followed by lyophilization11. The resulting cryogel was rehydrated with DI water or cell suspension. In contrast, the microporous cryogel was prepared by placing the flat or microgrooved gel in a copper chamber at sub-zero temperature followed by lyophilization.
Hydrogel characterization
The water distribution within the resulting hydrogel was monitored using a 600 MHz Varian Unity/Inova nuclear magnetic resonance (NMR) spectrometer (14.1 T magnet) at room temperature, after dropping the water on the gel surface. The spin echo multi-slice (SEMS) pulse sequence was applied to acquire resonance data and water density maps were obtained using VNMR 6.1 C software. The repetition time (TR) was 500 ms and the echo time (TE) was 9.5 ms. Separately, an increase of the gel mass over time was monitored while incubating the cryogel in DI water. In parallel, the gel stiffness was evaluated by measuring a compressive elastic modulus.
Cell assays
After 24 hours since incorporating BMSCs with a cell number of 5 × 104 into the gel, the number of metabolically active cells within the hydrogels was measured using a MTT cell proliferation assay kit (Invitrogen). Cells plated on a glass with a number of 5 × 104 were also examined as a control. The absorbance of samples treated with MTT reagents following the manufacturer's protocol was measured at 570 nm using a spectrophotometer (Synergy HT, BioTek). The neural differentiation was activated by incubating cells in a neurogenic differentiation media (PromoCell). After 7 days, following fixation and permeabilization, cells were incubated with the rabbit polyclonal anti-microtubule-associated protein 2 (anti-MAP2) (10 μg/mL, Invitrogen) or mouse monoclonal anti-glial fibrillary acidic protein antibody (anti-GFAP) (4 μg/mL, Sigma) overnight. Thereafter, cells were incubated with the secondary fluorescent antibodies to image intracellular MAP2 and GFAP using the laser-scanning confocal microscope (LSM700, Zeiss). Cells located at depth of 60 mm from the top surface of the gel were captured. Calcium channels of the differentiated BMSCs were imaged by staining cells with Fluo-4AM (Invitrogen). The positively stained calcium channel was imaged using the confocal microscope. Approximately 300 cells were imaged in 8 separate gel matrix.
Statistical analysis
All averaged data are presented as means ± SE. To determine significance, comparisons between groups were performed by one-way ANOVA followed by Tukey's Multiple Comparison Test (p < 0.05).
References
Drury, J. L. & Mooney, D. J. Hydrogels for tissue engineering: scaffold design variables and applications. Biomaterials 24, 4337–4351 (2003).
Brandl, F., Sommer, F. & Goepferich, A. Rational Design of hydrogels for tissue engineering: impact of physical factors on cell behavior. Biomaterials 28, 134–146 (2007).
Jen, A. C., Wake, M. C. & Mikos, A. G. Review: Hydrogels for cell immobilization. Biotechnol. Bioeng. 50, 357–364 (1996).
Lee, K. Y. & Mooney, D. J. Hydrogels for tissue engineering. Chem. Rev. 101, 1869–1879 (2001).
Hwang, C. M. et al. A. Fabrication of three-dimensional porous cell-laden hydrogel for tissue engineering. Biofabrication 2, 1–12 (2010).
Stachowiak, A. N., Bershteyn, A., Tzatzalos, E. & Irvine, D. J. Bioactive hydrogels with and ordered cellular structure combine interconnected macroporosity and robust mechanical properties. Adv. Mater. 17, 399–403 (2005).
Park, J. H. et al. Microporous cell-laden hydrogels for engineered tissue constructs. Biotechnol. Bioeng. 106, 138–148 (2010).
Cha, C., Kim, E.–S., Kim, I. W. & Kong, H. J. Integrative design of a poly(ethylene glycol)-poly(propylene glycol)-alginate hydrogel to control three dimensional biomineralization. Biomaterials 32, 2695–2703 (2011).
