Abstract
Atomically thin semiconducting transition-metal dichalcogenides have been attracting lots of attentions, particularly, molybdenum disulfide (MoS2) monolayers show promising applications in field effect transistors, optoelectronics and valleytronics. However, the controlled synthesis of highly crystalline MoS2 remain a challenge especially the systematic approach to manipulate its structure and morphology. Herein, we report a method for controlled synthesis of highly crystalline MoS2 by using chemical vapor deposition method with carbonaceous materials as growth promoter. A uniform and highly crystalline MoS2 monolayer with the grain size close to 40 μm was achieved. Furthermore, we extend the method to the manipulation of MoS2 morphology, flower-shape vertical grown MoS2 layers were obtained on growth promoting substrates. This simple approach allows an easy access of highly crystalline MoS2 layers with morphology tuned in a controllable manner. Moreover, the flower-shape MoS2 grown on graphene oxide film used as an anode material for lithium-ion batteries showed excellent electrochemical performance.
Similar content being viewed by others
Introduction
Direct bandgap semiconducting transition metal dichalcogenide (TMD) monolayers are attractive for optoelectronics and energy harvesting1,2. Their high carrier mobility3, excellent on-off ratio4 and good bendability5 are promising for future flexible and low-power consumer electronics5,6. The fundamental studies on their electronic structures and valley-spin relations are also emerging7,8. Being a member of the TMDs family, molybdenum disulfide (MoS2) has already attracted considerable attention for its great potential in the fields of hydrogen evolution reaction (HER)9,10, bio-sensing11,12 and energy storage13,14,15. Recently, it has been demonstrated that ultra-thin MoS2 crystals with a typical thickness of ~0.65 nm holds even more significant promise in electronics4,16,17 and optoelectronics7,18,19,20,21,22.
Given the great promises hold, it is highly desirable to develop a scalable method to obtain large-area and high quality TMD monolayers. On the other hand, controlling the surface structure of MoS2 layers at the atomic scale is also critical for their successful implementation in each applications. For example, large specific surface areas are preferred for the energy storage application13,14. For the application of HER, only the edge sites of MoS2 are catalytically active, which require the controllable synthesis of MoS2 layers with abundant exposed edge sites10,23. Recently, chemical vapor deposition (CVD) method has led towards high-quality TMD layers with scalable size, controllable thickness and excellent electronic properties. Several groups have made remarkable progress in MoS2 synthesis8,24,25,26. Among the various approaches for MoS2 synthesis, those using MoO3 and sulfur powder as solid state precursors become dominant26,27,28,29,30, which is due to the simplified process and high yield of monolayers.
However, it is more challenging to grow single crystalline monolayer MoS2 thin film by CVD method comparing to other 2D materials synthesis such as graphene31,32 and boron nitride33,34, where catalyst were used to control the geometry, thickness and crystallinity. In contrast, the growth of MoS2 by CVD does not involve any catalysts35,36 and the growth of MoS2 is very sensitive to the substrate treatment prior to the growth18,22. Previous reports demonstrate nucleation of MoS2 can be facilitated by seeding the substrate with graphene-like species29,30,37. Meanwhile Najmaei et al. have shown that the MoS2 crystallines commonly nucleate on the step edges during growth without the present of seeding molecules28. Recently, Van der Zande et al. proved that large MoS2 crystalline islands can be obtained by using ultraclean substrates and fresh precursors and neither seeding molecules nor step-edge were used to promote the nucleation of MoS227. It was suggested that the MoS2 growth normally follows an analogous layer-plus-island (or Stranski-Krastanov) growth mode8. The Stranski-Krastanov mode is a two-step process: initially, monolayer MoS2 domains gather and interconnect with each other till the full coverage of monolayer is nearly completed. Beyond the critical layer number (1 for MoS2), the growth of MoS2 continues through the nucleation and coalescence of MoS2 nanoparticles or few layers islands8. In other words, the thermodynamics favors the basal plane growth, which limits the tunability of surface structure.
Nevertheless, the widely used method for MoS2 synthesis is based on the direct chemical vapor phase reaction of MoO3 by S gas in which the MoOx vapor generated from MoO3 powder reacts with sulfur vapor at elevated temperatures to form monolayer MoS2 on the collecting substrates26,29. Thus, it is common to obtain molybdenum oxide microcrystals byproducts since the reduction of MoO3 also produce MoO2 crystals under similar growth condition38. MoO3 was selected by Li et al. as an precursor for MoS2 growth on the basis that it has an evaporation temperature of ~700 °C26. However, the growth dynamics of MoO3-x and S are still not fully understood. It has been suggested in literatures39,40 that there are two channels for MoO3-x to react with S, one is it adsorb and diffuse on the substrate, reacting with S to form MoS2; the other is forming MoS2 clusters in vapour phase and crystalize on substrate. Both these two channels require the forming of vapour phase MoO3-x; and the growth temperature ranging from 530 °C to 850 °C. Thus far, it is demanding to have a better understanding of the growth mechanism and further develop a method which is capable of producing large monolayer MoS2 crystals, preventing the formation of MoO2 byproducts, meanwhile controlling the surface structure of MoS2 layers at the atomic scale.