Lambertsen, R. H. Internal mechanism of rorqual feeding. J. Mammal. 64, 76–88 (1983).
Dimond, A. E. Pressure and flow relations in vascular bundles of the tomato plant. Plant Physiol. 41, 119–131 (1966).
Lee, M. K. et al. Glacier moraine formation-mimicking colloidal particle assembly in microchanneled, bioactive hydrogel for guided vascular network construction. Adv. Healthcare Mater. 4, 195–201 (2015).
Van Stroe-Biezen, S. A. M., Everaerts, F. M., Janssen, L. J. J. & Tacken, R. A. Diffusion coefficients of oxygen, hydrogen peroxide and glucose in a hydrogel. Anal. Chim. Acta. 273, 553–560 (1993).
Pattappa, G., Heywood, H. K., de Bruijn, J. D. & Lee, D. A. The metabolism of human mesenchymal stem cells during proliferation and differentiation. J. Cell. Physiol. 226, 2562–2570 (2011).
Jorjani, P. & Ozturk, S. S. Effects of cell density and temperature on oxygen consumption rate for different mammalian cell lines. Biotechnol. Bioeng. 64, 349–356 (1999).
Lee, M. K. & Lee, J. A nano-frost array technique to prepare nanoporous PVDF membranes. Nanoscale 6, 8642–8648 (2014).
Lee, M. K. & Lee, J. Fabrication of ferroelectric polymer nanocrystals with tunable morphologies. Cryst. Growth Des. 13, 671–678 (2013).
Rowley, J. A. & Mooney, D. J. Alginate type and RGD density control myoblast phenotype. J. Biomed. Mat. Res. 60, 217–223 (2002).
Sanchez-Ramos, J. et al. Adult bone marrow stromal cells differentiate into neural cells in vitro. Exp. Neurol. 164, 247–256 (2000).
Bossolasco, P. et al. Neuro-glial differentiation of human bone marrow stem cells in vitro. Exp. Neurol. 193, 312–325 (2005).
Kopen, G. C., Prockop, D. J. & Phinney, D. G. Marrow stromal cells migrate throughout forebrain and cerebellum and they differentiate into astrocytes after injection intoneonatal mouse brains. Proc. Natl. Acad. Sci. USA 96, 10711–10716 (1999).
Hofstetter, C. P. et al. Marrow stromal cells from guiding strands in the injured spinal cord and promote recovery. Proc. Natl. Acad. Sci. USA 99, 2199–2204 (2002).
Discher, D. E., Janmey, P. & Wang, Y.-L. Tissue cells feel and respond to the stiffness of their substrate. Science 310, 1139–1143 (2005).
Cha, C., Kim, S. R., Jin, Y.-S. & Kong, H. J. Tuning structural durability of yeast-encapsulating alginategel beads with interpenetrating networks for sustained bioethanol production. Biotech. Bioeng. 109, 63–73 (2012).
Acknowledgements
This work was supported by National Science Foundation (CAREER: DMR-0847253, CBET-1403491 and STC-EBICS Grant CBET-0939511 to H.K.) and University Illinois at Urbana-Champaign research board. This work was also supported by National Research Foundation grant funded by the Korean Ministry of Science, ICT and Future Planning (No. 2012-014107 & Engineering Research Center of Excellence Program NRF-2014-009799 to J.L.). The authors wish to thank Mr. Frank Rauh (FMC BioPolymer) for the supply of alginate.
Author information
Authors and Affiliations
Contributions
M.K.L., J.L. and H.K. designed research; M.K.L. and M.H.R. performed research; Computational simulation was performed by K.B.; M.K.L. and H.K. wrote the main manuscript text. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Supplementary Information
Supplementary Information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Lee, M., Rich, M., Baek, K. et al. Bioinspired Tuning of Hydrogel Permeability-Rigidity Dependency for 3D Cell Culture. Sci Rep 5, 8948 (2015). https://doi.org/10.1038/srep08948
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep08948