Herein, we engineer the reduction process of MoO3 precursor by carbon based materials. In a typical synthesis, the solid state precursor of MoO3 powder is covered by a piece of carbon cloth. The carbon cloth is chosen simply due to its thermal stability, good mechanical property and micro porous structure. MoO3 powder can be thermally evaporated and only the gas phase MoO3 can pass through the opening of woven micro carbon fibers and it is then reduced by sulfur vapor at 650 to 700 °C. It was found that carbon can help reducing MoO3 and large MoO2 crystals can be trapped by the carbon cloth which effectively prevents the co-deposition of MoO2 and MoS2 on the collecting substrates. Finally, continuous large-area MoS2 thin films was successfully grown on substrate. The synthesized MoS2 layers are in a well-defined triangular shape with a typical lateral size ~40 μm. We further investigated the effects of carbonaceous promoter in the growth of MoS2 on various substrates. By simply replacing the SiO2/Si substrates with GO film or GO flakes, few-layer MoS2 preferentially form on the surface of GO under the same growth condition. The results suggest, the growth of MoS2 is very sensitive to the substrate treatment and carbon based materials can significantly promote the growth rate and yield of MoS2, which is due to the assisted reduction of MoO3 by carbon.
This work elucidates how morphological control of MoS2 at the nanoscale can be achieved by carbonaceous promoter. The surface morphology engineering of MoS2 layers enables new opportunities for enhancing surface properties for catalysis, energy storage and other important technological applications. As a proof-of-concept, the MoS2/GO composites were used as electrode materials to demonstrate its application in lithium ion batteries (LIBs). The surface structure engineering of MoS2/GO provides highly efficient pathways for both electronic and Li ion exchange during the charge/discharge cycles of the battery, which allows the composite to be directly used as working electrode and assembled into a coin cell without adding any conductive or binder materials. A remarkably high specific capacity (i.e., > 1000 mAh g−1) was achieved at the current density of 100 mA g−1, which is much higher than theoretical value for either GO or MoS2 alone (~566 and ~670 mAh g−1, respectively). The MoS2/GO composites also show an outstanding high-rate charge/discharge performance. Even at a very high current density of 1000 mA g−1, the composite electrode can still deliver a capacity of 776 mAh g−1 after 500 cycles. The reversible capacity only slightly decreases to 727 mAh g−1 after an additional 440 cycles under 2000 mA g−1. The high rate capability can be attributed to the unique nano-architecture engineering of MoS2, which provides structural stability and transport advantages for both electrons and lithium ions.
Materials and Methods
Monolayer CVD-MoS2 growth
CVD-MoS2 was prepared using chemical vapor deposition method with carbon based materials as a growth promoter. High-crystal-quality MoS2 can be grown on a silicon substrate with 300 nm SiO2 layer on top inside a hot-wall horizontal tube furnace. To be brief, the MoS2 films were synthesized using high purity MoO3 (99%, Aldrich) and S powder (99.5, Sigma-Aldrich) as precursors. The precursors were placed in two separated Al2O3 crucibles and the substrates were placed on the downstream side of the Ar carrying gas. A piece of carbon cloth was put on top of MoO3 powder for better growth control. The growth chamber was firstly heated to 105 °C with Ar flow rate of 1000 sccm, this step helps to remove the oxygen and moistures in the chamber. After that, the temperature was further increase to 700 °C with a heating rate of 15 °C/min. MoS2 monolayer in a triangle shape were obtained by annealing at 700 °C for 10 min followed by a naturally cooling process to room temperature Ar flow rate was kept at 10 sccm during MoS2 growth.
Flower shape MoS2 growth
Before the CVD synthesis, 1 mg/ml Graphene oxide (GO) dispersion in water was obtained after 30 min probe sonication of GO flakes (Graphene Supermarket, USA.) in deionized water (DI Water). The 300 W probe sonicator was set at 30% amplitude with alternating pulse. GO coated Si substrate was prepared by drop casting GO dispersion on a piece of cleaned SiO2/Si substrates and gently blow dried using N2 gas. Self-supporting GO thin film was obtained by vacuum filtration of GO dispersion with a polymer filter membranes (pore size 0.02 um, GE Whatman, USA). The filtration membrane was further removed by dissolving it in hot Acetone solution (at ~80 °C). The GO substrates were carried into the growth chamber after baking on hot plate at 90 °C for 1 hour to remove organic solvent and water. The growth condition was kept the same as monolayer MoS2 synthesis.
Chemicals and precursors
Graphene oxide powder was purchased from Graphene Supermarket, Calverton, NY, USA. MoO3 (purity 99%) and S powder (purity 99.5%) powder purchased from Sigma-Aldrich Co. (Singapore) were directly used for MoS2 synthesis without further purification. Carbon cloth was purchased from Hesen Shanghai Co., Ltd, China.
MoS2/GO transfer for TEM characterization
The CVD synthesized MoS2/GO composite was transferred by coating the film with a thin layer (~100 nm) of Poly[methylmethacrylate] (PMMA). After etching the underlying SiO2/Si substrates with NaOH aquariums (with a concentration of 3 M) at 80 °C, the PMMA/ MoS2/GO film was transferred to DI water and was suspended on the surface of water to remove the etchant residue for several hours. Subsequently, the film can be transferred to any substrate or TEM grids for analysis and characterization. Finally, the top layer of PMMA can be removed by acetone or by directly annealing the samples in an Ar and H2 atmosphere at 450 °C for 2 hours.
Raman measurements
The Raman measurements were carried out using a WITec alpha 300 confocal Raman microscope. The Raman spectra presented in this paper were collected using a 532 nm solid-state laser for excitation with the beam focused by a 100X objective lens. The laser beam diameter on sample is around 500 nm. Scanning electron microscopy (SEM) was performed on a field emission SEM (FESEM) instrument (JSM-7600F, Japan). A field-emission transmission electron microscope (JEOL JEM-2100F, operated at 200 keV), equipped with an energy dispersive spectrometer (EDS) was used to obtain the information of the microstructures and the chemical compositions.
Electrochemical measurement
The electrochemical performance of MoS2/GO nanocomposites electrode was measured with a half-cell lithium ion battery (LIBs) configuration. The 2032 coin-type cells were assembled in an argon-filled glove-box with both the moisture and oxygen level less than 0.5 ppm. MoS2/GO composites were directly used as cathodes. For control samples, the working electrode materials of GO and MoS2 were prepared by mix GO and MoS2 powders with a certain weight percentage in solution phase and then freeze-dried to form a self-supporting membrane. Lithium sheet was used as anodes and 1 M LiPF6 in a 1/1 (volume ratio) mixture of ethylene carbonate (EC)/dimethyl carbonate (DMC) as electrolyte. Celgard® 2400 was used as the separator of the battery. The cells were tested on a NEWARE multi-channel battery test system with galvanostatic charge and discharge in the voltage range between 0.01 and 3.0 V vs. Li/Li+ at various current density at room temperature. The cyclic Voltammetry (CV) and electrochemical impedance spectroscopy (EIS) were tested on an electrochemical workstation (VMP3, Bio-Logic).
Results and Discussion
Effect of carbon based materials on monolayer MoS2 growth
A schematically illustration of the experimental set-up used for MoS2 synthesis is presented in Fig. 1 (a). MoS2 monolayers were grown by CVD with solid MoO3 and S precursors. In contrast to previous reports, the MoO3 powder with a weight of ~15 mg was directly placed on a silicon wafer which is next to the collecting substrates for MoS2 growth. A piece of carbon cloth (thickness: 0.34 ± 0.02 mm, surface area ~50 mm2) was put on the top of MoO3 powder. Prior to the growth, argon gas was used to flush the quartz tube thoroughly in order to remove the oxygen and moistures. 10 sccm of argon was supplied during the synthesis of MoS2 monolayers, while the growth chamber was heated from room temperature to 700 °C with a temperature profile as shown in Fig. 1 (a).
Detailed growth procedure can be found in the method section. At such temperature, MoO3 powder evaporated and reacted with sulfur vapor to form a continuous MoS2 films and isolated triangular MoS2 domains can also be found at the edges along the film which are shown in the optical microscopy images (with different magnifications) of Fig. 1 (b), (c) and (d) where the MoS2 sheets were grown on the SiO2/Si substrate. The triangular shape of the crystallites reflects the 3-fold symmetry of MoS2 that suggests they are single-crystalline30,41. Similar to previous work, the monolayer MoS2 can be merged to form a large MoS2 sheet29 and among different growths the average size of MoS2 islands varies between 10 to 40 μm. The intensity of photoluminescence (PL) peak and the energy separation between the Raman A1g and E2g peaks have been found related to the number of MoS2 Layers42,43,44. Therefore, Raman and PL measurement were carried out to confirm the quality of the individual crystallites. Fig. 1 (e) and (f) show the PL intensity mapping and the corresponding intensity mapping of Raman peak of an isolated triangular MoS2 crystallite. Figure 1 (g) displays the typical spectra taken from the MoS2 crystallite that consisting both the Raman and PL peaks. The strong PL peak and high PL to Raman intensity ratio suggest the direct band gap photoluminescence. The inset figure in Fig. 1 (g) presents the Raman peak of monolayer MoS2, the E2g and A1g peaks locate at 385.8 and 403.8 cm−1, respectively with a peak distance of 18 cm−1. The small E2g and A1g peak distance suggests the monolayer nature of these MoS2 crystallites45,46.
We note that without the carbon cloth, triangular shape MoS2 can also be obtained but there will be few-layer MoS2 and/or MoO2 crystallites distributed among them, as shown in Supporting Data (Fig. S1). As a consequence, under our growth condition, carbon based materials play an important role in facilitating the monolayer MoS2 growth. It is worthy to mention that, recently reports demonstrated aromatic molecules are helpful for the nucleation of the MoS2 layers29,30. However, it is still controversial that a larger single layer MoS2 can be obtained by using carefully cleaned substrates27,28. In this study, the carbon cloth is separated from the collecting substrates and pre-annealed at 700 °C to exclude the influence of any impurities from the carbon cloth. It is generally believed that at elevated temperatures the MoOx vapor generated from MoO3 powder reacts with sulfur vapor and being sulfurized to form monolayer MoS2 on the collecting substrates, therefore the reduction of MoOx is a critical step for the MoS2 formation38.
Accordingly we further investigated the surface reaction of carbon cloth with MoOx during MoS2 synthesis. Figure 1 (h) and (i) show the Scanning Electron Microscope (SEM) images of the carbon cloth surface before and after the growth. The pristine carbon cloth is manufactured in bundles of thousands of tiny fibers and woven onto a fabric roll. After growth, the surface of carbon cloth facing the MoO3 precursor are fully covered by micro size flakes or large crystals, as displayed in Fig. 1 (j) and (k). Figure 1 (l) compares the Raman spectrums from carbon cloth before and after the CVD process. These micro crystals deposited on the carbon cloth surface show strong Raman peaks and the carbon peaks at around 1300 and 1600 cm−1 become comparatively weaker. According to the literature, the additional Raman peaks obtained after CVD process belongs to MoO247,48. However, there are no detectable MoS2 Raman peaks from carbon cloth.
The forming of MoO2 crystals on the surface of carbon cloth suggests carbon is more reductive under elevated temperature to react with vapor phase MoO3. In our experiments, the carbon cloth directly contacted with MoO3 powder, thus no sufficient sulfur vapor can penetrate through the carbon layer to react with the precursor underneath. In other words, the additional carbon layer helped to create an abrupt MoO3-x concentration change between the top and bottom layer of the carbon cloth. It is well know that the reduction of MoO3-x by sulfur can produce MoO2 and further sulfurization gives MoS2 layers27,29,30,37. Therefore, it is likely that during the growing process where the carbon layer provides a more steady and sustainable flow of MoO3-x (x>1) and results a more constant ratio of Mo and S to form stoichiometry MoS2 crystallites. The reduction capability of carbon cloth was also compared with other form of carbon such as well crystallized highly ordered pyrolytic graphite (HOPG). Our results suggest well crystallized carbon, such as HOPG is more inert in the reaction with MoO3 during the growth (See the Supporting Data). The Raman spectra in Fig. 1 (l) show a strong D band at around 1300 cm−1, which indicates the defective nature of carbon cloths. The defective nature of carbon cloth makes it more reactive and attractive for molybdenum source with a large interacting surface with MoO3-x. Thus these carbon fibers assist the reduction of MoO3-x for MoS2 growth with improved reactivity and efficiency.
Recently, Kong et al. reported vertically aligned MoS2 and molybdenum diselenide (MoSe2) layers can be produced by a rapid sulfurization/selenization process at 550 °C49. It is suggested that the formation of vertically aligned TMD layers is driven by a kinetic process. When the growth is limited by the diffusion of sulfur/selenium, due to the anisotropic structure of TMD layers, it is much faster for sulfur/selenium to diffuse along the van der Waals gaps. Therefore, the TMD layers naturally oriented perpendicular to the film, exposing van der Waals gaps for fast reactions49. The assisted reduction process of MoO3-x by carbon based materials is likely to alter the growth rate and thus provides a way to tune the surface structure of TMD layers.
In order to better understand the growth mechanism and further develop a method which is capable of engineering the surface structure of MoS2 layers in a controlled manner. Carbon based materials were deposited directly on the growth substrates to tune the local growth condition. Graphene oxide (GO) prepared by modified Hummers method is generally accepted as a defective form of carbon and GO flakes with abundant function groups also show similar Raman feature with the carbon cloth used in our study (See Supporting Data). Therefore, GO was chosen to reveal the reaction between carbon and MoO3-x and its effects on the crystallization of MoS2 crystallites. To investigate the growth mechanism and reveal the role of carbon promoter during MoS2 formation, GO dispersed in DI water was drop casted on cleaned Si wafer with 300 nm SiO2 top layer. The GO casted substrates were carried into CVD furnace and MoS2 growth was then carried out. Figure 2 (a), (b) and (c) show the optical image of GO coated SiO2/Si wafer after growth. The color contrast is due to the different layer thickness of deposited materials. Flakes with irregular shape can be found among the single layer MoS2. We chose a location that fully covered with MoS2 monolayer and GO flakes can be found distributed among the mono layer MoS2. The Raman measurement clearly shows the distribution of monolayer and few-layer MoS2. Spectrum in Fig. 2 (d) shows a typical comparison of PL and Raman peak intensity taken from an irregular shaped few layer MoS2 and its surrounding. Note that the Raman peak of GO becomes very weak after CVD synthesis. The mapping in Fig. 2 (e) and (f) displays the peak intensity distribution on the sample surface. Moreover, it is worthy to mention that for the typical growth, most of the SiO2/Si surface were covered with triangular monolayer MoS2 crystallites or MoS2 film. Meanwhile, all the MoS2 Raman peaks taken from the GO surface have a large E2g to A1g peak distance suggesting they are few-layers (see supporting information). These results are solid evidence that the GO tends to attract and promote MoS2 growth. We also noticed that without sulfur supply, monolayer GO is more reactive and can be totally etched away by MoO3 vapor (see supporting information) which also suggests the carbon MoO3 reduction reaction takes place during the growth.
Flower-shape MoS2 growth, characterization and application
Since it was reported that sulfurization process largely affects the layer orientations in the synthesized chalcogenide49,50,51. As discussed, at high temperatures, carbon can dramatically enhance the reduction of MoO3, thus promote the formation of MoO3-x (x>1) to react with sulfur vapor which further converts to MoS2 layers. Thereby under monolayer MoS2 growth condition, the introduction of additional carbon materials is likely to create a localized sulfur diffusion limited process for MoS2 growth. In order to investigate the effect of carbon on the layer orientations of synthesized chalcogenides, we intentionally apply more carbon based materials by utilizing filtrated GO thin film as the growth template and all the other growth conditions were kept unchanged. The as grown samples possess a dramatically different morphology as shown in Fig. 3 (a) and (b). Interestingly, the synthesized MoS2 layers tend to form in a micrometer flower shape as illustrated in Fig. 3 (c). Figure 3 (d) displays the energy-dispersive X-ray spectroscopy (EDS) mapping characterization, which confirms the chemical composition of the flower shape structure.
Further structural characterizations using transmission electron microscopy (TEM) provide additional insights into MoS2/GO composite film. Figure 4 shows the typical TEM images of MoS2/GO film. Figure 4 (a) displays a low magnification TEM image, where the MoS2 layers show a darker color contrast on GO thin film. Figure 4 (b) exhibits a high-resolution TEM (HRTEM) image taken along the edge part of these composites. Stripe-like grains with ~10 nm in length and several nanometers in width were found, however these grains are densely packed and overlapped with each other preventing an accurate lattice structure analysis. In Fig. 4 (c), the HRTEM image on a single grain reveals individual atomic planes ordered in the S–Mo–S sequence to form each layer. The carbon surface with a lighter color contrast under TEM was confirmed to be graphene by performing the selected area electron diffraction (SEAD) and the FFT confirms the hexagonal arraignment of S-Mo-S atoms. As shown in Fig. 4 (d), both the HRTEM image and fast Fourier transform (FFT) pattern reveal that MoS2 flakes grown on GO retain the crystal symmetry with the lattice constant ~0.32 nm. Both of the EDS and TEM analysis suggests the MoS2 layers tend to form a layered flower-shape structure on GO substrates compared to monolayer in plan growth on SiO2/Si substrates. The morphology change is likely due to the promoted conversion rate of MoO3-x, where the chemical conversion occurs much faster than the diffusion of sulfur gas into the film, forcing the MoS2 layers naturally oriented perpendicular to the growth substrates, exposing van der Waals gaps for fast reaction49.
As a proof-of-concept application, the electrochemical property of the MoS2/GO composite as an anode material of a Lithium ion battery (LIB) was further investigated by galvanostatic discharge/charge and cyclic voltammetry (CV) measurements. The measurement was based on a half-cell configuration as shown in the supporting materials. Figure 5 (a) illustrates the first, second and third discharge/charge voltage profiles of the flower shape MoS2/GO composite electrode grown by CVD method. The test were carried out in the voltage range from 0.01 to 3 V (vs. Li/Li+). The initial discharge and charge capacities were measured to be 1612 and 1149 mAh g−1, respectively, with a corresponding initial Coulombic efficiency of 71.3%. The irreversible capacity loss for the first cycle could be mainly attributed to the electrolyte decomposition and inevitable formation of the solid electrolyte interface (SEI), which are commonly observed for nanosized anode materials13. The second and third cycles show a decreased capacity but with a much higher Coulombic efficiency of 93.8% and 95.3%, respectively. In the first discharge process, the initial discharge capacity between 2.0 to 1.5 V can be attributed to the reaction of residual carbon surface functional group and the lithium insertion to MoS2 which forms LixMoS2. The following capacity between 1.0 to 0.5 V can be attributed to the conversion reaction process of MoS2, where the metal sulfide reacts with lithium ions forming metal nanoparticles and insoluble Li2S matrix, MoS2+4Li++4e−→Mo+2Li2S14. The formation of a SEI and the gel-like polymeric layer on the surface of the active materials contribute to the sloping plateau at the lower voltage region (< 0.5 V). In the charge process, the plateau at ~1.3 V and the sloping region above 2.2 V can be attributed to the reverse reaction process, where oxidation of Mo particles to MoS2 and the conversion of Li2S to S and Li+ occur14,52,53. It is noted that the lithium extraction from the LixMoS2 phase should also be considered.1
To further clarify the electrochemical process of MoS2/GO composite, cyclic voltammogram (CV) measurements of the first three cycles in the voltage range of 0.01-3.0 V at a scan rate of 0.1 mV s−1 were carried out as shown in Fig. 5 (b). In the initial cycle, two reduction peaks at 1.1 and 0.5 V were observed, which can be attributed to the formation of LixMoS2 and the conversion reaction that leading to Mo metal nanoparticles embedded in a Li2S matrix. In the reverse anodic scan, the oxidation peak at ~ 1.4 V can be partly attributed to the oxidation of Mo to MoS2 and the peak at ~ 2.3 V can be assigned to the oxidation of Li2S to S. In the 2nd CV scan, the reduction peak at 0.9 V can be attributed to the Li insertion into MoS2 lattice to form LixMoS2. The weak reduction peak at ca. 2.1 V indicates the formation of Li2S. In the anodic sweeps, the oxidation peaks at 1.4 V and 2.3 V correspond to the extraction of Li+ from LixMoS2 lattice and the oxidation of Li2S, respectively. The results are in agreement with the above lithiation and delithiation profiles.
The MoS2/GO composites also possess outstanding high-rate performance. Figure 5 (c) shows cycle performance of the composite electrodes under high current density of 1000 and 2000 mA g−1. The initial discharge and reversible capacities are ca. 1484 and 779 mAh g−1, respectively, at 1000 mA g−1, which retain ca. 68% of capacities at 100 mA g−1 (see supporting information). After the initial 36 cycles, the specific capacity slightly decreased to 542 mAh g−1. However, a subsequent increase of specific capacity was observed for MoS2/GO composites, which should be attributed to the gradual activation of the electrode during lithiation and delithiation and a formation of gel-like film resulting from decomposition of the electrolyte at a low voltage. Due to the vertical structure of MoS2, the Li+ could get sufficient contact with the atomic layers of MoS2. As a result, excellent electrochemical performance was achieved for vertical grown MoS2 and GO film. The reversible capacity can retain 776 mAh g−1 even after a long cycling period of 500 cycles. When the current density increases to 2000 mA g−1, the reversible capacity after 940 cycles can still retain ~727 mAh g−1, which is about 94% of that at 1000 mA g−1.
The MoS2/GO composites electrodes were further investigated by the electrochemical impedance spectroscopy measurement where the Nyquist plots of MoS2/GO composite and MoS2:GO (commercial MoS2 and GO powder mixed in solution phase followed by freeze-dried to form a self-supporting film) powder blended electrode after 10 discharge/charge activation cycles are shown in Fig. 5 (d). The corresponding equivalent circuit is shown in the inset of Fig. 5 (d). The measurement indicates that the film resistance (Rf) and charge-transfer resistance (Rct) of MoS2/GO are ca. 27 and 112 Ω, respectively. Both the Rf (106 Ω) and Rct (130 Ω) of MoS2:GO mixture are much larger than those of MoS2/GO electrode. Since the MoS2/GO composites electrode possesses lower charge-transfer resistance, the charge transfer is lower than that of MoS2: GO blends. The significantly improved charge capacity of MoS2/GO composites could be attributed to the unique nanostructure of MoS2 sheets on the surface of GO film. The vertical structured MoS2 with extruding layers on GO has a much larger surface area, which provide more active sites during charging-discharging processes. In addition, lithium ions can be inserted/extracted into/out-of the vertical MoS2 flakes from both sides of MoS2, leading to a quick lithiation and delithiation process even under a large current density, as shown in the schematic diagram in Fig. 5 (e). Therefore, the MoS2/GO composite electrodes show excellent rate performance.
Conclusion
In conclusion, we propose a carbon promoted process to synthesize large-area and highly crystalline MoS2 thin layers. The addition of carbon based materials during the high-temperature annealing drastically enhances the reduction of MoO3 vapor, as evidenced by various spectroscopic and microscopic characterizations including Raman, PL, TEM and SAED. In particular, using GO thin film as the growth template results in an edge-terminated layered chalcogenide films forming in a flower shaped MoS2/GO composite. These MoS2 thin layers tend to orientate perpendicular to the growth substrate due to the sulfur diffusion limited process. The synthetic approach is simple and scalable, providing not only an easy but also efficient way to manipulate the structure of chalcogenide films. The unique structure paves the way to use the edges of layered materials more effectively.
Additional Information
How to cite this article: Shi, Y. et al. MoS2 Surface Structure Tailoring via Carbonaceous Promoter. Sci. Rep. 5, 10378; doi: 10.1038/srep10378 (2015).
Change history
20 January 2016
A correction has been published and is appended to both the HTML and PDF versions of this paper. The error has not been fixed in the paper.
References
Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat Chem 5, 263–275 (2013).
Huang, X., Zeng, Z. & Zhang, H. Metal dichalcogenide nanosheets: preparation, properties and applications. Chem. Soc. Rev. 42, 1934–1946 (2013).
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nat Nano 6, 147–150 (2011).
Wang, H. et al. Integrated Circuits Based on Bilayer MoS2 Transistors. Nano Lett. 12, 4674–4680 (2012).
Lee, G.-H. et al. Flexible and Transparent MoS2 Field-Effect Transistors on Hexagonal Boron Nitride-Graphene Heterostructures. ACS Nano 7, 7931–7936 (2013).
Pu, J. et al. Highly Flexible MoS2 Thin-Film Transistors with Ion Gel Dielectrics. Nano Lett. 12, 4013–4017 (2012).
Mai, C. et al. Many-Body Effects in Valleytronics: Direct Measurement of Valley Lifetimes in Single-Layer MoS2 . Nano Lett. 14, 202–206 (2013).
Ji, Q. et al. Epitaxial Monolayer MoS2 on Mica with Novel Photoluminescence. Nano Lett. 13, 3870–3877 (2013).
Chang, Y.-H. et al. Three-Dimensional Molybdenum Sulfide Sponges for Electrocatalytic Water Splitting. Small 10, 895–900 (2014).
Chang, Y.-H. et al. Highly Efficient Electrocatalytic Hydrogen Production by MoSx Grown on Graphene-Protected 3D Ni Foams. Adv. Mater. 25, 756–760 (2013).
Wang, L. et al. Functionalized MoS2 Nanosheet-Based Field-Effect Biosensor for Label-Free Sensitive Detection of Cancer Marker Proteins in Solution. Small 10, 1101–1105 (2014).
Loan, P. T. K. et al. Graphene/MoS2 Heterostructures for Ultrasensitive Detection of DNA Hybridisation. Adv. Mater. 26, 4838–4844 (2014).
Cao, X. et al. Preparation of MoS2-Coated Three-Dimensional Graphene Networks for High-Performance Anode Material in Lithium-Ion Batteries. Small 9, 3433–3438 (2013).
Shi, Y. et al. Self-assembly of hierarchical MoSx/CNT nanocomposites (2<x<3): towards high performance anode materials for lithium ion batteries. Sci. Rep. 3 (2013).
Wang, Y. et al. Pre-lithiation of onion-like carbon/MoS2 nano-urchin anodes for high-performance rechargeable lithium ion batteries. Nanoscale 6, 8884–8890 (2014).
Salvatore, G. A. et al. Fabrication and Transfer of Flexible Few-Layers MoS2 Thin Film Transistors to Any Arbitrary Substrate. ACS Nano 7, 8809–8815 (2013).
Shi, Y. et al. Selective Decoration of Au Nanoparticles on Monolayer MoS2 Single Crystals. Sci. Rep . 3 (2013).
Roy, K. et al. Graphene-MoS2 hybrid structures for multifunctional photoresponsive memory devices. Nat Nano 8, 826–830 (2013).
Zhang, W. et al. Ultrahigh-Gain Photodetectors Based on Atomically Thin Graphene-MoS2 Heterostructures. Sci. Rep . 4 (2014).
Wu, S. et al. Vapor–Solid Growth of High Optical Quality MoS2 Monolayers with Near-Unity Valley Polarization. ACS Nano 7, 2768–2772 (2013).
Su, S.-H. et al. Band Gap-Tunable Molybdenum Sulfide Selenide Monolayer Alloy. Small 10, 2589–2594 (2014).
Mertens, J. et al. Excitons in a mirror: Formation of “optical bilayers” using MoS2 monolayers on gold substrates. Appl. Phys. Lett. 104, - (2014).
Kibsgaard, J., Chen, Z., Reinecke, B. N. & Jaramillo, T. F. Engineering the surface structure of MoS2 to preferentially expose active edge sites for electrocatalysis. Nat Mater 11, 963–969 (2012).
Zhan, Y., Liu, Z., Najmaei, S., Ajayan, P. M. & Lou, J. Large-Area Vapor-Phase Growth and Characterization of MoS2 Atomic Layers on a SiO2 Substrate. Small 8, 966–971 (2012).
Shi, Y. et al. van der Waals Epitaxy of MoS2 Layers Using Graphene As Growth Templates. Nano Lett. 12, 2784–2791 (2012).
Lin, Y.-C. et al. Wafer-scale MoS2 thin layers prepared by MoO3 sulfurization. Nanoscale 4, 6637–6641 (2012).
van der Zande, A. M. et al. Grains and grain boundaries in highly crystalline monolayer molybdenum disulphide. Nat Mater 12, 554–561 (2013).
Najmaei, S. et al. Vapour phase growth and grain boundary structure of molybdenum disulphide atomic layers. Nat Mater 12, 754–759 (2013).
Lee, Y.-H. et al. Synthesis of Large-Area MoS2 Atomic Layers with Chemical Vapor Deposition. Adv. Mater. 24, 2320–2325 (2012).
Ling, X. et al. Role of the Seeding Promoter in MoS2 Growth by Chemical Vapor Deposition. Nano Lett. 14, 464–472 (2014).
Reina, A. et al. Large Area, Few-Layer Graphene Films on Arbitrary Substrates by Chemical Vapor Deposition. Nano Lett. 9, 30–35 (2008).
Li, X. et al. Large-Area Graphene Single Crystals Grown by Low-Pressure Chemical Vapor Deposition of Methane on Copper. J. Am. Chem. Soc. 133, 2816–2819 (2011).
Shi, Y. et al. Synthesis of Few-Layer Hexagonal Boron Nitride Thin Film by Chemical Vapor Deposition. Nano Lett. 10, 4134–4139 (2010).
Kim, K. K. et al. Synthesis of Monolayer Hexagonal Boron Nitride on Cu Foil Using Chemical Vapor Deposition. Nano Lett. 12, 161–166 (2011).
Liu, K.-K. et al. Growth of Large-Area and Highly Crystalline MoS2 Thin Layers on Insulating Substrates. Nano Lett. 12, 1538–1544 (2012).
Liu, K.-K. et al. Chemical Vapor Deposited MoS2 Thin Layers and Their Applications. ECS Transactions 50, 61–63 (2013).
Lee, Y.-H. et al. Synthesis and Transfer of Single-Layer Transition Metal Disulfides on Diverse Surfaces. Nano Lett. 13, 1852–1857 (2013).
Wang, X., Feng, H., Wu, Y. & Jiao, L. Controlled Synthesis of Highly Crystalline MoS2 Flakes by Chemical Vapor Deposition. J. Am. Chem. Soc. 135, 5304–5307 (2013).
Ji, Q., Zhang, Y., Zhang, Y. & Liu, Z. Chemical vapour deposition of group-VIB metal dichalcogenide monolayers: engineered substrates from amorphous to single crystalline. Chem. Soc. Rev., doi: 10.1039/C1034cs00258j (2015).
Shi, Y., Li, H. & Li, L.-J. Recent advances in controlled synthesis of two-dimensional transition metal dichalcogenides via vapour deposition techniques. Chem. Soc. Rev., doi: 10.1039/c1034cs00256c (2015).
Schmidt, H. et al. Transport Properties of Monolayer MoS2 Grown by Chemical Vapor Deposition. Nano Lett. 14, 1909–1913 (2014).
Eda, G. et al. Photoluminescence from Chemically Exfoliated MoS2 . Nano Lett. 11, 5111–5116 (2011).
Splendiani, A. et al. Emerging Photoluminescence in Monolayer MoS2 . Nano Lett. 10, 1271–1275 (2010).
Li, H. et al. From Bulk to Monolayer MoS2: Evolution of Raman Scattering. Adv. Funct. Mater. 22, 1385–1390 (2012).
Lee, C. et al. Anomalous Lattice Vibrations of Single- and Few-Layer MoS2 . ACS Nano 4, 2695–2700 (2010).
Li, S.-L. et al. Quantitative Raman Spectrum and Reliable Thickness Identification for Atomic Layers on Insulating Substrates. ACS Nano 6, 7381–7388 (2012).
Camacho-López, M. A. et al. Micro-Raman study of the m-MoO2 to α-MoO3 transformation induced by cw-laser irradiation. Opt. Mater. 33, 480–484 (2011).
Dieterle, M. & Mestl, G. Raman spectroscopy of molybdenum oxides Part II. Resonance Raman spectroscopic characterization of the molybdenum oxides Mo4O11 and MoO2 . PCCP 4, 822–826 (2002).
Kong, D. et al. Synthesis of MoS2 and MoSe2 Films with Vertically Aligned Layers. Nano Lett. 13, 1341–1347 (2013).
Jäger-Waldau, A., Lux-Steiner, M., Jäger-Waldau, R., Burkhardt, R. & Bucher, E. Composition and morphology of MoSe2 thin films. Thin Solid Films 189, 339–345 (1990).
Jäger-Waldau, A. et al. MoS2 thin films prepared by sulphurization. Appl. Surf. Sci. 65-66, 465–472 (1993).
Yang, L. et al. Hierarchical MoS2/Polyaniline Nanowires with Excellent Electrochemical Performance for Lithium-Ion Batteries. Adv. Mater. 25, 1180–1184 (2013).
Gong, Y. et al. A Bottom-Up Approach to Build 3D Architectures from Nanosheets for Superior Lithium Storage. Adv. Funct. Mater. 24, 125–130 (2014).
Acknowledgements
This work was supported by SUTD-MIT international design center (IDC) grant.
Author information
Authors and Affiliations
Contributions
Y. S. and H. Y. Y. designed research and analyzed data. Y. S., H. L. and J. I. W., carried out the material growth, synthesis and characterization. X. Z., H. S. and Y. W. performed the electrochemical measurement. H.Y. Y. supervised the project. All authors contributed to the writing and editing.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Shi, Y., Li, H., Wong, J. et al. MoS2 Surface Structure Tailoring via Carbonaceous Promoter. Sci Rep 5, 10378 (2015). https://doi.org/10.1038/srep10378
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep10378
This article is cited by
-
On the Tribological Properties of RGO–MoS2 Composites Surface Modified by Oleic Acid
Tribology Letters (2022)
-
Unlocking the potential of SnS2: Transition metal catalyzed utilization of reversible conversion and alloying reactions
Scientific Reports (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.